Home Fabrication of flexible SiO2 nanofibrous yarn via a conjugate electrospinning process
Article Open Access

Fabrication of flexible SiO2 nanofibrous yarn via a conjugate electrospinning process

  • Zhang Dai , Fangfang Yan , Mei Qin and Xu Yan EMAIL logo
Published/Copyright: October 27, 2020
Download Article (PDF)
Become an author with De Gruyter Brill
Submit Manuscript Author Information
e-Polymers
From the journal e-Polymers Volume 20 Issue 1

Abstract

Nowadays, different kinds of polymers, including ceramics, are electrospun into fibrous materials with different structures by electrospinning. Generally, the as-spun ceramic fibers are randomly oriented membranes and brittle without flexibility. Here, we report the fabrication of flexible SiO2 electrospun yarns using poly(vinyl alcohol) (PVA) as a template through a conjugate electrospinning process and calcination. It was found that the calcined as-spun fibers and yarns are obviously thinned with PVA component removal. Fourier transform infrared spectroscopy and energy-dispersive spectroscopy examinations suggested that the obtained yarn after calcination was SiO2 yarn. The SiO2 yarn showed good flexibility without cracking after 180° bending. The flexible ceramic yarn may have potential application in functional textiles.

Keywords: electrospinning; PVA; SiO2; flexibility; nanofibrous yarn

1 Introduction

Nowadays, electrospinning is believed to be an effective and simple method to produce continuous functional fibrous materials. By electrospinning, different kinds of materials are electrospun into fibers, including both organic (1,2) and inorganic (3,4), with diameters ranging from subnanometers to several micrometers (5). These organic and inorganic as-spun fibrous materials have been applied in various fields such as thermal insulated sponges (6,7), filtration (8,9,10), stimuli-responsive materials (11), food packing (12), precursor fibers for carbon nanofibers (13), reinforced composites (14,15), drug carriers (16,17,18), actuators (19), wound care (20,21,22,23), smart textiles (24,25,26), and battery relative materials (27,28,29), partly due to their porous and designable structures (30,31,32).

Generally, electrospun fibrous materials were collected as a nonwoven mesh with fibers randomly arranged. After a thorough research, it was found that the structures of the as-spun fiber and fibrous materials may play important roles in their properties and applications (30,31,32). Consequently, more and more attention was paid to control and design the structures of the electrospun fibrous materials by modifying the spinnerets and collectors (32,33,34,35). Specific to the electrospun yarns, “conjugate electrospinning,” with which two spinnerets are connected to two opposite polarity high-voltage supply, was found to be obtained through the electrospun fiber yarn in one step (36,37,38,39). By conjugate electrospinning, a series of polymer yarns as well as inorganic oxide arrays were fabricated (38,39,40). However, flexible inorganic yarns were rarely reported due to the complex process and brittleness.

Generally, the electrospun inorganic fibers are too brittle without flexibility. To overcome this disadvantage, researchers had found that using poly(vinyl alcohol) (PVA) or polyvinyl pyrrolidone (PVP) as template materials blended with inorganic salt gel could help to produce flexible ceramic nanofibrous mats via electrospinning process and calcination (41,42,43,44). Nevertheless, flexible inorganic nanofibrous yarn is still a challenge. This study reports on the fabrication of flexible SiO2 nanofibrous yarn via a conjugate electrospinning process and calcination. The morphology, chemical structures, thermal stability, and flexibility of the prepared yarns are examined.

2 Materials and methods

2.1 Materials

PVA (Mw = 66,000), tetraethylorthosilica (TEOS; 98%), phosphoric acid (H3PO4, 85 wt%), and N,N-dimethylformamide were purchased from Aladdin Co., Ltd (Shanghai, China). Deionized water was made in lab. All the chemicals were used as received without further purification.

2.2 Preparation of electrospinning solutions

PVA was dissolved in deionized water at 11 wt% within a water bath at 40°C for 4 h and then cooled naturally. TEOS, H3PO4, and deionized water were mixed with a weight composition of TEOS:H2O:H3PO4 = 1:1:0.02 according to previous studies (41,42) and stirred at room temperature for 4 h to form a uniform silica gel, as suggested in Figure 1a. Then, the prepared silica gel was dropped slowly into PVA solutions with a weight ratio of 1:1 and stirred for another 3 h to obtain the spinning precursor (41).

Figure 1 Schematic image of the preparation of spinning precursor (a), the fabrication of electrospun yarn by conjugate electrospinning process (b) and calcination of the as-spun yarn (c).
Figure 1

Schematic image of the preparation of spinning precursor (a), the fabrication of electrospun yarn by conjugate electrospinning process (b) and calcination of the as-spun yarn (c).

2.3 Fabrication of SiO2 yarn

To produce SiO2 yarn, conjugate electrospinning was processed with two parallel separated opposite-polarity high-voltage supply and vertically placed rotating trumpet collector as well as a rotating drum collector, as suggested in Figure 1b. During the conjugate electrospinning process, the prepared spinning precursor was loaded into two 5 mL syringes with a flat metal needle (18G, inner diameter: 0.9 mm), and then the two syringes were fixed onto the syringe pumps with a feed rate of 18 mL/min. The needles were connected to two opposite-polarity high-voltage supply (−30 kV–0 and 0–30 kV), respectively. The high voltages were set to be ±16 kV, respectively. The horizontal distance between the high voltage supply to the collector was set to be about 19 cm, and the vertical distance between the two collectors was about 20 cm. The electrospinning process was taken at an ambient temperature of 26°C and a humidity of 56%. The rotating drum collector was static, however, and the average collected yarn length was about 12 cm.

The collected PVA/silica yarns were placed in a ceramic ark and then put into the tube furnace. Afterward, the yarns were calcined in air with a heating rate of 3°C/min to 800°C and then kept at 800°C for 6 h to remove the organic components (41). After natural cooling, the inorganic SiO2 yarns could be obtained.

2.4 Characterization

The morphology and the energy-dispersive spectroscopy (EDS) of the electropsun yarn were examined by a scanning electron microscope (SEM, Phenom Pro; Thermo Fisher Scientific). The average diameter of the as-spun fiber was measured through a soft: nano-measurement of 1.2 with ten yarns. The Fourier transform infrared spectroscopy (FTIR) spectra were characterized by a Thermo Scientific Nicolet iS10 spectrometer. The mechanical property of the fabricated yarns (5 cm length) was examined by a universal testing machine (Instron 3352) with a speed of 0.02 mm/min. The weight–temperature relationships of the yarns were tested through a thermal gravimetric analyzer (TGA/DSC3+, Mettler Toledo).

3 Results

The morphology of the fabricated yarn is shown in Figure 2. As can be seen in Figure 2a, the electrospun PVA/silica yarn with an average diameter of 199.77 ± 13.86 mm and a linear density of 14.8 tex had a relative uniform twisted structure with a little hairiness. The enlarged image in Figure 2c suggested that the electrospun fibers generally oriented well and had average diameters of about 380 ± 76 nm. After calcination, the yarn showed a more tight and lightly twisted structure without hairiness, and the yarn diameter was reduced to 128.96 ± 2.88 mm with the fiber diameters of about 315 ± 110 nm, as suggested in Figure 2b and d. Based on ten samples, after calcination, the reduction rate of the yarn diameters was found to be about 35.1%, while the fiber diameter reduced to about 17.3%. The reduction rate of the fiber diameter was nearly half of that of the yarns. It could be imagined that both the neighborhood fibers reduced due to the organic component removal after calcination, and then the extra space was filled by the calcined fibers.

Figure 2 SEM images of the prepared yarns (a) PVA/silica, the PVA/silica fibers (c), the calcined yarn (b), the fibers in calcined yarn (d), as well as the EDS of the as-spun fibers before and after calcination (e and f), respectively.
Figure 2

SEM images of the prepared yarns (a) PVA/silica, the PVA/silica fibers (c), the calcined yarn (b), the fibers in calcined yarn (d), as well as the EDS of the as-spun fibers before and after calcination (e and f), respectively.

We also examined the elements in the as-spun yarns. As shown in Figure 2e, there are mainly three elements in the PVA/silica yarn: carbon, oxygen, and silicon, While, after calcination, there are mainly oxygen and silicon elements (Figure 2f), which indicates that the organic components were removed during the calcination process and then only pure SiO2 yarn remained.

Figure 3a shows the FTIR spectra of the prepared yarns before and after calcination. As can be seen from the spectra, the fabricated PVA/silica yarn showed typical PVA absorption peaks at 3,430 cm−1 (–OH), 2,930 cm−1 (–CH2), and 1,720 cm−1 (C–O). There were also Si–O–Si bond absorption peaks at 1,080 cm−1, 804 cm−1 as well as the Si–OH bond peaks at 963 cm−1, suggesting the presence of silica in the as-spun yarn. After calcination, the PVA absorption peaks disappeared; only Si–O–Si absorption peaks could be found at 1,130 and 804 cm−1, indicating the calcined yarn was SiO2 yarn. Figure 3b presents the weight–temperature curve of the prepared yarns before and after calcination. For the as-spun PVA/silica yarn, as the temperature increased the yarn weight was reduced accordingly due to the PVA melt volatilization. When the temperature exceeded 500°C, the weight reduction was weakened, since the organic components almost completely evaporated. For the calcined yarn, the weight did not seem to change as the temperature increased.

Figure 3 FTIR spectra (a) and the weight–temperature curve (b) of the PVA/silica yarns before and after calcination.
Figure 3

FTIR spectra (a) and the weight–temperature curve (b) of the PVA/silica yarns before and after calcination.

As presented in Figure 4a, the tensile property of the prepared yarns before and after calcination was tested. It was found that the PVA/silica yarn showed a maximum stress of 3.8 MPa and maximum elongation to 0.32%. Once the PVA/silica yarn was broken, a few continuous fibers still remained, as suggested in the left inset image in Figure 4a. However, after calcination, the tensile property was obviously reduced to 1.5 MPa stress and about 0.03% strain. Once the calcined yarn was broken, one can find all the fibers were broken. The decreased strength of the calcined yarn may result from the brittle individual SiO2 fiber. Since the organic component PVA was removed after calcination, the remaining SiO2 formed a fiber with extremely small-sized crystal grains (41). In some sense, the SiO2 fiber was not a continuous one. Consequently, its strength is weakened. Thankfully, the calcined yarn showed a certain flexibility, as suggested in Figure 4b–d. The calcined SiO2 yarn could be bent without cracking. After bending, it could recover to the original form. From the SEM images before and after ten-circle bending, only a few fibers were broken, while the whole still retained the yarn structure. The flexibility was believed to result from the one-dimensional (1D) silica nanofiber with extremely small-sized crystal grains (41).

Figure 4 The mechanical property of the prepared yarns (a) with inset images of the broken yarns before and after calcination and the flexibility of the calcined yarn (b–d) with inset images of bending before and after ten circles.
Figure 4

The mechanical property of the prepared yarns (a) with inset images of the broken yarns before and after calcination and the flexibility of the calcined yarn (b–d) with inset images of bending before and after ten circles.

4 Conclusions

In summary, we have successfully fabricated PVA/silica nanofiber yarn through a conjugate electrospinning process and then calcined the PVA/silica yarn in air at 800°C for 6 h to obtain the SiO2 nanofiber yarn. The diameter of the calcined SiO2 fiber and yarn was reduced up to 17.3 and 35.1%, respectively. The EDS, FTIR as well as the weight–temperature examination suggested that the calcined yarn was mainly SiO2 yarn. Although the calcined SiO2 yarn showed a significant weakness in the tensile property, it had good flexibility due to the extremely small size of the crystal grains in the nanofiber. Once the mechanical property was improved, the flexible inorganic yarns could be applied in the functional textiles.

Acknowledgments

This work was supported by the National Natural Science Foundation of China (51703102), the China Postdoctoral Science Foundation (2020M671998), State Key Laboratory of Bio-Fibers and Eco-Textiles (Qingdao University) No. ZKT35, and the Innovation and Entrepreneurship Training Program for College Students of Qingdao University (X2019110650078).

References

(1) Ding B. Functional polymeric micro/nano-fibrous materials. Acta Polym Sin. 2019;50(8):764–74. 10.11777/j.issn1000-3304.2019.19069.Search in Google Scholar

(2) Huang ZM, Zhang YZ, Kotaki M, Ramakrishna SA. Review on polymer nanofibers by electrospinning and their applications in nanocomposites. Compos Sci Technol. 2003;63(15):2223–53. 10.1016/S0266-3538(03)00178-7.Search in Google Scholar

(3) Wu H, Pan W, Lin D, Li H. Electrospinning of ceramic nanofibers: Fabrication, assembly and applications. J Adv Ceram. 2012;1(1):2:1–23. 10.1007/s40145-012-0002-4.Search in Google Scholar

(4) Ostermann R, Cravillon J, Weidmann C, Wiebcke M, Smarsly BM. Metal-organic framework nanofibers via electrospinning. Chem Commun. 2010;47(1):442–4. 10.1039/c0cc02271c.Search in Google Scholar PubMed

(5) Jian SJ, Zhu J, Jiang SH, Chen SL, Fang H, Song YH, et al. Nanofibers with diameter below one nanometer from electrospinning. RSC Adv. 2018;8(9):4794–802. 10.1039/C7RA13444D.Search in Google Scholar

(6) Jiang S, Chen Y, Duan G, Mei C, Greiner A, Agarwal S, et al. High-density fibrous polyimide sponges with superior mechanical and thermal properties. ACS Appl Mater Inter. 2020;12(16):19006–14. 10.1021/acsami.0c02004.Search in Google Scholar PubMed

(7) Jiang SH, Helfricht N, Papastavrou G, Greiner A, Agarwal S. Low‐density self‐assembled poly(n-isopropyl acrylamide) sponges with ultrahigh and extremely fast water uptake and release. Macromol Rapid Commun. 2018;39(8):1700838. 10.1002/marc.201700838.Search in Google Scholar PubMed

(8) Pu Y, Yang X, Zhang Y, Li L, Xie Y, He B, et al. Fabrication and characterization of highly oriented composite nanofibers with excellent mechanical strength and thermal stability. Macromol Mater Eng. 2020;305:1900691. 10.1002/mame.201900691.Search in Google Scholar

(9) Yang X, Pu Y, Zhang Y, Liu X, Li J, Yuan D, et al. Multifunctional composite membrane based on BaTiO3@PU/PSA nanofibers for high-efficiency PM2.5 removal. J Hazard Mater. 2020;391:122254. 10.1016/j.jhazmat.2020.122254.Search in Google Scholar PubMed

(10) Wang N, Zhai Y, Yang Y, Yang X, Zhu Z. Electrostatic assembly of superwetting porous nanofibrous membrane toward oil-in-water microemulsion separation. Chem Eng J. 2020;354:463–72. 10.1016/j.cej.2018.08.019.Search in Google Scholar

(11) Molnar K, Jedlovszky-Hajdu A, Zrinyi M, Jiang SH, Agarwal S. Poly(amino acid)-based gel fibers with ph responsivity by coaxial reactive electrospinning. Macromol Rapid Commun. 2017;38(14):1700147. 10.1002/marc.201700147.Search in Google Scholar PubMed

(12) Zhao LY, Duan GG, Zhang GY, Yang HQ, He SJ, Jiang SH. Electrospun functional materials toward food packaging applications: A review. Nanomaterials. 2020;10(1):150. 10.3390/nano10010150.Search in Google Scholar PubMed PubMed Central

(13) Duan GG, Fang H, Huang CB, Jiang SH, Hou HQ. Microstructures and mechanical properties of aligned electrospun carbon nanofibers from binary composites of polyacrylonitrile and polyamic acid. J Mater Sci. 2018;53:1–11. 10.1007/s10853-018-2700-y.Search in Google Scholar

(14) Jiang SH, Chen YM, Duan GG, Mei CT, Greiner A, Agarwal S. Electrospun nanofiber reinforced composites: A review. Polym Chem-UK. 2018;9:2685–720. 10.1039/C8PY00378E.Search in Google Scholar

(15) Chen Y, Sui L, Fang H, Ding C, Li Z, Jiang S, et al. Superior mechanical enhancement of epoxy composites reinforced by polyimide nanofibers via a vacuum-assisted hot-pressing. Compos Sci Technol. 2019;174(12):20–6. 10.1016/j.compscitech.2019.02.012.Search in Google Scholar

(16) Duan GG, Bagheri ARR, Jiang SH, Golenser J, Agarwal S, Greiner A. Exploration of macroporous polymeric sponges as drug carriers. Biomacromolecules. 2017;18(10):3215–21. 10.1021/acs.biomac.7b00852.Search in Google Scholar PubMed

(17) Zhang J, Li S, Ju DD, Li X, Zhang JC, Yan X, et al. Flexible inorganic core-shell nanofibers endowed with tunable multicolor upconversion fluorescence for simultaneous monitoring dual drug delivery. Chem Eng J. 2018;349:554–61. 10.1016/j.cej.2018.05.112.Search in Google Scholar

(18) Wang K, Wen HF, Yu DG, Yang Y, Zhang DF. Electrosprayed hydrophilic nanocomposites coated with shellac for colon-specific delayed drug delivery. Mater Des. 2018;143:248–55. 10.1016/j.matdes.2018.02.016.Search in Google Scholar

(19) Liu L, Bakhshi H, Jiang SH, Schmalz H, Agarwal S. Composite polymeric membranes with directionally embedded fibers for controlled dual actuation. Macromol Rapid Commun. 2018;39(10):1800082. 10.1002/marc.201800082.Search in Google Scholar PubMed

(20) Liu GS, Yan X, Yan FF, Chen FX, Hao LY, Chen SJ, et al. In situ electrospinning iodine-based fibrous meshes for antibacterial wound dressing. Nanoscale Res Lett. 2018;13:309. 10.1186/s11671-018-2733-9.Search in Google Scholar PubMed PubMed Central

(21) Dong WH, Liu JX, Mou XJ, Liu GS, Huang XW, Yan X, et al.Performance of polyvinyl pyrrolidone-isatis root antibacterial wound dressings produced in situ by handheld electrospinner. Colloid Surf B. 2020;188:110766. 10.1016/j.colsurfb.2019.110766.Search in Google Scholar PubMed

(22) Zhang J, Zhao YT, Hu PY, Liu JJ, Liu XF, Hu M, et al.Laparoscopic electrospinning for in situ hemostasis in minimally invasive operation. Chem Eng J. 2020;395:125089. 10.1016/j.cej.2020.125089.Search in Google Scholar

(23) Liu XF, Zhang J, Liu JJ, Zhou QH, Hu PY, Yuan Z, et al. Bifunctional CuS composite nanofibers via in-situ electrospinning for outdoor rapid hemostasis and simultaneous ablating superbug. Chem Eng J. 2020;401:126096. 10.1016/j.cej.2020.126096.Search in Google Scholar

(24) Tan C, Zhu H, Ma T, Guo W, Liu X, Huang X, et al. A stretchable laminated GNRs/BNNSs nanocomposite with high electrical and thermal conductivity. Nanoscale. 2019;11(43):20648–58. 10.1039/C9NR06060J.Search in Google Scholar PubMed

(25) Chen W, Huang G, Li X, Li Y, Wang H, Jiang H, et al. Revealing the position effect of an alkylthio side chain in phenyl-substituted benzodithiophene-based donor polymers on the photovoltaic performance of non-fullerene organic solar cells. ACS Appl Mater Interfaces. 2019;11(36):33173–78. 10.1021/acsami.9b07112.Search in Google Scholar PubMed

(26) Tan CX, Dong ZG, Li YY, Zhao HG, Huang XY, Zhou ZC, et al. A high performance wearable strain sensor with advanced thermal management for motion monitoring. Nat Commun. 2020;11(1):3530. 10.1038/s41467-020-17301-6.Search in Google Scholar PubMed PubMed Central

(27) Wang H, Wang X, Fan T, Zhou R, Li J, Long Y, et al. Fabrication of electrospun sulfonated poly(ether sulfone) nanofibers with amino modified SiO2 nanosphere for optimization of nanochannels in proton exchange membrane. Solid State Ion. 2020;349:115300. 10.1016/j.ssi.2020.115300.Search in Google Scholar

(28) Wang H, Li X, Zhuang X, Cheng B, Wang W, Kang W, et al.Modification of nafion membrane with biofunctional SiO2 nanofiber for proton exchange membrane fuel cells. J Power Sources. 2017;340(1):201–9. 10.1016/j.jpowsour.2016.11.072.Search in Google Scholar

(29) Yu JJ, Liu SW, Duan GG, Fang H, Hou HQ. Dense and thin coating of gel polymer electrolyte on sulfur cathode toward high performance li-sulfur battery. Compos Commun. 2020;19:239–45. 10.1016/j.coco.2020.04.015.Search in Google Scholar

(30) Yang G, Li X, He Y, Ma J, Ni G, Zhou S. From nano to micro to macro: Electrospun hierarchically structured polymeric fibers for biomedical applications. Prog Polym Sci. 2017;81:80–113. 10.1016/j.progpolymsci.2017.12.003.Search in Google Scholar

(31) Chen S, Liu GS, He HW, Zhou CF, Yan X, Zhang JC. Physical structure induced hydrophobicity analyzed from electrospinning and coating polyvinyl butyral films. Adv Cond Matter Phys. 2019;2019:1–5. 10.1155/2019/6179456.Search in Google Scholar

(32) Nicole E. Zander. Hierarchically Structured Electrospun Fibers. Polymers. 2013;5(1):19–44. 10.3390/polym5010019.Search in Google Scholar

(33) Zhou H, Shi Z, Wan X, Fang H, Yu DG, Chen X, et al. The relationships between process parameters and polymeric nanofibers fabricated using a modified coaxial electrospinning. Nanomaterials. 2019;9(6):843. 10.3390/nano9060843.Search in Google Scholar PubMed PubMed Central

(34) Duan GG, Greiner A. Air-blowing-assisted coaxial electrospinning towards high productivity of core/sheath and hollow fibers. Macromol Mater Eng. 2019;304(5):1800669. 10.1002/mame.201800669.Search in Google Scholar

(35) Cai M, Yuan D, Zhang X, Pu Y, Liu XF, He HW, et al. Lithium ion battery separator with improved performance via side-by-side bicomponent electrospinning of PVDF-HFP/PI followed by 3D thermal crosslinking. J Power Sources. 2020;461:228123. 10.1016/j.jpowsour.Search in Google Scholar

(36) Wei L, Qin XH. Nanofiber bundles and nanofiber yarn device and their mechanical properties: A review. Tex Res J. 2016;86(17):1885–98. 10.1177/0040517515617422.Search in Google Scholar

(37) Ali U, Zhou YQ, Wang XG, Lin T. Direct electrospinning of highly twisted, continuous nanofiber yarns. J Text I. 2012;103(1):80–8. 10.1080/00405000.2011.552254.Search in Google Scholar

(38) He JX, Zhou YM, Qi K, Wang LD, Li PP, Cui SZ. Continuous Twisted Nanofiber Yarns Fabricated by Double Conjugate Electrospinning. Fiber Polym. 2013;14(11):1857–63. 10.1007/s12221-013-1857-x.Search in Google Scholar

(39) Sun F, Qi HN, Xie YR, Ma QL, He W, Xu D, et al. Flexible self-supporting bifunctional [TiO2/C]//[Bi2WO6/C] carbon-based Janus nanofiber heterojunction photocatalysts for efficient hydrogen evolution and degradation of organic pollutant. J Alloy Compd. 2020;830:154673. 10.1016/j.jallcom.2020.154673.Search in Google Scholar

(40) Sheng YQ, Tian J, Xie YR, Yang XL, Qi H, Ma QL, et al. Neoteric conjugative electrospinning towards alloplastic nanofiber yarns affording enhanced upconversion luminescence and tailored magnetism. ChemNanoMat. 2020;6:298–307. 10.1002/cnma.201900621.Search in Google Scholar

(41) Guo M, Ding B, Li X, Wang X, Yu J, Wang M. Amphiphobic nanofibrous silica mats with flexible and high-heat-resistant properties. J Phys Chem C. 2010;114(2):916–21. 10.1021/jp909672r.Search in Google Scholar

(42) Mao X, Si Y, Chen Y, Yang L, Zhao F, Ding B, et al. Silica nanofibrous membranes with robust flexibility and thermal stability for high-efficiency fine particulate filtration. Rsc Adv. 2012;2(32):12216–23. 10.1039/c2ra22086e.Search in Google Scholar

(43) Mao X, Bai Y, Yu J, Ding B. Flexible and highly temperature resistant polynanocrystalline zirconia nanofibrous membranes designed for air filtration. J Am Ceram Soc. 2016;99(8):2760–68. 10.1111/jace.14278.Search in Google Scholar

(44) Han WD, Ding B, Park M, Cui FH, Chae SH, Kim HY. Insight into the precursor nanofibers on the flexibility of La2O3-ZrO2 nanofibrous membranes. e-Polymers. 2017;17(3):243–8. 10.1515/epoly-2016-0088.Search in Google Scholar

Received: 2020-08-19
Revised: 2020-09-16
Accepted: 2020-09-17
Published Online: 2020-10-27

© 2020 Zhang Dai et al., published by De Gruyter

This work is licensed under the Creative Commons Attribution 4.0 International License.

Articles in the same Issue

  1. Regular Articles
  2. The regulatory effects of the number of VP(N-vinylpyrrolidone) function groups on macrostructure and photochromic properties of polyoxometalates/copolymer hybrid films
  3. How the hindered amines affect the microstructure and mechanical properties of nitrile-butadiene rubber composites
  4. Novel benzimidazole-based conjugated polyelectrolytes: synthesis, solution photophysics and fluorescent sensing of metal ions
  5. Study on the variation of rock pore structure after polymer gel flooding
  6. Investigation on compatibility of PLA/PBAT blends modified by epoxy-terminated branched polymers through chemical micro-crosslinking
  7. Investigation on degradation mechanism of polymer blockages in unconsolidated sandstone reservoirs
  8. Investigation on the effect of active-polymers with different functional groups for EOR
  9. Fabrication and characterization of hexadecyl acrylate cross-linked phase change microspheres
  10. Surface-induced phase transitions in thin films of dendrimer block copolymers
  11. ZnO-assisted coating of tetracalcium phosphate/ gelatin on the polyethylene terephthalate woven nets by atomic layer deposition
  12. Animal fat and glycerol bioconversion to polyhydroxyalkanoate by produced water bacteria
  13. Effect of microstructure on the properties of polystyrene microporous foaming material
  14. Synthesis of amphiphilic poly(ethylene glycol)-block-poly(methyl methacrylate) containing trityl ether acid cleavable junction group and its self-assembly into ordered nanoporous thin films
  15. On-demand optimize design of sound-absorbing porous material based on multi-population genetic algorithm
  16. Enhancement of mechanical, thermal and water uptake performance of TPU/jute fiber green composites via chemical treatments on fiber surface
  17. Enhancement of mechanical properties of natural rubber–clay nanocomposites through incorporation of silanated organoclay into natural rubber latex
  18. Preparation and characterization of corn starch/PVA/glycerol composite films incorporated with ε-polylysine as a novel antimicrobial packaging material
  19. Preparation of novel amphoteric polyacrylamide and its synergistic retention with cationic polymers
  20. Effect of montmorillonite on PEBAX® 1074-based mixed matrix membranes to be used in humidifiers in proton exchange membrane fuel cells
  21. Insight on the effect of a piperonylic acid derivative on the crystallization process, melting behavior, thermal stability, optical and mechanical properties of poly(l-lactic acid)
  22. Lipase-catalyzed synthesis and post-polymerization modification of new fully bio-based poly(hexamethylene γ-ketopimelate) and poly(hexamethylene γ-ketopimelate-co-hexamethylene adipate) copolyesters
  23. Dielectric, mechanical and thermal properties of all-organic PI/PSF composite films by in situ polymerization
  24. Morphological transition of amphiphilic block copolymer/PEGylated phospholipid complexes induced by the dynamic subtle balance interactions in the self-assembled aggregates
  25. Silica/polymer core–shell particles prepared via soap-free emulsion polymerization
  26. Antibacterial epoxy composites with addition of natural Artemisia annua waste
  27. Design and preparation of 3D printing intelligent poly N,N-dimethylacrylamide hydrogel actuators
  28. Multilayer-structured fibrous membrane with directional moisture transportability and thermal radiation for high-performance air filtration
  29. Reaction characteristics of polymer expansive jet impact on explosive reactive armour
  30. Synthesis of a novel modified chitosan as an intumescent flame retardant for epoxy resin
  31. Synthesis of aminated polystyrene and its self-assembly with nanoparticles at oil/water interface
  32. The synthesis and characterisation of porous and monodisperse, chemically modified hypercrosslinked poly(acrylonitrile)-based terpolymer as a sorbent for the adsorption of acidic pharmaceuticals
  33. Crystal transition and thermal behavior of Nylon 12
  34. All-optical non-conjugated multi-functionalized photorefractive polymers via ring-opening metathesis polymerization
  35. Fabrication of LDPE/PS interpolymer resin particles through a swelling suspension polymerization approach
  36. Determination of the carbonyl index of polyethylene and polypropylene using specified area under band methodology with ATR-FTIR spectroscopy
  37. Synthesis, electropolymerization, and electrochromic performances of two novel tetrathiafulvalene–thiophene assemblies
  38. Wetting behaviors of fluoroterpolymer fiber films
  39. Plugging mechanisms of polymer gel used for hydraulic fracture water shutoff
  40. Synthesis of flexible poly(l-lactide)-b-polyethylene glycol-b-poly(l-lactide) bioplastics by ring-opening polymerization in the presence of chain extender
  41. Sulfonated poly(arylene ether sulfone) functionalized polysilsesquioxane hybrid membranes with enhanced proton conductivity
  42. Fmoc-diphenylalanine-based hydrogels as a potential carrier for drug delivery
  43. Effect of diacylhydrazine as chain extender on microphase separation and performance of energetic polyurethane elastomer
  44. Improved high-temperature damping performance of nitrile-butadiene rubber/phenolic resin composites by introducing different hindered amine molecules
  45. Rational synthesis of silicon into polyimide-derived hollow electrospun carbon nanofibers for enhanced lithium storage
  46. Synthesis, characterization and properties of phthalonitrile-etherified resole resin
  47. Highly thermally conductive boron nitride@UHMWPE composites with segregated structure
  48. Synthesis of high-temperature thermally expandable microcapsules and their effects on foaming quality and surface quality of foamed ABS materials
  49. Tribological and nanomechanical properties of a lignin-based biopolymer
  50. Hydroxyapatite/polyetheretherketone nanocomposites for selective laser sintering: Thermal and mechanical performances
  51. Synthesis of a phosphoramidate flame retardant and its flame retardancy on cotton fabrics
  52. Preparation and characterization of thermoresponsive poly(N-isopropylacrylamide) copolymers with enhanced hydrophilicity
  53. Fabrication of flexible SiO2 nanofibrous yarn via a conjugate electrospinning process
  54. Silver-loaded carbon nanofibers for ammonia sensing
  55. Polar migration behavior of phosphonate groups in phosphonate esterified acrylic grafted epoxy ester composites and their role in substrate protection
  56. Solubility and diffusion coefficient of supercritical CO2 in polystyrene dynamic melt
  57. Curcumin-loaded polyvinyl butyral film with antibacterial activity
  58. Experimental-numerical studies of the effect of cell structure on the mechanical properties of polypropylene foams
  59. Experimental investigation on the three-dimensional flow field from a meltblowing slot die
  60. Enhancing tribo-mechanical properties and thermal stability of nylon 6 by hexagonal boron nitride fillers
  61. Preparation and characterization of electrospun fibrous scaffolds of either PVA or PVP for fast release of sildenafil citrate
  62. Seawater degradation of PLA accelerated by water-soluble PVA
  63. Review Article
  64. Mechanical properties and application analysis of spider silk bionic material
  65. Additive manufacturing of PLA-based scaffolds intended for bone regeneration and strategies to improve their biological properties
  66. Structural design toward functional materials by electrospinning: A review
  67. Special Issue: XXXII National Congress of the Mexican Polymer Society
  68. Tailoring the morphology of poly(high internal phase emulsions) synthesized by using deep eutectic solvents
  69. Modification of Ceiba pentandra cellulose for drug release applications
  70. Redox initiation in semicontinuous polymerization to search for specific mechanical properties of copolymers
  71. pH-responsive polymer micelles for methotrexate delivery at tumor microenvironments
  72. Microwave-assisted synthesis of the lipase-catalyzed ring-opening copolymerization of ε-caprolactone and ω-pentadecanolactone: Thermal and FTIR characterization
  73. Rapid Communications
  74. Pilot-scale production of polylactic acid nanofibers by melt electrospinning
  75. Erratum
  76. Erratum to: Synthesis and characterization of new macromolecule systems for colon-specific drug delivery
https://doi.org/10.1515/epoly-2020-0063
Keywords for this article
electrospinning; PVA; SiO2; flexibility; nanofibrous yarn
Creative Commons
BY 4.0

Articles in the same Issue

  1. Regular Articles
  2. The regulatory effects of the number of VP(N-vinylpyrrolidone) function groups on macrostructure and photochromic properties of polyoxometalates/copolymer hybrid films
  3. How the hindered amines affect the microstructure and mechanical properties of nitrile-butadiene rubber composites
  4. Novel benzimidazole-based conjugated polyelectrolytes: synthesis, solution photophysics and fluorescent sensing of metal ions
  5. Study on the variation of rock pore structure after polymer gel flooding
  6. Investigation on compatibility of PLA/PBAT blends modified by epoxy-terminated branched polymers through chemical micro-crosslinking
  7. Investigation on degradation mechanism of polymer blockages in unconsolidated sandstone reservoirs
  8. Investigation on the effect of active-polymers with different functional groups for EOR
  9. Fabrication and characterization of hexadecyl acrylate cross-linked phase change microspheres
  10. Surface-induced phase transitions in thin films of dendrimer block copolymers
  11. ZnO-assisted coating of tetracalcium phosphate/ gelatin on the polyethylene terephthalate woven nets by atomic layer deposition
  12. Animal fat and glycerol bioconversion to polyhydroxyalkanoate by produced water bacteria
  13. Effect of microstructure on the properties of polystyrene microporous foaming material
  14. Synthesis of amphiphilic poly(ethylene glycol)-block-poly(methyl methacrylate) containing trityl ether acid cleavable junction group and its self-assembly into ordered nanoporous thin films
  15. On-demand optimize design of sound-absorbing porous material based on multi-population genetic algorithm
  16. Enhancement of mechanical, thermal and water uptake performance of TPU/jute fiber green composites via chemical treatments on fiber surface
  17. Enhancement of mechanical properties of natural rubber–clay nanocomposites through incorporation of silanated organoclay into natural rubber latex
  18. Preparation and characterization of corn starch/PVA/glycerol composite films incorporated with ε-polylysine as a novel antimicrobial packaging material
  19. Preparation of novel amphoteric polyacrylamide and its synergistic retention with cationic polymers
  20. Effect of montmorillonite on PEBAX® 1074-based mixed matrix membranes to be used in humidifiers in proton exchange membrane fuel cells
  21. Insight on the effect of a piperonylic acid derivative on the crystallization process, melting behavior, thermal stability, optical and mechanical properties of poly(l-lactic acid)
  22. Lipase-catalyzed synthesis and post-polymerization modification of new fully bio-based poly(hexamethylene γ-ketopimelate) and poly(hexamethylene γ-ketopimelate-co-hexamethylene adipate) copolyesters
  23. Dielectric, mechanical and thermal properties of all-organic PI/PSF composite films by in situ polymerization
  24. Morphological transition of amphiphilic block copolymer/PEGylated phospholipid complexes induced by the dynamic subtle balance interactions in the self-assembled aggregates
  25. Silica/polymer core–shell particles prepared via soap-free emulsion polymerization
  26. Antibacterial epoxy composites with addition of natural Artemisia annua waste
  27. Design and preparation of 3D printing intelligent poly N,N-dimethylacrylamide hydrogel actuators
  28. Multilayer-structured fibrous membrane with directional moisture transportability and thermal radiation for high-performance air filtration
  29. Reaction characteristics of polymer expansive jet impact on explosive reactive armour
  30. Synthesis of a novel modified chitosan as an intumescent flame retardant for epoxy resin
  31. Synthesis of aminated polystyrene and its self-assembly with nanoparticles at oil/water interface
  32. The synthesis and characterisation of porous and monodisperse, chemically modified hypercrosslinked poly(acrylonitrile)-based terpolymer as a sorbent for the adsorption of acidic pharmaceuticals
  33. Crystal transition and thermal behavior of Nylon 12
  34. All-optical non-conjugated multi-functionalized photorefractive polymers via ring-opening metathesis polymerization
  35. Fabrication of LDPE/PS interpolymer resin particles through a swelling suspension polymerization approach
  36. Determination of the carbonyl index of polyethylene and polypropylene using specified area under band methodology with ATR-FTIR spectroscopy
  37. Synthesis, electropolymerization, and electrochromic performances of two novel tetrathiafulvalene–thiophene assemblies
  38. Wetting behaviors of fluoroterpolymer fiber films
  39. Plugging mechanisms of polymer gel used for hydraulic fracture water shutoff
  40. Synthesis of flexible poly(l-lactide)-b-polyethylene glycol-b-poly(l-lactide) bioplastics by ring-opening polymerization in the presence of chain extender
  41. Sulfonated poly(arylene ether sulfone) functionalized polysilsesquioxane hybrid membranes with enhanced proton conductivity
  42. Fmoc-diphenylalanine-based hydrogels as a potential carrier for drug delivery
  43. Effect of diacylhydrazine as chain extender on microphase separation and performance of energetic polyurethane elastomer
  44. Improved high-temperature damping performance of nitrile-butadiene rubber/phenolic resin composites by introducing different hindered amine molecules
  45. Rational synthesis of silicon into polyimide-derived hollow electrospun carbon nanofibers for enhanced lithium storage
  46. Synthesis, characterization and properties of phthalonitrile-etherified resole resin
  47. Highly thermally conductive boron nitride@UHMWPE composites with segregated structure
  48. Synthesis of high-temperature thermally expandable microcapsules and their effects on foaming quality and surface quality of foamed ABS materials
  49. Tribological and nanomechanical properties of a lignin-based biopolymer
  50. Hydroxyapatite/polyetheretherketone nanocomposites for selective laser sintering: Thermal and mechanical performances
  51. Synthesis of a phosphoramidate flame retardant and its flame retardancy on cotton fabrics
  52. Preparation and characterization of thermoresponsive poly(N-isopropylacrylamide) copolymers with enhanced hydrophilicity
  53. Fabrication of flexible SiO2 nanofibrous yarn via a conjugate electrospinning process
  54. Silver-loaded carbon nanofibers for ammonia sensing
  55. Polar migration behavior of phosphonate groups in phosphonate esterified acrylic grafted epoxy ester composites and their role in substrate protection
  56. Solubility and diffusion coefficient of supercritical CO2 in polystyrene dynamic melt
  57. Curcumin-loaded polyvinyl butyral film with antibacterial activity
  58. Experimental-numerical studies of the effect of cell structure on the mechanical properties of polypropylene foams
  59. Experimental investigation on the three-dimensional flow field from a meltblowing slot die
  60. Enhancing tribo-mechanical properties and thermal stability of nylon 6 by hexagonal boron nitride fillers
  61. Preparation and characterization of electrospun fibrous scaffolds of either PVA or PVP for fast release of sildenafil citrate
  62. Seawater degradation of PLA accelerated by water-soluble PVA
  63. Review Article
  64. Mechanical properties and application analysis of spider silk bionic material
  65. Additive manufacturing of PLA-based scaffolds intended for bone regeneration and strategies to improve their biological properties
  66. Structural design toward functional materials by electrospinning: A review
  67. Special Issue: XXXII National Congress of the Mexican Polymer Society
  68. Tailoring the morphology of poly(high internal phase emulsions) synthesized by using deep eutectic solvents
  69. Modification of Ceiba pentandra cellulose for drug release applications
  70. Redox initiation in semicontinuous polymerization to search for specific mechanical properties of copolymers
  71. pH-responsive polymer micelles for methotrexate delivery at tumor microenvironments
  72. Microwave-assisted synthesis of the lipase-catalyzed ring-opening copolymerization of ε-caprolactone and ω-pentadecanolactone: Thermal and FTIR characterization
  73. Rapid Communications
  74. Pilot-scale production of polylactic acid nanofibers by melt electrospinning
  75. Erratum
  76. Erratum to: Synthesis and characterization of new macromolecule systems for colon-specific drug delivery
Sign up now to receive a 20% welcome discount
Institutional Access
How does access work?
Have an idea on how to improve our website?
Please write us.
© 2025 De Gruyter Brill
Downloaded on 31.10.2025 from https://www.degruyterbrill.com/document/doi/10.1515/epoly-2020-0063/html?lang=en
Scroll to top button