Home Silica/polymer core–shell particles prepared via soap-free emulsion polymerization
Article Open Access

Silica/polymer core–shell particles prepared via soap-free emulsion polymerization

  • Mina Ishihara , Tomofumi Kaeda and Takashi Sasaki EMAIL logo
Published/Copyright: June 2, 2020
Download Article (PDF)
Become an author with De Gruyter Brill
Submit Manuscript Author Information
e-Polymers
From the journal e-Polymers Volume 20 Issue 1

Abstract

In this study, core–shell particles were prepared as a hybrid material, in which a thin polymer shell was formed on the surface of the SiO2 sphere particles. The core–shell structure was successfully achieved without adding a surfactant via simple free-radical polymerization (soap-free emulsion polymerization) for various monomers of styrene, methyl methacrylate (MMA), and their derivatives. MMA formed thin homogeneous shells of polymer (PMMA) less than 100 nm in thickness with complete surface coverage and a very smooth shell surface. The obtained shell morphology strongly depended on the monomers, which suggests different shell formation mechanisms with respect to the monomers. It was found that the cross-linking monomer 1,4-divinylbenzene tends to promote shell formation, and the cross-linking reaction may stabilize the core–shell structure throughout radical polymerization. It should also be noted that the present method produced a considerable amount of pure polymer besides the core–shell particles. The glass transition temperatures of the obtained polymer shells were higher than those of the corresponding bulk materials. This result suggests strong interactions at the core–shell interface.

Graphical Abstract

Core–shell particles with a shell of various polymer materials were prepared via soap-free emulsion polymerization. Unique morphologies that are characteristic to the polymer material were obtained.

Keywords: soap-free polymerization; core–shell particles; silica; glass transition; cross-link

1 Introduction

Hybrid nanoparticles composed of inorganic and organic materials have been attracting immense attention and can contribute to the development of various composite materials. Numerous studies have attempted to manufacture core–shell particles with a polymeric shell and an inorganic core (1). Such composite particles can be used as fillers for nanocomposites, where the filler reinforces the matrix resin because of its excellent compatibility with the matrix (2,3,4,5,6). Other potential applications for core–shell particles are electronics (7,8,9,10), pharmaceutical materials (11,12), optics (13), and catalysis (14,15,16,17). Various methods have been developed to prepare the core–shell particles (1,15,18,19,20,21,22). Among them, emulsion or suspension polymerization is the most common technique used to prepare the inorganic/polymeric core–shell particles, where the radical polymerization is performed in the presence of suspended core particles in water (23,24,25,26,27,28,29,30). The suspension (or emulsion) polymerization technique can also be applied to prepare whisker-shaped core–shell and hollow particles using CaCO3 core particles (31,32,33,34).

To stabilize the suspended droplets of monomer and core particles in water, amphiphilic surfactants are often used. However, in general, it is difficult to remove the surfactant completely after polymerization (1). The residual surfactant may significantly affect the properties of the obtained nanomaterials, such as the glass transition temperature (35). Therefore, developing a technique to obtain core–shell particles without using any surfactants is essential to elucidate the nano-size effects on their physical and thermal properties.

In this study, core–shell particles were prepared using spherical silica particles as cores. Emulsion polymerization with an aqueous initiator without a surfactant (soap-free polymerization) was performed for various monomers of styrene, methyl methacrylate (MMA), and their derivatives to obtain polymer layers that cover the surface of the silica cores. The polymerization conditions were optimized for each monomer to successfully achieve a core–shell architecture. The glass transition temperature Tg of the obtained polymer shells was investigated via the differential scanning calorimetry (DSC), and the results were compared with the corresponding bulk Tg.

2 Experimental

Silica nanoparticles with diameters of 300, 500, and 1,000 nm (KE-S30, KE-S50, and KE-S100; Nippon Shokubai, Osaka Japan) were used as core materials. MMA, 2-hydroxyethyl methacrylate (HEMA), styrene (S), 4-chlorostyrene (ClS), 4-methoxystyrene (MOS), 4-methylstyrene (MS), and the cross-linking reagent 1,4-divinylbenzene (DVB) were distilled under reduced pressure before use. The surfaces of the silica particles were modified with a silane coupling reagent, 3-(trimethoxysilyl)propyl methacrylate (MAPTMS), which was used as received. It was found that the SiO2 particles with no surface treatment did not successfully yield core–shell particles (36). The surface modification of the silica particles was performed as follows: 90 ml of ethanol and 1.0 ml of MAPTMS were added to 10 g of silica particles suspended in 90 ml of pure water. Then, acetic acid was added until the pH became 4.0. The obtained weakly acidic suspension was stirred for 30 min at 25°C and sonicated for 3.5 h. The mixture was stirred again for 24 h at 25°C. The suspended particles were precipitated via centrifugation at 2,000 rpm for 8 min, and the precipitated particles were soaked in methanol for neutralization. The precipitates were dried in air at 25°C. The obtained powder-like material (surface-modified SiO2 particles) is referred to as SiO2–MAPTMS henceforth. The modification with MAPTMS was confirmed using X-ray photoelectron spectroscopy (JPS-9010MCY; Jeol, Akishima, Japan) from a signal of the C═C bond on the surface of the modified silica.

The polymer/SiO2–MAPTMS core–shell particles were prepared via soap-free emulsion polymerization. Sodium peroxodisulfate or potassium peroxodisulfate was used as an initiator, and the aforementioned monomers were polymerized. In some cases, the cross-linking reagent DVB was included in the polymerization reaction (random copolymerization). All these monomers were distilled under reduced pressure before use. Polymerization was performed under a nitrogen atmosphere at a constant temperature (40, 60, or 80°C). Various recipes with respect to the amount of each reagent were tried to yield core–shell particles successfully. The optimized conditions that were found by trial and error are listed in Table 1.

Table 1

Optimized conditions for emulsion polymerization

PolymerTemperature (°C)Monomer (M)Initiator (10−3 M)Diameter of core (nm)DVB (10−3 M)
PMMA (a)800.414.181,0000
PMMA (b)800.41405000
PMMA (c)800.1151005000
PClS600.194.183007.9
PMS800.174.183004.0
PMOS800.174.183004.0
PHEMA400.184.183007.9
PS with no cross-linker800.879.411,0000
PS with a cross-linker600.194.183007.9

The morphology of the obtained particles was investigated via transmission electron microscopy (TEM) using a Jeol JEM-2000FXII operated at an acceleration voltage of 200 kV. The sample was dispersed and diluted in methanol, and it was deposited onto a microgrid covered with a carbon-coated nitrocellulose membrane. The glass transition behaviors of the polymer shells were investigated using a DSC (Pyris Diamond, Perkin Elmer). The temperature and heat flow were calibrated using an indium standard, and the measurements were conducted under a nitrogen atmosphere. The step-scan heating mode, which is a type of temperature-modulated DSC, was used to yield nonreversing heat flow and reversing heat capacity. Scans were performed with a temperature step of 2 K at a heating rate of 5 K min−1 and a holding time of 1.5 min. As the prepared core–shell particles often contained only small fractions of polymer, their Tg signal tended to be rather weak. To emphasize the weak Tg signal, the samples were annealed below the bulk Tg(Tgbulk–30°C) for 72 h before the DSC scan. Then, the Tg of the polymer shell was evaluated from the signal of the enthalpy overshoot that appeared in the nonreversing heat flow trace.

To evaluate the bulk values of Tg, the polymer samples were synthesized under the exact same conditions in the absence of the core particles. The obtained polymers were separated in methanol and then dissolved in toluene, followed by precipitation in methanol (or n-hexane). The bulk reference samples thus obtained were dried under vacuum at room temperature for 24 h. The molar mass of PMMA (non-cross-linked) was also determined for the bulk reference samples prepared above via gel permeation chromatography with three polystyrene (PS) gel columns (TSK gel G-MHHR-M) connected to a Waters Alliance e22695 (Tokyo, Japan). To evaluate the polymer content in the obtained core–shell samples, the thermogravimetric analysis was performed using a thermogravimetric analyzer (DTG-60; Shimadzu, Kyoto, Japan).

3 Results and discussion

Figure 1 shows the TEM images of the PMMA/SiO2–MAPTMS core–shell particles prepared via emulsion polymerization under three different conditions. Core–shell particles were successfully obtained for PMMA shells with no cross-linking reagent. The surface of the PMMA shell was rather smooth, and the shell thickness was homogeneous, especially for PMMA (a). This may be due to the compatibility of MMA with the silica surface. The surface of the silica particles used in this study is considered to be slightly hydrophilic even after modification with MAPTMS; therefore, it is compatible with MMA. In the suspended state before polymerization, the surface of the SiO2–MAPTMS particles was possibly covered with a thin monomer layer. It is likely that at first the initiator reacted with MMA in the aqueous phase, then it migrated into the monomer phase around the core (8,37). In addition, it was found that a considerable amount of pure PMMA besides the shell part was produced. Comparison of the result of the thermogravimetric analysis and the average shell thickness obtained through the TEM revealed that the mass ratio of the shell to the total mass of PMMA ranged from 30 to 37%. The formation of pure polymer originates from the mechanism of emulsion polymerization, where the initiation reaction occurs in the aqueous phase. Thus, our method of polymerization has a disadvantage that it produces core–shell particles only partially, although well-defined homogeneous core–shell structures can be easily obtained. On the other hand, TEM observation revealed nearly 100% of surface coverage of the core by the polymer shell.

Figure 1 TEM images of the PMMA/SiO2–MAPTMS core–shell particles prepared under three conditions: PMMA (a), PMMA (b), and PMMA (c), as shown in Table 1.
Figure 1

TEM images of the PMMA/SiO2–MAPTMS core–shell particles prepared under three conditions: PMMA (a), PMMA (b), and PMMA (c), as shown in Table 1.

Such a core–shell structure is rather stable during polymerization because of the high compatibility. It was found that the shell thickness depends weakly on the amount of monomer fed. The shell of PMMA (a) exhibited the most homogeneous morphology with a thickness of 42 nm. As for PMMA (b), the shell thickness showed a distribution that ranged from 37 to 52 nm. The molar mass of the shell of PMMA (b) was determined to be Mn = 26,400 Da and Mw = 36,400 Da and for PMMA (c), Mn = 19,900 Da and Mw = 24,500 Da.

For the monomers of styrene derivatives, a core–shell structure was obtained when a cross-linking monomer (DVB) was added. Figure 2 shows PClS/SiO2–MAPTMS core–shell particles, where the PClS shell was cross-linked with DVB. Thicker shells up to 140 nm were obtained. In addition, pure PClS spheres without a core were simultaneously obtained, but most of the core particles were covered with the polymer shell as in the case of PMMA. Shell formation was not observed if polymerization was performed without the cross-linker. This was also the case for PMS and PMOS. Cross-linking may stabilize the shell structure during polymerization in aqueous suspensions of the core particles, as was reported in studies on calcium carbonate cores (31,32). Furthermore, gaps between the core and the shell occurred occasionally, as indicated by the arrow in Figure 2 (left panel). This suggests that no chemical (covalent) linkage was formed between MAPTMS and PClS in the areas of the gaps because of low affinity of ClS with the core surface compared with that of MMA. The mechanism of the gap formation may be related to the difference in thermal shrinkage between the core and the shell on cooling after polymerization. The gap between the core and the shell tends to form when the shell thickness is relatively large. The gap also formed for PMOS and PMS, of which the shells are thicker than that of PClS, as shown below. In contrast, for PMMA and PHEMA, which exhibited thinner shells, no gap was observed.

Figure 2 TEM images of the PClS/SiO2–MAPTMS core–shell particles. The polymer shell was cross-linked with DVB. The white arrow in the left panel indicates the gap between the core and the shell.
Figure 2

TEM images of the PClS/SiO2–MAPTMS core–shell particles. The polymer shell was cross-linked with DVB. The white arrow in the left panel indicates the gap between the core and the shell.

Figure 3 shows the TEM images of the PMOS/SiO2–MAPTMS particles with cross-linked shells. Here, very thick outer shells are observed. Interestingly, the cores were not necessarily located at the center of the particles, and the entire shape of the particles was ellipsoidal in general. The thickness of the PMOS shell ranged rather widely (140–500 nm). These morphological features are similar to those of the particles with PS shells prepared using different methods (9,10). Figure 4 shows PMS/SiO2–MAPTMS particles with cross-linked shells. The features of the core–shell structure are similar to those of the PMOS/SiO2–MAPTMS particles. Similar to the PMOS shell, the thickness of the PMS shell was also in a wide range (140–400 nm). It is noted again that the gaps between the core and the shell partially occur for some particles. The morphological similarity between the PMOS and the PMS shells may originate from their similar chemical nature. It was also found that almost all the core particles were covered with the polymer for both PMOS and PMS.

Figure 3 TEM images of the PMOS/SiO2–MAPTMS core–shell particles. The polymer shell was cross-linked with DVB.
Figure 3

TEM images of the PMOS/SiO2–MAPTMS core–shell particles. The polymer shell was cross-linked with DVB.

Figure 4 TEM images of the PMS/SiO2–MAPTMS core–shell particles. The polymer shell was cross-linked with DVB.
Figure 4

TEM images of the PMS/SiO2–MAPTMS core–shell particles. The polymer shell was cross-linked with DVB.

Figure 5 shows the TEM images of the PS/SiO2–MAPTMS composite particles. When the cross-linker DVB was not included, many small PS spheres were obtained, which were attached to the surface of the core particles. This resulted in a flower-like morphology (Figure 5a). The morphology suggests that the small PS particles formed separately from small monomer droplets suspended in water and then migrated and attached to the surface of the cores. The diameter of these PS particles ranged from 90 to 280 nm. In addition, the surface of the core was not completely covered with the PS particles, as shown in the right image of Figure 5a. In contrast, thick and ragged shells formed when the cross-linker was included in the polymerization, as shown in Figure 5b. However, the obtained shells were thicker but less homogeneous than those in PMMA, and the surface coverage was incomplete. Some of the particles still appeared to be flower-like, suggesting the same mechanism of shell formation as in the case of non-cross-linked shells (Figure 5a). The results for PS suggest that the compatibility of the monomer (styrene) with the core surface is lower than that of the monomers exhibiting thicker shells, as shown in Figures 2–4 (chlorostyrene, methylstyrene, and methoxystyrene). It is likely that for the monomers with thicker shells, a monomer layer formed on the core surface prior to the commencement of polymerization because of their higher compatibility with the core. Core–shell particles with very thick PS shells have been reported to form successfully via emulsion polymerization when an aqueous monomer (styrene sulfonate sodium salt) was included (9,10). Such an aqueous monomer that is highly compatible with SiO2 may promote the formation of a homogeneous monomer layer on the core surface during polymerization.

Figure 5 TEM images of the PS/SiO2–MAPTMS particles for (a) PS polymerized with no cross-linker and (b) PS polymerized with a cross-linker DVB.
Figure 5

TEM images of the PS/SiO2–MAPTMS particles for (a) PS polymerized with no cross-linker and (b) PS polymerized with a cross-linker DVB.

A hydrophilic monomer, HEMA with the cross-linker DVB (Table 1), was also investigated. The obtained TEM images are presented in Figure 6, where very thin shells of PHEMA are observed on the core particles. The surface of the shell appeared to be ragged compared with that of PMMA. The average shell thickness was determined to be 7.3 nm. No gap was observed between the core and the shell; this suggests that the shell was covalently bonded through the silane coupling reagent to the core surface. Nearly 100% surface coverage was achieved, which suggests high affinity of the monomer because of its hydrophilic nature. The mass ratio of the shell to the total mass of PHEMA was evaluated to be 17%.

Figure 6 TEM images of the PHEMA/SiO2–MAPTMS particles. The polymer shell was cross-linked with DVB.
Figure 6

TEM images of the PHEMA/SiO2–MAPTMS particles. The polymer shell was cross-linked with DVB.

For the polymer shells, the thermal properties were investigated via the DSC measurements and their Tg was evaluated. Table 2 shows the results with the average shell thickness. In general, the Tg’s of the polymer shells were higher than the corresponding bulk values. Note that Tgbulk reported in this table is for polymers with the same degree of cross-linking in a bulk state. The increase in Tg may be due to the strong interactions at the core–shell interface, where the polymer chains have limited mobility owing to the binding at the interface. MAPTMS may play a role in decreasing the polymer mobility at the interface. PClS/SiO2–MAPTMS exhibited partial gaps at the core–shell interface, but they still showed a higher Tg than the bulk value. The increase in Tg for PClS may be partially attributed to the heterogeneous distribution of cross-linking points in the shell; a similar phenomenon of Tg enhancement was reported previously for the cross-linked polymer shells in other core–shell systems (31,32). In addition, it should be noted that the prepared samples contained polymer particles without a core (polymer spheres and/or larger bulk-like entities of pure polymer), which affected the observed Tg. Nevertheless, the general trend of increase in Tg for the core–shell particles is assured because the pure polymer particles with bulk-like nature do not contribute to the increase in Tg, although quantitative discussion with respect to the shell thickness could not be made.

Table 2

Average shell thickness d and the glass transition temperature Tg of the shells

Polymerd (nm)Tg (°C)Tgbulk(°C)
PMMA (a)42140127
PMMA (b)37–52127123
PMMA (c)100123114
PClS140145140
PHEMA7.3115100
PS with a cross-linker20–90137130

4 Conclusions

In this study, the SiO2/polymer composite particles with core–shell structures were successfully synthesized via soap-free emulsion polymerization. The obtained morphology strongly depended on the monomer used, which determined the mechanism of the radical polymerization. PMMA showed homogeneous shells with rather smooth shell surfaces. This may be a result of the compatibility of MMA with the silica surface modified with MAPTMS. The shells of PMS, PMOS, and PClS were also obtained if the cross-linking monomer DVB was copolymerized. The shells of these polymers were much thicker than those of PMMA. For non-cross-linked PS, small polymer spheres were aggregated on the silica surface to form a flower-like structure. The cross-linked PS shells were still less homogeneous than those of PMMA. These results may originate from the low compatibility of styrene with the core surface. This low compatibility may prevent the formation of a monomer layer on the core surface in a suspended state prior to polymerization. Very thin shells were successfully obtained for PHEMA, although the shell surface was ragged. The glass transition temperature of the obtained shells was found to be higher than the corresponding bulk value for all the polymers investigated. This finding indicates that the interaction at the core–shell interface is essential in determining the physical properties of the composite materials with nano-sized geometries.

It should be noted that the present method of soap-free emulsion polymerization produces a considerable fraction of pure polymer besides the core–shell particles. The fraction of pure polymer may be reduced by improving the preparation procedures. In addition, separation of the core–shell particles from the pure polymer may be possible by centrifugation of the as-polymerized suspension.

Acknowledgments

We thank Prof. Shinji Sugihara, University of Fukui, for help in determining the molar mass of the PMMA samples. We also thank Prof. Jae-Ho Kim, University of Fukui, for help with the surface analysis of the core particles. This work was supported by JSPS KAKENHI Grant Number JP16K05907 from the Ministry of Education, Culture, Sports, Science and Technology of Japan.

References

(1) Chaudhuri RG, Paria S. Core/shell nanoparticles: classes, properties, synthesis mechanisms, characterization, and applications. Chem Rev. 2012;112(4):2373–433.10.1021/cr100449nSearch in Google Scholar PubMed

(2) Percy MJ, Amalvy JI, Randall DP, Armes SP, Greaves SJ, Watts JF. Synthesis of vinyl polymer–silica colloidal nanocomposites prepared using commercial alcoholic silica sols. Langmuir. 2004;20(6):2184–90.10.1021/la035868sSearch in Google Scholar PubMed

(3) Xie XL, Li RKY, Liu QX, Mai YW. Structure–property relationships of in situ PMMA modified nano-sized antimony trioxide filled poly(vinyl chloride) nanocomposites. Polymer. 2004;45(8):2793–802.10.1016/j.polymer.2004.02.028Search in Google Scholar

(4) Palkovits R, Althues H, Rumplecker A, Tesche B, Dreier A, Holle U, et al. Polymerization of w/o microemulsions for the preparation of transparent SiO2/PMMA nanocomposites. Langmuir. 2005;21(13):6048–53.10.1021/la050630kSearch in Google Scholar PubMed

(5) Haldorai Y, Lyoo WS, Noh SK, Shim JJ. Ionic liquid mediated synthesis of silica/polystyrene core–shell composite nanospheres by radical dispersion polymerization. React Funct Polym. 2010;70(7):393–9.10.1016/j.reactfunctpolym.2010.03.009Search in Google Scholar

(6) Song Y, Bu J, Zuo M, Gao Y, Zhang W, Zheng Q. Glass transition of poly(methyl methacrylate) filled with nanosilica and core–shell structured silica. Polymer. 2017;127:141–9.10.1016/j.polymer.2017.08.038Search in Google Scholar

(7) Maliakal A, Katz H, Cotts PM, Subramoney S, Mirau P. Inorganic oxide core, polymer shell nanocomposite as a high K gate dielectric for flexible electronics applications. J Am Chem Soc. 2005;127(42):14655–62.10.1021/ja052035aSearch in Google Scholar PubMed

(8) Okada A, Nagao D, Ishii H, Konno M. Direct observation of micron-sized silica rattles to demonstrate movability of inner spheres in the silica compartment suspended in aqueous media. Soft Matter. 2012;8(12):3442–5.10.1039/c2sm06946fSearch in Google Scholar

(9) Okada A, Nagao D, Ueno T, Ishii H, Konno M. Colloidal polarization of yolk/shell particles by reconfiguration of inner cores responsive to an external magnetic field. Langmuir. 2013;29(28):9004–9.10.1021/la401646tSearch in Google Scholar PubMed

(10) Watanabe K, Nagao D, Ishii H, Konno M. Rattle-type colloidal crystals composed of spherical hollow particles containing an anisotropic, movable core. Langmuir. 2015;31(19):5306–10.10.1021/acs.langmuir.5b01148Search in Google Scholar PubMed

(11) Balivada S, Rachakatla RS, Wang H. A/C magnetic hyperthermia of melanoma mediated by iron(0)/iron oxide core/shell magnetic nanoparticles: a mouse study. BMC Cancer. 2010;10:119.10.1186/1471-2407-10-119Search in Google Scholar

(12) Schärtl W. Current directions in core–shell nanoparticle design. Nanoscale. 2010;2(6):829–43.10.1039/c0nr00028kSearch in Google Scholar

(13) Fielding LA, Tonnar J, Armes SP. All-acrylic film-forming colloidal polymer/silica nanocomposite particles prepared by aqueous emulsion polymerization. Langmuir. 2011;27(17):11129–44.10.1021/la202066nSearch in Google Scholar

(14) Spanhel L, Haase M, Weller H, Henglein A. Photochemistry of colloidal semiconductors. 20. Surface modification and stability of strong luminescing CdS particles. J Am Chem Soc. 1987;109(19):5649–55.10.1021/ja00253a015Search in Google Scholar

(15) Daniel MC, Astruc D. Gold nanoparticles: assembly, supramolecular chemistry, quantum-size-related properties, and applications toward biology, catalysis, and nanotechnology. Chem Rev. 2004;104(1):293–346.10.1021/cr030698+Search in Google Scholar

(16) Xuan S, Wang YXJ, Yu JC, Leung KCF. Preparation, characterization, and catalytic activity of core/shell Fe3O4@polyaniline@Au nanocomposites. Langmuir. 2009;25(19):11835–43.10.1021/la901462tSearch in Google Scholar

(17) Zeng HC. Integrated nanocatalysts. Acc Chem Res. 2013;46(2):226–35.10.1021/ar3001662Search in Google Scholar

(18) Thurmond KB, Kowalewski T, Wooley KL. Shell cross-linked knedels: a synthetic study of the factors affecting the dimensions and properties of amphiphilic core–shell nanospheres. J Am Chem Soc. 1997;119(28):6656–65.10.1021/ja9710520Search in Google Scholar

(19) Rong MZ, Zhang MQ, Zheng YX, Walter R, Friedrich K. Structure–property relationships of irradiation grafted nano-inorganic particle filled polypropylene composites. Polymer. 2001;42(1):167–83.10.1016/S0032-3861(00)00325-6Search in Google Scholar

(20) Rong MZ, Zhang MQ, Zheng YX, Friedrich K. Improvement of tensile properties of nano-SiO2/PP composites in relation to percolation mechanism. Polymer. 2001;42(7):3301–4.10.1016/S0032-3861(00)00741-2Search in Google Scholar

(21) Sertchook H, Avnir D. Submicron silica/polystyrene composite particles prepared by a one-step sol–gel process. Chem Mater. 2003;15(8):1690–4.10.1021/cm020980hSearch in Google Scholar

(22) Ohno K, Morinaga T, Koh K, Tsujii Y, Fukuda T. Synthesis of monodisperse silica particles coated with well-defined, high-density polymer brushes by surface-initiated atom transfer radical polymerization. Macromolecules. 2005;38(6):2137–42.10.1021/ma048011qSearch in Google Scholar

(23) Hergeth WD, Peller M, Hauptmann P. Polymerizations in the presence of seeds. II. Monitoring the emulsion polymerization in the presence of fillers by means of ultrasound. Acta Polym. 1986;37(7):468–9.10.1002/actp.1986.010370714Search in Google Scholar

(24) Hergeth WD, Starre P, Schmutzer K. Polymerizations in the presence of seeds: 3. Emulsion polymerization of vinyl acetate in the presence of quartz powder. Polymer. 1988;29(7):1323–8.10.1016/0032-3861(88)90064-XSearch in Google Scholar

(25) Hergeth WD, Steinau UJ, Bittrich HJ, Simon G, Schmutzer K. Polymerization in the presence of seeds. Part IV: emulsion polymers containing inorganic filler particles. Polymer. 1989;30(2):254–8.10.1016/0032-3861(89)90114-6Search in Google Scholar

(26) Bourgeat-Lami E, Espiard P, Guyot A, Briat S, Gauthier C, Vigier G, et al. Composite polymer colloid nucleated by functionalized silica. ACS Symp Ser. 1995;585(10):112–24.10.1021/bk-1995-0585.ch010Search in Google Scholar

(27) Bourgeat-Lami E, Espiard P, Guyot A. Poly(ethyl acrylate) latexes encapsulating nanoparticles of silica: 1. Functionalization and dispersion of silica. Polymer. 1995;36(23):4385–9.10.1016/0032-3861(95)96843-WSearch in Google Scholar

(28) Bourgeat-Lami E, Lang J. Encapsulation of inorganic particles by dispersion polymerization in polar media: 1. Silica nanoparticles encapsulated by polystyrene. J Colloid Interface Sci. 1998;197(2):293–308.10.1006/jcis.1997.5265Search in Google Scholar

(29) Bourgeat-Lami E, Lang J. Silica–polystyrene composite particles. Macromol Symp. 2000;151(1):337–85.10.1002/1521-3900(200002)151:1<377::AID-MASY377>3.0.CO;2-HSearch in Google Scholar

(30) Ramli RA, Laftah WA, Hashim S. Core–shell polymers: a review. RSC Adv. 2013;3(36):15543–65.10.1039/c3ra41296bSearch in Google Scholar

(31) Sasaki T, Kawagoe S, Mitsuya H, Irie S, Sakurai K. Glass transition of crosslinked polystyrene shells formed on the surface of calcium carbonate whisker. J Polym Sci B Polym Phys. 2006;44(17):2475–85.10.1002/polb.20912Search in Google Scholar

(32) Sasaki T, Misu M, Shimada T, Teramoto M. Glass transition and its characteristic length for thin crosslinked polystyrene shells of rodlike capsules. J Polym Sci B Polym Phys. 2008;46(19):2116–25.10.1002/polb.21545Search in Google Scholar

(33) Sasaki T, Kuroda R, Teramoto M, Yonezawa S, Tsuji H, Sakurai K, et al. Glass transition properties of PMMA thin shells deposited on rodlike calcium carbonate particles. Polym J. 2011;43(5):464–70.10.1038/pj.2011.7Search in Google Scholar

(34) Sasaki T, Suzuki K, Yonezawa S, Irie S, Sakurai K. Preparation and glass transition of crosslinked poly(vinyl acetate) thin shells on the surface of a calcium carbonate core. Polym J. 2011;43(11):881–6.10.1038/pj.2011.90Search in Google Scholar

(35) Kim H, Cang Y, Kang E, Graczykowski B, Secchi M, Montagna M, et al. Direct observation of polymer surface mobility via nanoparticle vibrations. Nat Commun. 2018;9:2918.10.1038/s41467-018-04854-wSearch in Google Scholar PubMed PubMed Central

(36) Lee D, Balmer JA, Schmid A, Tonnar J, Armes SP, Titman JJ. Solid-state nuclear magnetic resonance studies of vinyl polymer/silica colloidal nanocomposite particles. Langmuir. 2010;26(19):15592–8.10.1021/la102298xSearch in Google Scholar PubMed

(37) Kang J-S, Yu C, Zhang F-A. Effect of silane modified SiO2 particles on poly(MMA-HEMA) soap-free emulsion polymerization. Iranian Polym J. 2009;18(12):927–35.Search in Google Scholar

Received: 2020-03-22
Revised: 2020-04-14
Accepted: 2020-04-14
Published Online: 2020-06-02

© 2020 Mina Ishihara et al., published by De Gruyter

This work is licensed under the Creative Commons Attribution 4.0 International License.

Articles in the same Issue

  1. Regular Articles
  2. The regulatory effects of the number of VP(N-vinylpyrrolidone) function groups on macrostructure and photochromic properties of polyoxometalates/copolymer hybrid films
  3. How the hindered amines affect the microstructure and mechanical properties of nitrile-butadiene rubber composites
  4. Novel benzimidazole-based conjugated polyelectrolytes: synthesis, solution photophysics and fluorescent sensing of metal ions
  5. Study on the variation of rock pore structure after polymer gel flooding
  6. Investigation on compatibility of PLA/PBAT blends modified by epoxy-terminated branched polymers through chemical micro-crosslinking
  7. Investigation on degradation mechanism of polymer blockages in unconsolidated sandstone reservoirs
  8. Investigation on the effect of active-polymers with different functional groups for EOR
  9. Fabrication and characterization of hexadecyl acrylate cross-linked phase change microspheres
  10. Surface-induced phase transitions in thin films of dendrimer block copolymers
  11. ZnO-assisted coating of tetracalcium phosphate/ gelatin on the polyethylene terephthalate woven nets by atomic layer deposition
  12. Animal fat and glycerol bioconversion to polyhydroxyalkanoate by produced water bacteria
  13. Effect of microstructure on the properties of polystyrene microporous foaming material
  14. Synthesis of amphiphilic poly(ethylene glycol)-block-poly(methyl methacrylate) containing trityl ether acid cleavable junction group and its self-assembly into ordered nanoporous thin films
  15. On-demand optimize design of sound-absorbing porous material based on multi-population genetic algorithm
  16. Enhancement of mechanical, thermal and water uptake performance of TPU/jute fiber green composites via chemical treatments on fiber surface
  17. Enhancement of mechanical properties of natural rubber–clay nanocomposites through incorporation of silanated organoclay into natural rubber latex
  18. Preparation and characterization of corn starch/PVA/glycerol composite films incorporated with ε-polylysine as a novel antimicrobial packaging material
  19. Preparation of novel amphoteric polyacrylamide and its synergistic retention with cationic polymers
  20. Effect of montmorillonite on PEBAX® 1074-based mixed matrix membranes to be used in humidifiers in proton exchange membrane fuel cells
  21. Insight on the effect of a piperonylic acid derivative on the crystallization process, melting behavior, thermal stability, optical and mechanical properties of poly(l-lactic acid)
  22. Lipase-catalyzed synthesis and post-polymerization modification of new fully bio-based poly(hexamethylene γ-ketopimelate) and poly(hexamethylene γ-ketopimelate-co-hexamethylene adipate) copolyesters
  23. Dielectric, mechanical and thermal properties of all-organic PI/PSF composite films by in situ polymerization
  24. Morphological transition of amphiphilic block copolymer/PEGylated phospholipid complexes induced by the dynamic subtle balance interactions in the self-assembled aggregates
  25. Silica/polymer core–shell particles prepared via soap-free emulsion polymerization
  26. Antibacterial epoxy composites with addition of natural Artemisia annua waste
  27. Design and preparation of 3D printing intelligent poly N,N-dimethylacrylamide hydrogel actuators
  28. Multilayer-structured fibrous membrane with directional moisture transportability and thermal radiation for high-performance air filtration
  29. Reaction characteristics of polymer expansive jet impact on explosive reactive armour
  30. Synthesis of a novel modified chitosan as an intumescent flame retardant for epoxy resin
  31. Synthesis of aminated polystyrene and its self-assembly with nanoparticles at oil/water interface
  32. The synthesis and characterisation of porous and monodisperse, chemically modified hypercrosslinked poly(acrylonitrile)-based terpolymer as a sorbent for the adsorption of acidic pharmaceuticals
  33. Crystal transition and thermal behavior of Nylon 12
  34. All-optical non-conjugated multi-functionalized photorefractive polymers via ring-opening metathesis polymerization
  35. Fabrication of LDPE/PS interpolymer resin particles through a swelling suspension polymerization approach
  36. Determination of the carbonyl index of polyethylene and polypropylene using specified area under band methodology with ATR-FTIR spectroscopy
  37. Synthesis, electropolymerization, and electrochromic performances of two novel tetrathiafulvalene–thiophene assemblies
  38. Wetting behaviors of fluoroterpolymer fiber films
  39. Plugging mechanisms of polymer gel used for hydraulic fracture water shutoff
  40. Synthesis of flexible poly(l-lactide)-b-polyethylene glycol-b-poly(l-lactide) bioplastics by ring-opening polymerization in the presence of chain extender
  41. Sulfonated poly(arylene ether sulfone) functionalized polysilsesquioxane hybrid membranes with enhanced proton conductivity
  42. Fmoc-diphenylalanine-based hydrogels as a potential carrier for drug delivery
  43. Effect of diacylhydrazine as chain extender on microphase separation and performance of energetic polyurethane elastomer
  44. Improved high-temperature damping performance of nitrile-butadiene rubber/phenolic resin composites by introducing different hindered amine molecules
  45. Rational synthesis of silicon into polyimide-derived hollow electrospun carbon nanofibers for enhanced lithium storage
  46. Synthesis, characterization and properties of phthalonitrile-etherified resole resin
  47. Highly thermally conductive boron nitride@UHMWPE composites with segregated structure
  48. Synthesis of high-temperature thermally expandable microcapsules and their effects on foaming quality and surface quality of foamed ABS materials
  49. Tribological and nanomechanical properties of a lignin-based biopolymer
  50. Hydroxyapatite/polyetheretherketone nanocomposites for selective laser sintering: Thermal and mechanical performances
  51. Synthesis of a phosphoramidate flame retardant and its flame retardancy on cotton fabrics
  52. Preparation and characterization of thermoresponsive poly(N-isopropylacrylamide) copolymers with enhanced hydrophilicity
  53. Fabrication of flexible SiO2 nanofibrous yarn via a conjugate electrospinning process
  54. Silver-loaded carbon nanofibers for ammonia sensing
  55. Polar migration behavior of phosphonate groups in phosphonate esterified acrylic grafted epoxy ester composites and their role in substrate protection
  56. Solubility and diffusion coefficient of supercritical CO2 in polystyrene dynamic melt
  57. Curcumin-loaded polyvinyl butyral film with antibacterial activity
  58. Experimental-numerical studies of the effect of cell structure on the mechanical properties of polypropylene foams
  59. Experimental investigation on the three-dimensional flow field from a meltblowing slot die
  60. Enhancing tribo-mechanical properties and thermal stability of nylon 6 by hexagonal boron nitride fillers
  61. Preparation and characterization of electrospun fibrous scaffolds of either PVA or PVP for fast release of sildenafil citrate
  62. Seawater degradation of PLA accelerated by water-soluble PVA
  63. Review Article
  64. Mechanical properties and application analysis of spider silk bionic material
  65. Additive manufacturing of PLA-based scaffolds intended for bone regeneration and strategies to improve their biological properties
  66. Structural design toward functional materials by electrospinning: A review
  67. Special Issue: XXXII National Congress of the Mexican Polymer Society
  68. Tailoring the morphology of poly(high internal phase emulsions) synthesized by using deep eutectic solvents
  69. Modification of Ceiba pentandra cellulose for drug release applications
  70. Redox initiation in semicontinuous polymerization to search for specific mechanical properties of copolymers
  71. pH-responsive polymer micelles for methotrexate delivery at tumor microenvironments
  72. Microwave-assisted synthesis of the lipase-catalyzed ring-opening copolymerization of ε-caprolactone and ω-pentadecanolactone: Thermal and FTIR characterization
  73. Rapid Communications
  74. Pilot-scale production of polylactic acid nanofibers by melt electrospinning
  75. Erratum
  76. Erratum to: Synthesis and characterization of new macromolecule systems for colon-specific drug delivery
https://doi.org/10.1515/epoly-2020-0028
Keywords for this article
soap-free polymerization; core–shell particles; silica; glass transition; cross-link
Creative Commons
BY 4.0

Articles in the same Issue

  1. Regular Articles
  2. The regulatory effects of the number of VP(N-vinylpyrrolidone) function groups on macrostructure and photochromic properties of polyoxometalates/copolymer hybrid films
  3. How the hindered amines affect the microstructure and mechanical properties of nitrile-butadiene rubber composites
  4. Novel benzimidazole-based conjugated polyelectrolytes: synthesis, solution photophysics and fluorescent sensing of metal ions
  5. Study on the variation of rock pore structure after polymer gel flooding
  6. Investigation on compatibility of PLA/PBAT blends modified by epoxy-terminated branched polymers through chemical micro-crosslinking
  7. Investigation on degradation mechanism of polymer blockages in unconsolidated sandstone reservoirs
  8. Investigation on the effect of active-polymers with different functional groups for EOR
  9. Fabrication and characterization of hexadecyl acrylate cross-linked phase change microspheres
  10. Surface-induced phase transitions in thin films of dendrimer block copolymers
  11. ZnO-assisted coating of tetracalcium phosphate/ gelatin on the polyethylene terephthalate woven nets by atomic layer deposition
  12. Animal fat and glycerol bioconversion to polyhydroxyalkanoate by produced water bacteria
  13. Effect of microstructure on the properties of polystyrene microporous foaming material
  14. Synthesis of amphiphilic poly(ethylene glycol)-block-poly(methyl methacrylate) containing trityl ether acid cleavable junction group and its self-assembly into ordered nanoporous thin films
  15. On-demand optimize design of sound-absorbing porous material based on multi-population genetic algorithm
  16. Enhancement of mechanical, thermal and water uptake performance of TPU/jute fiber green composites via chemical treatments on fiber surface
  17. Enhancement of mechanical properties of natural rubber–clay nanocomposites through incorporation of silanated organoclay into natural rubber latex
  18. Preparation and characterization of corn starch/PVA/glycerol composite films incorporated with ε-polylysine as a novel antimicrobial packaging material
  19. Preparation of novel amphoteric polyacrylamide and its synergistic retention with cationic polymers
  20. Effect of montmorillonite on PEBAX® 1074-based mixed matrix membranes to be used in humidifiers in proton exchange membrane fuel cells
  21. Insight on the effect of a piperonylic acid derivative on the crystallization process, melting behavior, thermal stability, optical and mechanical properties of poly(l-lactic acid)
  22. Lipase-catalyzed synthesis and post-polymerization modification of new fully bio-based poly(hexamethylene γ-ketopimelate) and poly(hexamethylene γ-ketopimelate-co-hexamethylene adipate) copolyesters
  23. Dielectric, mechanical and thermal properties of all-organic PI/PSF composite films by in situ polymerization
  24. Morphological transition of amphiphilic block copolymer/PEGylated phospholipid complexes induced by the dynamic subtle balance interactions in the self-assembled aggregates
  25. Silica/polymer core–shell particles prepared via soap-free emulsion polymerization
  26. Antibacterial epoxy composites with addition of natural Artemisia annua waste
  27. Design and preparation of 3D printing intelligent poly N,N-dimethylacrylamide hydrogel actuators
  28. Multilayer-structured fibrous membrane with directional moisture transportability and thermal radiation for high-performance air filtration
  29. Reaction characteristics of polymer expansive jet impact on explosive reactive armour
  30. Synthesis of a novel modified chitosan as an intumescent flame retardant for epoxy resin
  31. Synthesis of aminated polystyrene and its self-assembly with nanoparticles at oil/water interface
  32. The synthesis and characterisation of porous and monodisperse, chemically modified hypercrosslinked poly(acrylonitrile)-based terpolymer as a sorbent for the adsorption of acidic pharmaceuticals
  33. Crystal transition and thermal behavior of Nylon 12
  34. All-optical non-conjugated multi-functionalized photorefractive polymers via ring-opening metathesis polymerization
  35. Fabrication of LDPE/PS interpolymer resin particles through a swelling suspension polymerization approach
  36. Determination of the carbonyl index of polyethylene and polypropylene using specified area under band methodology with ATR-FTIR spectroscopy
  37. Synthesis, electropolymerization, and electrochromic performances of two novel tetrathiafulvalene–thiophene assemblies
  38. Wetting behaviors of fluoroterpolymer fiber films
  39. Plugging mechanisms of polymer gel used for hydraulic fracture water shutoff
  40. Synthesis of flexible poly(l-lactide)-b-polyethylene glycol-b-poly(l-lactide) bioplastics by ring-opening polymerization in the presence of chain extender
  41. Sulfonated poly(arylene ether sulfone) functionalized polysilsesquioxane hybrid membranes with enhanced proton conductivity
  42. Fmoc-diphenylalanine-based hydrogels as a potential carrier for drug delivery
  43. Effect of diacylhydrazine as chain extender on microphase separation and performance of energetic polyurethane elastomer
  44. Improved high-temperature damping performance of nitrile-butadiene rubber/phenolic resin composites by introducing different hindered amine molecules
  45. Rational synthesis of silicon into polyimide-derived hollow electrospun carbon nanofibers for enhanced lithium storage
  46. Synthesis, characterization and properties of phthalonitrile-etherified resole resin
  47. Highly thermally conductive boron nitride@UHMWPE composites with segregated structure
  48. Synthesis of high-temperature thermally expandable microcapsules and their effects on foaming quality and surface quality of foamed ABS materials
  49. Tribological and nanomechanical properties of a lignin-based biopolymer
  50. Hydroxyapatite/polyetheretherketone nanocomposites for selective laser sintering: Thermal and mechanical performances
  51. Synthesis of a phosphoramidate flame retardant and its flame retardancy on cotton fabrics
  52. Preparation and characterization of thermoresponsive poly(N-isopropylacrylamide) copolymers with enhanced hydrophilicity
  53. Fabrication of flexible SiO2 nanofibrous yarn via a conjugate electrospinning process
  54. Silver-loaded carbon nanofibers for ammonia sensing
  55. Polar migration behavior of phosphonate groups in phosphonate esterified acrylic grafted epoxy ester composites and their role in substrate protection
  56. Solubility and diffusion coefficient of supercritical CO2 in polystyrene dynamic melt
  57. Curcumin-loaded polyvinyl butyral film with antibacterial activity
  58. Experimental-numerical studies of the effect of cell structure on the mechanical properties of polypropylene foams
  59. Experimental investigation on the three-dimensional flow field from a meltblowing slot die
  60. Enhancing tribo-mechanical properties and thermal stability of nylon 6 by hexagonal boron nitride fillers
  61. Preparation and characterization of electrospun fibrous scaffolds of either PVA or PVP for fast release of sildenafil citrate
  62. Seawater degradation of PLA accelerated by water-soluble PVA
  63. Review Article
  64. Mechanical properties and application analysis of spider silk bionic material
  65. Additive manufacturing of PLA-based scaffolds intended for bone regeneration and strategies to improve their biological properties
  66. Structural design toward functional materials by electrospinning: A review
  67. Special Issue: XXXII National Congress of the Mexican Polymer Society
  68. Tailoring the morphology of poly(high internal phase emulsions) synthesized by using deep eutectic solvents
  69. Modification of Ceiba pentandra cellulose for drug release applications
  70. Redox initiation in semicontinuous polymerization to search for specific mechanical properties of copolymers
  71. pH-responsive polymer micelles for methotrexate delivery at tumor microenvironments
  72. Microwave-assisted synthesis of the lipase-catalyzed ring-opening copolymerization of ε-caprolactone and ω-pentadecanolactone: Thermal and FTIR characterization
  73. Rapid Communications
  74. Pilot-scale production of polylactic acid nanofibers by melt electrospinning
  75. Erratum
  76. Erratum to: Synthesis and characterization of new macromolecule systems for colon-specific drug delivery
Sign up now to receive a 20% welcome discount
Institutional Access
How does access work?
Have an idea on how to improve our website?
Please write us.
© 2025 De Gruyter Brill
Downloaded on 19.9.2025 from https://www.degruyterbrill.com/document/doi/10.1515/epoly-2020-0028/html
Scroll to top button