Startseite Thermal conductivity of silicone elastomer with a porous alumina continuum
Artikel Open Access

Thermal conductivity of silicone elastomer with a porous alumina continuum

  • Qichao Song , Bo Wang , Zhiyu Han und Zhidong Han EMAIL logo
Veröffentlicht/Copyright: 3. November 2021
Artikel downloaden (PDF)
Veröffentlichen auch Sie bei De Gruyter Brill
Manuskript einreichen Informationen für Autor*innen
e-Polymers
Aus der Zeitschrift e-Polymers Band 21 Heft 1

Abstract

In this paper, porous alumina continuum (PAC) was prepared with alumina powders (APs) by the gel-casting method and was applied to obtain silicone elastomer (SR) composites (PAC/SR) by the impregnating process. The structure was investigated by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The influences of PAC on thermal conductivity and dielectric permittivity of PAC/SR composites were studied in comparison with AP/SR composites. When the alumina content was 14 vol%, the thermal conductivity of the PAC/SR composites reached 0.84 W·(m·K)−1, which was 3.1 times higher than that of the AP/SR composites. The thermal conductivity of PAC/SR and AP/SR was simulated by theoretical models, and the interfacial thermal resistance was calculated by effective medium theory, which indicated the advantages of PAC in enhancing the thermal conductivity of SR-based composites and the reduced interfacial thermal resistance between PAC and SR.

Graphical abstract

PAC provided numerous interpenetrated channels for the access of SR and prompted the formation of interconnected three-dimensional networks for remarkable improvement on the thermal conductivity of PAC/SR composites.

Keywords: porous alumina continuum; thermal conductivity; three-dimensional network; silicone elastomer; thermal interface materials

1 Introduction

The increasing demand for thermally conductive materials has inspired to meet the rapidly developing requirements of thermal management in electronic devices with integrated, miniaturized, and functionalized characteristics (1). Due to high heat accumulation inside the devices, heat dissipation becomes crucial to maintain the stability and reliability of the devices (2). Thermal interface materials (TIMs) are thus applied to improve the thermal conductivity between electronic components and heat sinks. As a kind of typical TIM, polymer-based composites have been widely investigated in facing the challenges of the poor thermal conductivity of polymers and their potential applications as substitutes of metals in some industrial scenarios of lightweight, low cost, high specific modulus, and easy to manufacture (3). Fillers with high thermal conductivity, such as carbon fillers (4), ceramic (5), and metal particles (6), are usually introduced to obtain thermally conductive polymer-based composites. Much effort has been devoted to build an efficient pathway for heat dissipation in thermally conductive composites by closest packing of fillers (7), hybrid fillers (8), orientations of fillers (9), and thermally conductive framework (10).

Recently, the construction of a thermally conductive network in polymers has attracted much attention. The addition of hybrid fillers into composites was investigated as an efficient way to form a thermally conductive network and achieve a synergistic effect on the enhancement of thermal conductivity of polymer-based composites (11). A three-dimensional network was constructed with modified multiwall carbon nanotubes and graphene in the PVDF matrix and the composites presented a thermal conductivity of 1.46 W·(m·K)−1 at 10 wt% filler loading (12). 3D phonon skeleton was built with stacked boron nitride (BN) platelets and reduced graphene oxide (rGO) by the combination of ice-templated and infiltrating methods, which resulted in a through-plane thermal conductivity of 5.05 W·(m·K)−1 for epoxy-based composites at a filler loading of 13.16 vol% (13). The oriented carbon fiber/alumina/silicon rubber composites were fabricated by 3D printing, which showed a thermal conductivity of 7.36 W·(m·K)−1 at 12 vol% carbon fiber and 30 vol% alumina loadings (14). 3D printing was also applied to construct the filler networks with oriented BN platelets and spherical alumina and resulted in 3.64 W·(m·K)−1 in-plane thermal conductivity of the polydimethylsiloxane (PDMS) composites with hybrid fillers of 35 wt% BN and 30 wt% alumina (15).

Alumina (Al2O3) is one of the most popular thermally conductive fillers owing to its good thermal conductivity, electric insulation, and low cost (16). The morphology, crystalline structure, and loading fraction of alumina exert strong influences on the thermal conductivity of polymer-based composites (17,18,19). High thermal conductivity is usually attained by increasing the loading fraction of alumina fillers in the composites. A thermal conductivity of 6.7 W·(m·K)−1 was achieved at a high alumina fraction of up to 79 vol% in epoxy-based composites by using spherical particles with different size scales (20). A thermal conductivity of 13.46 W·(m·K)−1 was reported at a high alumina fraction of up to 70 vol% in epoxy-based composites by using sintered porous alumina ceramic skeletons (21). Thermal conductivity of 2.92 W·(m·K)−1 of silicone-based composites with 80 vol% hybrid alumina powder was obtained through in situ polymerization (22). In addition, attempts were also made to fabricate a 3D alumina scaffold in order to decrease the loading fraction of alumina while reaching a high thermal conductivity. A continuous alumina framework in epoxy was realized through a protein foaming technique followed with infiltration, and a thermal conductivity of 2.58 W·(m·K)−1 was obtained at a filler fraction of 23.32 vol% (23). A thermally conductive 3D framework in silicone rubber (SR) was constructed by foaming of alumina/SR composites with NH4HCO3 and a thermal conductivity of the composites with 32.6 wt% alumina reached 0.747 W·(m·K)−1 (24).

Silicone resin, owing to its low toxicity, excellent electrical insulation, good mechanical properties, high chemical stability, and thermal stability, has been widely applied as one of the typical polymeric materials to develop TIM (25,26). In view of the poor thermal conductivity of silicone resin and the insulation requirements of TIM applications, alumina is considered to be an ideal candidate filler to prepare silicone-based composites with good thermally conductive and electrically insulating properties (27). To obtain thermally conductive silicone-based composites with relatively low dielectric permittivity at a low fraction of alumina, this paper aims at constructing a porous alumina continuum (PAC) with alumina powders (AP) by the gel-casting method and forming a three-dimensional thermally conductive network in silicone elastomer by the impregnating process. Using these methods, a new solution would be proposed for the development of silicone-based TIM.

2 Materials and methods

2.1 Materials

Alumina powder (AP) with a purity of 99.9% and an average size of 3 μm was purchased from Dongguan Dongchao Material Technology Co., Ltd. Magnesium oxide (MgO) with a purity of 99.9% was purchased from Shanghai Macklin Biochemical Technology Co., Ltd. Agarose was obtained from Shanghai Lanji Technology Development Co., Ltd. Sodium dodecyl sulfate (SDS) was purchased from Tianjin Guangfu Fine Chemical Research Institute. Silicone elastomer (Sylgard 184) was purchased from Dow Corning Corp.

2.2 Preparation methods

Alumina powder (AP) was used as a raw material to prepare the porous alumina continuum (PAC) by the gel-casting method. The ceramic slurry with an alumina content of 40 vol% was prepared by ball milling for 4 h with the addition of 1.0 wt% agarose as a monomer, 0.6 wt% SDS as a dispersant, 1.0 wt% MgO as a sintering aid, and deionized water as a solvent. The well-dispersed slurry was foamed with 3.0 wt% SDS under stirring with a blender for 30 min. The foamed slurry was then cast into a rubber mold and matured at room temperature for 48 h to form a green body. The green body was transferred into the tube furnace and sintered under an air atmosphere. The furnace was heated to 1,250°C at a rate of 5°C·min−1 and maintained at 1,250°C for 1 h. After the furnace was naturally cooled, PAC was obtained and sanded to the required size. The content of AP in the slurry was adjusted to obtain the PAC for the applications in thermal conductive composites.

The PAC was immersed in the silicone elastomer (SR) solution to prepare PAC/SR composites by the impregnating process. SR solution was obtained by blending two components together according to the ratio recommended by the supplier. The mixture of PAC and SR solution was treated under a vacuum environment for 1 h and then cured at 100°C for 1 h. The composites of PAC/SR were thus obtained. The processes of preparing PAC and PAC/SR composites are schematically illustrated in Figure 1. The samples with PAC contents of 5.0, 7.5, 10, and 14 vol% were prepared and named PAC5.0/SR, PAC7.5/SR, PAC10/SR, and PAC14/SR, respectively.

Figure 1 Schematic process to prepare PAC and PAC/SR composites.
Figure 1

Schematic process to prepare PAC and PAC/SR composites.

The composites of AP and SR (AP/SR) were also prepared to make a comparison with PAC/SR composites. AP was mixed together with the components of SR and treated under a vacuum environment for 1 h and cured at 100°C for 1 h. The samples with AP contents of 5.0, 7.5, 10, 14, and 41 vol% were prepared and named as AP5.0/SR, AP7.5/SR, AP10/SR, AP14/SR, and AP41/SR, respectively.

2.3 Characterization

A field emission scanning electron microscope (SEM, Sirion200, FEI) was used to observe the morphological structure of PAC and the composites with the cryo-fractured section metalized with gold. X-ray diffractometer (XRD, X’Pert PRO, PANalytical) was used to characterize the crystalline structure of the AP and PAC with Cu Kα radiation (λ = 1.5406 Å) at a voltage of 40 kV and a current of 40 mA with a step of 0.013° and a scanning speed of 8°·min−1 in the range of 5–80°. The thermal conductivity (λ) of the composites was tested by using a thermal conductivity meter (LFA447, Nanoflash, Netzsch) with a sample diameter of 12.7 mm and a thickness of 2.0 mm. A thermoviewer (E8, FLIR) was used to capture the infrared thermal images and record the thermographic observations. The samples with a thickness of 2.0 mm were placed horizontally on the plate preheated to a constant temperature of 80°C. The images on the top surface of samples were recorded at 2, 10, 20, 40, and 60 s after the samples were exposed to the heated plate. A broadband dielectric spectrometer (Alpha-A, Novocontrol, Germany) was used to analyze the dielectric constant and loss factor at room temperature at a voltage of 3 V in the frequency range of 1–106 Hz on the sample coated with circular aluminum electrodes with a diameter of 25 mm using a high-vacuum resistance evaporation coating machine (Model ZHD-400, Beijing Techno Technology Co., Ltd.).

3 Results and discussion

The SEM micrographs of the PAC are shown in Figure 2. From the full view of the PAC, as shown in Figure 2a, the continuous network was observed with a uniform pore structure. The cells in Figure 2b were connected by the thin alumina wall and the windows were observed between two neighboring cells. The joint of the cell walls is clearly noticed in Figure 2c, which was used to build the three-dimensional structure of PAC. The alumina particles in the cross-section of the joint were found to be well connected in Figure 2d and present in good continuity. The closely bonded particles of alumina were attributed to the high-temperature sintering with the aid of MgO, which can be also used as a good thermally conductive filler. Accordingly, PAC with a well-structured scaffold was obtained and its good thermal conductivity could be expected by decreasing the interfacial thermal resistance between fillers due to the bonded alumina particles (28).

Figure 2 SEM micrographs of PAC at different magnifications: (a) a network structure of PAC at a magnification of 160×, (b) three-dimensional cell structure of PAC at a magnification of 500×, (c) a continuous wall structure of PAC at a magnification of 1,000×, and (d) the micro-morphological structure of alumina particles in the joint of PAC at a magnification of 10,000×.
Figure 2

SEM micrographs of PAC at different magnifications: (a) a network structure of PAC at a magnification of 160×, (b) three-dimensional cell structure of PAC at a magnification of 500×, (c) a continuous wall structure of PAC at a magnification of 1,000×, and (d) the micro-morphological structure of alumina particles in the joint of PAC at a magnification of 10,000×.

The thermal conductivity of alumina shows a strong dependence on the crystalline structure (17). The XRD patterns of AP and PAC are shown in Figure 3. The same diffraction peaks were observed for AP and PAC, which were assigned to the reflections of α-Al2O3 according to the standard pattern of Corundum (ICDD PDF#83-2080). The results revealed the same crystalline structure of PAC as AP after the gel-casting process and indicated their same intrinsic thermal conductivities as thermally conductive fillers.

Figure 3 XRD patterns of PAC and AP.
Figure 3

XRD patterns of PAC and AP.

3.1 Morphology of the composites

Figure 4 illustrates the photographs and SEM micrographs of AP/SR and PAC/SR composites. Comparing the photographs of SR, PAC, and PAC14/SR in Figure 4a, the integrated structure of PAC was demonstrated in the composites of PAC14/SR, which showed the transparent parts of SR and the macropores of PAC. Meanwhile, the composites of AP14/SR presented the homogeneous appearance in white, thanks to the well-dispersed alumina particles in SR as shown in Figure 4b. The SEM micrograph of cryo-fractured sections of AP14/SR in Figure 4c evidenced the continuous structure of PAC in the SR matrix. The joints and the cell walls of PAC are clearly observed in Figure 4d. Furthermore, there were no noticeable voids in the composites. The good compatibility between the cell wall of PAC and the matrix of SR is revealed in the inserted SEM micrograph in Figure 4d. Consequently, PAC can provide numerous interpenetrated channels for the access of SR, thanks to its ample open pores and high porosity, which is quite a contrast to the randomly distributed alumina particles in AP/SR composites by adding thermal conductive fillers.

Figure 4 Morphological images of the composites: (a) photographs of SR, PAC, AP14/SR, and PAC14/SR, (b) SEM micrograph of the cryo-fractured section of AP14/SR, (c) SEM micrograph of the cryo-fractured section of the PAC14/SR composite at low magnification and (d) that at high magnification with inserted micrograph of the cell wall in the SR matrix.
Figure 4

Morphological images of the composites: (a) photographs of SR, PAC, AP14/SR, and PAC14/SR, (b) SEM micrograph of the cryo-fractured section of AP14/SR, (c) SEM micrograph of the cryo-fractured section of the PAC14/SR composite at low magnification and (d) that at high magnification with inserted micrograph of the cell wall in the SR matrix.

3.2 Thermal conductivity

Figure 5 presents the thermal conductivity of PAC/SR and AP/SR as a function of the filler content. A continuously increasing thermal conductivity of the composites was observed as the filler content increased. The PAC/SR composites exhibited significantly higher thermal conductivity than the AP/SR composites. The thermal conductivity of the PAC/SR composites with the alumina content of 14 vol% reached 0.84 W·(m·K)−1, which increased by 3.1 times in comparison to the AP/SR composites with the same alumina content. The remarkable advantage of PAC was evidenced in improving the thermal conductivity of the composites. PAC as an integrated filler prompted the formation of interconnected three-dimensional networks of alumina in PAC/SR composites and exerted the effective function on the thermal conductivity. In contrast, the randomly dispersed alumina particles in AP/SR composites arranged disorderly and failed to construct a good thermally conductive pathway.

Figure 5 Thermal conductivity of AP/SR and PAC/SR at different filler contents.
Figure 5

Thermal conductivity of AP/SR and PAC/SR at different filler contents.

The enhancement of thermal conductivity (η) was adopted to make a comparison between PAC/SR and AP/SR according to Eq. 1 (15). As shown in Figure 6, the thermal conductivity enhancement of PAC/SR in contrast to AP/SR increased with the filler content. The enhancement increased from 30% to 236% as the filler content increased from 5 to 14 vol%. Thanks to the effective thermal conducting network of PAC, the high thermal conductivity of PAC/SR composites was realized at a much lower content of alumina. While considering the contribution per unit volume fraction of PAC and AP to the thermal conductivity of the composites with an alumina content of 14 vol%, a value of 0.054 W·(m·K)−1 per unit volume was obtained for PAC in contrast to that of 0.013 W·(m·K)−1 per unit volume for AP. The results indicated the importance of the three-dimensional continuum of alumina on the enhancement of thermal conductivity of composites:

(1) η = λ PAC/SR − λ AP/SR λ AP/SR × 100

where λ PAC/SR and λ AP/SR are the thermal conductivities of the PAC/SR and AP/SR composites, respectively.

Figure 6 The thermal conductivity enhancement of PAC/SR in contrast to AP/SR.
Figure 6

The thermal conductivity enhancement of PAC/SR in contrast to AP/SR.

The thermal conductivity of the composites was simulated according to four theoretical models, viz., the series model, parallel model, Maxwell model, and EMT model as expressed in Eqs. 2–5 (29,30). As can be seen in Figure 5, the values of thermal conductivities of PAC/SR and AP/SR were situated between the simulated lines of the series model and parallel model. The simulated line of the series model represented the lower bound of the composites while that of the parallel model gave the upper bound. Good fitting was found in simulating the thermal conductivity of AP/SR by the Maxwell model, which was proved to be useful for the homogeneous composites with randomly dispersed particles. Taking the thermal conductivity of PAC/SR into account, none of the models could fit the experimental results of PAC/SR. The three-dimensional continuum of alumina was challenged in the description of its size and shape during simulations. On the other hand, the experimental thermal conductivity of PAC/SR was much close to the simulated results by the parallel model. In view of the co-continuous structure of PAC and SR in the composites, we used a combined model of the series and parallel models (S-P model) to simulate the thermal conductivity of PAC/SR according to Eq. 6 (31, 32). After simulations with the experimental results of PAC/SR, a good fitting curve was obtained when n = 0.38. As a result, a model was obtained, which was of good predictability in simulating the thermal conductivity of PAC/SR.

(2) 1 λ c = V f λ f + ( 1 − V f ) λ p

(3) λ c = V f λ f + ( 1 − V f ) λ p

(4) λ c = λ p λ f + 2 λ p + 2 V f ( λ f − λ p ) λ f + 2 λ p − V f ( λ f − λ p )

(5) V f λ f − λ c λ f + 2 λ c + ( 1 − V f ) λ p − λ c λ p + 2 λ c = 0

where V f is the volume fraction of the filler; λ p, λ f, and λ c are the thermal conductivities of the polymer matrix, the filler, and the composites, respectively. The thermal conductivities of 0.16 W·(m·K)−1 and 28 W·(m·K)−1 were adopted for SR and alumina during simulations, respectively.

(6) λ c n = V f λ f n + ( 1 − V f ) λ p n

where n is the coefficient in the range of −1 and 1. When n = −1, the series model is obtained; when n = 1, the parallel model is obtained.

3.3 Interfacial thermal resistance

As well known, the parallel model overestimates the contribution of the fillers because it assumes the independent contributions from each phase to the total conductivity and the perfect contact between particles. Even though a good continuous structure was designed in PAC, the defect can hardly be avoided and weakened the thermal conductivity of PAC. Furthermore, the influences of interfacial thermal resistance (R B) between the filler and the matrix should be taken into consideration while taking the advantage of the three-dimensional network of PAC and maximizing its contribution at a much lower content. Here, the Maxwell-Garnett effective medium theory (MG-EMT) was introduced to calculate the value of R B according to Eq. 7 (33):

(7) λ c = λ f 3 λ p + 2 V f ( λ f − λ p ) ( 3 − V f ) λ f + V f λ p + R B V f λ p λ f H

where R B is the interfacial thermal resistance at the filler/matrix interface and H is the thickness of the filler. Considering the particle size of alumina, 3 μm was adopted as H during calculations.

Figure 7 presents interfacial thermal resistance of AP/SR and PAC/SR as a function of the filler content. The composites of PAC/SR showed much lower interfacial thermal resistance than that of AP/SR. The positive influence of PAC on the thermal conductivity could be attributed to the decreased interfacial thermal resistance. Meanwhile, the interfacial thermal resistance could also dramatically alter the thermal conductivity of the composites, which gave rise to the much lower thermal conductivity of the composites than that of alumina (34). The high interfacial thermal resistance was induced by the phonon scattering in the filler network and the interface between the fillers and polymer matrix. The dispersed alumina in AP/SR failed to form an effective path in the SR matrix and contributed little to heat conduction due to the high interfacial thermal resistance of the interface between the particles and the matrix (21). PAC, owing to its good integrity and interconnected structure, was used to build a three-dimensional network in the SR matrix and played a vital role in heat conduction.

Figure 7 Interfacial thermal resistance of AP/SR and PAC/SR by the MG-EMT model.
Figure 7

Interfacial thermal resistance of AP/SR and PAC/SR by the MG-EMT model.

3.4 Heat dissipation

In order to further illustrate the heat transfer performances of the composites, infrared thermal imaging was applied to characterize the temperature profiles of SR, AP14/SR, and PAC14/SR, as shown in Figure 8. The temperature distribution on the top surface of PAC14/SR was obviously different from that of SR and AP14/SR. At 10 s, PAC14/SR showed higher temperatures than SR and AP14/SR. It took 40 s for PAC14/SR to reach 70°C, while it took 55 s for AP14/SR and 66 s for SR. According to the temperature profiles vs time, the temperature on the surface tended to level off after 60 s. At 90 s, the temperature of PAC14/SR settled at 79°C, while those of AP14/SR and SR settled at 75°C and 72°C, respectively. As can be seen, the temperature of PAC14/SR increased much faster in comparison with AP14/SR and SR and the temperature at 90 s was much closer to the plate temperature (80°C). The results revealed better heat transfer performances of PAC14/SR than AP14/SR and SR, which can be beneficial to accelerate heat dissipation.

Figure 8 The temperature profiles vs time of SR, AP14/SR, and PAC14/SR; inset: photos of infrared thermal imaging.
Figure 8

The temperature profiles vs time of SR, AP14/SR, and PAC14/SR; inset: photos of infrared thermal imaging.

3.5 Dielectric constant and loss factor

As TIM, dielectric properties are very important parameters to be considered. Thanks to the good electrically insulative characteristics of alumina, the composites usually present good insulation properties in terms of resistivity. Recently, attention has been paid to composites with certain dielectric permittivity and dielectric loss due to the rapid development in the fields of high frequency. Considering the opportunities in these fields, the dielectric permittivity and loss factor were investigated by a dielectric spectrometer on two samples with similar thermal conductivities, AP63/SR and PAC21/SR. Figure 9 shows their curves as a function of frequency. The permittivity of PAC21/SR was 4.30 at 100 Hz while that of AP63/SR was 6.06. A remarkable increase in permittivity was observed due to a higher content of alumina in AP63/SR. The loss factor curve of PAC21/SR showed a peak around 45 Hz, which gave rise to a higher loss factor than AP63/SR. As a result, the loss factor of PAC21/SR was 0.009 at 100 Hz while that of AP63/SR was 0.003. Taking the continuous network structure of PAC into account, the dielectric loss peak could be attributed to the interface polarization between alumina particles. The loss factor of AP63/SR and PAC21/SR tended to be similar after 104 Hz.

Figure 9 The dielectric permittivity (ε′) and the loss factor (tan δ) of AP63/SR and PAC21/SR composites as a function of frequency.
Figure 9

The dielectric permittivity (ε′) and the loss factor (tan δ) of AP63/SR and PAC21/SR composites as a function of frequency.

4 Conclusion

PAC with a structured scaffold was obtained by the gel-casting method and applied in SR to construct a thermally conductive network for heat dissipation. The good compatibility between PAC and SR was revealed, and no voids were found in the composites. The integrated structure of PAC in the SR matrix was demonstrated by the continuous joints and cell walls, which were used to build a three-dimensional alumina network in the composites. A remarkable enhancement of thermal conductivity was revealed for PAC/SR composites in comparison with AP/SR composites and neat SR. The thermal conductivity of the PAC/SR composites with an alumina content of 14 vol% reached 0.84 W·(m·K)−1, which was 3.1 times that of the AP/SR composites with the same alumina content and 5.3 times than the neat SR. The Maxwell model and S-P model were found to well fit the experimental results of AP/SR and PAC/SR, respectively. The effects of PAC on the thermal conductivity of the composites can be explained by the decreased interfacial thermal resistance between the filler and the matrix, as well as that between the fillers due to the densely packed alumina particles. Such an effective thermal conductive network was beneficial to accelerate the heat dissipation and resulted in the better heat transfer performances of PAC14/SR. As a result, much lower loading of PAC would be required to obtain a certain thermal conductivity of the silicone-based composites in contrast to AP, which gave rise to a lower dielectric permittivity of the composites and would meet the developing demands for TIM.

  1. Funding information: This research was funded by the Key projects of Natural Science Foundation of Heilongjiang Province, grant number ZD2020E007.

  2. Author contributions: Qichao Song: conceptualization, methodology, project administration; Bo Wang: investigation, data curation, writing-original draft preparation; Zhiyu Han: software, validation; Zhidong Han: supervision, writing-reviewing and editing, funding acquisition. All authors have read and agreed to the published version of the manuscript.

  3. Conflict of interest: The authors state no conflict of interest.

References

(1) Li Q, Chen L, Gadinski M, Zhang S, Zhang G, Li H, et al. Flexible high-temperature dielectric materials from polymer nanocomposites. Nature. 2015;523:576–9.10.1038/nature14647Suche in Google Scholar PubMed

(2) Moore A, Shi L. Emerging challenges and materials for thermal management of electronics. Mater Today. 2014;17(1):163–74.10.1016/j.mattod.2014.04.003Suche in Google Scholar

(3) Gu J, Ruan K. Breaking through bottlenecks for thermally conductive polymer composites: a perspective for intrinsic thermal conductivity, interfacial thermal resistance and theoretics. Nano-Micro Lett. 2021;13:110.10.1007/s40820-021-00640-4Suche in Google Scholar PubMed PubMed Central

(4) Wang G, Gao M, Yang B, Chen Q. The morphological effect of carbon fibers on the thermal conductive composites. Int J Heat Mass Tran. 2020;152:119477.10.1016/j.ijheatmasstransfer.2020.119477Suche in Google Scholar

(5) Wu X, Liu W, Ren L, Zhang C. Highly thermally conductive boron nitride@UHMWPE composites with segregated structure. e-Polymers. 2020;20:510–8.10.1515/epoly-2020-0053Suche in Google Scholar

(6) Ma F, Zhang P, Xia ZZ, Li M. How to enhance the effective thermal conductivity of composite material based on optimization method? Energy. 2015;87:400–11.10.1016/j.energy.2015.05.006Suche in Google Scholar

(7) Li H, Zheng W. Enhanced thermal conductivity of epoxy/alumina composite through multiscale-disperse packing. J Compos Mater. 2021;55(1):17–25.10.1177/0021998320942575Suche in Google Scholar

(8) Gao C, Shen Y, Wang T. Enhanced thermal conductivity for traditional epoxy packaging composites by constructing hybrid conductive network. Mater Res Express. 2020;7:065308.10.1088/2053-1591/ab99e8Suche in Google Scholar

(9) Huang Y, Hu J, Yao Y, Zeng X, Sun J, Pan G, et al. Manipulating orientation of silicon carbide nanowire in polymer composites to achieve high thermal conductivity. Adv Mater Interfaces. 2017;4:1700446.10.1002/admi.201700446Suche in Google Scholar

(10) Song J, Wu L, Zhang Y. Thermal conductivity enhancement of alumina/silicone rubber composites through constructing a thermally conductive 3D framework. Polym Bull. 2020;77:2139–53.10.1007/s00289-019-02839-3Suche in Google Scholar

(11) Zhang H, Zhang X, Li D, Yang X, Wu D, Sun J. Thermal conductivity enhancement via conductive network conversion from “sand-like” to “stone-like” in the polydimethylsiloxane composites. Compos Comm. 2020;22:100509.10.1016/j.coco.2020.100509Suche in Google Scholar

(12) Guo H, Liu J, Wang Q, Liu M, Du C, Li B, et al. High thermal conductive poly(vinylidene fluoride)-based composites with well-dispersed carbon nanotubes/graphene three-dimensional network structure via reduced interfacial thermal resistance. Compos Sci Technol. 2019;181:107713.10.1016/j.compscitech.2019.107713Suche in Google Scholar

(13) Yao Y, Sun J, Zeng X, Sun R, Xu J, Wong C. Construction of 3D skeleton for polymer composites achieving a high thermal conductivity. Small. 2018;14:1704044.10.1002/smll.201704044Suche in Google Scholar PubMed

(14) Ji J, Chiang S, Liu M, Liang X, Li J, Gan L, et al. Enhanced thermal conductivity of alumina and carbon fibre filled composites by 3-D printing. Thermochim Acta. 2020;690:178649.10.1016/j.tca.2020.178649Suche in Google Scholar

(15) Liu M, Chiang S, Chu X, Li J, Gan L, He Y, et al. Polymer composites with enhanced thermal conductivity via oriented boron nitride and alumina hybrid fillers assisted by 3-D printing. Ceram Int. 2020;46(13):20810–8.10.1016/j.ceramint.2020.05.096Suche in Google Scholar

(16) Agari Y, Ueda A, Tanaka M, Nagai S. Thermal conductivity of a polymer filled with particles in the wide range from low to super-high volume content. J Appl Polym Sci. 1990;40(5–6):929–41.10.1002/app.1990.070400526Suche in Google Scholar

(17) Huda N, Whitney M, Razmpoosh M, Gerlich A, Wen J, Corbin S. How phase (alpha and gamma) and porosity affect specific heat capacity and thermal conductivity of thermal storage alumina. J Am Ceram Soc. 2021;104:1436–47.10.1111/jace.17528Suche in Google Scholar

(18) Huang L, Lv X, Tang Y, Ge G, Zhang P, Li Y. Effect of alumina nanowires on the thermal conductivity and electrical performance of epoxy composites. Polymers. 2020;12:2126.10.3390/polym12092126Suche in Google Scholar PubMed PubMed Central

(19) Abad B, Maiz J, Ruiz-Clavijo A, Caballero-Calero O, Martin-Gonzalez M. Tailoring thermal conductivity via three-dimensional porous alumina. Sci Rep. 2016;6:38595.10.1038/srep38595Suche in Google Scholar PubMed PubMed Central

(20) Li H, Zheng E. Enhanced thermal conductivity of epoxy/alumina composite through multiscale-disperse packing. J Compos Mater. 2021;55:17–25.10.1177/0021998320942575Suche in Google Scholar

(21) Hu Y, Du G, Chen N. A novel approach for Al2O3/epoxy composites with high strength and thermal conductivity. Compos Sci Technol. 2016;124:36–43.10.1016/j.compscitech.2016.01.010Suche in Google Scholar

(22) Liu Y, Chen Z, Shen Y, Zhou Y, Wang D, Lei Z, et al. Silicone-based alumina composites synthesized through in situ polymerization for high thermal conductivity and thermal stability. Mater Lett. 2020;261:127002.10.1016/j.matlet.2019.127002Suche in Google Scholar

(23) Xiao C, Chen L, Tang Y, Zhang X, Zheng K, Tiana X. Three dimensional porous alumina network for polymer composites with enhanced thermal conductivity. Compos A. 2019;124:105511.10.1016/j.compositesa.2019.105511Suche in Google Scholar

(24) Song J, Wu L, Zhang Y. Thermal conductivity enhancement of alumina/silicone rubber composites through constructing a thermally conductive 3D framework. Polym Bull. 2020;77:2139–53.10.1007/s00289-019-02839-3Suche in Google Scholar

(25) Paul DR, Mark JE. Fillers for polysiloxane (“silicone”) elastomers. Prog Polym Sci. 2010;35(7):893–901.10.1016/j.progpolymsci.2010.03.004Suche in Google Scholar

(26) Khan J, Momin SA, Mariatti M. A review on advanced carbon-based thermal interface materials for electronic devices. Carbon. 2020;168:65–112.10.1016/j.carbon.2020.06.012Suche in Google Scholar

(27) Hansson J, Nilsson T, Ye L, Liu J. Novel nanostructured thermal interface materials: a review. Int Mater Rev. 2018;63(1):22–45.10.1080/09506608.2017.1301014Suche in Google Scholar

(28) Shigeno K, Kuraoka Y, Asakawa T, Fujimori H. Sintering mechanism of low-temperature co-fired alumina featuring superior thermal conductivity. J Am Ceram Soc. 2021;104(5):2017–29.10.1111/jace.17626Suche in Google Scholar

(29) Ebadi-Dehaghani H, Reiszadeh M, Chavoshi A, Nazempour M, Vakili MH. The effect of zinc oxide and calcium carbonate nanoparticles on the thermal conductivity of polypropylene. J Macromol Sci B. 2014;53:93–107.10.1080/00222348.2013.810032Suche in Google Scholar

(30) Kaddouri W, Moumen AEl, Kanita T, Madani S, Imad A. On the effect of inclusion shape on effective thermal conductivity of heterogeneous materials. Mech Mater. 2016;92:28–41.10.1016/j.mechmat.2015.08.010Suche in Google Scholar

(31) Wang J, Carson J, North M, Cleland D. A new approach to modelling the effective thermal conductivity of heterogeneous materials. Int J Heat Mass Tran. 2006;49:3075–83.10.1016/j.ijheatmasstransfer.2006.02.007Suche in Google Scholar

(32) Agari Y, Ueda A, Nagai S. Thermal conductivity of a polymer composite. J Appl Polym Sci. 1993;49(9):1625–34.10.1002/app.1993.070490914Suche in Google Scholar

(33) Hu Z, Wang S, Chen G, Zhang Q, Wu K, Shi J, et al. An aqueous-only, green route to exfoliate boron nitride for preparation of high thermal conductive boron nitride nanosheet/cellulose nanofiber flexible film. Compos Sci Technol. 2018;168:287–95.10.1016/j.compscitech.2018.09.020Suche in Google Scholar

(34) Warzoha RJ, Fleischer AS. Heat flow at nanoparticle interfaces. Nano Energy. 2014;6:137–58.10.1016/j.nanoen.2014.03.014Suche in Google Scholar
Received: 2021-07-12
Revised: 2021-09-23
Accepted: 2021-10-01
Published Online: 2021-11-03

© 2021 Qichao Song et al., published by De Gruyter

This work is licensed under the Creative Commons Attribution 4.0 International License.

Artikel in diesem Heft

  1. Research Articles
  2. Research on the mechanism of gel accelerator on gel transition of PAN solution by rheology and dynamic light scattering
  3. Gel point determination of gellan biopolymer gel from DC electrical conductivity
  4. Composite of polylactic acid and microcellulose from kombucha membranes
  5. Synthesis of highly branched water-soluble polyester and its surface sizing agent strengthening mechanism
  6. Fabrication and characterization of poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) modified with nano-montmorillonite biocomposite
  7. Fabrication of N-halamine polyurethane films with excellent antibacterial properties
  8. Formulation and optimization of gastroretentive bilayer tablets of calcium carbonate using D-optimal mixture design
  9. Sustainable nanocomposite films based on SiO2 and biodegradable poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) (PHBH) for food packaging
  10. Evaluation of physicochemical properties of film-based alginate for food packing applications
  11. Electrically conductive and light-weight branched polylactic acid-based carbon nanotube foams
  12. Structuring of hydroxy-terminated polydimethylsiloxane filled by fumed silica
  13. Surface functionalization of nanostructured Cu/Ag-deposited polypropylene fiber by magnetron sputtering
  14. Influence of composite structure design on the ablation performance of ethylene propylene diene monomer composites
  15. MOFs/PVA hybrid membranes with enhanced mechanical and ion-conductive properties
  16. Improvement of the electromechanical properties of thermoplastic polyurethane composite by ionic liquid modified multiwall carbon nanotubes
  17. Natural rubber latex/MXene foam with robust and multifunctional properties
  18. Rheological properties of two high polymers suspended in an abrasive slurry jet
  19. Two-step polyaniline loading in polyelectrolyte complex membranes for improved pseudo-capacitor electrodes
  20. Preparation and application of carbon and hollow TiO2 microspheres by microwave heating at a low temperature
  21. Properties of a bovine collagen type I membrane for guided bone regeneration applications
  22. Fabrication and characterization of thermoresponsive composite carriers: PNIPAAm-grafted glass spheres
  23. Effect of talc and diatomite on compatible, morphological, and mechanical behavior of PLA/PBAT blends
  24. Multifunctional graphene nanofiller in flame retarded polybutadiene/chloroprene/carbon black composites
  25. Strain-dependent wicking behavior of cotton/lycra elastic woven fabric for sportswear
  26. Enhanced dielectric properties and breakdown strength of polymer/carbon nanotube composites by coating an SrTiO3 layer
  27. Analysis of effect of modification of silica and carbon black co-filled rubber composite on mechanical properties
  28. Polytriazole resins toughened by an azide-terminated polyhedral oligomeric silsesquioxane (OADTP)
  29. Phosphine oxide for reducing flammability of ethylene-vinyl-acetate copolymer
  30. Study on preparation and properties of bentonite-modified epoxy sheet molding compound
  31. Polyhedral oligomeric silsesquioxane (POSS)-modified phenolic resin: Synthesis and anti-oxidation properties
  32. Study on structure and properties of natural indigo spun-dyed viscose fiber
  33. Biodegradable thermoplastic copolyester elastomers: Methyl branched PBAmT
  34. Investigations of polyethylene of raised temperature resistance service performance using autoclave test under sour medium conditions
  35. Investigation of corrosion and thermal behavior of PU–PDMS-coated AISI 316L
  36. Modification of sodium bicarbonate and its effect on foaming behavior of polypropylene
  37. Effect of coupling agents on the olive pomace-filled polypropylene composite
  38. High strength and conductive hydrogel with fully interpenetrated structure from alginate and acrylamide
  39. Removal of methylene blue in water by electrospun PAN/β-CD nanofibre membrane
  40. Theoretical and experimental studies on the fabrication of cylindrical-electrode-assisted solution blowing spinning nanofibers
  41. Influence of l-quebrachitol on the properties of centrifuged natural rubber
  42. Ultrasonic-modified montmorillonite uniting ethylene glycol diglycidyl ether to reinforce protein-based composite films
  43. Experimental study on the dissolution of supercritical CO2 in PS under different agitators
  44. Experimental research on the performance of the thermal-reflective coatings with liquid silicone rubber for pavement applications
  45. Study on controlling nicotine release from snus by the SIPN membranes
  46. Catalase biosensor based on the PAni/cMWCNT support for peroxide sensing
  47. Synthesis and characterization of different soybean oil-based polyols with fatty alcohol and aromatic alcohol
  48. Molecularly imprinted electrospun fiber membrane for colorimetric detection of hexanoic acid
  49. Poly(propylene carbonate) networks with excellent properties: Terpolymerization of carbon dioxide, propylene oxide, and 4,4ʹ-(hexafluoroisopropylidene) diphthalic anhydride
  50. Polypropylene/graphene nanoplatelets nanocomposites with high conductivity via solid-state shear mixing
  51. Mechanical properties of fiber-reinforced asphalt concrete: Finite element simulation and experimental study
  52. Applying design of experiments (DoE) on the properties of buccal film for nicotine delivery
  53. Preparation and characterizations of antibacterial–antioxidant film from soy protein isolate incorporated with mangosteen peel extract
  54. Preparation and adsorption properties of Ni(ii) ion-imprinted polymers based on synthesized novel functional monomer
  55. Rare-earth doped radioluminescent hydrogel as a potential phantom material for 3D gel dosimeter
  56. Effects of cryogenic treatment and interface modifications of basalt fibre on the mechanical properties of hybrid fibre-reinforced composites
  57. Stable super-hydrophobic and comfort PDMS-coated polyester fabric
  58. Impact of a nanomixture of carbon black and clay on the mechanical properties of a series of irradiated natural rubber/butyl rubber blend
  59. Preparation and characterization of a novel composite membrane of natural silk fiber/nano-hydroxyapatite/chitosan for guided bone tissue regeneration
  60. Study on the thermal properties and insulation resistance of epoxy resin modified by hexagonal boron nitride
  61. A new method for plugging the dominant seepage channel after polymer flooding and its mechanism: Fracturing–seepage–plugging
  62. Analysis of the rheological property and crystallization behavior of polylactic acid (Ingeo™ Biopolymer 4032D) at different process temperatures
  63. Hybrid green organic/inorganic filler polypropylene composites: Morphological study and mechanical performance investigations
  64. In situ polymerization of PEDOT:PSS films based on EMI-TFSI and the analysis of electrochromic performance
  65. Effect of laser irradiation on morphology and dielectric properties of quartz fiber reinforced epoxy resin composite
  66. The optimization of Carreau model and rheological behavior of alumina/linear low-density polyethylene composites with different alumina content and diameter
  67. Properties of polyurethane foam with fourth-generation blowing agent
  68. Hydrophobicity and corrosion resistance of waterborne fluorinated acrylate/silica nanocomposite coatings
  69. Investigation on in situ silica dispersed in natural rubber latex matrix combined with spray sputtering technology
  70. The degradable time evaluation of degradable polymer film in agriculture based on polyethylene film experiments
  71. Improving mechanical and water vapor barrier properties of the parylene C film by UV-curable polyurethane acrylate coating
  72. Thermal conductivity of silicone elastomer with a porous alumina continuum
  73. Copolymerization of CO2, propylene oxide, and itaconic anhydride with double metal cyanide complex catalyst to form crosslinked polypropylene carbonate
  74. Combining good dispersion with tailored charge trapping in nanodielectrics by hybrid functionalization of silica
  75. Thermosensitive hydrogel for in situ-controlled methotrexate delivery
  76. Analysis of the aging mechanism and life evaluation of elastomers in simulated proton exchange membrane fuel cell environments
  77. The crystallization and mechanical properties of poly(4-methyl-1-pentene) hard elastic film with different melt draw ratios
  78. Review Articles
  79. Aromatic polyamide nonporous membranes for gas separation application
  80. Optical elements from 3D printed polymers
  81. Evidence for bicomponent fibers: A review
  82. Mapping the scientific research on the ionizing radiation impacts on polymers (1975–2019)
  83. Recent advances in compatibility and toughness of poly(lactic acid)/poly(butylene succinate) blends
  84. Topical Issue: (Micro)plastics pollution - Knowns and unknows (Guest Editor: João Pinto da Costa)
  85. Simple pyrolysis of polystyrene into valuable chemicals
  86. Topical Issue: Recent advances of chitosan- and cellulose-based materials: From production to application (Guest Editor: Marc Delgado-Aguilar)
  87. In situ photo-crosslinking hydrogel with rapid healing, antibacterial, and hemostatic activities
  88. A novel CT contrast agent for intestinal-targeted imaging through rectal administration
  89. Properties and applications of cellulose regenerated from cellulose/imidazolium-based ionic liquid/co-solvent solutions: A short review
  90. Towards the use of acrylic acid graft-copolymerized plant biofiber in sustainable fortified composites: Manufacturing and characterization
https://doi.org/10.1515/epoly-2021-0083
Schlagwörter für diesen Artikel
porous alumina continuum; thermal conductivity; three-dimensional network; silicone elastomer; thermal interface materials
Creative Commons
BY 4.0

Artikel in diesem Heft

  1. Research Articles
  2. Research on the mechanism of gel accelerator on gel transition of PAN solution by rheology and dynamic light scattering
  3. Gel point determination of gellan biopolymer gel from DC electrical conductivity
  4. Composite of polylactic acid and microcellulose from kombucha membranes
  5. Synthesis of highly branched water-soluble polyester and its surface sizing agent strengthening mechanism
  6. Fabrication and characterization of poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) modified with nano-montmorillonite biocomposite
  7. Fabrication of N-halamine polyurethane films with excellent antibacterial properties
  8. Formulation and optimization of gastroretentive bilayer tablets of calcium carbonate using D-optimal mixture design
  9. Sustainable nanocomposite films based on SiO2 and biodegradable poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) (PHBH) for food packaging
  10. Evaluation of physicochemical properties of film-based alginate for food packing applications
  11. Electrically conductive and light-weight branched polylactic acid-based carbon nanotube foams
  12. Structuring of hydroxy-terminated polydimethylsiloxane filled by fumed silica
  13. Surface functionalization of nanostructured Cu/Ag-deposited polypropylene fiber by magnetron sputtering
  14. Influence of composite structure design on the ablation performance of ethylene propylene diene monomer composites
  15. MOFs/PVA hybrid membranes with enhanced mechanical and ion-conductive properties
  16. Improvement of the electromechanical properties of thermoplastic polyurethane composite by ionic liquid modified multiwall carbon nanotubes
  17. Natural rubber latex/MXene foam with robust and multifunctional properties
  18. Rheological properties of two high polymers suspended in an abrasive slurry jet
  19. Two-step polyaniline loading in polyelectrolyte complex membranes for improved pseudo-capacitor electrodes
  20. Preparation and application of carbon and hollow TiO2 microspheres by microwave heating at a low temperature
  21. Properties of a bovine collagen type I membrane for guided bone regeneration applications
  22. Fabrication and characterization of thermoresponsive composite carriers: PNIPAAm-grafted glass spheres
  23. Effect of talc and diatomite on compatible, morphological, and mechanical behavior of PLA/PBAT blends
  24. Multifunctional graphene nanofiller in flame retarded polybutadiene/chloroprene/carbon black composites
  25. Strain-dependent wicking behavior of cotton/lycra elastic woven fabric for sportswear
  26. Enhanced dielectric properties and breakdown strength of polymer/carbon nanotube composites by coating an SrTiO3 layer
  27. Analysis of effect of modification of silica and carbon black co-filled rubber composite on mechanical properties
  28. Polytriazole resins toughened by an azide-terminated polyhedral oligomeric silsesquioxane (OADTP)
  29. Phosphine oxide for reducing flammability of ethylene-vinyl-acetate copolymer
  30. Study on preparation and properties of bentonite-modified epoxy sheet molding compound
  31. Polyhedral oligomeric silsesquioxane (POSS)-modified phenolic resin: Synthesis and anti-oxidation properties
  32. Study on structure and properties of natural indigo spun-dyed viscose fiber
  33. Biodegradable thermoplastic copolyester elastomers: Methyl branched PBAmT
  34. Investigations of polyethylene of raised temperature resistance service performance using autoclave test under sour medium conditions
  35. Investigation of corrosion and thermal behavior of PU–PDMS-coated AISI 316L
  36. Modification of sodium bicarbonate and its effect on foaming behavior of polypropylene
  37. Effect of coupling agents on the olive pomace-filled polypropylene composite
  38. High strength and conductive hydrogel with fully interpenetrated structure from alginate and acrylamide
  39. Removal of methylene blue in water by electrospun PAN/β-CD nanofibre membrane
  40. Theoretical and experimental studies on the fabrication of cylindrical-electrode-assisted solution blowing spinning nanofibers
  41. Influence of l-quebrachitol on the properties of centrifuged natural rubber
  42. Ultrasonic-modified montmorillonite uniting ethylene glycol diglycidyl ether to reinforce protein-based composite films
  43. Experimental study on the dissolution of supercritical CO2 in PS under different agitators
  44. Experimental research on the performance of the thermal-reflective coatings with liquid silicone rubber for pavement applications
  45. Study on controlling nicotine release from snus by the SIPN membranes
  46. Catalase biosensor based on the PAni/cMWCNT support for peroxide sensing
  47. Synthesis and characterization of different soybean oil-based polyols with fatty alcohol and aromatic alcohol
  48. Molecularly imprinted electrospun fiber membrane for colorimetric detection of hexanoic acid
  49. Poly(propylene carbonate) networks with excellent properties: Terpolymerization of carbon dioxide, propylene oxide, and 4,4ʹ-(hexafluoroisopropylidene) diphthalic anhydride
  50. Polypropylene/graphene nanoplatelets nanocomposites with high conductivity via solid-state shear mixing
  51. Mechanical properties of fiber-reinforced asphalt concrete: Finite element simulation and experimental study
  52. Applying design of experiments (DoE) on the properties of buccal film for nicotine delivery
  53. Preparation and characterizations of antibacterial–antioxidant film from soy protein isolate incorporated with mangosteen peel extract
  54. Preparation and adsorption properties of Ni(ii) ion-imprinted polymers based on synthesized novel functional monomer
  55. Rare-earth doped radioluminescent hydrogel as a potential phantom material for 3D gel dosimeter
  56. Effects of cryogenic treatment and interface modifications of basalt fibre on the mechanical properties of hybrid fibre-reinforced composites
  57. Stable super-hydrophobic and comfort PDMS-coated polyester fabric
  58. Impact of a nanomixture of carbon black and clay on the mechanical properties of a series of irradiated natural rubber/butyl rubber blend
  59. Preparation and characterization of a novel composite membrane of natural silk fiber/nano-hydroxyapatite/chitosan for guided bone tissue regeneration
  60. Study on the thermal properties and insulation resistance of epoxy resin modified by hexagonal boron nitride
  61. A new method for plugging the dominant seepage channel after polymer flooding and its mechanism: Fracturing–seepage–plugging
  62. Analysis of the rheological property and crystallization behavior of polylactic acid (Ingeo™ Biopolymer 4032D) at different process temperatures
  63. Hybrid green organic/inorganic filler polypropylene composites: Morphological study and mechanical performance investigations
  64. In situ polymerization of PEDOT:PSS films based on EMI-TFSI and the analysis of electrochromic performance
  65. Effect of laser irradiation on morphology and dielectric properties of quartz fiber reinforced epoxy resin composite
  66. The optimization of Carreau model and rheological behavior of alumina/linear low-density polyethylene composites with different alumina content and diameter
  67. Properties of polyurethane foam with fourth-generation blowing agent
  68. Hydrophobicity and corrosion resistance of waterborne fluorinated acrylate/silica nanocomposite coatings
  69. Investigation on in situ silica dispersed in natural rubber latex matrix combined with spray sputtering technology
  70. The degradable time evaluation of degradable polymer film in agriculture based on polyethylene film experiments
  71. Improving mechanical and water vapor barrier properties of the parylene C film by UV-curable polyurethane acrylate coating
  72. Thermal conductivity of silicone elastomer with a porous alumina continuum
  73. Copolymerization of CO2, propylene oxide, and itaconic anhydride with double metal cyanide complex catalyst to form crosslinked polypropylene carbonate
  74. Combining good dispersion with tailored charge trapping in nanodielectrics by hybrid functionalization of silica
  75. Thermosensitive hydrogel for in situ-controlled methotrexate delivery
  76. Analysis of the aging mechanism and life evaluation of elastomers in simulated proton exchange membrane fuel cell environments
  77. The crystallization and mechanical properties of poly(4-methyl-1-pentene) hard elastic film with different melt draw ratios
  78. Review Articles
  79. Aromatic polyamide nonporous membranes for gas separation application
  80. Optical elements from 3D printed polymers
  81. Evidence for bicomponent fibers: A review
  82. Mapping the scientific research on the ionizing radiation impacts on polymers (1975–2019)
  83. Recent advances in compatibility and toughness of poly(lactic acid)/poly(butylene succinate) blends
  84. Topical Issue: (Micro)plastics pollution - Knowns and unknows (Guest Editor: João Pinto da Costa)
  85. Simple pyrolysis of polystyrene into valuable chemicals
  86. Topical Issue: Recent advances of chitosan- and cellulose-based materials: From production to application (Guest Editor: Marc Delgado-Aguilar)
  87. In situ photo-crosslinking hydrogel with rapid healing, antibacterial, and hemostatic activities
  88. A novel CT contrast agent for intestinal-targeted imaging through rectal administration
  89. Properties and applications of cellulose regenerated from cellulose/imidazolium-based ionic liquid/co-solvent solutions: A short review
  90. Towards the use of acrylic acid graft-copolymerized plant biofiber in sustainable fortified composites: Manufacturing and characterization
Jetzt anmelden und 20% sparen
Institutioneller Zugang
Wie funktioniert Authentifizierung?
Haben Sie eine Idee, wie wir unsere Website verbessern können?
Bitte schreiben Sie uns.
© 2025 De Gruyter Brill
Heruntergeladen am 17.9.2025 von https://www.degruyterbrill.com/document/doi/10.1515/epoly-2021-0083/html
Button zum nach oben scrollen