Startseite Adsorption of bovine serum albumin onto titanium dioxide nanotube arrays
Artikel
Lizenziert
Nicht lizenziert Erfordert eine Authentifizierung

Adsorption of bovine serum albumin onto titanium dioxide nanotube arrays

  • Jie Shi , Bo Feng , Xiong Lu und Jie Weng
Veröffentlicht/Copyright: 11. Juni 2013
Veröffentlichen auch Sie bei De Gruyter Brill
Informationen für Autor*innen
International Journal of Materials Research
Aus der Zeitschrift International Journal of Materials Research Band 103 Heft 7

Abstract

Titanium dioxide nanotube arrays on titanium were fabricated via anodic oxidation and heat treatment. The diameters of nanotubes ranged from 20 to 200 nm, and the lengths were 500 and 1000 nm. The adsorption behavior of bovine serum albumin onto the nanotube arrays was investigated. Surface characterization for samples was carried out using scanning electron microscopy, X-ray diffraction, Fourier transform infrared spectroscopy, and X-ray photoelectron spectroscopy. Adsorbance of bovine serum albumin was detected with an ultraviolet spectrophotometer. The results showed that the nanotube arrays on titanium surfaces significantly enhanced bovine serum albumin adsorption. The nanotube arrays with larger diameter could adsorb more bovine serum albumin, but longer nanotubes showed less adsorbance than shorter nanotubes. In the present work, the nanotube arrays with 160–200 nm diameter, the largest diameter, showed the highest adsorption ability, and the maximum adsorption capacity qm was 31.40 mg · cm−2. In addition, the adsorbance of bovine serum albumin increased with increase of initial bovine serum albumin concentrations, and a saturation value was achieved at the initial bovine serum albumin concentration of 2.0 mg · ml−1.

Keywords: Titanium dioxide nanotube arrays; Nanotube diameter; Nanotube length; Bovine serum albumin; Adsorption
* Correspondence address Bo Feng Key Laboratory of Advanced Technologies of MaterialsMinistry of Education, Southwest Jiaotong UniversityChengdu 610031, PR China Tel.: +86 28 87634023 Fax: +86 28 87601371 E-mail:

References

[1] P.Roach, D.Farrar, C.C.Perry: J. Am. Chem. Soc.127 (2005) 8168. 10.1021/ja042898oSuche in Google Scholar

[2] D.D.Deligianni, N.Katsala, S.Ladas, D.Sotiropoulou, J.Amedee: Biomater.22 (2001) 1241. 10.1016/S0142-9612(00)00274-XSuche in Google Scholar

[3] L.Richert, F.Variola, F.Rosei, J.D.Wuest, A.Nanci: Surf. Sci.604 (2010) 1445. 10.1016/j.susc.2010.05.007Suche in Google Scholar

[4] K.Y.Cai, M.Frant, J.Bossert, G.Hildebrand: Colloid. Surf. B50 (2006) 1. 10.1016/j.colsurfb.2006.03.016Suche in Google Scholar

[5] M.C.Liu, G.H.Zhao, K.J.Zhao, X.L.Tong, Y.T.Tang: Electrochem. Commun.34 (2009) 1397. 10.1016/j.elecom.2009.05.015Suche in Google Scholar

[6] W.L.Gao, B.Feng, Y.X.Ni, Y.L.Yang, X.Lu, J.Weng: Appl. Surf. Sci.257 (2010) 538. 10.1016/j.apsusc.2010.07.029Suche in Google Scholar

[7] C.Galli, M.C.Coen, R.Hauert, V.L.Katanaev, P.Groning, L.Schlapbach: Colloid. Surf. B26 (2002) 255. 10.1016/S0927-7765(02)00015-2Suche in Google Scholar

[8] B.Feng, J.Y.Chen, X.D.Zhang: Biomater.23 (2002) 2499. 10.1016/S0142-9612(01)00384-2Suche in Google Scholar

[9] S.Oh, R.R.Finones, C.Daraio, L.H.Chen, S.Jin: Biomater.26 (2005) 4938. 10.1016/j.biomaterials.2005.01.048Suche in Google Scholar PubMed

[10] A.Kodama, S.Bauer, A.Komatsu, H.Asoh, S.Ono, P.Schmuki: Acta. Biomater.5 (2009) 2322. 10.1016/j.actbio.2009.02.032Suche in Google Scholar PubMed

[11] Y.Q.Wang, J.Tao, L.Wang, P.T.He, T.Wang: Trans. Nonferrous. Met. Soc. China.18 (2008) 631. 10.1016/S1003-6326(08)60110-7Suche in Google Scholar

[12] J.Jakubowicz, K.Jurczyk, K.Niespodzian, M.Jurczyk: Electrochem. Commun.11 (2009) 461. 10.1016/j.elecom.2008.12.024Suche in Google Scholar

[13] O.Zinger, K.Anselme, A.Denzer, P.Habersetzer, M.Wieland, J.Jeanfils, P.Hardouin, D.Landolt: Biomater.25 (2004) 2695. 10.1016/j.biomaterials.2003.09.111Suche in Google Scholar

[14] L.Le Guehennec, A.Soueidan, P.Layrolle, Y.Amouriq: Dent. Mater.23 (2007) 844. 10.1016/j.dental.2006.06.025Suche in Google Scholar

[15] V.Zwilling, E.Darque-Ceretti, A.Boutry-Forveille, D.David, M.Y.Perrin, M.Aucouturier: Surf. Interf. Anal.27 (1999) 629. 10.1002/(SICI)1096-9918(199907)27:7<629::AID-SIA551>3.0.CO;2-0Suche in Google Scholar

[16] S.Bauer, S.Kleber, P.Schmuki: Electrochem. Commun.8 (2006) 1321. 10.1016/j.elecom.2006.05.030Suche in Google Scholar

[17] S.Oh, C.Daraio, L.H.Chen, T.R.Pisanic, R.R.Finones, S.Jin: J. Biomed. Mater. Res.78 (2006) 97. 10.1002/jbm.a.30722Suche in Google Scholar

[18] K.S.Brammer, S.Oh, J.O.Gallagher, S.Jin: Nano Lett.8 (2008) 786. 10.1021/nl072572oSuche in Google Scholar

[19] J.Park, S.Bauer, K.Mark, P.Schmuki: Nano Lett.7 (2007) 1686. 10.1021/nl070678dSuche in Google Scholar

[20] H.Tsuchiya, J.M.Macak, L.Muller, J.Kunze, F.Muller, P.Greil, S.Virtanen, P.Schmuki: J. Biomed. Mater. Res. A10 (2006) 534. 10.1002/jbm.a.30677Suche in Google Scholar

[21] C.V.Wilmowsky, S.Bauer, R.Lutz, M.Meisel, W.F.Neukam, T.Toyoshima, P.Schmuki, E.Nkenke, A.K.Schlegel: J. Biomed. Mater. Res. B10 (2009) 165.Suche in Google Scholar

[22] G.A.Crawford, N.Chawla: Acta Mater.57 (2009) 854. 10.1016/j.actamat.2008.10.032Suche in Google Scholar

[23] D.L.Liu, B.Feng, X.Lu, J.M.Cheng: Rare Metal. Mat. Eng.39 (2010) 325.Suche in Google Scholar

[24] B.Feng, X.J.Chu, J.M.Chen, J.X.Wang, X.Lu, J.Weng: J. Porous Mat.17 (2010) 453. 10.1007/s10934-009-9307-2Suche in Google Scholar

[25] Q.Cui, B.Feng, W.Chen, J.X.Wang, X.Lu, J.Weng: J. Inorg. Mater.25 (2010) 916. 10.3724/SP.J.1077.2010.00916Suche in Google Scholar

[26] L.Gao, B.Feng, J.X.Wang, X.Lu, D.L.Liu, S.X.Qu, J.Weng: J. Biomed. Mater. Res. B89 (2008) 335.Suche in Google Scholar

[27] G.A.Crawford, N.Chawla, J.E.Houston: J. Mech. Behav. Biomed. Mater.2 (2009) 580. 10.1016/j.jmbbm.2008.10.004Suche in Google Scholar

[28] M.C.Chang, J.Tanaka: Biomater.23 (2002) 4811. 10.1016/S0142-9612(02)00232-6Suche in Google Scholar

[29] B.Feng, J.Weng, B.C.Yang, J.Y.Chen, J.Z.Zhao, L.He, S.K.Qi, X.D.Zhang: Mater. Character.49 (2003) 129. 10.1016/S1044-5803(02)00341-8Suche in Google Scholar

[30] C.K.Simi, T.Emilia Abraham: Colloid. Surf. B71 (2009) 319. 10.1016/j.colsurfb.2009.02.019Suche in Google Scholar PubMed

[31] Z.Wei, W.Huang, G.H.Hou, Z.Yuan, J.Fang: Process, Biochem.42 (2007) 285. 10.1016/j.procbio.2006.08.004Suche in Google Scholar

[32] C.B.Ran, G.Q.Ding, W.C.Liu, Y.Deng, W.T.Hou: Langmuir.24 (2008) 9952. 10.1021/la801461jSuche in Google Scholar PubMed

Received: 2011-3-22
Accepted: 2011-12-7
Published Online: 2013-06-11
Published in Print: 2012-07-01

© 2012, Carl Hanser Verlag, München

Artikel in diesem Heft

  1. Contents
  2. Contents
  3. Original Contributions
  4. Diffusivities and atomic mobilities in Cu-rich fcc Al–Cu–Mn alloys
  5. Phase transformations in non-isothermally annealed as-cast and cold-rolled AlMnScZr alloys
  6. High-temperature deformation behavior and thermal properties of an Ni30Co17Fe53 alloy
  7. Microstructural and mechanical properties of dual-phase steels welded using GMAW with solid and flux-cored welding wires
  8. Microstructure – wear performance relationship of hypoeutectic 15% Cr-2% Mo white iron
  9. The enhancement of wear properties of squeeze-cast A356 composites reinforced with B4C particulates
  10. Phase diagram of the Al–Dy–Zr ternary system at 773 K
  11. Calorimetric investigations of liquid gold–antimony–tin alloys
  12. Combustion synthesis and characterization of bulk nanostructured Ni50Al17Fe33 alloy
  13. Effect of sand blasting on structural, thermal, and mechanical properties of Zr58.3Cu18.8Al14.6Ni8.3 bulk metallic glass
  14. Studies of dynamic mass transfer at the slag–metal interface – Interfacial velocity measurements
  15. Structural and optical investigation of gadolinia-doped ceria powders prepared by polymer complex solution method
  16. Adsorption of bovine serum albumin onto titanium dioxide nanotube arrays
  17. CNT-based displacement sensor
  18. Non-covalent assembly of hybrid nanostructures of gold and palladium nanoparticles with carbon nanotubes
  19. Effect of solid content on performance of conductive silver paste for crystalline silicon solar cells
  20. Effect of inhomogeneous size and shape of graphite particles on the in-plane electrical conductivity of PP/G/CB composites
  21. The durability of fired brick incorporating textile factory waste ash and basaltic pumice
  22. DGM News
  23. DGM News
https://doi.org/10.3139/146.110696
Schlagwörter für diesen Artikel
Titanium dioxide nanotube arrays; Nanotube diameter; Nanotube length; Bovine serum albumin; Adsorption

Artikel in diesem Heft

  1. Contents
  2. Contents
  3. Original Contributions
  4. Diffusivities and atomic mobilities in Cu-rich fcc Al–Cu–Mn alloys
  5. Phase transformations in non-isothermally annealed as-cast and cold-rolled AlMnScZr alloys
  6. High-temperature deformation behavior and thermal properties of an Ni30Co17Fe53 alloy
  7. Microstructural and mechanical properties of dual-phase steels welded using GMAW with solid and flux-cored welding wires
  8. Microstructure – wear performance relationship of hypoeutectic 15% Cr-2% Mo white iron
  9. The enhancement of wear properties of squeeze-cast A356 composites reinforced with B4C particulates
  10. Phase diagram of the Al–Dy–Zr ternary system at 773 K
  11. Calorimetric investigations of liquid gold–antimony–tin alloys
  12. Combustion synthesis and characterization of bulk nanostructured Ni50Al17Fe33 alloy
  13. Effect of sand blasting on structural, thermal, and mechanical properties of Zr58.3Cu18.8Al14.6Ni8.3 bulk metallic glass
  14. Studies of dynamic mass transfer at the slag–metal interface – Interfacial velocity measurements
  15. Structural and optical investigation of gadolinia-doped ceria powders prepared by polymer complex solution method
  16. Adsorption of bovine serum albumin onto titanium dioxide nanotube arrays
  17. CNT-based displacement sensor
  18. Non-covalent assembly of hybrid nanostructures of gold and palladium nanoparticles with carbon nanotubes
  19. Effect of solid content on performance of conductive silver paste for crystalline silicon solar cells
  20. Effect of inhomogeneous size and shape of graphite particles on the in-plane electrical conductivity of PP/G/CB composites
  21. The durability of fired brick incorporating textile factory waste ash and basaltic pumice
  22. DGM News
  23. DGM News
Jetzt anmelden und 20% sparen
Institutioneller Zugang
Wie funktioniert Authentifizierung?
Haben Sie eine Idee, wie wir unsere Website verbessern können?
Bitte schreiben Sie uns.
© 2025 De Gruyter Brill
Heruntergeladen am 5.10.2025 von https://www.degruyterbrill.com/document/doi/10.3139/146.110696/html?lang=de
Button zum nach oben scrollen