Abstract

The results have been achieved by adjusting the structure to improve the performance of micro injection molded isotactic polypropylene products. Annealing was adopted to optimize the performance of isotactic polypropylene micro injection molded gears. It was found that the annealing temperature shows greater influence on the crystalline structure of the micro injection molded gears than annealing time. The layer mechanical properties were greatly improved after annealing, about 1.7-fold for modulus and 1.9-fold for hardness of the micro injection molded gears relative to the unannealed sample. This is due to the fact the state of molecular chain aggregation tends to be consistent after high temperature annealing in the micro injection molded isotactic polypropylene gear sample.

*Correspondence address, Mail address: Shiwei Wang, National Center for International Joint Research of Micro-Nano Molding Technology, School of Mechanics and Engineering Science, Zhengzhou University, Zhengzhou, 450001 Henan, PRC, E-mail: shiweiwang@zzu.edu.cn

References

Geng, C. Z., Su, J. J., Zhou, C. Y., Bai, H. W., Yang, G. H. and Fu, Q., “Largely Improved Toughness of Polypropylene/Long Glass Fiber Composites by B-Modification and Annealing”, J. Mater. Chem. A., 96, 56–62 (2014) 10.1039/B905995DSuche in Google Scholar

Giboz, J., Copponnex, T. and Mele, P., “Microinjection Molding of Thermoplastic Polymers: A Review”, J. Micromech. Microeng., 17, 96–109 (2007) 10.1088/0960-1317/17/6/R02Suche in Google Scholar

Heckele, M., Schomburg, W. K., “Review on Micro Molding of Thermoplastic Polymers”, J. Micromech. Microeng., 14, 1–14 (2004) 10.1088/0960-1317/14/4/R01Suche in Google Scholar

Jiang, J., Wang, S. W., Sun, B., Ma, S. J., Zhang, J. M., Li, Q. and Hu, G. H., “Effect of Mold Temperature on the Structures and Mechanical Properties of Micro-Injection Molded Polypropylene”, Mater. Des., 88, 245–251 (2015) 10.1016/j.matdes.2015.09.003Suche in Google Scholar

Jiang, Z., Chen, Y. H. and Liu, Z., “The Morphology, Crystallization and Conductive Performance of a Polyoxymethylene/Carbon Nanotube Nanocomposite Prepared under Microinjection Molding Conditions”, J. Polym. Res., 21, 451–466 (2014) 10.1007/s10965-014-0451-2Suche in Google Scholar

Kamal, M. R., Chu, J., Derdouri, S. and Hrymak, A., “Morphology of Microinjection Moulded Polyoxymethylene”, Plast. Rubber. Compos., 39, 332–341 (2010) 10.1179/174328910X12691245470518Suche in Google Scholar

Li, D. X., Fei, G. X., Xia, H. S., Spencer, P. E. and Coates, P. D., “Micro-Contact Reconstruction of Adjacent Carbon Nanotubes in Polymer Matrix through Annealing-Induced Relaxation of Interfacial Residual Stress and Strain”, J. Appl. Polym. Sci., 132, 42416–42427 (2015) 10.1002/app.42610Suche in Google Scholar

Liu, F., Guo, C., Wu, X., Qian, X., Liu, H. and Zhang, J., “Morphological Comparison of Isotactic Polypropylene Parts Prepared by Micro-Injection Molding and Conventional Injection Molding”, Polym. Adv. Tech., 23, 686–694 (2012) 10.1002/pat.1946Suche in Google Scholar

Masato, D., Sorgato, M. and Lucchetta, G., “Analysis of the Influence of Part Thickness on the Replication of Micro-Structured Surfaces by Injection Molding”, Mater. Des., 95, 219–224 (2016) 10.1016/j.matdes.2016.01.115Suche in Google Scholar

Shi, S. Y., Pan, Y. M., Lu, B., Zheng, G. Q., Liu, C. T., Dai, K. and Shen, C. Y., “Realizing the Simultaneously Improved Toughness and Strength of Ultra-Thin LLDPE Parts through Annealing”, Polymer, 54, 6843–6852 (2013) 10.1016/j.polymer.2013.10.020Suche in Google Scholar

Wang, S. W., Wang, Z. W., Zhao, N., Jiang, J. and Li, Q., “A Novel Morphology Development of Micro-injection Molded Isotactic Polypropylene”, RSC. Adv., 5, 41608–41610 (2015) 10.1039/C5RA04626BSuche in Google Scholar

Wang, Y. M., Zhang, H. H., Li, M., Cao, W., Liu, C. T. and Shen, C. Y., “Orientation and Structural Development of Semicrystalline Poly(lactic acid) under Uniaxial Drawing Assessed by Infrared Spectroscopy and X-Ray Diffraction”, Polym. Test., 41, 163–171 (2015) 10.1016/j.polymertesting.2014.11.010Suche in Google Scholar

Zhang, N., Su, Q. L., Choi, S. Y. and Michael, D. G., “Effects of Gate Design and Cavity Thickness on Filling, Morphology and Mechanical Properties of Microinjection”, Mater. Des., 83, 835–847 (2015) 10.1016/j.matdes.2015.06.012Suche in Google Scholar

Zhang, R. Y., Yang, W., Zhang, Q. P., Xia, X. C., Zhu, C. X., He, S., Huang, Y. H., Liu, Z. Y. and Yang, M. B., “Hierarchical Crystalline Morphologies Induced by a Distinctly Different Melt Penetrating Process”, RSC. Adv., 5, 98299–98308 (2015) 10.1039/C5RA18885GSuche in Google Scholar

Received: 2016-08-25

Accepted: 2016-11-01

Published Online: 2017-02-20

Published in Print: 2017-03-03

Sie haben derzeit keinen Zugang zu diesem Inhalt.

Artikel in diesem Heft

https://doi.org/10.3139/217.3349