Experimental evaluation of forming limit diagram and mechanical properties of nano/ultra-fine grained aluminum strips fabricated by accumulative roll bonding

  • Davood Rahmatabadi und Ramin Hashemi
Veröffentlicht/Copyright: 25. November 2017
Veröffentlichen auch Sie bei De Gruyter Brill
Informationen für Autor*innen
International Journal of Materials Research
Aus der Zeitschrift International Journal of Materials Research Band 108 Heft 12

Abstract

In this research, for the first time, forming limit diagrams (FLDs) of ultra-fine grained Al/Al samples produced by accumulative roll bonding (ARB) process were evaluated. The samples were successfully prepared through ARB up to the 7th pass. Mechanical properties, tensile fracture surfaces, and crystallite size of samples were investigated. The level of the FLD and elongation at first decreased and then increased, continuously. The results of tensile testing revealed that by increasing the number of ARB passes, the tensile strength increased continuously. Microhardness of Al strips increased and reached a value of 51 VHN after the seventh pass. Results of X-ray diffraction demonstrated that crystallite size decreased from 1 341 nm for annealed condition and it reached to 175 nm for ARBed samples after the 7th pass. SEM images showed that the fracture mode in the ARBed samples was a shear ductile fracture with elongated sophomoric shear dimples.

Keywords: Forming limit diagrams; Accumulative roll bonding; Mechanical properties; SEM; AA1050
*Correspondence address, Dr Ramin Hashemi, Assistant professor, School of Mechanical Engineering, Iran University of Science and Technology, Tehran 16844, Iran, Tel.: +98-21-77240068, Fax: +98-21-77240540, E-mail:

References

[1] J.Evancho, J.Kaufman: SAE Technical Paper. 1977.10.4271/770307Suche in Google Scholar

[2] L.Troeger, E.Starke: Mater. Sci. Eng. A277 (2000) 102. 10.1016/S0921-5093(99)00543-2Suche in Google Scholar

[3] S.Lee, Y.Saito, T.Sakai, H.Utsunomiya: Mater. Sci. Eng. A325 (2002) 228. 10.1016/S0921-5093(01)01416-2Suche in Google Scholar

[4] R.Jamaati, M.R.Toroghinejad: Mater. Des.31 (2010) 4816. 10.1016/j.matdes.2010.04.048Suche in Google Scholar

[5] M.Raei, M.R.Toroghinejad, R.Jamaati: Mater. Manuf. Pro.26 (2011) 1352. 10.1080/10426914.2011.557133Suche in Google Scholar

[6] H.Pirgazi, A.Akbarzadeh, R.Petrov, L.Kestens: Mater. Sci. Eng. A497 (2008) 132. 10.1016/j.msea.2008.06.025Suche in Google Scholar

[7] M.R.Toroghinejad, F.Ashrafizadeh, R.Jamaati: Mater. Sci. Eng. A561 (2013) 145. 10.1016/j.msea.2012.11.010Suche in Google Scholar

[8] R.Z.Valiev, T.G.Langdon: Prog. Mater. Sci.51 (2006) 881. 10.1016/j.pmatsci.2006.02.003Suche in Google Scholar

[9] R.Z.Valiev, N.Krasilnikov, N.Tsenev: Mater. Sci. Eng. A137 (1991) 35. 10.1016/0921-5093(91)90316-FSuche in Google Scholar

[10] V.Segal: Mater. Sci. Eng. A197 (1995) 157. 10.1016/0921-5093(95)09705-8Suche in Google Scholar

[11] M.Furukawa, Y.Iwahashi, Z.Horita, M.Nemoto, T.G.Langdon: Mater. Sci. Eng. A257 (1998) 328. 10.1016/S0921-5093(98)00750-3Suche in Google Scholar

[12] G.Sakai, Z.Horita, T.G.Langdon: Mater. Sci. Eng. A393 (2005) 344. 10.1016/j.msea.2004.11.007Suche in Google Scholar

[13] A.P.Zhilyaev, T.G.Langdon: Prog. Mater. Sci.53 (2008) 893. 10.1016/j.pmatsci.2008.03.002Suche in Google Scholar

[14] Z.Horita, D.J.Smith, M.Furukawa, M.Nemoto, R.Z.Valiev, T.G.Langdon: J. Mater. Res.11 (1996) 1880. 10.1557/JMR.1996.0239Suche in Google Scholar

[15] M.Richert, H.Stüwe, J.Richert, R.Pippan, C.Motz: Mater. Sci. Eng. A.301 (2001) 237. 10.1016/S0921-5093(00)01803-7Suche in Google Scholar

[16] J.Yin, J.Lu, H.Ma, P.Zhang: J. Mater. Sci.39 (2004) 2851. 10.1023/B:JMSC.0000021463.83899.b3Suche in Google Scholar

[17] D.H.Shin, J.-J.Park, Y.-S.Kim, K.-T.Park: Mater. Sci. Eng. A328 (2002) 98.10.1016/S0921-5093(01)01665-3Suche in Google Scholar

[18] Y.Saito, H.Utsunomiya, N.Tsuji, T.Sakai: Acta. Mater.47 (1999) 579. 10.1016/S1359-6454(98)00365-6Suche in Google Scholar

[19] N.Tsuji, Y.Saito, S.H.Lee, Y.Minamino: Adv. Eng. Mater.5 (2003) 338. 10.1002/adem.200310077Suche in Google Scholar

[20] X.Huang, N.Tsuji, N.Hansen, Y.Minamino: Mater. Sci. Eng. A340 (2003) 265.10.1016/S0921-5093(02)00182-XSuche in Google Scholar

[21] M.R.Rezaei, M.R.Toroghinejad, F.Ashrafizadeh: Mater. Sci. Eng. A529 (2011) 442. 10.1016/j.msea.2011.09.057Suche in Google Scholar

[22] P.Hsieh, Y.Hung, J.Huang: Scr. Mater.49 (2003) 173. 10.1016/S1359-6462(03)00207-0Suche in Google Scholar

[23] M.Shaarbaf, M.R.Toroghinejad: Mater. Sci. Eng. A473 (2008) 28. 10.1016/j.msea.2007.03.065Suche in Google Scholar

[24] S.Pasebani, M.R.Toroghinejad: Mater. Sci. Eng. A527 (2010) 491. 10.1016/j.msea.2009.09.029Suche in Google Scholar

[25] D.Terada, S.Inoue, N.Tsuji: J. Mater. Sci.42 (2007) 1673. 10.1007/s10853-006-0909-7Suche in Google Scholar

[26] M.Zhan, Y.Li, W.Chen, W.Chen: J. Mater. Sci.42 (2007) 9256. 10.1007/s10853-007-1885-2Suche in Google Scholar

[27] N.Tsuji, R.Ueji, Y.Minamino: Scr. Mater.47 (2002) 69. 10.1016/S1359-6462(02)00088-XSuche in Google Scholar

[28] D.Yang, P.Cizek, P.Hodgson, C.e.Wen: Scr. Mater.62 (2010) 321. 10.1016/j.scriptamat.2009.11.036Suche in Google Scholar

[29] S.P.Keeler: SAE Technical Paper. 1965.10.4271/650535Suche in Google Scholar

[30] R.Hashemi, H.Mamusi, A.Masoumi: Proceedings of the Institution of Mechanical Engineers, Part B: J. Eng. Manuf. (2014).10.1177/0954405414522448Suche in Google Scholar

[31] C.Zhang, L.Leotoing, D.Guines, E.Ragneau: J. Mater. Pro. Technol.209 (2009) 3849. 10.1016/j.jmatprotec.2008.09.003Suche in Google Scholar

[32] C.Zhang, X.Chu, D.Guines, L.Leotoing, J.Ding, G.Zhao: Mater. Des.67 (2015) 522. 10.1016/j.matdes.2014.10.074Suche in Google Scholar

[33] A.Rezaee-Bazzaz, H.Noori, R.Mahmudi: Int. J. Mech. Sci.53 (2011) 262. 10.1016/j.ijmecsci.2011.01.007Suche in Google Scholar

[34] F.Zhang, J.Chen, J.Chen, X.Zhu: Int. J. Mech. Sci.89 (2014) 40. 10.1016/j.ijmecsci.2014.08.016Suche in Google Scholar

[35] K.Wang, J.E.Carsley, L.Zhang, T.B.Stoughton, J.Li, B.E.Carlson: Int. J. Mech. Sci.82 (2014) 13. 10.1016/j.ijmecsci.2014.02.025Suche in Google Scholar

[36] N.B.K.Babu, M.Davidson, A.N.Rao, K.Balasubramanian, M.Govindaraju: Mater. Design.55 (2014) 35. 10.1016/j.matdes.2013.10.004Suche in Google Scholar

[37] W.Lee, X.Wen: Int. J. Mech. Sci.48 (2006) 134. 10.1016/j.ijmecsci.2005.08.005Suche in Google Scholar

[38] E.Karajibani, R.Hashemi, M.Sedighi: Int. J. Adv. Manuf. Technol.90 (2017) 2713. 10.1007/s00170-016-9585-1Suche in Google Scholar

[39] M.Nurcheshmeh, D.E.Green: Int. J. Mech. Sci.53 (2011) 145. 10.1016/j.ijmecsci.2010.12.004Suche in Google Scholar

[40] A.Assempour, R.Hashemi, K.Abrinia, M.Ganjiani, E.Masoumi: Comput. Mater. Sci.45 (2009) 195. 10.1016/j.commatsci.2008.09.025Suche in Google Scholar

[41] O.Yigit: Int. J. Adv. Manuf. Technol.67 (2013) 2689. 10.1007/s00170-012-4684-0Suche in Google Scholar

[42] K.Ito, K.Satoh, M.Goya, T.Yoshida: Int. J. Mech. Sci.42 (2000) 2233. 10.1016/S0020-7403(00)00004-7Suche in Google Scholar

[43] H.Rahimi, M.Sedighi, R.Hashemi: Part L: J. Mater. Des. Appl. (2016).10.1177/1464420716655560Suche in Google Scholar

[44] R.Lapovok, I.Timokhina, P.McKenzie, R.O'Donnell: J. Mater. Pro. Technol.200 (2008) 441. 10.1016/j.jmatprotec.2007.08.083Suche in Google Scholar

[45] R.Hashemi, G.Faraji, K.Abrinia, A.F.Dizaji: Int. J. Adv. Manuf. Technol.46 (2010) 551. 10.1007/s00170-009-2121-9Suche in Google Scholar

[46] F.Ozturk, D.Lee: Journal of Materials Processing Technology. J. Mater. Pro. Technol.170 (2005) 247. 10.1016/j.jmatprotec.2005.05.010Suche in Google Scholar

[47] D.Hughes, N.Hansen: Acta. Mater.45 (1997) 3871. 10.1016/S1359-6454(97)00027-XSuche in Google Scholar

[48] M.Naseri, A.Hassani, M.Tajally: Cer. Int.41 (2015) 3952. 10.1016/j.ceramint.2014.11.079Suche in Google Scholar

[49] L.Ceschini, G.Minak, A.Morri: Comp. Sci. Technol.66 (2006) 333. 10.1016/j.compscitech.2005.04.044Suche in Google Scholar

[50] A.Shabani, M.R.Toroghinejad, A.Shafyei: Mater. Sci. Eng.A558 (2012) 386.10.1016/j.msea.2012.08.017Suche in Google Scholar

[51] M.Reihanian, F.K.Hadadian, M.Paydar: Mater. Sci. Eng. A607 (2014) 188. 10.1016/j.msea.2014.04.013Suche in Google Scholar

[52] M.Alizadeh, M.Samiei: Mater. Des.56 (2014) 680. 10.1016/j.matdes.2013.11.067Suche in Google Scholar

[53] N.Hansen, X.Huang, R.Ueji, N.Tsuji: Mater. Sci. Eng. A387 (2004) 191. 10.1016/j.msea.2004.02.078Suche in Google Scholar

[54] Y.Wang, E.Ma: Acta. Mater.52 (2004) 1699. 10.1016/j.actamat.2003.12.022Suche in Google Scholar

[55] N.Tsuji, Y.Ito, Y.Saito, Y.Minamino: Scr. Mater.47 (2002) 893. 10.1016/S1359-6462(02)00282-8Suche in Google Scholar

[56] L.Su, C.Lu, H.Li, G.Deng, K.Tieu: Mater. Sci. Eng. A614 (2014) 148. 10.1016/j.msea.2014.07.032Suche in Google Scholar

[57] M.Alizadeh, M.Paydar, F.S.Jazi: Comp. Part B: Eng.44 (2013) 339. 10.1016/j.compositesb.2012.04.069Suche in Google Scholar

[58] S.O.Gashti, A.Fattah-alhosseini, Y.Mazaheri, M.K.Keshavarz: J. Alloy. Compound.688, Part B (2016) 44. 10.1016/j.jallcom.2016.07.177Suche in Google Scholar

[59] M.Sedighi, M.H.Vini, P.Farhadipour: Powder. Metal. Cer.55 (2016) 413. 10.1007/s11106-016-9821-0Suche in Google Scholar

[60] M.H.Vini, M.Sedighi, M.Mondali: Int. J. Mater. Res.108 (2017) 53. 10.3139/146.111450Suche in Google Scholar

Received: 2017-02-17
Accepted: 2017-08-08
Published Online: 2017-11-25
Published in Print: 2017-12-08

© 2017, Carl Hanser Verlag, München

Artikel in diesem Heft

  1. Contents
  2. Contents
  3. Original Contributions
  4. First principles, thermal stability and thermodynamic assessment of the binary Ni–W system
  5. Experimental evaluation of forming limit diagram and mechanical properties of nano/ultra-fine grained aluminum strips fabricated by accumulative roll bonding
  6. FSW of bimodal reinforced Al-based composites produced via spark plasma sintering
  7. Modelling analysis and experiments of polycrystalline silicon directional solidification in an annular heating field
  8. Effect of flow, heat transfer and magnetic energy on the grain refinement of 7A04 alloy under electromagnetic pulse
  9. A study on effects of a new two-step strain induced melt activation process on characteristics of Al 7075 alloy
  10. Synthesis and characterization of mechanically alloyed cerium oxide reinforced Al-4.5Mg alloy composite
  11. Densification rate and interfacial adhesion of bilayer cemented tungsten carbide and steel
  12. Short Communications
  13. Cavitation erosion of 17-4 PH stainless steels following sub-zero treatment
  14. Investigation on microstructure and thermal properties of in-situ synthesized Cu–ZrO2 nanocomposites
  15. DGM News
  16. DGM News
https://doi.org/10.3139/146.111566
Schlagwörter für diesen Artikel
Forming limit diagrams; Accumulative roll bonding; Mechanical properties; SEM; AA1050

Artikel in diesem Heft

  1. Contents
  2. Contents
  3. Original Contributions
  4. First principles, thermal stability and thermodynamic assessment of the binary Ni–W system
  5. Experimental evaluation of forming limit diagram and mechanical properties of nano/ultra-fine grained aluminum strips fabricated by accumulative roll bonding
  6. FSW of bimodal reinforced Al-based composites produced via spark plasma sintering
  7. Modelling analysis and experiments of polycrystalline silicon directional solidification in an annular heating field
  8. Effect of flow, heat transfer and magnetic energy on the grain refinement of 7A04 alloy under electromagnetic pulse
  9. A study on effects of a new two-step strain induced melt activation process on characteristics of Al 7075 alloy
  10. Synthesis and characterization of mechanically alloyed cerium oxide reinforced Al-4.5Mg alloy composite
  11. Densification rate and interfacial adhesion of bilayer cemented tungsten carbide and steel
  12. Short Communications
  13. Cavitation erosion of 17-4 PH stainless steels following sub-zero treatment
  14. Investigation on microstructure and thermal properties of in-situ synthesized Cu–ZrO2 nanocomposites
  15. DGM News
  16. DGM News
Jetzt anmelden und 20% sparen
Institutioneller Zugang
Wie funktioniert Authentifizierung?
Haben Sie eine Idee, wie wir unsere Website verbessern können?
Bitte schreiben Sie uns.
© 2025 De Gruyter Brill
Heruntergeladen am 16.11.2025 von https://www.degruyterbrill.com/document/doi/10.3139/146.111566/pdf
Button zum nach oben scrollen