Preparation and post-treatment of silver powders for front contact pastes of silicon solar cells
-
Dunying Deng
und
Xiubing Liang
Abstract
Corrugated-surface silver powders were prepared for front contact pastes of silicon solar cells. The effects of using different pH controlling agents on the powder diameter, morphology, and conversion of silver ions to silver powders were investigated. Silver powders with wrinkled surface and 100% conversion were prepared, and ground by using spiral jet milling and tumbling ball milling, respectively. Silver powders ground by using spiral jet milling had better size distribution, higher tap density, and corrugated surface, the tap density of silver powders ground by using spiral jet milling was 6.52 g cm–3. The silver powders were used to prepare front contact pastes of silicon solar cells, the aspect ratio of printed gridlines was 0.34.
Funding statement: This work was supported by the National Key R&D Program of China (No. 2018YFC1902401).
References
[1] C. Yüce, K. Okamotob, L. Karpowichc, A. Adriand, N. Willenbacher: Sol. Energ. Mater. Sol. C. 200 (2019) 110040. DOI:10.1016/j.solmat.2019.11004010.1016/j.solmat.2019.110040Suche in Google Scholar
[2] K. Shetty, Y. Kaushal, D.S. Murthy, C.M. Kumar: Sol. Energy 180 (2019) 301. DOI:10.1016/j.solener.2019.01.02010.1016/j.solener.2019.01.020Suche in Google Scholar
[3] S. Jonai, A. Tanaka, K. Muramatsu, G. Saito, K. Nakamura, A. Ogura, Y. Ohshita, A. Masuda: Sol. Energy 188 (2019) 1292. DOI:10.1016/j.solener.2019.07.01210.1016/j.solener.2019.07.012Suche in Google Scholar
[4] G.Q. Guo, W.P. Gan, H. Liu, Y.L. Chen, F. Xiang, J. Luo, Z.B. Chen, J.Q. Li: Int. J. Mater. Res. 103 (2012) 7. DOI:10.3139/146.11069810.3139/146.110698Suche in Google Scholar
[5] S. Tepner, N. Wengenmeyr, M. Linse, A. Lorenz, M. Pospischil, F. Clement: Adv. Mater. Technol. 5 (2020) 2000654. DOI:10.1002/admt.20200065410.1002/admt.202000654Suche in Google Scholar
[6] S. Tepner, L. Ney, M, Linse, A. Lorenz, M. Pospischil, K. Masuri, F. Clement: Prog. Photovolt: Res. Appl. 28 (2020) 1. DOI:10.1002/pip.331310.1002/pip.3313Suche in Google Scholar
[7] M.M. Hilali, 2018 IEEE 7th World Conference on Photovoltaic Energy Conversion (WCPEC), IEEE.Suche in Google Scholar
[8] L.B. Mo, Y.Y. Zhang, L. Zhao, C.L. Zhou, W.J. Wang: J. Alloys Compd. 742 (2018) 256. DOI:10.1016/j.jallcom.2018.01.32110.1016/j.jallcom.2018.01.321Suche in Google Scholar
[9] Y.X. Chao, H.W. Yang, Y.X. Li, S.L. Guo, C. Wang: Chem. Phys. Lett. 708 (2018) 183. DOI:10.1016/j.cplett.2018.08.02110.1016/j.cplett.2018.08.021Suche in Google Scholar
[10] F. Lan, J.T. Bai, H. Wang: RSC Adv. 8 (2018) 16866. DOI:10.1039/c8ra02620c10.1039/c8ra02620cSuche in Google Scholar PubMed PubMed Central
[11] G. Wang, H. Wang, Y.B. Cui, J.T. Bai: J. Mater. Sci-Mater. El. 25 (2014) 487. DOI:10.1007/s10854-013-1613-410.1007/s10854-013-1613-4Suche in Google Scholar
[12] N. Moudir, Y. Boukennous, N. Moulaï-Mostefa, I. Bozetine, M. Maoudj, N. Kamel, Z. Kamel, D. Moudir: Energy Procedia 36 (2013) 1184. DOI:10.1016/j.egypro.2013.07.13410.1016/j.egypro.2013.07.134Suche in Google Scholar
[13] Y.W. Ao, Y.X. Yang, S.L. Yuan, L.H. Ding, G.R. Chen: Mater. Chem. Phys. 104 (2007) 158. DOI:10.1016/j.matchemphys.2007.02.10210.1016/j.matchemphys.2007.02.102Suche in Google Scholar
[14] Z.T. Chen, L. Gao: Mater. Res. Bull. 42 (2007) 1657. DOI:10.1016/j.materresbull.2006.11.02810.1016/j.materresbull.2006.11.028Suche in Google Scholar
[15] G.A. Martínez-Castañón, N. Niño-Martínez, J.P. Loyola-Rodríguez, N. Patiño-Marín, J.R. Martínez-Mendoza, F. Ruiz: Mater. Lett. 63 (2009) 1266. DOI:10.1016/j.matlet.2009.02.06110.1016/j.matlet.2009.02.061Suche in Google Scholar
[16] Y.F. Li, W.P. Gan, X.G. Liu, T. Lin, B. Huang: Korean J. Chem. Eng. 31(2014) 1490. DOI:10.1007/s11814-014-0069-410.1007/s11814-014-0069-4Suche in Google Scholar
[17] S.L.C. Hsu, R.T. Wu: Mater. Lett. 61 (2007) 3719. DOI:10.1016/j.matlet.2006.12.04010.1016/j.matlet.2006.12.040Suche in Google Scholar
[18] Q.D. Che, H.X. Yang, L. Lu, Y.H. Wang, H. Wang: Electron Mater. Lett. 9 (2013) 353. DOI:10.1007/s13391-012-2215-710.1007/s13391-012-2215-7Suche in Google Scholar
[19] Q.H. Tian, D. Deng, Y. LI, X.Y. Guo: Trans. Nonferrous Met. Soc. China 28 (2018) 524. DOI:10.1016/S1003-6326(18)64685-010.1016/S1003-6326(18)64685-0Suche in Google Scholar
[20] K.S. Chou, C.Y. Ren: Mater. Chem. Phys. 64 (2000) 241. DOI:10.1016/S0254-0584(00)00223-610.1016/S0254-0584(00)00223-6Suche in Google Scholar
[21] L. Lei, T. Gao, X. Yan: Diamond & Abrasives Engineering 31 (2016) 65–72. DOI:10.3969/j.issn.1006-852X.2011.03.01710.3969/j.issn.1006-852X.2011.03.017Suche in Google Scholar
[22] Dowa Mining Co., Ltd. Silver powder and method for producing same. US Patent: us 7618475B2 (2009).Suche in Google Scholar
[23] A. Katz, H. Kalman: Part. Part. Syst. Char. 24 (2007) 332. DOI:10.1002/ppsc.20060111410.1002/ppsc.200601114Suche in Google Scholar
© 2021 Walter de Gruyter GmbH, Berlin/Boston, Germany
Artikel in diesem Heft
- Contents
- Effects of sintering temperature on the microstructural properties of Al2O3–Y2O3 powder mixtures
- Synthesis of Al/Cu core–shell particles through optimization of galvanic replacement method in alkaline solution
- Study on the synthesis and application of BaTiO3 nanospheres
- Preparation and post-treatment of silver powders for front contact pastes of silicon solar cells
- Microwave absorption properties of Zn-doped barium ferrite (BaFe12-xZnxO19) decorated reduced graphene oxide
- The effect of electroplating current density on microstructure, corrosion, and wear behavior of Ni–P–W–TiO2 coating
- Investigation on the tool worn surface morphology and machining characteristics of the Hardox steel using minimum quantity lubrication
- Optimal removal of iron impurities from kaolin by combination of Aspergillus niger & Bacillus subtilis
- Review on the mechanical properties and biocompatibility of titanium implant: The role of niobium alloying element
- Notifications
- Deutsche Gesellschaft für Materialkunde / German Materials Science Society
Artikel in diesem Heft
- Contents
- Effects of sintering temperature on the microstructural properties of Al2O3–Y2O3 powder mixtures
- Synthesis of Al/Cu core–shell particles through optimization of galvanic replacement method in alkaline solution
- Study on the synthesis and application of BaTiO3 nanospheres
- Preparation and post-treatment of silver powders for front contact pastes of silicon solar cells
- Microwave absorption properties of Zn-doped barium ferrite (BaFe12-xZnxO19) decorated reduced graphene oxide
- The effect of electroplating current density on microstructure, corrosion, and wear behavior of Ni–P–W–TiO2 coating
- Investigation on the tool worn surface morphology and machining characteristics of the Hardox steel using minimum quantity lubrication
- Optimal removal of iron impurities from kaolin by combination of Aspergillus niger & Bacillus subtilis
- Review on the mechanical properties and biocompatibility of titanium implant: The role of niobium alloying element
- Notifications
- Deutsche Gesellschaft für Materialkunde / German Materials Science Society