Phase equilibria in the Zn–Fe–S system at 450°C
-
Zheng Tan
Abstract
The 450 °C isothermal section of the Zn – Fe – S phase diagram has been constructed using scanning electron microscopy coupled with energy dispersive X-ray spectroscopy and X-ray diffraction. In addition to the ternary extensions of the binary Zn – Fe intermediate compounds of ς, δ, Γ1, and Γ, the extensions of the ZnS, FeS and FeS2 compounds were also determined. The solubility of Fe in ZnS is about 20.2 at.%. The solubility of sulfur in all Fe – Zn intermetallic compounds is negligible. The zinc contents of Fe sulfides were not detectable.
References
[1] Y.Lepretre, J.M.Mataingne, in: Frank E.Goodwin (Ed.), Zn-Based Steel Coating System: Proudction and Performance, TMS, Warrendale, PA. (1998) 303.Suche in Google Scholar
[2] X.P.Su, N.Y.Tang, J.M.Toguri: Can. Metall. Q.40 (2001) 377.10.1179/000844301794388353Suche in Google Scholar
[3] X.P.Su, N.Y.Tang, J.M.Toguri: J. Alloys Comp.325 (2001) 129.10.1016/S0925-8388(01)01273-7Suche in Google Scholar
[4] R.W.Sandlin: Wire and wire products11 (1940) 3.Suche in Google Scholar
[5] J.Foct, P.Perrot, G.Reumont: Scripta Metall. Mater.28 (1993) 1195.10.1016/0956-716X(93)90453-YSuche in Google Scholar
[6] W.W.Barker, T.C.Parks: Gecchim. Comsmocim AC.50 (1986) 2185.10.1016/0016-7037(86)90073-6Suche in Google Scholar
[7] V.Raghavan: J. Phase Equilibria25 (2004) 382.10.1361/15477030420179Suche in Google Scholar
[8] P.B.BartonJr., P.ToulminIII: Econ. Geol.61 (1966) 815.10.2113/gsecongeo.61.5.815Suche in Google Scholar
[9] T.B.Massalski, in: Binary Alloys Phase Diagrams, ASM, Materials Park, OH (1990).Suche in Google Scholar
[10] O.Kubaschewski: Iron-Binary Phase Diagram, Springer-Verlag, Berlin (1982).Suche in Google Scholar
[11] S.Itoh: Trans. Met.40 (1999) 618.10.2320/matertrans1989.40.618Suche in Google Scholar
[12] F.Swanson: Natl. Bur. Stand. (U.S.), Circ.539 (1953) 15.Suche in Google Scholar
[13] H.E.King, C.T.Prewitt: Acta Cryst. Sec. B38 (1982) 1876.10.1107/S0567740882007511Suche in Google Scholar
[14] G.Brostigen, A.Kjekshus: Acta Chem. Scand.23 (1969) 2185.10.3891/acta.chem.scand.23-2186Suche in Google Scholar
[15] P.J.Brown: Acta Cryst.15 (1962) 608.10.1107/S0365110X62001528Suche in Google Scholar
[16] K.B.Almin: Acta Chem. Scand2 (1948) 399.10.3891/acta.chem.scand.02-0400Suche in Google Scholar
[17] G.F.Bastin, F.J.J.van Loo, G.D.Rieck: Z. Metallkd.65 (1974) 665.Suche in Google Scholar
[18] J.K.Brandon, R. Y.Brizard, P.C.Chieh, R.K.McMillan, W.B.Pearson: Acta. Cryst. Sec. B30 (1974) 1412.10.1107/S0567740874004997Suche in Google Scholar
© 2007, Carl Hanser Verlag, München
Artikel in diesem Heft
- Contents
- Contents
- Editorial
- Editorial
- Basic
- Synthesis and oxidation of Zr3Al3C5 powders
- Standard Gibbs energy of formation of Zn17Y2 and Zn12Y determined by solution calorimetry and measurement of heat capacity from near zero Kelvin
- Phase equilibria in the Zn–Fe–S system at 450°C
- Formation of δ-Al2O3 hollow nanoparticles via a chemical vapor condensation process
- Low-cycle fatigue and damage of an uncoated and coated single crystal nickel-base superalloy SCB
- Fluidity of Mg–Al–Ca alloys in the high-pressure die casting process
- Applied
- Mechanical properties of rope-reinforced aluminium extrusions under quasistatic loading conditions
- Influence of interfaces on the mechanical properties of ultrahigh carbon steel multilayer laminates
- Thermomechanical processing of AA6061 billets for semi-solid forming
- Infrared spectroscopy and X-ray diffraction data of In – Se compounds
- Synthesis and characterization of MgAlON–BN composites
- Neutron diffraction residual stress analysis of steel engineering components: a study of the elastic and plastic anisotropy
- Notifications
- DGM News
Artikel in diesem Heft
- Contents
- Contents
- Editorial
- Editorial
- Basic
- Synthesis and oxidation of Zr3Al3C5 powders
- Standard Gibbs energy of formation of Zn17Y2 and Zn12Y determined by solution calorimetry and measurement of heat capacity from near zero Kelvin
- Phase equilibria in the Zn–Fe–S system at 450°C
- Formation of δ-Al2O3 hollow nanoparticles via a chemical vapor condensation process
- Low-cycle fatigue and damage of an uncoated and coated single crystal nickel-base superalloy SCB
- Fluidity of Mg–Al–Ca alloys in the high-pressure die casting process
- Applied
- Mechanical properties of rope-reinforced aluminium extrusions under quasistatic loading conditions
- Influence of interfaces on the mechanical properties of ultrahigh carbon steel multilayer laminates
- Thermomechanical processing of AA6061 billets for semi-solid forming
- Infrared spectroscopy and X-ray diffraction data of In – Se compounds
- Synthesis and characterization of MgAlON–BN composites
- Neutron diffraction residual stress analysis of steel engineering components: a study of the elastic and plastic anisotropy
- Notifications
- DGM News