Preparation of epoxy/acrylonitrile-butadiene-styrene copolymer/short carbon fiber composites with a self-made conical mixer
-
Mingjing Yang
Abstract
Acrylonitrile-butadiene-styrene copolymer (ABS) was introduced to modify the epoxy resin (EP) by the solution mixing method. The results showed that the modulus was decreased with the addition of ABS. Short carbon fibers (SCF) were chosen as the reinforcement agent to prepare high-performance EP/ABS/SCF composites. Meanwhile, a self-made conical mixer was applied to improve the dispersion behavior of the SCF in EP. The properties of both EP/ABS matrix and EP/ABS/SCF composites were investigated and discussed. The results showed that the tensile strength and impact strength of EP/ABS matrix are remarkably improved in the presence of 4,4-diaminodiphenyl methane (DDM), which reached the maximum value at 4 wt% ABS. The introduction of ABS and SCF eventually can maintain the excellent original properties of EP and greatly improve the tensile modulus of EP/ABS/SCF composites with the specialized self-made conical mixer.
Acknowledgments
The authors gratefully acknowledge Tao Xiang, Yu Hua and Changyin Hao at the College of Polymer Science and Engineering, Sichuan University and Rong You at the School of Chemical Engineering, Sichuan University, for providing good advice with the experiment.
References
[1] Saidina DS, Mariatti M, Julie MJ. J. Mater. Sci-Mater. El. 2015, 26, 6245.10.1007/s10854-015-3210-1Suche in Google Scholar
[2] Wu P, Wan JP, Gan WK, Tang BM, An XF, Zhang M. Hong Du Sci. Technol. 2008, 4, 18–25.Suche in Google Scholar
[3] Zhou YQ. China Ship Repair. 2004, 1, 36–37.10.1017/S0033822200014302Suche in Google Scholar
[4] Chen P, Wang DZ. Epoxy Resin and its Application, 1st ed., Chemical Industry Press: Beijing, 2011, p 236–314.Suche in Google Scholar
[5] Guo LY, Wang LY, Su X. Adv. Mater. Res. 2012, 3, 3598–3602.10.4028/www.scientific.net/AMR.490-495.3598Suche in Google Scholar
[6] Sobrinho LL, Calado VMA, Bastian FL. Polym. Compos. 2012, 33, 295–305.10.1002/pc.21265Suche in Google Scholar
[7] Ying FY, Ming HW. Ind. Eng. Chem. Res. 2008, 47, 9361–9369.10.1021/ie800845pSuche in Google Scholar
[8] Ribeiro MCS, Tavares CML, Ferreira AJM. J. Polym. Eng. 2011, 22, 27–44.Suche in Google Scholar
[9] Wu CF, Xu WJ. Polymer 2007, 48, 5802–5812.10.1016/j.polymer.2007.07.019Suche in Google Scholar
[10] Hall SA, Howlin BJ, Hamerton I, Baidak A, Billaud C, Ward S. PLoS One 2012, 7, 1–12.10.1371/journal.pone.0042928Suche in Google Scholar PubMed PubMed Central
[11] Xiu YY, Wang Q, Luo ZY. China Adhes. 2007, 16, 36–40.Suche in Google Scholar
[12] Wei C, Tan ST, Wang XY. J. Mater. Sci. Lett. 2002, 21, 719–722.10.1023/A:1015789122841Suche in Google Scholar
[13] Xuan ZL, Yi JZ, Duan ZQ, Zhang Q. Fiber Reinf. Plast./Compos. 2004, 1, 24–27.Suche in Google Scholar
[14] Mottahedin L. J. Polym. Eng. 2012, 32, 311–317.10.1515/polyeng-2011-0120Suche in Google Scholar
[15] Thomas R, Ding YM, He YL, Yang L, Moldenagers P, Yang WM, Czigany T, Thomas S. Polymer 2008, 49, 278–294.10.1016/j.polymer.2007.11.030Suche in Google Scholar
[16] Thomas R, Abraham J, Selvin TP, Thomas S. J. Polym. Sci. Polym. Phys. 2004, 42, 2531–2544.10.1002/polb.20115Suche in Google Scholar
[17] Tripathi G, Srivastava D. Mater. Sci. Eng. 2007, 443, 262–269.10.1016/j.msea.2006.09.031Suche in Google Scholar
[18] Russella B, Chartoff R. Polymer 2005, 46, 785–798.10.1016/j.polymer.2004.11.090Suche in Google Scholar
[19] Lee J, Yee AF. Polym. Eng. Sci. 2000, 40, 2457–2470.10.1002/pen.11377Suche in Google Scholar
[20] Xiao K, Ye L. Polym. Eng. Sci. 2004, 40, 70–81.10.1002/pen.11140Suche in Google Scholar
[21] Bommaud L, Bonnet A, Pascault JP, Sautereau H, Riccardi CC. J. Appl. Polym. Sci. 2002, 83, 1385–1396.10.1002/app.10029Suche in Google Scholar
[22] Dumont D, Seveno D, Coninck JD, Bailly C. Polym. Int. 2012, 61, 1263–1271.10.1002/pi.4201Suche in Google Scholar
[23] Jyotishkumar P, Koetz J, Tiersch B, Strehmel V, Ozdilek C, Moldenaers P, Hassler R, Thomas S. J. Phys. Chem. B 2009, 113, 5418–5430.10.1021/jp8094566Suche in Google Scholar PubMed
[24] Perez M, Dumont M, Acevedo-Reyes D. Acta. Mater. 2008, 56, 2119–2132.10.1016/j.actamat.2007.12.050Suche in Google Scholar
[25] Vehkamaki H. Classical Nucleation Theory in Multicomponent Systems. Springer: Berlin, 2006, p 123.Suche in Google Scholar
[26] Mirmohseni A, Zavareh S. J. Polym. Res. 2009, 17, 191–201.10.1007/s10965-009-9305-8Suche in Google Scholar
[27] Yan Z. China Patent. Report No. 200920079756.4, December 16, 2009.Suche in Google Scholar
[28] Kaynak C, Orgun O, Tincer T. Polym. Test. 2005, 24, 455–462.10.1016/j.polymertesting.2005.01.004Suche in Google Scholar
[29] Zhang ZW, Tan YF, Tu YQ, Dong GY, Yang ZS. Acta Armamentarii. 2013, 34, 869–875.Suche in Google Scholar
[30] Blanco I, Cicala G, Lofaro C, Recca A. J. Polym. Eng. 2003, 23, 163–176.10.1515/POLYENG.2003.23.3.163Suche in Google Scholar
[31] Jagadeesh KS, Shashikiran K. J. Polym. Eng. 2011, 26, 87–116.Suche in Google Scholar
[32] Mafi ER, Ebrahimi M, Moghbeli MR. J. Polym. Eng. 2009, 29, 293–308.10.1515/POLYENG.2009.29.5.293Suche in Google Scholar
[33] Wang P, Sui G, Yang XP. Fiber Reinf. Plast./Compos. 2013, 2, 22–27.Suche in Google Scholar
[34] Bellenger V, Dhaoui W, Verdu J, Boye J, Lacabanne C. Polym. Eng. Sci. 1990, 30, 321–325.10.1002/pen.760300602Suche in Google Scholar
[35] Morgan RJ, Kong FM, Walkup CM. Polymer 1984, 25, 375–386.10.1016/0032-3861(84)90291-XSuche in Google Scholar
[36] Palmese GR, McCullough RL. J. Appl. Polym. Sci. 1992, 46, 1863–1873.10.1002/app.1992.070461018Suche in Google Scholar
[37] Fernandez N, Valea A. Eur. Polym. J. 1996, 32, 257–266.10.1016/0014-3057(95)00122-0Suche in Google Scholar
[38] Meng DHZ, Pan DK, Yan Z. China Plast. Ind. 2013, 41, 64–67.Suche in Google Scholar
[39] Su W, Peng H, Chen H, Zhang XX, Yan Z. Eng. Plast. Appl. 2014, 42, 52–55.Suche in Google Scholar
[40] Mirmohseni A, Zavareh S. Mater. Des. 2010, 31, 2699–2706.10.1016/j.matdes.2010.01.035Suche in Google Scholar
[41] Mirmohseni A, Zavareh S. J. Polym. Res. 2010, 18, 509–517.10.1007/s10965-010-9443-zSuche in Google Scholar
©2017 Walter de Gruyter GmbH, Berlin/Boston
Artikel in diesem Heft
- Frontmatter
- Original articles
- Preparation of epoxy/acrylonitrile-butadiene-styrene copolymer/short carbon fiber composites with a self-made conical mixer
- Preparation and characterization of poly (amide-ester-imide)/Na+-MMT nanocomposite via ultrasonic method
- Polyurethane membrane with a cyclodextrin-modified carbon nanotube for pervaporation of phenol/water mixture
- Fabrication of chitosan/PEO nanofiber mats with mica by electrospinning
- Effect of cooling induced crystallization upon the properties of segmented thermoplastic polyurethanes
- Conductivity and dielectric analysis of nanocolloidal polypyrrole particles functionalized with higher weight percentage of poly(styrene sulfonate) using the dispersion polymerization method
- Mechanism and solutions of appearance defects on microfluidic chips manufactured by UV-curing assisted injection molding
- Effect of gas counter pressure on shrinkage and residual stress for injection molding process
- Ablation and mechanical investigation of heat vulcanizing silicone rubber (HVSR) composite containing carbon fibers
- Cavitation desulfurization in vulcanized rubber recycling under ultra-high pressure water jet
Artikel in diesem Heft
- Frontmatter
- Original articles
- Preparation of epoxy/acrylonitrile-butadiene-styrene copolymer/short carbon fiber composites with a self-made conical mixer
- Preparation and characterization of poly (amide-ester-imide)/Na+-MMT nanocomposite via ultrasonic method
- Polyurethane membrane with a cyclodextrin-modified carbon nanotube for pervaporation of phenol/water mixture
- Fabrication of chitosan/PEO nanofiber mats with mica by electrospinning
- Effect of cooling induced crystallization upon the properties of segmented thermoplastic polyurethanes
- Conductivity and dielectric analysis of nanocolloidal polypyrrole particles functionalized with higher weight percentage of poly(styrene sulfonate) using the dispersion polymerization method
- Mechanism and solutions of appearance defects on microfluidic chips manufactured by UV-curing assisted injection molding
- Effect of gas counter pressure on shrinkage and residual stress for injection molding process
- Ablation and mechanical investigation of heat vulcanizing silicone rubber (HVSR) composite containing carbon fibers
- Cavitation desulfurization in vulcanized rubber recycling under ultra-high pressure water jet