Influence of backing layers on the interlaminar fracture toughness energy – Mode I – of quasi-unidirectional GFRP
-
Simon Backens
Dipl. Ing. Simon Backens, born in 1990, studied mechanical engineering at the TU Kaiserslautern. Since 2016, he has been a research assistant at the Fraunhofer Institute for Large Structures in Production Engineering IGP in Rostock. He works in the Fiber Composite Technology Group of the New Materials and Processes Department.
,
Stefan Schmidt
Dr.Ing. Stefan Schmidt, born in 1988, studied mechanical engineering at the University of Rostock and has been working at the Fraunhofer Institute for Large Structures in Production Engineering IGP in Rostock since 2014. In 2020, he completed his doctorate on the topic of “Structural bonding of fiber-reinforced plastic composites”. Since 2020, he is head of the Fiber Composite Technology Group.
Prof. Dr. Ing. Wilko Flügge, born in 1969, studied mechanical engineering at the TU Clausthal. At the University of Paderborn, he completed his doctorate on the subject of “Punch riveting of stainless steels”. Until 2017, he worked in research in the field of application technology at Salzgitter AG. Since June 2017, he has been chair holder of the Chair of Production Engineering at the University of Rostock and head of the Fraunhofer Institute for Large Structures in Production Engineering IGP.
Abstract
Quasi-unidirectional glass fiber non-crimp fabrics consist of a unidirectional main layer in the 0° direction stabilized by a backing layer in the 90° direction with a significantly lower amount of fibers. It is known that the backing layers impair the fatigue performance of respective reinforced plastics due to their orientation perpendicular to the main load direction. They act as damage initiators for the failure of the load-carrying unidirectional fibers. In the present work, the positive influence of the backing layers on the interlaminar fracture toughness energy – Mode I – GIC is demonstrated by tests in accordance with DIN EN 6033. The presence of backing fibers in the delamination plane can improve the GIC values by up to 43 %. Furthermore, results from evaluation according to DIN EN 6033 and ASTM D5528 are shown to have a good agreement, if the correction factor for large displacements recommended in the ASTM standard is not applied. If it is applied, however, there is a clear gap of up to 19 % between the two standards because the DIN simply does not provide a correction for large deflections.
About the authors
Dipl. Ing. Simon Backens, born in 1990, studied mechanical engineering at the TU Kaiserslautern. Since 2016, he has been a research assistant at the Fraunhofer Institute for Large Structures in Production Engineering IGP in Rostock. He works in the Fiber Composite Technology Group of the New Materials and Processes Department.
Dr.Ing. Stefan Schmidt, born in 1988, studied mechanical engineering at the University of Rostock and has been working at the Fraunhofer Institute for Large Structures in Production Engineering IGP in Rostock since 2014. In 2020, he completed his doctorate on the topic of “Structural bonding of fiber-reinforced plastic composites”. Since 2020, he is head of the Fiber Composite Technology Group.
Prof. Dr. Ing. Wilko Flügge, born in 1969, studied mechanical engineering at the TU Clausthal. At the University of Paderborn, he completed his doctorate on the subject of “Punch riveting of stainless steels”. Until 2017, he worked in research in the field of application technology at Salzgitter AG. Since June 2017, he has been chair holder of the Chair of Production Engineering at the University of Rostock and head of the Fraunhofer Institute for Large Structures in Production Engineering IGP.
Acknowledgments
The authors thank Viktoria Nikolova and Kathrin Hasche (both New Materials and Processes, Fraunhofer IGP) for the manufacturing of the GFRP laminates and the determination of the fiber volume contents. They thank Laurens Nagel and Elisa Deiß for their support in carrying out and evaluating the tests. Their thanks also go to Nordex Energy SE & Co. KG for providing the materials used.
-
Research ethics: Not applicable.
-
Author contributions: The authors have accepted responsibility for the entire content of this manuscript and approved its submission.
-
Competing interests: The authors state no conflict of interest.
-
Research funding: None declared.
-
Data availability: The raw data can be obtained on request from the corresponding author.
References
[1] K. Vallons, G. Adolphs, P. Lucas, S. V. Lomov, and I. Verpoest, “Quasi-UD glass fibreNCF composites for wind energy applications: a review of requirements and existing fatigue data for blade materials,” Mech. Ind., vol. 14, no. 3, pp. 175–189, 2013, https://doi.org/10.1051/meca/2013045.Suche in Google Scholar
[2] J. Zangenberg, P. Brøndsted, and J. W. Gillespie, “Fatigue damage propagation in unidirectional glass fibre reinforced composites made of a non-crimp fabric,” J. Compos. Mater., vol. 48, no. 22, pp. 2711–2727, 2014, https://doi.org/10.1177/0021998313502062.Suche in Google Scholar
[3] K. M. Jespersen, J. Zangenberg, T. Lowe, P. J. Withers, and L. P. Mikkelsen, “Fatigue damage assessment of uni-directional non-crimp fabric reinforced polyester composite using X-ray computed tomography,” Compos. Sci. Technol., vol. 136, pp. 94–103, 2016, https://doi.org/10.1016/j.compscitech.2016.10.006.Suche in Google Scholar
[4] K. M. Jespersen and L. P. Mikkelsen, “Three dimensional fatigue damage evolution in non-crimp glass fibre fabric based composites used for wind turbine blades,” Compos. Sci. Technol., vol. 153, pp. 261–272, 2017, https://doi.org/10.1016/j.compscitech.2017.10.004.Suche in Google Scholar
[5] K. M. Jespersen, J. A. Glud, J. Zangenberg, A. Hosoi, H. Kawada, and L. P. Mikkelsen, “Uncovering the fatigue damage initiation and progression in uni-directional non-crimp fabric reinforced polyester composite,” Compos. Part A Appl. Sci., vol. 109, pp. 481–497, 2018, https://doi.org/10.1016/j.compositesa.2018.03.002.Suche in Google Scholar
[6] S. Korkiakoski, P. Brøndsted, E. Sarlin, and O. Saarela, “Influence of specimen type and reinforcement on measured tension–tension fatigue life of unidirectional GFRP laminates,” Int. J. Fatigue, vol. 85, pp. 114–129, 2016, https://doi.org/10.1016/j.ijfatigue.2015.12.008.Suche in Google Scholar
[7] D. D. Samborsky, J. F. Mandell, and D. Miller, “The SNL/MSU/DOE fatigue of composite materials database: recent trends,” in 53rd AIAA/ASME/ASCE/AHS/ASC, Structures, Structural Dynamics and Materials Conf, Honolulu, Haiwaii, 2012.10.2514/6.2012-1573Suche in Google Scholar
[8] R. Rikards, A. Korjakin, F. G. Buchholz, H. Wang, A. K. Bledzki, and G. Wacker, “Interlaminar fracture toughness of GFRP influenced by fiber surface treatment,” J. Compos. Mater., vol. 32, no. 17, pp. 1528–1559, 1998, https://doi.org/10.1177/002199839803201701.Suche in Google Scholar
[9] P. Robinson and J. M. Hodgkinson, “Interlaminar fracture toughness,” in Mechanical testing of advanced fibre composites, J. M. Hodgkinson, Ed., Cambridge, England, Boca Raton, FL, USA, Woodhead Publishing Limited, CRC Press, 2000, pp. 170–210. ch. 9.10.1533/9781855738911.170Suche in Google Scholar
[10] European Standards, Luft- und Raumfahrt – Kohlenstofffaserverstärkte Kunststoffe – Prüfverfahren – Bestimmung der interlaminaren Energiefreisetzungsrate – Mode I – GIC, DIN EN 6033:2015, Berlin, Germany, DIN Deutsches Institut für Normung e.V., 2016.Suche in Google Scholar
[11] ASTM International, Standard Test Method for Mode I Interlaminar Fracture Toughness of Unidirectional Fiber-Reinforced Polymer Matrix Composites, ASTM D5528 – 13, West Conshohocken, PA, USA, ASTM International, 2013.Suche in Google Scholar
[12] ISO - International Organization for Standardization, Fibre-Reinforced Plastic Composites – Determination of Mode I Interlaminar Fracture Toughness, GIC, for Unidirectionally Reinforced Materials, ISO 15024:2001(E), Geneve, Switzerland, ISO International Organization for Standardisation, 2001.Suche in Google Scholar
[13] T. K. O’Brien, and R. H. Martin, “Round robin testing for mode I interlaminar fracture toughness of composite materials,” J. Compos. Technol. Res., vol. 15, no. 4, pp. 269–281, 1993, https://doi.org/10.1520/CTR10379J.Suche in Google Scholar
[14] D. C. Hartlen, J. Montesano, and D. S. Cronin, “A composite rigid double cantilever beam specimen for assessing the traction–separation response of mode I delamination in composite laminates,” Exp. Mech., vol. 63, no. 8, pp. 1273–1283, 2023, https://doi.org/10.1007/s11340-023-00987-2.Suche in Google Scholar
[15] V. Tamuzs, S. Tarasovs, and U. Vilks, “Progressive delamination and fiber bridging modeling in double cantilever beam composite specimens,” Eng. Fract. Mech., vol. 68, pp. 513–525, 2001, https://doi.org/10.1016/S0013-7944(00)00131-4.Suche in Google Scholar
[16] E. Farmand-Ashtiani, J. Cugnoni, and J. Botsis, “Specimen thickness dependence of large scale fiber bridging in mode I interlaminar fracture of carbon epoxy composite,” Int. J. Solids Struct., vol. 55, pp. 58–65, 2015, https://doi.org/10.1016/j.ijsolstr.2014.03.031.Suche in Google Scholar
[17] R. Marat-Mendes and M. Freitas, “DCB, ENF and ECT tests for interlaminar fracture of glass/epoxy unidirectional laminates,” in 10th Portugueses Conf. on Fracture, Braga, Portugal, 2006.Suche in Google Scholar
© 2024 Walter de Gruyter GmbH, Berlin/Boston
Artikel in diesem Heft
- Frontmatter
- Development and validation of a test facility for bending corrosion fatigue of hybrid laminates
- A comparative analysis of corrosion assessment techniques for steel in reinforced concrete exposed to brine water environments
- Experimental analysis of S–N curves of welded joints with different fatigue life extension approaches
- New generation steels for light weight vehicle safety related applications
- Fatigue life evaluation of laser welded lap joints of dissimilar aluminum alloys
- Weld interface metallurgy of dissimilar alloys welded by TIG technique
- Wear characteristics of cold tool steels for recycling plastic preprocessing
- Influence of backing layers on the interlaminar fracture toughness energy – Mode I – of quasi-unidirectional GFRP
- Influence of Borides on microstructure and mechanical properties of a Ni alloy
- Characterization of material flow behavior in friction stir welded AA2014 aluminum alloy joints
- Enhancing the structural performance of engineering components using the geometric mean optimizer
- Stress relaxation experimental research and prediction of GFRP pipes under ring deflection condition
- Experimental testing and numerical simulations of 3D-printed PETG pins used for vehicle pedals
- Low-temperature creep performance of additive manufactured Ti–6Al–4V
Artikel in diesem Heft
- Frontmatter
- Development and validation of a test facility for bending corrosion fatigue of hybrid laminates
- A comparative analysis of corrosion assessment techniques for steel in reinforced concrete exposed to brine water environments
- Experimental analysis of S–N curves of welded joints with different fatigue life extension approaches
- New generation steels for light weight vehicle safety related applications
- Fatigue life evaluation of laser welded lap joints of dissimilar aluminum alloys
- Weld interface metallurgy of dissimilar alloys welded by TIG technique
- Wear characteristics of cold tool steels for recycling plastic preprocessing
- Influence of backing layers on the interlaminar fracture toughness energy – Mode I – of quasi-unidirectional GFRP
- Influence of Borides on microstructure and mechanical properties of a Ni alloy
- Characterization of material flow behavior in friction stir welded AA2014 aluminum alloy joints
- Enhancing the structural performance of engineering components using the geometric mean optimizer
- Stress relaxation experimental research and prediction of GFRP pipes under ring deflection condition
- Experimental testing and numerical simulations of 3D-printed PETG pins used for vehicle pedals
- Low-temperature creep performance of additive manufactured Ti–6Al–4V