Effect of lignin and hemicelluloses on the tensile strength of micro-veneers determined at finite span and zero span
-
André Klüppel
Published/Copyright:
December 13, 2011
Abstract
Scots pine micro-veneers were subjected to hydrolysis with sulphuric acid or delignification with acidic sodium chlorite and a combination of both treatments. The tensile strength of untreated and treated veneers was determined at finite span (f-strength) and zero span (z-strength) under both dry (20°C, 65% relative humidity) and water-saturated conditions. Acidic hydrolysis resulted in significant strength losses in both testing modes and both moisture conditions, with the greatest strength reduction found for f-strength tested dry. After delignification, only f-strength under wet conditions was substantially reduced; dry f-strength and both dry and wet z-strength hardly changed. A combined treatment of prehydrolysis and delignification resulted in disintegration of the veneers, which made strength determination impossible. It was concluded that, in addition to cellulose, the hemicelluloses determine the f-strength under dry conditions, while lignin confers wet strength but appears not to contribute to interfibre adhesion and f-strength under dry conditions.
Received: 2011-7-22
Accepted: 2011-11-1
Published Online: 2011-12-13
Published in Print: 2012-05-01
©2012 by Walter de Gruyter Berlin Boston
You are currently not able to access this content.
You are currently not able to access this content.
Articles in the same Issue
- Original Papers
- Synthesis of glucose esters from cellulose in ionic liquids
- A new soy flour-polyepoxide adhesive system for making interior plywood
- Hydrophobisation of mechanical pulp fibres with sodium dodecyl sulphate functionalised layered double hydroxide particles
- Effect of pH on lignin analysis by Raman spectroscopy
- Fractionation and characterization of lignin carbohydrate complexes (LCCs) of Eucalyptus globulus in residues left after MWL isolation. Part I: Analyses of hemicellulose-lignin fraction (HC-L)
- Surface and internal micro/ultrastructure of TMP fibres produced during high-intensity refining elucidate the development of pulp and paper properties
- Mechanoradical formation and its effects on birch kraft pulp during the preparation of nanofibrillated cellulose with Masuko refining
- Influence of specimen configuration on the measurement of the off-axis Young’s modulus of wood by vibration tests
- Effect of lignin and hemicelluloses on the tensile strength of micro-veneers determined at finite span and zero span
- Revisiting the neutral axis in wood beams
- Relationship between copper species in solution and leaching from alkaline copper quat (ACQ) treated wood
- Assessment of the early signs of decay of Populus deltoides wafers exposed to Trametes versicolor by near infrared spectroscopy
- Community analysis of preservative-treated southern pine (Pinus spp.) using terminal restriction fragment length polymorphism (T-RFLP) analysis. Part 1: Fungal field study
- Community analysis of preservative-treated southern pine (Pinus spp.) using terminal restriction fragment length polymorphism (T-RFLP) analysis. Part 2: Bacteria field study
- Phylogenetic analysis and discoloration characteristics of major molds inhabiting woods. Part 3. Genus Cladosporium
- Identification of biochemical differences between the sapwood and transition zone in Robinia pseudoacacia L. by differential display of proteins
- Short Notes
- Reduction of formaldehyde emission from light MDF panels by adding chestnut shell flour
- On the structure of the active compound in mass deacidification of paper
- Meetings
- Meetings
- Masthead
- Masthead
Keywords for this article
dry strength;
finite span;
microtensile testing;
micro-veneers;
wet strength;
zero span
Articles in the same Issue
- Original Papers
- Synthesis of glucose esters from cellulose in ionic liquids
- A new soy flour-polyepoxide adhesive system for making interior plywood
- Hydrophobisation of mechanical pulp fibres with sodium dodecyl sulphate functionalised layered double hydroxide particles
- Effect of pH on lignin analysis by Raman spectroscopy
- Fractionation and characterization of lignin carbohydrate complexes (LCCs) of Eucalyptus globulus in residues left after MWL isolation. Part I: Analyses of hemicellulose-lignin fraction (HC-L)
- Surface and internal micro/ultrastructure of TMP fibres produced during high-intensity refining elucidate the development of pulp and paper properties
- Mechanoradical formation and its effects on birch kraft pulp during the preparation of nanofibrillated cellulose with Masuko refining
- Influence of specimen configuration on the measurement of the off-axis Young’s modulus of wood by vibration tests
- Effect of lignin and hemicelluloses on the tensile strength of micro-veneers determined at finite span and zero span
- Revisiting the neutral axis in wood beams
- Relationship between copper species in solution and leaching from alkaline copper quat (ACQ) treated wood
- Assessment of the early signs of decay of Populus deltoides wafers exposed to Trametes versicolor by near infrared spectroscopy
- Community analysis of preservative-treated southern pine (Pinus spp.) using terminal restriction fragment length polymorphism (T-RFLP) analysis. Part 1: Fungal field study
- Community analysis of preservative-treated southern pine (Pinus spp.) using terminal restriction fragment length polymorphism (T-RFLP) analysis. Part 2: Bacteria field study
- Phylogenetic analysis and discoloration characteristics of major molds inhabiting woods. Part 3. Genus Cladosporium
- Identification of biochemical differences between the sapwood and transition zone in Robinia pseudoacacia L. by differential display of proteins
- Short Notes
- Reduction of formaldehyde emission from light MDF panels by adding chestnut shell flour
- On the structure of the active compound in mass deacidification of paper
- Meetings
- Meetings
- Masthead
- Masthead