Iso-thermal Section of the Phase Diagram of the System Na2MoO4-MoO3-CeO2 at 1073 K
-
M. Hasegawa,
Veröffentlicht/Copyright:
10. März 2011
Published Online: 2011-03-10
Published in Print: 2009-12
©2011 by Walter de Gruyter GmbH & Co.
Artikel in diesem Heft
- TABLE OF CONTENTS
- Coating Degradation of First and Second Stage Gas Turbine Blades
- Growth of Small Alumina Clusters during Ladle Deoxidation
- Ultrasonic Attenuation Measurement Method for Characterization of Clay Particles Mass Fraction in Dilute Suspension.
- Synthesis and Characterization of New Copoly(amide-imide)s Based on Bicyclo[2,2,2] oct-7-ene-2,3,5,6-tetracarboxylic diimide and Azobenzene Group in the Main Chain
- Iso-thermal Section of the Phase Diagram of the System Na2MoO4-MoO3-CeO2 at 1073 K
- Degradation of Fe- xCr-5Al Alloys Induced by KCl-ZnCl2 Deposits at 773K
- Coating of Nickel Aluminide by Pack Cementation to Improve Oxidation Resistance of Nickel-Based Superalloy, Grade IN 738
- Modeling of Reactions between Gas Bubble and Molten Metal Bath—Experimental Validation in the Case of Decarburization of Fe-Cr-C melts
Creative Commons
BY-NC-ND 3.0
Artikel in diesem Heft
- TABLE OF CONTENTS
- Coating Degradation of First and Second Stage Gas Turbine Blades
- Growth of Small Alumina Clusters during Ladle Deoxidation
- Ultrasonic Attenuation Measurement Method for Characterization of Clay Particles Mass Fraction in Dilute Suspension.
- Synthesis and Characterization of New Copoly(amide-imide)s Based on Bicyclo[2,2,2] oct-7-ene-2,3,5,6-tetracarboxylic diimide and Azobenzene Group in the Main Chain
- Iso-thermal Section of the Phase Diagram of the System Na2MoO4-MoO3-CeO2 at 1073 K
- Degradation of Fe- xCr-5Al Alloys Induced by KCl-ZnCl2 Deposits at 773K
- Coating of Nickel Aluminide by Pack Cementation to Improve Oxidation Resistance of Nickel-Based Superalloy, Grade IN 738
- Modeling of Reactions between Gas Bubble and Molten Metal Bath—Experimental Validation in the Case of Decarburization of Fe-Cr-C melts