Coating of Nickel Aluminide by Pack Cementation to Improve Oxidation Resistance of Nickel-Based Superalloy, Grade IN 738

  • Patama Visuttipitukul, , Sirinya Chansaksoong, and Panyawat Wangyao,
Published/Copyright: March 10, 2011
Download Article (PDF)
High Temperature Materials and Processes
From the journal High Temperature Materials and Processes Volume 28 Issue 6

Published Online: 2011-03-10
Published in Print: 2009-12

©2011 by Walter de Gruyter GmbH & Co.

Articles in the same Issue

  1. TABLE OF CONTENTS
  2. Coating Degradation of First and Second Stage Gas Turbine Blades
  3. Growth of Small Alumina Clusters during Ladle Deoxidation
  4. Ultrasonic Attenuation Measurement Method for Characterization of Clay Particles Mass Fraction in Dilute Suspension.
  5. Synthesis and Characterization of New Copoly(amide-imide)s Based on Bicyclo[2,2,2] oct-7-ene-2,3,5,6-tetracarboxylic diimide and Azobenzene Group in the Main Chain
  6. Iso-thermal Section of the Phase Diagram of the System Na2MoO4-MoO3-CeO2 at 1073 K
  7. Degradation of Fe- xCr-5Al Alloys Induced by KCl-ZnCl2 Deposits at 773K
  8. Coating of Nickel Aluminide by Pack Cementation to Improve Oxidation Resistance of Nickel-Based Superalloy, Grade IN 738
  9. Modeling of Reactions between Gas Bubble and Molten Metal Bath—Experimental Validation in the Case of Decarburization of Fe-Cr-C melts
https://doi.org/10.1515/HTMP.2009.28.6.401
Creative Commons
BY-NC-ND 3.0

Articles in the same Issue

  1. TABLE OF CONTENTS
  2. Coating Degradation of First and Second Stage Gas Turbine Blades
  3. Growth of Small Alumina Clusters during Ladle Deoxidation
  4. Ultrasonic Attenuation Measurement Method for Characterization of Clay Particles Mass Fraction in Dilute Suspension.
  5. Synthesis and Characterization of New Copoly(amide-imide)s Based on Bicyclo[2,2,2] oct-7-ene-2,3,5,6-tetracarboxylic diimide and Azobenzene Group in the Main Chain
  6. Iso-thermal Section of the Phase Diagram of the System Na2MoO4-MoO3-CeO2 at 1073 K
  7. Degradation of Fe- xCr-5Al Alloys Induced by KCl-ZnCl2 Deposits at 773K
  8. Coating of Nickel Aluminide by Pack Cementation to Improve Oxidation Resistance of Nickel-Based Superalloy, Grade IN 738
  9. Modeling of Reactions between Gas Bubble and Molten Metal Bath—Experimental Validation in the Case of Decarburization of Fe-Cr-C melts
Sign up now to receive a 20% welcome discount
Institutional Access
How does access work?
Have an idea on how to improve our website?
Please write us.
© 2026 De Gruyter Brill
Downloaded on 10.2.2026 from https://www.degruyterbrill.com/document/doi/10.1515/HTMP.2009.28.6.401/html
Scroll to top button