Startseite Technik The origin and development of the P{011}<111> orientation during recrystallization of particle-containing alloys
Artikel
Lizenziert
Nicht lizenziert Erfordert eine Authentifizierung

The origin and development of the P{011}<111> orientation during recrystallization of particle-containing alloys

Dedicated to Prof. Dr.-Ing. Heinrich Wollenberger on the occasion of his 80th birthday
  • Carmen Schäfer und Günter Gottstein
Veröffentlicht/Copyright: 18. Mai 2013
Veröffentlichen auch Sie bei De Gruyter Brill
Manuskript einreichen Informationen für Autor*innen
International Journal of Materials Research
Aus der Zeitschrift International Journal of Materials Research Band 102 Heft 9

Abstract

During annealing of particle-containing aluminum alloys, very often the development of the so-called P {011}<111>-texture and ND-rotated Cube {001}<310>-texture components are observed. The present paper focuses on the origin of the P-component near particles in an Al-1.1 wt.% Mn alloy and its further evolution during annealing. It is shown that the occurrence of these components depends on the annealing treatment rather than on the absolute annealing temperature.

Keywords: Recrystallization; Particle-stimulated nucleation; Recovery; Precipitation
∗ Correspondence address, Dr.-Ing. Carmen Schäfer, Institut fr Metallkunde und Metallphysik, Kopernikusstr. 14, D-52074 Aachen, Germany, Tel.: +49241 8026877, Fax: +49241 8022301, E-mail:

References

[1] K.C.Russell, M.F.Ashby: Acta Metall.18 (1970) 891.10.1016/0001-6160(70)90017-9Suche in Google Scholar

[2] M.F.Ashby: Phil. Mag.21 (1970) 399.10.1080/14786437008238426Suche in Google Scholar

[3] F.J.Humphreys: Acta Metall.25 (1977) 1323.10.1016/0001-6160(77)90109-2Suche in Google Scholar

[4] P.Herbst, J.Huber, in: G.Gottstein, K.Lücke (Eds.), Texture of Metallic Materials, Vol. 1, Springer Verlag, Berlin (1978) 453.10.1007/978-3-642-81313-9_43Suche in Google Scholar

[5] B.Bay, N.Hansen: Metall. Trans. A10 (1979) 279.Suche in Google Scholar

[6] J.Liu, J.G.Morris: Metall. Trans. A34 (2003) 2029.10.1007/s11661-003-0169-ySuche in Google Scholar

[7] F.Haessner, E.Hornbogen, M.Mukherjee: Z. Metallkd., 57 (1966) 171.Suche in Google Scholar

[8] F.J.Humphreys, M.G.Ardakani: Acta Metall. Mater.42 (1994) 749.10.1016/0956-7151(94)90272-0Suche in Google Scholar

[9] M.G.Ardakani, F.J.Humphreys: Acta Metall.42 (1994) 763.10.1016/0956-7151(94)90273-9Suche in Google Scholar

[10] M.Ferry, F.J.Humphreys: Acta Mater.44 (1996) 3089.10.1016/1359-6454(95)00432-7Suche in Google Scholar

[11] M.Ferry, F.J.Humphreys: Mater. Sci. Forum217-222 (1996) 493.10.4028/www.scientific.net/MSF.217-222.493Suche in Google Scholar

[12] F.J.Humphreys, M.Hatherly: Recrystallization and related annealing phenomena, Elsevier, Oxford (2004).Suche in Google Scholar

[13] O.Engler, X.W.Kong, P.Yang: Scripta Mater.37 (1997) 1665.10.1016/S1359-6462(97)00315-1Suche in Google Scholar

[14] O.Engler, J.Hirsch, K.Lücke: Acta Metall. Mater.43 (1995) 121.Suche in Google Scholar

[15] O.Engler: Tex. and Microstructures23 (1995) 61.10.1155/TSM.23.61Suche in Google Scholar

[16] O.Engler, P.Yang, X.W.Kong: Acta Mater.44 (1996) 3349.10.1016/1359-6454(95)00416-5Suche in Google Scholar

[17] K.Lücke, O.Engler: Mat. Sci. Tech.6 (1990) 1113.10.1179/026708390790190009Suche in Google Scholar

[18] O.Engler: Mat. Sci. Tech.12 (1996) 859.10.1179/026708396790122206Suche in Google Scholar

[19] D.Juul Jensen, N.Hansen, Y.L.Liu: Mat. Sci. and Tech.2 (1991) 369.10.1179/026708391790183330Suche in Google Scholar

[20] K.Lücke, O.Engler, in: L.Arnberg, O.Lohne, E.Nes, N.Ryum (Eds.), Proc. ICAA3, Vol. III, Norway (1992) 439.Suche in Google Scholar

[21] K.Sjølstad, O.Engler, S.Tangen, K.Marthinsen, E.Nes: Mater. Sci. Forum408–412 (2002) 1471.10.4028/www.scientific.net/MSF.408-412.1471Suche in Google Scholar

[22] O.Daaland, E.Nes: Acta Mater.44 (1996) 1413.10.1016/1359-6454(95)00290-1Suche in Google Scholar

[23] H.E.Vatne, S.Benum, O.Daaland, E.Nes: Tex. and Microstructures26-27 (1996) 385.10.1155/TSM.26-27.385Suche in Google Scholar

[24] M.Somerday, F.J.Humphreys: Mater. Sci. Techn.19 (2003) 20.Suche in Google Scholar

[25] W.C.Liu, J.G.Morris: Metall. Mater. Trans. A36 (2005) 2829.10.1007/s11661-005-0279-9Suche in Google Scholar

[26] M.Dahms, H.J.Bunge: Tex. and Microstructures 8, 9 (1988) 97.10.1155/TSM.8-9.97Suche in Google Scholar

[27] K.Lücke, J.Pospiech, K.H.Virnich, J.Jura: Acta Metall.29 (1981) 167.10.1016/0001-6160(81)90097-3Suche in Google Scholar

[28] K.H.Virnich, J.Pospiech, A.Flemmer, K.Lücke, in: G.Gottstein, K.Lücke (Eds.), ICOTOM 5, Vol. 1, Springer, Berlin (1978) 129.10.1007/978-3-642-81313-9_9Suche in Google Scholar

[29] W.Truszkowski, J.Pospiech, J.Jura, B.Major, in: Proc. of the 3àme colloque européen sur les textures de deformation et de recristallisation des métaux et leurs aaplications industrielles, Pont-à-Mousson (1973) 235.Suche in Google Scholar

[30] R.Fortunier, J.Hirsch, in: H.J. Bunge (Ed.), Theoretical Methods of Texture Analysis (1987) 231.Suche in Google Scholar

[31] H.J.Bunge: Texture Analysis in Materials Science, Butterworths, London (1982).Suche in Google Scholar

[32] C.Schäfer, J.Song, G.Gottstein: Acta Mater.57 (2009) 1026.10.1016/j.actamat.2008.10.052Suche in Google Scholar

[33] J.Pospiech, K.Lücke: Acta Metall.23 (1975) 997.10.1016/0001-6160(75)90014-0Suche in Google Scholar

[34] J.Jura, in: H.J.Bunge, R.Penelle, C.Esling (Eds.), ICOTOM 9, Avignon, France, Textures Microstructures14–18 (1991) 193.10.1155/TSM.14-18.193Suche in Google Scholar

[35] E.Nes: Aluminium52 (1976) 560.10.1111/j.1751-0813.1976.tb05420.xSuche in Google Scholar

[36] P.Furrer, H.Warlimont: Aluminium54 (1978) 135.Suche in Google Scholar

[37] C.C.Bampton, J.A.Wert, M.W.Mahoney: Metall. Trans. A13 (1982) 193.Suche in Google Scholar

[38] S.Tangen: Deformation and annealing behaviour of commercial non-heat treatable aluminium alloys, Doctoral Thesis, NTNU, Norway (2004).Suche in Google Scholar

[39] W.C.Liu, Z.Li, C.-S.Man: Mater. Sci. Eng. A478 (2008) 173.10.1016/j.msea.2007.05.107Suche in Google Scholar

[40] P.van Houtte: Acta Metall. Mater.43 (1995) 2859.10.1016/0956-7151(94)00479-2Suche in Google Scholar

[41] S.Tangen, K.Sjølstad, E.Nes, T.Furu, K.Marthinsen: Mater. Sci. Forum396–402 (2002) 469.10.4028/www.scientific.net/MSF.396-402.469Suche in Google Scholar

Received: 2010-11-9
Accepted: 2011-7-1
Published Online: 2013-05-18
Published in Print: 2011-09-01

© 2011, Carl Hanser Verlag, München

Artikel in diesem Heft

  1. Contents
  2. Contents
  3. Editorial
  4. Prof. Dr.-Ing. Heinrich Wollenberger — 80 years
  5. Original Contributions
  6. Atom probe tomography: from physical metallurgy towards microelectronics
  7. Accumulation of radiation damage and disordering in MgAl2O4 under swift heavy ion irradiation
  8. TEM study of irradiation induced copper precipitation in boron alloyed EUROFER97 steel
  9. Order – disorder transformation in Ni – V alloys under electron irradiation
  10. Materials issues of the SINQ high-power spallation target
  11. The origin and development of the P{011}<111> orientation during recrystallization of particle-containing alloys
  12. Coarsening kinetics of Cu-rich precipitates in a concentrated multicomponent Fe–Cu based steel
  13. Beyond Ni-based superalloys: Development of CoRe-based alloys for gas turbine applications at very high temperatures
  14. The effect of heat treatments on the microstructure, texture and mechanical properties of the extruded magnesium alloy ME21
  15. Analysing SANS data to determine magnetisation reversal processes in composite perpendicular magnetic recording media using TEM images
  16. Dislocationless sliding in a polycluster glass
  17. Evolution of transformation plasticity during bainitic transformation
  18. Surface tension and viscosity of NiAl catalytic precursor alloys from microgravity experiments
  19. Synthesis of carbon nanotubes by fine Ni particles in Ni3Al foam
  20. Fabrication of dielectric thin films by sputtering deposition at different pressures with (Ba0.3Sr0.7)(Zn1/3Nb2/3)O3 ceramic as target
  21. DGM News
  22. DGM News
https://doi.org/10.3139/146.110567
Schlagwörter für diesen Artikel
Recrystallization; Particle-stimulated nucleation; Recovery; Precipitation

Artikel in diesem Heft

  1. Contents
  2. Contents
  3. Editorial
  4. Prof. Dr.-Ing. Heinrich Wollenberger — 80 years
  5. Original Contributions
  6. Atom probe tomography: from physical metallurgy towards microelectronics
  7. Accumulation of radiation damage and disordering in MgAl2O4 under swift heavy ion irradiation
  8. TEM study of irradiation induced copper precipitation in boron alloyed EUROFER97 steel
  9. Order – disorder transformation in Ni – V alloys under electron irradiation
  10. Materials issues of the SINQ high-power spallation target
  11. The origin and development of the P{011}<111> orientation during recrystallization of particle-containing alloys
  12. Coarsening kinetics of Cu-rich precipitates in a concentrated multicomponent Fe–Cu based steel
  13. Beyond Ni-based superalloys: Development of CoRe-based alloys for gas turbine applications at very high temperatures
  14. The effect of heat treatments on the microstructure, texture and mechanical properties of the extruded magnesium alloy ME21
  15. Analysing SANS data to determine magnetisation reversal processes in composite perpendicular magnetic recording media using TEM images
  16. Dislocationless sliding in a polycluster glass
  17. Evolution of transformation plasticity during bainitic transformation
  18. Surface tension and viscosity of NiAl catalytic precursor alloys from microgravity experiments
  19. Synthesis of carbon nanotubes by fine Ni particles in Ni3Al foam
  20. Fabrication of dielectric thin films by sputtering deposition at different pressures with (Ba0.3Sr0.7)(Zn1/3Nb2/3)O3 ceramic as target
  21. DGM News
  22. DGM News
Jetzt anmelden und 20% sparen
Institutioneller Zugang
Wie funktioniert Authentifizierung?
Haben Sie eine Idee, wie wir unsere Website verbessern können?
Bitte schreiben Sie uns.
© 2026 De Gruyter Brill
Heruntergeladen am 17.1.2026 von https://www.degruyterbrill.com/document/doi/10.3139/146.110567/html
Button zum nach oben scrollen