Band 7, Heft 1

The most important classical orange organic pigments are disazopyrazolones, also referred to as diarylide oranges. The first pigment in this series, CI Pigment Orange 13, was discovered in 1910 although it was a further 20 years before it was introduced as a commercial product. Currently, two orange disazopyrazolones are extremely important industrial organic pigments, while two red products are of lesser importance. The products are structurally analogous to the disazoacetoacetanilides (diarylide yellows), which are discussed in a separate chapter. For example, they are symmetrical compounds that exist in the bis-ketohydrazone tautomeric form. The pigments also exhibit similar technical and color properties compared with disazoacetoacetanilide pigments, for example providing high color strength and transparency, features that determine their importance as printing ink pigments. They are manufactured in a process that parallels those used for the disazoacetoacetanilide (diarylide) yellows, but with coupling components containing the pyrazolone heterocyclic system, in place of acetoacetanilides.

Mixed metal oxide (MMO) pigments, also knowns as complex inorganic color pigments (CICPs), are an important class of inorganic pigments. They are representatives of the blue, green, yellow, brown, and black pigments. These pigments are called mixed complex because they contain two or more different metals in the composition. Their main advantages are high opacity, heat stability, useful infrared properties, light- and weather fastness, and chemical resistance. MMOs are solid solutions of metal oxides, which are homogenously distributed in their crystal lattices. They are based on different types of crystal structures, such as rutile, spinel, inverse spinel, hematite, priderite, and pseudobrookite. Other products belonging to the CICPs besides the rutile and spinel type MMOs are pigments based on zirconium silicate (zircon, ZrSiO 4 ). Such compositions belong to the class of ceramic pigments (color stains for glazes).

A series of azo pigments containing the benzimidazolone ring were introduced in the mid to late twentieth century as high-performance organic pigments in the yellow, orange, red, and brown shade areas. The structures of the commercial benzimidazolone azo pigments are derived from either the monoazoacetoacetanilide or monoazonaphtharylamide classical azo pigments systems and exist in the ketohydrazone tautomeric forms. The high-performance properties of the pigments have been attributed to a network of intermolecular hydrogen bonds involving the benzimidazolone group, and efficient molecular packing, as demonstrated by X-ray crystal structure determinations. The manufacturing processes leading to the pigments involve traditional diazotization and azo coupling reaction procedures, although they require special conditioning aftertreatments to optimize their performance. Although benzimidazolone azo pigments were initially developed for the coloration of plastics, they have probably had a greater impact on the paint industry. The application properties of the benzimidazolone azo pigments are discussed for individual products.

Chromate and molybdate pigments are representatives of the inorganic yellow, orange and red pigments. They are characterized by excellent optical and application properties in particular regarding brightness of shade, hiding power, tinting strength, and weather fastness. The declining use of lead- and chromate-containing materials in the last decades is a result of the environmental discussion and the development of less problematic substitute products, especially of bismuth vanadate and high-value organic, temperature-stable yellow and red pigments.

Oxonol dyes are classified as anionic polymethine dyes, which cover a wide variety of structural types. The name of the class originates from the oxygen atoms which terminate each end of the polymethine chains that form the backbone of their structure. In technically useful dyes, these oxygen atoms tend to be substituents of heterocycles. The main technical application of water soluble oxonol dyes was in silver halide photography as filter dyes and antihalation dyes. Lipophilic oxonol dyes are used in bio-analysis and medical diagnostics to stain cells, bacteria or liposomes for example. Their main bioanalytical usage is in the determination of membrane potentials in eukaryotic cells and prokaryotic bacteria.

Cerium sulfide pigments belong to the inorganic orange and red pigments. They were developed to substitute cadmium and lead containing red and orange colored pigments, in particular in plastics. Cerium(III) sulfide exists in three allotropic modifications, but only γ-Ce 2 S 3 , which is colored dark red, is suitable for the use as a pigment. Cerium sulfide pigments are characterized by high color strength, strong hiding power and sufficient thermal stability. Their limited stability in water containing systems and in humid atmospheres is not without problems. The pigments tend to degradation in the presence of water or humidity to form hydrogen sulfide, which limits the application possibilities significantly.