Fractures in High-Strength Bolts due to Hydrogen Induced Stress Corrosion – Causes and Corrective Actions
-
H. Hoche
Abstract
Delayed brittle fractures of high-strength bolts of the strength class 10.9 are presented, taking the example of three damage cases. The respective damage mechanisms could be attributed to hydrogen induced stress corrosion which was caused, in turn, by hydrogen absorption during operation. The examples were chosen with a particular focus on the material condition‘s susceptibility which explains the cause for the occurrence of the damage mechanism. However, in only one of the three cases the susceptibility was evident and could be explained by violations of normative specifications and an unfavorable material choice. Whereas in the two other examples, only slight or no deviations from the standards and/or regulations could be found.
The influencing parameters that caused the damage, those that further promoted the damage, as well as possible corrective actions are discussed taking into account the three exemplary damage cases.
Kurzfassung
Anhand von drei Schadensbeispielen werden zeitverzögerte Sprödbrüche hochfester Schrauben der Festigkeitsklasse 10.9 vorgestellt, deren Mechanismus auf wasserstoffinduzierte Spannungsrisskorrosion durch den im Betrieb aufgenommenen Wasserstoff zurückgeführt werden konnte. Die Auswahl der Beispiele zielt insbesondere auf die Anfälligkeit des Werkstoffzustands ab, der die Ursache für das Auftreten des Schadensmechanismus begründet. Dabei ist nur in einem der drei Fälle die Anfälligkeit aufgrund sehr grober Verletzungen normativer Vorgaben und der Auswahl eines ungünstigen Werkstoffs offensichtlich. In den beiden weiteren Beispielen konnten hingegen nur geringfügige bzw. gar keine Abweichungen der Normen bzw. Richtlinien festgestellt werden.
Abschließend werden unter Berücksichtigung der drei Schadensbeispiele die schadensursächlichen und schadensbegünstigenden Einflussfaktoren sowie mögliche Abhilfemaßnahmen diskutiert.
References / Literatur
[1] Nagumo, M.; Nakamura, M; Takai, K.: Metall and Mat Trans A, 32, 2001, 33910.1007/s11661-001-0265-9Suche in Google Scholar
[2] Landgrebe, R.: Wasserstoffinduzierte Sprödbruchbildung bei hochfesten Schrauben aus Vergütungsstählen, Dissertation, Technische Universität Darmstadt, Darmstadt, 1993.Suche in Google Scholar
[3] DIN EN 14399-4: 2006: Hochfeste planmäßig vorspannbare Schraubenverbindungen für den Metallbau, System HV, Beuth-VerlagBerlin2006Suche in Google Scholar
[4] Richtlinie für die Herstellung feuerverzinkter Schrauben, Herausgegeben vom Deutschen Schraubenverband e.V. (DSV) und dem Gemeinschaftsausschuss Verzinken e.V. (GAV), 2009Suche in Google Scholar
[5] DIN 50969-2:2013: Vermeidung fertigungsbedingter wasserstoffinduzierter Sprödbruche bei hochfesten Bauteilen aus Stahl–Teil 2: Prüfungen, Beuth-VerlagBerlin, 2013Suche in Google Scholar
[6] DIN EN ISO 898-1:2011: Mechanische Eigenschaften von Verbindungselementen aus Kohlenstoffstahl und legiertem Stahl–Teil 1: Schrauben mit festgelegten Festigkeitsklassen, Beuth-VerlagBerllin, 2011Suche in Google Scholar
[7] Rajagopalan, M.; Tschopp, M. A.; Solanki, K. N.: The Minerals, Metals & Materials Society JOM, 66, 2014, 12910.1007/s11837-013-0807-9Suche in Google Scholar
[8] DIN EN 26157-3: 1991: Verbindungselemente, Oberflächenfehler, Schrauben für spezielle Anforderungen, Beuth-VerlagBerlin2001Suche in Google Scholar
[9] Kloos, K. H., Schneider, W.: Matwiss. & Werkstofftech.21, 1990, 29510.1002/mawe.19900210805Suche in Google Scholar
[10] U.Hasselmann, Flüssigmetallinduzierte Rissbildung bei der Feuerverzinkung hochfester HV-Schrauben großer Abmessungen infolge thermisch bedingter Zugeigenspannungen, Dissertation am Institut für Werkstofftechnik der TU-Darmstadt, 199710.1002/mawe.19970281210Suche in Google Scholar
[11] Riecke, E.; Liesegang, H.; Grabke, H. J.: Werkstoffe und Korrosion, 38, 198731010.1002/maco.19870380603Suche in Google Scholar
[12] Zikeer, V. N.; Golovanenko, S. A.: Industrial Heating, 10, 1991, 15Suche in Google Scholar
[13] Riecke, E.; Johnen, B.; Liesegang, H.; Thoms, A.; Reynders, B.; Grabke, H. J.: Werkstoffe und Korrosion, 39, 1988, 52510.1002/maco.19880391108Suche in Google Scholar
[14] Riecke, E.; Möller, R.; Johnen, B.; Grabke, H. J.: Werkstoffe und Korrosion, 36, 1985 Teil I: 435, Teil I: 447, Teil III: 45510.1002/maco.19850361004Suche in Google Scholar
[15] Yoshino, Y.: Corrosion, 39, 1983, 43510.5006/1.3581904Suche in Google Scholar
[16] Riecke, E.; Johnen, B.: Werkstoffe und Korrosion, 4, 1991, 62610.1002/maco.19910421204Suche in Google Scholar
[17] Kim, J. S.; Lee, Y. H.; Lee, D. L.; Park, K.-T.; Lee, C. S.: Materials Science and Engineering A, 505, 2009, 10510.1016/j.msea.2008.11.040Suche in Google Scholar
[18] Nagao, A.; Martin, M. L.; Dadfarnia, M.; Sofronis, P.; Robertson, I.: Acta Materialia74, 2014, 22410.1016/j.actamat.2014.04.051Suche in Google Scholar
[19] McMahon, C.J.: Engineering Fracture Mechanics, 68, 2001, 77310.1016/S0013-7944(00)00124-7Suche in Google Scholar
© 2017, Carl Hanser Verlag, München
Artikel in diesem Heft
- Contents/Inhalt
- Contents
- Editorial
- Editorial
- Technical Contributions/Fachbeiträge
- Stress Corrosion Cracking on a Stainless Steel Container Triggered by the Ageing of a Polyurethane Insulation
- A Comparative Study on the Microstructure Evaluation of Thixoforged A356 and A380 Aluminium Alloys
- Fractures in High-Strength Bolts due to Hydrogen Induced Stress Corrosion – Causes and Corrective Actions
- Meeting Diary/Veranstaltungskalender
- Meeting Diary
Artikel in diesem Heft
- Contents/Inhalt
- Contents
- Editorial
- Editorial
- Technical Contributions/Fachbeiträge
- Stress Corrosion Cracking on a Stainless Steel Container Triggered by the Ageing of a Polyurethane Insulation
- A Comparative Study on the Microstructure Evaluation of Thixoforged A356 and A380 Aluminium Alloys
- Fractures in High-Strength Bolts due to Hydrogen Induced Stress Corrosion – Causes and Corrective Actions
- Meeting Diary/Veranstaltungskalender
- Meeting Diary