Stress Corrosion Cracking on a Stainless Steel Container Triggered by the Ageing of a Polyurethane Insulation
-
S. Strobl
Abstract
A failure in the form of leakages caused by crack formation occurred after approximately 25 years of operationn on a type 1.4301 stainless steel container thermally insulated with polyurethane. From the appearance of the damages it was clear that the failure was caused by stress corrosion cracking. It was shown that chloride release by the ageing of the PU foam was responsible for the corrosion. The damages were documented via 3D digital microscopy and metallography. To avoid these kinds of damages, insulation materials free of halogen compounds should be used. Regular checks of old stainless steel reactors insulated with PU foam and operated at elevated temperatures are recommended.
Kurzfassung
An einem mit Polyurethan thermisch isolierten Behälter aus rostfreiem Stahl der Qualität 1.4301 trat nach etwa 25 Betriebsjahren ein Schadensfall in der Form von Leckagen durch Rissbildung auf. Das Erscheinungsbild der Schäden ließ klar auf Spannungsrisskorrosion schließen. Es wurde gezeigt, dass durch die Alterung des PU-Schaums freigesetztes Chlorid für die Korrosion verantwortlich war. Die aufgetretenen Schäden wurden zuerst mit 3D-Digitalmikroskopie und danach mittels Metallographie dokumentiert. Zur Vermeidung derartiger Schadensfälle sollten halogenfreie Isoliermaterialien eingesetzt werden. Regelmäßige Kontrollen an alten, mit PU-Schaum isolierten und bei erhöhten Temperaturen betriebenen Reaktoren aus nichtrostendem Stahl wären anzuraten.
References / Literatur
[1] Vander Voort, G. F.: Metallography. ASM International, 3rd printing, 2004.10.31399/asm.hb.v09.a0003752Search in Google Scholar
[2] DIN EN 10088–1: Nichtrostende Stähle–Teil 1: Verzeichnis der nichtrostenden Stähle, Ausgabedatum: Dezember 2014.Search in Google Scholar
[3] Wendler-Kalsch, E.; Gräfen, H.: Korrosionsschadenkunde, Springer Verlag, 1998. 10.1007/978-3-642-30431-6Search in Google Scholar
[4] Haumann, T.: Versteckte Schadstoffe im Baualltag–Bau- und Montageschäume, Vortrag beim 3. Deutsches Forum Innenraumhygiene, 15. + 16.02.2011, Essen (D).Search in Google Scholar
[5] https://de.wikipedia.org/wiki/Polyurethane(17.5.2016)Search in Google Scholar
© 2017, Carl Hanser Verlag, München
Articles in the same Issue
- Contents/Inhalt
- Contents
- Editorial
- Editorial
- Technical Contributions/Fachbeiträge
- Stress Corrosion Cracking on a Stainless Steel Container Triggered by the Ageing of a Polyurethane Insulation
- A Comparative Study on the Microstructure Evaluation of Thixoforged A356 and A380 Aluminium Alloys
- Fractures in High-Strength Bolts due to Hydrogen Induced Stress Corrosion – Causes and Corrective Actions
- Meeting Diary/Veranstaltungskalender
- Meeting Diary
Articles in the same Issue
- Contents/Inhalt
- Contents
- Editorial
- Editorial
- Technical Contributions/Fachbeiträge
- Stress Corrosion Cracking on a Stainless Steel Container Triggered by the Ageing of a Polyurethane Insulation
- A Comparative Study on the Microstructure Evaluation of Thixoforged A356 and A380 Aluminium Alloys
- Fractures in High-Strength Bolts due to Hydrogen Induced Stress Corrosion – Causes and Corrective Actions
- Meeting Diary/Veranstaltungskalender
- Meeting Diary