Practical Test on Brass Valves Using the 5% Ammonia Test to Elucidate the Reasons of Specific Failure Patterns of Stress Corrosion Cracking SCC
-
K. Kerschbaumer
Published/Copyright:
May 23, 2013
Received: 2011-3-28
Accepted: 2011-8-12
Published Online: 2013-05-23
Published in Print: 2012-04-01
© 2012, Carl Hanser Verlag, München
You are currently not able to access this content.
You are currently not able to access this content.
Articles in the same Issue
- Contents/Inhalt
- Contents
- Editorial
- Editorial
- Technical Contributions/Fachbeiträge
- Determining the Uncertainty in Measuring Length in Light and Scanning-Electron Microscopy
- Examination of the Mg-Zn Phase Formation in Hot-Dip Galvanized Steel Sheet
- An Investigation into Porosity in Medical Drills Caused by Broken Carbides
- Practical Test on Brass Valves Using the 5% Ammonia Test to Elucidate the Reasons of Specific Failure Patterns of Stress Corrosion Cracking SCC
- Meeting Diary/Veranstaltungskalender
- Meeting Diary
Articles in the same Issue
- Contents/Inhalt
- Contents
- Editorial
- Editorial
- Technical Contributions/Fachbeiträge
- Determining the Uncertainty in Measuring Length in Light and Scanning-Electron Microscopy
- Examination of the Mg-Zn Phase Formation in Hot-Dip Galvanized Steel Sheet
- An Investigation into Porosity in Medical Drills Caused by Broken Carbides
- Practical Test on Brass Valves Using the 5% Ammonia Test to Elucidate the Reasons of Specific Failure Patterns of Stress Corrosion Cracking SCC
- Meeting Diary/Veranstaltungskalender
- Meeting Diary