A study of the Si-phase growth mechanismin thixocast (A356) alloy during hot deformation

  • M. Haghshenas , A. Zarei-Hanzaki und S. M. Fatemi-Varzaneh
Veröffentlicht/Copyright: 1. März 2013
Veröffentlichen auch Sie bei De Gruyter Brill

Abstract

The microstructure in modified semi-solid thixocast (A356) alloy consists of an α-Al phase with an Al/Si eutectic structure. The silicon phase in the eutectic structure is coral-like with fine fibers. The lack of good ductility in this alloy is related to the presence of silicon fibers. Accordingly, many investigations have been recently conducted to modify the Si morphology through thermomechanical processing on this alloy. In the present work, a thixocast (A356) alloy was deformed at 450 °C, 500 °C and 540 °C through different strain rates. Consequently the silicon fibers were broken into small particles. The results indicated that the Si particles might coarsen at 540 °C when deformed by rates of 0.0005 s−1 and 0.0001 s−1.


2 Correspondence address: Meysam Haghshenas, Master of Science, School of Metallurgy and Materials Science Engineering, University of Tehran, P. O. Box 11365-4563, North Karegar, Tehran, Iran, Tel.: +98 21 6111 4167, Fax: +98 21 8800 6076. E-mail: (Preferred E-mail)

References

[1] M.Lebyodkin, A.Deschamps, Y.Brechet: Mater. Sci. Eng. A234(1997)481484.10.1016/S0921-5093(97)00314-6Suche in Google Scholar

[2] M.Tiryakioglu: Mater. Sci. Eng. A(2007), in press, doi: 10.1016/j.msea.2007.03.044.Suche in Google Scholar

[3] E.Ogrish, A.Wahlen, H.Luchinger, P.J.Uggowitzer: Journal of Light Metals2(2002)263269.10.1016/S1471-5317(03)00010-5Suche in Google Scholar

[4] R.N.Stevens, C.K.L.Davies: Scripta Mater.46(2002)1923.10.1016/S1359-6462(01)01189-7Suche in Google Scholar

[5] G.Madras, B.J.McCoy: Chemical Engineering Science58(2003)29032909.10.1016/S0009-2509(03)00156-8Suche in Google Scholar

[6] E.Ogrish, H.Luchinger, P.J.Uggowitzer: Mater. Sci. Forum396–402(2002)149154.10.4028/www.scientific.net/MSF.396-402.149Suche in Google Scholar

[7] A.Claveria, B.Colombeau, F.Cristiano, A.Altibelli, C.Bonafos: NIM B B186(2002)281286.10.1016/S0168-583X(01)00914-4Suche in Google Scholar

[8] D.J.Lloyd: Acta Metall. Mater.39(1991)5971.10.1016/0956-7151(91)90328-XSuche in Google Scholar

[9] P.W.Voorhees: J. Stat. Phys.38(1985)231.10.1007/BF01017860Suche in Google Scholar

[10] A.J.Ardell, in: G.W.Lorimer (Ed.), Phase Transformations'87, 1988, p. 485.Suche in Google Scholar

[11] C.W.Meyers: AFS Trans.93(1985)641.10.1016/0040-6031(85)85161-3Suche in Google Scholar

[12] S.Shivkumar, S.Ricci, B.Steenhoff, D.Apelian, G.Sigworth: AFS Trans.97(1989)791.Suche in Google Scholar

[13] P.A.Rometsch, G.B.Schaffer, J.A.Taylor: Int. J. Cast Met. Res.14(2001)59.10.1080/13640461.2001.11819426Suche in Google Scholar

Received: 2007-01-20
Accepted: 2007-11-08
Published Online: 2013-03-01
Published in Print: 2008-02-01

© 2008, Carl Hanser Verlag, Munich

Heruntergeladen am 24.12.2025 von https://www.degruyterbrill.com/document/doi/10.3139/146.101617/html?lang=de
Button zum nach oben scrollen