Non-destructive determination of local damage and material condition in high-performance components
-
Abstract
In modern aircraft engines, a high number of complex high-performance components are employed, which are partly subjected to extreme loading. For instance, the high-pressure turbine blades of the first stage after the combustor are both thermally-mechanically loaded and experience severe corrosive attack. Therefore they are furnished with several protective systems in order to improve the fatigue life and reliability of the high-temperature material blades employed. A ceramic thermal barrier coating insulates the internally and film-cooled blades against the hot gas stream whilst the underlying layer (PtAl, Al, MCrAlY) protects the substrate material against corrosive attack and oxidation. Owing to the low electrical conductivity of the materials employed in the multilayered system of the high-pressure turbine blades with layer thicknesses of 20–150 μm, conventional eddy-current and thermographic technologies are only suitable to a limited extent to non-destructively detect the condition of the individual layers separately from the substrate material. In contrast to this, with the aid of multi-parameter, high-frequency eddy-current technologies and high-frequency induction thermography using pulsed excitation, the eddy-currents with test frequencies in the mega-Hertz range (up to 100 MHz) can be limited to the near subsurface and produce standard penetration depths of <50 μm; which enables the layer and substrate materials to be differentially studied. The objective of the present study was to non-destructively detect the condition of the coatings, to characterise and determine the thickness of the coating as well as to detect the condition of the substrate material and sensitively analyse local damage and defects.
Kurzfassung
In modernen Flugtriebwerken kommen eine Vielzahl komplexer Hochleistungsbauteile zum Einsatz, die teils extremen Belastungen ausgesetzt sind. Die Hochdruckturbinenschaufeln der ersten Stufe nach der Brennkammer sind sowohl thermisch und mechanisch als auch korrosiv hoch belastet und daher mit mehreren Schutzsystemen ausgestattet, um die Lebensdauer und Zuverlässigkeit der eingesetzten Beschaufelung aus Hochtemperaturwerkstoffen zu verbessern. Eine keramische Wärmedämmschicht isoliert die innen- und filmgekühlten Schaufeln zusätzlich gegenüber der Heißgasströmung, während die darunterliegende Heißgaskorrosionsschutzschicht (PtAl, Al, MCrAlY) den Grundwerkstoff vor korrosiven Angriffen und Oxidation schützt. Um den Zustand der einzelnen Beschichtungen im Mehrschichtsystem der Hochdruckturbinenschaufel mit Schichtdicken von 20–150 μm zerstörungsfrei und getrennt vom Grundwerkstoff zu erfassen, sind aufgrund der geringen elektrischen Leitfähigkeit der verwendeten Werkstoffe konventionelle Wirbelstrom- und Thermografietechniken nur bedingt geeignet. Mithilfe der Mehrparameter-Hochfrequenz-Wirbelstromtechnik und der Hochfrequenz-Induktionsthermografie mit gepulster Anregung lassen sich hingegen die Wirbelströme bei Prüffrequenzen im Megahertzbereich bis 100 MHz auf die oberflächennahe Randzone begrenzen und Standardeindringtiefen von <50 μm realisieren, was eine differenzierte Betrachtung von Schicht- und Grundwerkstoff ermöglicht. Ziel der Untersuchungen ist die zerstörungsfreie Zustandserfassung der Beschichtungen, die Schichtcharakterisierung und die Schichtdickenbestimmung sowie die Zustandserfassung des Grundwerkstoffs und der empfindliche Nachweis lokaler Schädigungen und Defekte.
References
1. Bräunling, W.: Flugzeugtriebwerke. 3. ed., Springer, Berlin, 200910.1007/978-3-540-76370-3Suche in Google Scholar
2. Cosack, T.: Schutzschichten auf Turbinenschaufeln im Flugtriebwerk. Publication, MTU Aero Engines, Munich, 2009Suche in Google Scholar
3. Lechner, C.; Seume, J.: Stationäre Gasturbinen. 2. ed., Springer, Berlin, 201010.1007/978-3-540-92788-4Suche in Google Scholar
4. Olfe, J.; Reimche, W.; Bach, Fr.-W.: Balance Strip: An Effective Method for Stripping Aluminide Coatings. Lecture held on: Turbine Forum, Effective Repair of Gas Turbine Components, 9–11.04.03, Nice/France; Forum of Technology, Dorsten/Germany, 2003Suche in Google Scholar
5. Scheer, C.; Reimche, W.; Möhwald, K.; Bach, Fr.-W.: Entwicklung einer Online-Schichtdickenmessung für das Plasmaspritzen von Keramik auf Basis einer Wirbelstromsensorik. Schweissen und Schneiden60 (2008) 6, p. 331–336Suche in Google Scholar
6. Reimche, W.; Duhm, R.: Nondestructive testing and assessment of coatings. In: Bach, Fr.-W.; Möhwald, K.; Laarmann, A.; Wenz, T. (Ed.): Modern Surface Technology, Wiley-VCH, Weinheim, 2006Suche in Google Scholar
7. Reimche, W.; Bernard, M.; Bombosch, S.; Scheer, Ch.; Bach, Fr.-W.: Nachweis von Anrissen in der Randzone von Hochleistungsbauteilen mit Wirbelstromtechnik und induktiv angeregter Thermographie. HTM J. Heat Treatm. Mat.63 (2008) 5, p. 284–297Suche in Google Scholar
8. Mooshofer, H.; Goldammer, M.; Rothenfusser, M.; Bass, J.; Lombardo, E.; Vrana, J.: Induktionsthermografie zur automatischen Prüfung von Generatorkomponenten. DGZfP-Jahrestagung2009, DGZfP-Berichtsband BB 115, Mi.2.C.2, on CDSuche in Google Scholar
9. Vrana, J.: Grundlagen und Anwendungen der aktiven Thermographie mit elektromagnetischer Anregung: Induktions- und Konduktionsthermographie. PhD thesis, Universität des Saarlandes, Saarbrücken, 2008Suche in Google Scholar
© 2013, Carl Hanser Verlag, München
Artikel in diesem Heft
- Veranstaltungen/Events
- Veranstaltungen in Zusammenarbeit mit der AWT
- HTM-Praxis
- HTM-Praxis
- Kurzfassungen/Abstracts
- Kurzfassungen
- Inhalt/Contents
- Inhalt
- Fachbeiträge/Technical Contributions
- Non-destructive determination of local damage and material condition in high-performance components
- Sensor für die Regelung der Kohlenstoffübertragung bei der Niederdruckaufkohlung∗
- Influence of short-cycle heat treatment conditions on the hardness-toughness-relationship of the steels 51CrV4, 74NiCr2 mod. and 100Cr6∗
- Nitrieren und Nitrocarburieren∗
- Distortion of steel flat ring products during the production cycle∗
- Perspektiven der Heißzerspanung aus der Schmiedewärme
Artikel in diesem Heft
- Veranstaltungen/Events
- Veranstaltungen in Zusammenarbeit mit der AWT
- HTM-Praxis
- HTM-Praxis
- Kurzfassungen/Abstracts
- Kurzfassungen
- Inhalt/Contents
- Inhalt
- Fachbeiträge/Technical Contributions
- Non-destructive determination of local damage and material condition in high-performance components
- Sensor für die Regelung der Kohlenstoffübertragung bei der Niederdruckaufkohlung∗
- Influence of short-cycle heat treatment conditions on the hardness-toughness-relationship of the steels 51CrV4, 74NiCr2 mod. and 100Cr6∗
- Nitrieren und Nitrocarburieren∗
- Distortion of steel flat ring products during the production cycle∗
- Perspektiven der Heißzerspanung aus der Schmiedewärme