Homogenization effect on precipitation kinetics and mechanical properties of an extruded AA7050 alloy

Ş. Hakan Atapek; İrfan Eker; Fulya Kahrıman; Şeyda Polat

doi:10.1515/mt-2022-0190

Article

Homogenization effect on precipitation kinetics and mechanical properties of an extruded AA7050 alloy

Ş. Hakan Atapek , İrfan Eker , Fulya Kahrıman and Şeyda Polat

Published/Copyright: October 7, 2022

Published by

Become an author with De Gruyter Brill

Submit Manuscript Author Information

From the journal Materials Testing Volume 64 Issue 10

Abstract

In this study, effect of homogenization on precipitation kinetics and mechanical properties during aging in AA7050 alloy was investigated. The billet material produced by direct chill method was homogenized at 470 °C for 12–20 h and then extruded to form T-profile. The electrical conductivity of the alloy aged at 120 and 185 °C for 0–36 h were measured and precipitation kinetics were calculated based on the relationship between increased electrical conductivity and amount of precipitates during aging. Time dependent precipitation fraction change curves using Avrami equations revealed that precipitation accelerated as the homogenization time increased due to increased nucleation and growth rates of precipitates. Peak hardness values in aging were reached depending on the increase in homogenization time, however, lower peak hardness (∼185 HV) was determined at 185 °C aging compared to the obtained ones (195–197 HV) at 120 °C aging. Depending on the increase in homogenization time, an increase trend in strength was detected in peak aged alloys. The application of longer time homogenization and subsequent aging caused an increase in strengths. The studied homogenization and aging conditions could be a useful guide for achieving the highest strength and ideal elongation values in commercial practice for the AA7050 alloy.

Keywords: AA7050 alloy; homogenization; kinetics; precipitation; strength

Corresponding author: Ş. Hakan Atapek, Department of Metallurgical and Materials Engineering, Kocaeli University, Umuttepe Campus, 41001, Kocaeli, Turkey, E-mail: hatapek@kocaeli.edu.tr

The author contributions: All the authors have accepted responsibility for the entire content of this submitted manuscript and approved submission.
Research funding: None declared.
Conflict of interest statement: The authors declare no conflicts of interest regarding this article.

References

[1] S. K. Das and W. Yin, “The worldwide aluminium economy: the current state of the industry,” J. Met., vol. 59, no. 11, pp. 57–63, 2007, https://doi.org/10.1007/s11837-007-0142-0.Search in Google Scholar

[2] E. A. StarkeJr. and J. T. Staley, “Application of modern aluminum alloys to aircraft,” Prog. Aerosp. Sci., 32, nos. 2–3, pp. 131–172, 1996, https://doi.org/10.1016/0376-0421(95)00004-6.Search in Google Scholar

[3] A. E. A. Chemin, C. M. Afonso, F. A. Pascoal, C. I. dos Santos Maciel, C. O. F. T. Ruchert, and W. W. B. Filho, “Characterization of phases, tensile properties, and fracture toughness in aircraft-grade aluminum alloy,” Mat. Des Pro. Commun., vol. 1, no. e79, pp. 1–13, 2019, https://doi.org/10.1002/mdp2.79.Search in Google Scholar

[4] H. B. Younis, K. Kamal, M. F. Sheikh, and A. Hamza, “Prediction of fatigue crack growth rate in aircraft aluminum alloys using optimized neural networks,” Theor. Appl. Fract. Mech., vol. 117, 2022, Art no. 103196, https://doi.org/10.1016/j.tafmec.2021.103196.Search in Google Scholar

[5] M. O. Speidel, “Stress corrosion cracking of aluminum alloys,” Metall. Trans. A., vol. 6, pp. 631–651, 1975, https://doi.org/10.1007/BF02672284.Search in Google Scholar

[6] R. G. Guan and D. Tie, “A review on grain refinement of aluminum alloys: progresses, challenges and prospects,” Acta Metall. Sin., vol. 30, no. 5, pp. 409–432, 2017, https://doi.org/10.1007/s40195-017-0565-8.Search in Google Scholar

[7] M. Tajally, Z. Huda, and H. H. Masjuki, “Effect of deformation and recrystallization conditions on tensile behavior of aluminum alloy 7075,” Met. Sci. Heat Treat., vol. 53, nos. 3–4, pp. 165–168, 2011, https://doi.org/10.1007/s11041-011-9361-7.Search in Google Scholar

[8] D. Xu, K. Chen, Y. Chen, and S. Chen, “Evolution of the second-phase particles and their effect on tensile fracture behavior of 2219 Al-xCu alloys,” Metals, vol. 10, no.2, pp. 197, 2020, https://doi.org/10.3390/met10020197.Search in Google Scholar

[9] M. Dixit, R. S. Mishra, and K. K. Sankaran, “Structure–property correlations in Al 7050 and Al 7055 high-strength aluminum alloys,” Mater. Sci. Eng., A, vol. 478, nos. 1–2, pp. 163–172, 2008, https://doi.org/10.1016/j.msea.2007.05.116.Search in Google Scholar

[10] A. Gloria, R. Montanari, M. Richetta, and A. Varone, “Alloys for aeronautic applications: state of the art and perspectives,” Metals, vol. 9, no. 6, p. 662, 2019, https://doi.org/10.3390/met9060662.Search in Google Scholar

[11] A. Karaaslan, I. Kaya, and H. Atapek, “Tensile strength and impact toughness of an AA7075 T6 alloy,” Mater. Test., vol. 50, no. 5, pp. 256–258, 2008, https://doi.org/10.3139/120.100882.Search in Google Scholar

[12] T. Sonar, V. Balasubramanian, and S. Malarvizhi, “Mitigation of heat treatment distortion of AA 7075 aluminum alloy by deep cryogenic processing using the Navy C-ring test,” Mater. Test., vol. 63, no. 8, pp. 758–763, 2021, https://doi.org/10.1515/mt-2020-0121.Search in Google Scholar

[13] K. R. Cardoso, D. N. Travessa, A. G. Escorial, and M. Lieblich, “Effect of mechanical alloying and Ti addition on solution and ageing treatment of an AA7050 aluminium alloy,” Mater. Res., vol. 10, no. 2, pp. 199–203, 2007, https://doi.org/10.1590/S1516-14392007000200017.Search in Google Scholar

[14] W. Li, Y. Liu, S. Jiang et al.., “A study of thermomechanical behaviour and grain size evolution of AA7050 under hot forging conditions,” Int. J. Lightweight Mater. Manuf., vol. 2, no. 1, pp. 31–39, 2019, https://doi.org/10.1016/j.ijlmm.2018.10.002.Search in Google Scholar

[15] K. Kang, D. Li, A. Wang, D. Shi, G. Gao, and Z. Xu, “Experimental investigation on aging treatment of 7050 alloy assisted by electric pulse,” Results Phys., vol. 16, 2020, Art no. 103016, https://doi.org/10.1016/j.rinp.2020.103016.Search in Google Scholar

[16] J. P. Li, J. Shen, X. D. Yan, B. P. Mao, and L. M. Yan, “Microstructure evolution of 7050 aluminum alloy during hot deformation,” Trans. Nonferrous Metals Soc. China, vol. 20, no. 2, pp. 189–194, 2010, https://doi.org/10.1016/S1003-6326(09)60119-9.Search in Google Scholar

[17] F. G. Cong, G. Zhao, F. Jiang, N. Tian, and R. F. Li, “Effect of homogenization treatment on microstructure and mechanical properties of DC cast 7X50 aluminum alloy,” Trans. Nonferrous Metals Soc. China, vol. 25, no. 4, pp. 1027–1034, 2015, https://doi.org/10.1016/S1003-6326(15)63694-9.Search in Google Scholar

[18] P. Jia, Y. Cao, Y. Geng, L. He, N. Xiao, and J. Cui, “Studies on the microstructures and properties in phase transformation of homogenized 7050 alloy,” Mater. Sci. Eng., A, vol. 612, pp. 335–342, 2014, https://doi.org/10.1016/j.msea.2014.06.027.Search in Google Scholar

[19] X. Fan, D. Jiang, Q. Meng, and L. Zhong, “The microstructural evolution of an Al-Zn-Mg-Cu alloy during homogenization,” Mater. Lett., vol. 60, no. 12, pp. 1475–1479, 2006, https://doi.org/10.1016/j.matlet.2005.11.049.Search in Google Scholar

[20] Z. Cao, Y. Feng, T. Li, and J. Wang, “Variation of the microstructure of ingots of DC cast alloy 7050 during homogenization,” Met. Sci. Heat Treat., vol. 52, nos. 3–4, pp. 179–182, 2010, https://doi.org/10.1007/s11041-010-9251-4.Search in Google Scholar

[21] J. T. Staley, “Aging kinetics of aluminum alloy 7050,” Metall. Mater. Trans. B, vol. 5, pp. 929–932, 1974, https://doi.org/10.1007/BF02643150.Search in Google Scholar

[22] Ş. H. Atapek, “Effect of cobalt on the aging kinetics and the properties of a CuCoNiBe alloy,” Mater. Test., vol. 57, no. 1, pp. 17–21, 2015, https://doi.org/10.3139/120.110669.Search in Google Scholar

[23] F. Kahrıman and M. Zeren, “The effect of Zr on aging kinetics and properties of as-cast AA6082 alloy,” Int. J. Metalcast., vol. 11, no. 2, pp. 216–222, 2017, https://doi.org/10.1007/s40962-016-0047-1.Search in Google Scholar

[24] A. Staszczyk, J. Sawicki, and B. Adamczyk-Cieslak, “A study of second-phase precipitates and dispersoid particles in 2024 aluminum alloy after different aging treatments,” Materials, vol. 12, no. 4168, pp. 1–10, 2019, https://doi.org/10.3390/ma12244168.Search in Google Scholar PubMed PubMed Central

Published Online: 2022-10-07

Published in Print: 2022-10-26

You are currently not able to access this content.

Articles in the same Issue

https://doi.org/10.1515/mt-2022-0190

Keywords for this article

AA7050 alloy; homogenization; kinetics; precipitation; strength