Phase relationships in the Fe-rich region of the Ce–Nd–B–Fe quaternary system at 773 K

Ketong Luo; Jianlie Liang; Jinming Zhu; Xuehong Cui

doi:10.1515/ijmr-2021-8260

Artikel

Phase relationships in the Fe-rich region of the Ce–Nd–B–Fe quaternary system at 773 K

Ketong Luo , Jianlie Liang , Jinming Zhu und Xuehong Cui

Veröffentlicht/Copyright: 24. September 2021

Veröffentlicht von

Veröffentlichen auch Sie bei De Gruyter Brill

Informationen für Autor*innen

Aus der Zeitschrift International Journal of Materials Research Band 112 Heft 9

Abstract

The Fe-rich corner of the Ce–Nd–B–Fe quaternary system at 773 K has been experimentally investigated by means of X-ray powder diffraction and scanning electron microscopy equipped with energy dispersive X-ray spectroscopy techniques. No quaternary compound was observed in this system. Ce₂Fe₁₄B and Nd₂Fe₁₄B were found to form the continuous solid solution (Ce,Nd)₂Fe₁₄B. Ce-Fe₄B₄ and NdFe₄B₄ also form the solid solution (Ce,Nd)-Fe₄B₄. The isothermal section consists of 8 three-phase regions and 2 four-phase regions.

Keywords: Ce–Nd–B–Fe quaternary system; Isothermal section; Rare-earth metals; Phase diagram

Xuehong Cui Key Laboratory for Metal and Functional Materials College of Materials and Environment Guangxi University for Nationalities Da Xue Dong Road 188 Nanning + 530006 P.R. China Tel.: +86 15994367050

Funding statement: This work is supported by Guangxi Natural Science Foundation (Grant No. 2017GXNSFBA198004 and 2018GXNSFAA138043), Natural Science Foundation of China (Grant No. 51601042), the Research Funds of Guangxi University for Nationalities (Grant No. 2019XJGY51 and gxun-chxzs2018040), Open Foundation of Guangxi Key Laboratory of Processing for Non-ferrous Metals and Featured Materials, Guangxi University (Grant No. GXYSOF1803).

References

[1] K. Kumar: J. Appl. Phys. 63 (1988) 13. DOI:10.1063/1.34108410.1063/1.341084Suche in Google Scholar

[2] G.V. Chernyak, N.F. Chaban, Yu.B. Kuz’ma: Sov. Powder Metall. Met. Ceram. 22 (1983) 479. DOI:10.1007/bf0079322610.1007/bf00793226Suche in Google Scholar

[3] S.K. Besenicar, J. Holc, G. Drazic, B. Saje: IEEE T Magn. 30 (1994) 693. DOI:10.1109/20.31237910.1109/20.312379Suche in Google Scholar

[4] R. Grossinger, R. Krewenka, H.R. Kirchmayr: J. Less-Common Met. 134 (1987) 17. DOI:10.1016/0022-5088(87)90569-810.1016/0022-5088(87)90569-8Suche in Google Scholar

[5] M. Tokunaga, M. Tobise, N. Meguro, H. Harada: IEEE T Magn. 22 (1986) 904. DOI:10.1109/TMAG.1986.106460110.1109/TMAG.1986.1064601Suche in Google Scholar

[6] K.Y. Koab, S. Yoon’, J.G. Boothb: J. Magn. Magn. Mater. 176 (1997) 313. DOI:10.1016/S0304-8853(97)00652-510.1016/S0304-8853(97)00652-5Suche in Google Scholar

[7] J.Y. Jin, Z. Wang, G.H. Bai, B.X. Peng, Y.S. Liu, M. Yan: J. Alloys Compd. 749 (2018) 580. DOI:10.1016/j.jallcom.2018.03.29110.1016/j.jallcom.2018.03.291Suche in Google Scholar

[8] A.C. Neiva, A.P. Tschiptschin, F.P. Missell: J. Alloys Compd. 217 (1995) 273. DOI:10.1016/0925-8388(94)01356-X10.1016/0925-8388(94)01356-XSuche in Google Scholar

[9] L.L. Zhang, Z.B. Li, Q. Ma, Y.F. Li, Q. Zhao, X.F. Zhang: J. Magn. Magn. Mater. 435 (2017) 96. DOI:10.1016/j.jmmm.2017.03.07810.1016/j.jmmm.2017.03.078Suche in Google Scholar

[10] R.Q. Wang, X. Shen, Y. Liu, J. Li: IEEE-ASME T MECH. 52 (2016) 1. DOI:10.1109/tmag.2016.256951910.1109/tmag.2016.2569519Suche in Google Scholar

[11] C.J. Yan, S. Guo, R.J. Chen, D. Lee, A.R. Yan: Chin. Phys. B. 23 (2014) 1. DOI:10.1088/1674-1056/23/10/10750110.1088/1674-1056/23/10/107501Suche in Google Scholar

[12] X.C. Wang, M.G. Zhu, W. Li, L.Y. Zheng, D.L. Zhao, X. Du, A. Du: Electron. Mater. Lett. 11 (2015) 109. DOI:10.1007/s13391-014-4173-810.1007/s13391-014-4173-8Suche in Google Scholar

[13] M. Ito, M. Yano, N. Sakuma, H. Kishimoto, A. Manabe, T. Shoj, A. Kato, N.M. Dempsey, D. Givord, G.T. Zimanyi: AIP Advances. 6. (2016) 1. DOI:10.1063/1.494504010.1063/1.4945040Suche in Google Scholar

[14] J.Y. Jin, G.H. Bai, Z.H. Zhang, M. Yan: J. Alloys Compd. 763 (2018) 854. DOI:10.1016/j.jallcom.2018.06.01910.1016/j.jallcom.2018.06.019Suche in Google Scholar

[15] M. Zhang, Z.B. Li, B.G. Shen, F.X. Hu, J.R. Sun: J. Alloys Compd. 651 (2015) 144. DOI:10.1016/j.jallcom.2015.08.04410.1016/j.jallcom.2015.08.044Suche in Google Scholar

[16] D. Liu, T.Y. Zhao, R. Li, M. Zhang, R.X. Shang, J.F. Xiong, J. Zhang, J.R. Sun, B.G. Shen: AIP Advances. 7 (2017) 1. DOI:10.1063/1.497280310.1063/1.4972803Suche in Google Scholar

[17] A. Alam, M. Khan, R.W. McCallum, D.D. Johnson: Appl. Phys. Lett. 102 (2013) 1. DOI:10.1063/1.478952710.1063/1.4789527Suche in Google Scholar

[18] M.N. Yang, H. Wang, Y.F. Hu, L.Y.M. Yang, A. Maclennan, B. Yang: J. Alloys Compd. 710 (2017) 519. DOI:10.1016/j.jallcom.2017.03.30510.1016/j.jallcom.2017.03.305Suche in Google Scholar

[19] T.B. Massalski, H. Okamoto, P.R. Subramanian, L. Kacprzak: Binary Alloy Phase Diagrams, 2nd Edition, ASM International, Materials Park, (1990).Suche in Google Scholar

[20] W. Zhang, G. Liu, K. Han: J. Phase Equilib. 13 (1992) 645. DOI:10.1007/BF0266721610.1007/BF02667216Suche in Google Scholar

[21] Y.C. Chuang, C.H. Wu, Z.B. Shao: J. Less-Common Met. 136 (1987) 147. DOI:10.1016/0022-5088(87)90018-X10.1016/0022-5088(87)90018-XSuche in Google Scholar

[22] C. Lin, C.X. Liu, Y.X. Sun, Z.X. Liu, D.F. Chen, C. Gou, K. Sun, J.L. Yang: J. Magn. Magn. Mater. 186 (1998) 129. DOI:10.1016/S0304-8853(98)00052-310.1016/S0304-8853(98)00052-3Suche in Google Scholar

[23] J.M. Moreau, L. Paccard, J.P. Nozieres, F.P. Missell, G. Schneider, V. Villas-Boas: J. Less-Common Met.163 (1990) 245. DOI:10.1016/0022-5088(90)90590-g10.1016/0022-5088(90)90590-gSuche in Google Scholar

[24] J.F. Herbst, J.J. Croat, F.E. Pinkerton: Phys. Rev. B. 29 (1986) 4176. DOI:10.1103/PhysRevB.29.417610.1103/PhysRevB.29.4176Suche in Google Scholar

[25] A. Bezinge, H.F. Braun, J. Muller, K. Yvon: Solid State Commun. 55 (1985) 131. DOI:10.1016/0038-1098(85)90264-910.1016/0038-1098(85)90264-9Suche in Google Scholar

[26] Z.B. Li, D.S. Wang, Z.X. Zhang, X.F. Zhang, F.X. Hu, J.R. Sun, B.G. Shen: J. Alloys Compd. 729 (2017) 988. DOI:10.1016/j.jallcom.2017.09.24310.1016/j.jallcom.2017.09.243Suche in Google Scholar

[27] O.M. Dub, Yu.B. Kuz’ma: Sov. Powder Metall. Met. Ceram. 25 (1986) 572. DOI:10.1007/bf0079236410.1007/bf00792364Suche in Google Scholar

[28] O.M. Dub, N.F. Chaban, Yu.B. Kuz’ma: J. Less-Common Met. 117 (1986) 297. DOI:10.1016/0022-5088(86)90050-010.1016/0022-5088(86)90050-0Suche in Google Scholar

[29] V. Raghavan: Phase diagrams of ternary alloys (monogragh series on alloy phase diagram), Part 6A, NRC, 1992.Suche in Google Scholar

[30] K.H.J. Buschow: Mater. Sci. Rep. 1 (1986) 1. DOI:10.1016/0920-2307(86)90003-410.1016/0920-2307(86)90003-4Suche in Google Scholar

[31] G. Fu, J. Wang, M.H. Rong, G.H. Rao, H.Y. Zhou: J. Phase Equilib. Diffus. 37 (2016) 308. DOI:10.1007/s11669-016-0458-y10.1007/s11669-016-0458-ySuche in Google Scholar

[32] X.H. Cui, J.M. Zhu, K.T. Luo, J.L. Liang: Int. J. Mater. Res. 111 (2020) 526. DOI:10.3139/146.11190910.3139/146.111909Suche in Google Scholar

[33] K.T. Luo, X.H. Cui, J.M. Zhu, J.L. Liang, W. Qin: J. Phase Equilib. Diffus. 41 (2020) 148. DOI:10.1007/s11669-020-00792-710.1007/s11669-020-00792-7Suche in Google Scholar

[34] T. Wang, D. Kevorkov, M. Medraj: Materials 10 (2016) 16. PMid:28772379; DOI:10.3390/ma1001001610.3390/ma10010016Suche in Google Scholar PubMed PubMed Central

Received: 2021-02-26

Accepted: 2021-07-01

Published Online: 2021-09-24

Published in Print: 2021-09-30

Sie haben derzeit keinen Zugang zu diesem Inhalt.

Artikel in diesem Heft

https://doi.org/10.1515/ijmr-2021-8260

Schlagwörter für diesen Artikel

Ce–Nd–B–Fe quaternary system; Isothermal section; Rare-earth metals; Phase diagram