Penetration of amino-silicone micro- and macro-emulsions into Scots pine sapwood and the effect on water-related properties
-
Oliver Weigenand
Abstract
An amino-silicone in the form of a micro- and a macro-emulsion (average particle size 40 and 120 nm, respectively) was tested in impregnation of solid wood. During vacuum-pressure impregnation, the uptake of 5% emulsions was only slightly reduced compared to water up-take. At 15% concentration, a significant reduction in emulsion uptake was observed, particularly in the radial and tangential directions of the wood. The penetration of silicone into the cell wall was dependent on the particle size of the emulsion. Applied as a macro-emulsion, a maximum of only 14% of the total silicone penetrated the cell wall, whereas 25–35% of the silicone was found in the cell wall when applied as a micro-emulsion. The degree of cell wall penetration of silicone for the micro-emulsion was confirmed by X-ray micro-analysis (SEM-EDX). The penetrated silicone caused bulking and dimensional stability. 1H NMR relaxometry T2 distributions were determined for dried and moisture-conditioned wood samples. The silicone-treated specimens displayed spin-spin interactions of protons from water and silicones (or their emulsifiers). Conditioning of samples at 25°C and 65% relative humidity appeared to cause a decrease in the mobility of the non-water protons of the silicone and/or emulsifier. Freezing to -5°C caused separation of protons from bound water and from the silicone at low relaxation times. It is assumed that treatment with the micro-emulsion reduced water sorption due to micro-pore blocking in the cell wall. The formation of a sandwich complex is postulated, which comprises cell wall polymers, water molecules and a layer of silicone.
References
Belyi, V.A., Kupcinov, B.I., Savickij, V.N. (1985) Einfluß der Modifizierung von Birkenholz mit siliciumorganischen Verbindungen auf seine Eigenschaften. Holztechnologie26:247–249.Suche in Google Scholar
Borgin, K. (1965) The testing and evaluation of water repellents. In: BWPA Annual Convention. pp. 67–84.Suche in Google Scholar
Borgin, K., Corbett, K. (1970) Stability and weathering properties of wood treated with various oils, waxes and resins. Plastics Paint Rubber4:69–72.Suche in Google Scholar
Buro, A., Buro, E.-A. (1959) Beitrag zur Kenntnis der Eindringwege für Flüssigkeiten in Kiefernholz. Holzforschung13:71–77.10.1515/hfsg.1959.13.3.71Suche in Google Scholar
Dawson, H.B., Czipri, J.J. (1991) Microemulsions – a new development for the wood preservation industry. Wood Protect.1:55–60.Suche in Google Scholar
Donath, S., Militz H., Mai, C. (2004) Wood modification with alkoxysilanes. Wood Sci. Technol.38:555–566.10.1007/s00226-004-0257-1Suche in Google Scholar
Donath, S., Militz, H., Mai, C. (2006) Creating water-repellent effects on wood by treatment with silanes. Holzforschung60:40–46.10.1515/HF.2006.008Suche in Google Scholar
Flournoy, D.S., Paul, J.A., Kirk, T.K., Highley, T.L. (1993) Changes in the size and volume of pores in sweetgum wood during simultaneous rot by Phanerochaete chrysosporium Burds. Holzforschung47:297–301.10.1515/hfsg.1993.47.4.297Suche in Google Scholar
Greaves, H. (1974) Electron probe X-ray analysis of selected anatomical structures in copper-chrome-arsenic-treated wood. For. Prod. J.7:164–168.Suche in Google Scholar
Haranczyk, H., Weglarz, W.P., Sojka, Z. (1999) The investigation of hydration processes in horse chestnut (Aesculus hippocastanum L.) and pine (Pinus silvestris L.) bark and bast using proton magnetic relaxation. Holzforschung53:299–310.Suche in Google Scholar
Hartley, I.D., Avramidis, S., MacKay, A.L. (1996) H-NMR studies of water interactions in Sitka spruce and western hemlock: moisture content determination and second moments. Wood Sci. Technol.30:141–148.10.1007/BF00224966Suche in Google Scholar
Hill, C.A.S., Jones, D. (1996) The dimensional stabilisation of Corsican pine sapwood by reaction with carboxylic acid anhydride. The effect of chain length. Holzforschung50:457–462.Suche in Google Scholar
Hill, C.A.S., Mallon, S. (1998) The chemical modification of Scots pine with succinic anhydride or octenyl succinic anhydride I. Dimensional stabilisation. Holzforschung52:427–433.Suche in Google Scholar
Hill, C.A.S., Papadopoulos, A.N. (2001) A review of methods used to determine the size of the cell wall microvoids of wood. J. Inst. Wood. Sci.90:337–345.Suche in Google Scholar
Jusoh, I.B., Nzokou P., Kamdem P. (2005) The effect of silicone on some properties of flakeboard. Holz Roh Werkst.63:266–271.10.1007/s00107-004-0550-6Suche in Google Scholar
Kabir, F.R.A., Nicholas, D.D., Vasishth, R.C., Barnes, H.M. (1992) Laboratory methods to predict the weathering characteristics of wood. Holzforschung46:395–401.10.1515/hfsg.1992.46.5.395Suche in Google Scholar
Labbé, N., De Jéso, B., Lartigue, J.-C., Daudé, G., Pétraud, M., Ratier, M. (2002) Moisture content and extractive materials in maritime pine wood by low field 1H NMR. Holzforschung56:25–31.10.1515/HF.2002.005Suche in Google Scholar
Labbé, N., De Jéso, B., Lartigue, J.-C., Daudé, G., Pétraud, M., Ratier, M. (2006) Time-domain 1H NMR characterization of the liquid phase in greenwood. Holzforschung60:265–270.10.1515/HF.2006.043Suche in Google Scholar
Larnøy, E., Militz, H., Eikenes, M. (2005) Uptake of chitosan based impregnation solutions with varying viscosities in four different European wood species. Holz Roh Werkst.63:456–462.10.1007/s00107-005-0014-7Suche in Google Scholar
Le Botlan, D.J., Ouguerram, L. (1997) Spin-spin relaxation time determination of intermediate states in heterogeneous products from free induction decay NMR signals Anal. Chim. Acta349:339–347.10.1016/S0003-2670(97)00274-2Suche in Google Scholar
Lebow, S., Williams, R.S., Lebow, P. (2003) Effect of simulated rainfall and weathering on release of preservative elements from CCA treated wood. Environ. Sci. Technol.37:4077–4082.10.1021/es0343048Suche in Google Scholar
Liese, W. (1951) Über die Bedeutung der Holzstruktur für das Eindringung öliger Holzschutzmittel. Dissertation. Forstliche Fakultät, University of Göttingen.Suche in Google Scholar
Mai, C., Militz, H. (2004) Modification of wood with silicon compounds. Treatment systems based on organic silicon compounds – a review. Wood Sci. Technol.37:453–461.Suche in Google Scholar
Meiboom, S., Gill, D. (1958) Modified spin echo method for measuring relaxation times. Rev. Sci. Instrum.23:688–691.10.1063/1.1716296Suche in Google Scholar
Menon, R.S., MacKay, A.L., Hailey, J.R.T., Bloom, M., Burgess, A.E., Swanson, J.S. (1987) An NMR determination of the physiological water distribution in wood during drying. J. Appl. Polym. Sci.33:1141–1155.10.1002/app.1987.070330408Suche in Google Scholar
Menon, R.S., MacKay, A.L., Flibotte, S., Hailey, J.R.T. (1989) Quantitative separation of NMR images of water in wood on the basis of T2. J. Magn. Reson.82:205–210.10.1016/0022-2364(89)90184-4Suche in Google Scholar
Milota, M.R, Tschernitz, J.L. Verrill, S.P., Mianowski, T. (1995) Gas permeability of plantation loblolly pine. Wood Fiber Sci.27:34–40.Suche in Google Scholar
Nakano, T. (1994) Mechanism of thermoplasticity of chemically modified wood. Holzforschung48:318–324.10.1515/hfsg.1994.48.4.318Suche in Google Scholar
Nicholas, D.D. (1971) Characteristics of preservative solutions which influence their penetration into wood. Forest Prod. J.22:31–36.Suche in Google Scholar
Noll, W. Chemie und Technologie der Silicone. 2nd edition. Verlag Chemie, Weinheim, 1968.Suche in Google Scholar
Olsson, T., Megnis, M., Varna, J., Lindberg, H. (2001) Study of the transverse liquid flow paths in pine and spruce using scanning electron microscopy. J. Wood Sci.47:282–288.10.1007/BF00766714Suche in Google Scholar
Peylo, A., Willeitner, H. (1995) The problem of reducing the leachability of boron by water repellents. Holzforschung49:211–216.10.1515/hfsg.1995.49.3.211Suche in Google Scholar
Provencher, S.W. (1982) Contin: A general purpose constrained regularization program for inverting noisy linear algebraic and integral equations. Comput. Phys. Commun.27:229–242.10.1016/0010-4655(82)90174-6Suche in Google Scholar
Provencher, S.W., Dovi V.G. (1979) Direct analysis of continuous relaxation spectra. J. Biochem. Biophys. Methods1:313–318.10.1016/0165-022X(79)90021-6Suche in Google Scholar
Rapp, A.O., Peek, R.-D., Sailer, M. (2000) Modelling the moisture induced risk of decay for treated and untreated wood above ground. Holzforschung54:111–118.10.1515/HF.2000.019Suche in Google Scholar
Rowell, R.M. (1983) Chemical modification of wood. For. Prod. Abstr.6:363–382.Suche in Google Scholar
Sell, J. (1977) Hydrophobierende Holzimprägnierung-Wirkungsweise, Eigenschaften, Anwendungsmöglichkeiten. Holz Roh Werkst.35:75–78.10.1007/BF02608139Suche in Google Scholar
Stone, J.E., Scallan, A.M. (1968) A structural model for the cell wall of water-swollen wood pulp fibres based on their accessibility to macromolecules. Cell. Chem. Technol.2:343–358.Suche in Google Scholar
Taylor, J.L., Cooper, P.A. (2003) Leaching of CCA from lumber exposed to natural rain aboveground. For. Prod. J.53(9):81–86.Suche in Google Scholar
Voulgaridis, E.V., Banks, W.B. (1981) Degradation of wood during weathering in relation to water repellent long-term effectiveness. J. Inst. Wood Sci.9(2):72–83.Suche in Google Scholar
Voulgaridis, E.V., Banks, W.B. (1983) Laboratory evaluation of the performance of water repellents applied to long wood specimens. Holzforschung37:261–266.10.1515/hfsg.1983.37.5.261Suche in Google Scholar
Wardrop, A.B., Davies, G.W. (1961) Morphological factors relating to the penetration of liquids into wood. Holzforschung15:129–141.10.1515/hfsg.1961.15.5.129Suche in Google Scholar
©2007 by Walter de Gruyter Berlin New York
Artikel in diesem Heft
- MWL fraction with a high concentration of lignin-carbohydrate linkages: Isolation and 2D NMR spectroscopic analysis
- Papermaking properties of the ECF-bleached kraft pulps from first-thinning Scots pine (Pinus sylvestris L.)
- Syntheses and properties of liquefied products of ozone treated wood/epoxy resins having high wood contents
- Quality control of thermally modified timber: Interrelationship between heat treatment intensities and CIE L*a*b* color data on homogenized wood samples
- Violet light causes photodegradation of wood beyond the zone affected by ultraviolet radiation
- Dynamic mechanical analysis of dry wood: Linear viscoelastic response region and effects of minor moisture changes
- Material properties and their interrelation in chemically modified clear wood of Scots pine
- Effect of treatments with 1,3-dimethylol-4,5-dihydroxy-ethyleneurea (DMDHEU) on the tensile properties of wood
- Penetration of amino-silicone micro- and macro-emulsions into Scots pine sapwood and the effect on water-related properties
- Search for a relationship between stress wave velocity and internal stresses in eucalypts and radiata pine
- Kiln-drying lumber quality of hybrid poplar clones
- Heat and mass transfer in wood composite panels during hot pressing: Part 3. Predicted variations and interactions of the pressing variables
- Heat and mass transfer in wood composite panels during hot pressing: Part 4. Experimental investigation and model validation
- Dielectric relaxation of water adsorbed on wood and charcoal
- Properties of piezoelectric voltage considering the microscopic structure of wood cell walls
- Adjusting for fibre length-biased sampling probability using increment cores from standing trees
- External and internal fungal flora of pine sapwood (Pinus sylvestris L.) specimens in above-ground field tests at six different sites in south-west Germany
- Award Presentation on the occasion of the European Workshop on Lignocellulosics and Pulp (EWLP 2006) in Vienna
- Phenolic compounds in silver birch (Betula pendula Roth) wood
Artikel in diesem Heft
- MWL fraction with a high concentration of lignin-carbohydrate linkages: Isolation and 2D NMR spectroscopic analysis
- Papermaking properties of the ECF-bleached kraft pulps from first-thinning Scots pine (Pinus sylvestris L.)
- Syntheses and properties of liquefied products of ozone treated wood/epoxy resins having high wood contents
- Quality control of thermally modified timber: Interrelationship between heat treatment intensities and CIE L*a*b* color data on homogenized wood samples
- Violet light causes photodegradation of wood beyond the zone affected by ultraviolet radiation
- Dynamic mechanical analysis of dry wood: Linear viscoelastic response region and effects of minor moisture changes
- Material properties and their interrelation in chemically modified clear wood of Scots pine
- Effect of treatments with 1,3-dimethylol-4,5-dihydroxy-ethyleneurea (DMDHEU) on the tensile properties of wood
- Penetration of amino-silicone micro- and macro-emulsions into Scots pine sapwood and the effect on water-related properties
- Search for a relationship between stress wave velocity and internal stresses in eucalypts and radiata pine
- Kiln-drying lumber quality of hybrid poplar clones
- Heat and mass transfer in wood composite panels during hot pressing: Part 3. Predicted variations and interactions of the pressing variables
- Heat and mass transfer in wood composite panels during hot pressing: Part 4. Experimental investigation and model validation
- Dielectric relaxation of water adsorbed on wood and charcoal
- Properties of piezoelectric voltage considering the microscopic structure of wood cell walls
- Adjusting for fibre length-biased sampling probability using increment cores from standing trees
- External and internal fungal flora of pine sapwood (Pinus sylvestris L.) specimens in above-ground field tests at six different sites in south-west Germany
- Award Presentation on the occasion of the European Workshop on Lignocellulosics and Pulp (EWLP 2006) in Vienna
- Phenolic compounds in silver birch (Betula pendula Roth) wood