Microstructure and magnetic properties of iron–cobalt-based alloys processed by metal injection moulding

  • Jidong Ma , Mingli Qin , Xiangying Ding , Dil Faraz Khan und Houan Zhang
Veröffentlicht/Copyright: 29. Januar 2018
Veröffentlichen auch Sie bei De Gruyter Brill
Informationen für Autor*innen
International Journal of Materials Research
Aus der Zeitschrift International Journal of Materials Research Band 109 Heft 2

Abstract

Fe–Co-based soft magnetic alloys with excellent magnetic properties were prepared by metal injection moulding and hot isostatic pressing. The effect of processing parameters on microstructure and magnetic properties of the alloy were investigated. Good magnetic performance of Fe-50 %Co alloy with a maximum permeability of 9550, saturation induction of 2.42 T, and coercive force of 68.14 A m–1 was achieved. Hot isostatic pressing processing resulted in a near-full density and the achieved saturation induction exceeded the reported value (1.99 to 2.26 T) of Fe-50 %Co produced by metal injection moulding.

Keywords: Fe-50 %Co; Metal injection moulding; Magnetic properties; Microstructure
*Correspondence address, Jidong Ma, School of Materials Science and Engineering, Xiamen University of Technology, No. 600 Ligong Road, Xiamen 361024, P.R. China, Tel.: +8605926291326, Fax: +8605926291326, E-mail:

References

[1] A.Zelenáková, D.Olekšáková, J.Degmová: J. Magn. Magn. Mater.316 (2007) 519. 10.1016/j.jmmm.2007.03.005Suche in Google Scholar

[2] R.Gilles, M.Hofmann, F.Johnson: J. Alloys Compd.509 (2011) 195. 10.1016/j.jallcom.2010.09.075Suche in Google Scholar

[3] P.Nautiyal, M.M.Seikh, O.I.Lebedev, A.K.Kundu: J. Magn. Magn. Mater.377 (2015) 402. 10.1016/j.jmmm.2014.10.157Suche in Google Scholar

[4] M.D.Chermahini, M.R.Rahimipour, A.H.Pakseresht: Adv. Powder Technol.25 (2014) 462. 10.1016/j.apt.2013.07.010Suche in Google Scholar

[5] Z.Ahmad, A.Ali, M.Farooque, A.ul Haq: Mater. Des.30 (2009) 3885. 10.1016/j.matdes.2009.03.033Suche in Google Scholar

[6] B.Nabi, A.L.Helbert, F.Brisset, G.André, T.Waeckerlé, T.Baudin: Mater. Sci. Eng.A 578 (2013) 215. 10.1016/j.msea.2013.04.066Suche in Google Scholar

[7] A.Silva, J.A.Lozano, R.Machado, J.A.Escobar, A.P.Wendhausen: J. Magn. Magn. Mater.320 (2008) e393. 10.1016/j.jmmm.2008.02.178Suche in Google Scholar

[8] G.Oliver, A.Matthew, E.B.Willard, H.C.Christina, S.G.Sankar, J.P.Liu: Adv. Mater.23 (2011) 821. PMid:21294168; 10.1002/adma.201002180Suche in Google Scholar PubMed

[9] N.C.Hamilton: J. Magn. Magn. Mater.377 (2015) 496. 10.1016/j.jmmm.2014.10.061Suche in Google Scholar

[10] A.Páez-Pavón, A.Jiménez-Morales, T.G.Santos, L.Quintino, J.M.Torralba: J. Magn. Magn. Mater.416 (2016) 342. 10.1016/j.jmmm.2016.05.031Suche in Google Scholar

[11] X.L.Du, M.L.Qin, Y.Sun, Z.H.Yuan, B.H.Yang, X.H.Qu: Adv. Powder Technol.121 (2014) 145.Suche in Google Scholar

[12] H.Shokrollahi: Mater. Des.30 (2009) 3374. 10.1016/j.matdes.2009.03.035Suche in Google Scholar

[13] H.H.Stadelmaier: Mater. Sci. Eng.A 287 (2000) 138. 10.1016/S0921-5093(00)00766-8Suche in Google Scholar

[14] M.J.Sharif, M.Yamauchi, S.Toh, S.Matsumura, S.Noro, K.Kato, M.Takata, T.Tsukuda: Nanoscale5 (2013) 1489. PMid:23334346; 10.1039/c2nr33467dSuche in Google Scholar PubMed

[15] H.Shokollahi, K.Janghorban: J. Mater. Process. Technol.189 (2007) 1. 10.1016/j.jmatprotec.2007.02.034Suche in Google Scholar

[16] A.Urata, H.Matsumoto, S.Yoshida, A.Makino: J. Alloys Compd.509S (2011) S431. 10.1016/j.jallcom.2010.12.104Suche in Google Scholar

Received: 2017-05-06
Accepted: 2017-09-18
Published Online: 2018-01-29
Published in Print: 2018-02-12

© 2018, Carl Hanser Verlag, München

Artikel in diesem Heft

  1. Contents
  2. Contents
  3. Original Contributions
  4. Phase-field simulation of the solidified microstructure in a new commercial 6××× aluminum alloy ingot supported by experimental measurements
  5. Hydrogen sorption and corrosion properties of La2Ni9CoSn0.2 alloy
  6. Isothermal sections of the Co–Ni–Ti system at 950 and 1 000 °C
  7. Experimental and theoretical study of temperature-dependent variable stiffness of magnetorheological elastomers
  8. Photocatalytic properties of nano-structured carbon nitride: a comparison with bulk graphitic carbon nitride
  9. Effects of solution treatment on mechanical properties and corrosion resistance of 4A duplex stainless steel
  10. Three-body abrasive wear behaviour of metastable spheroidal carbide cast irons with different chromium contents
  11. Intermetallic precipitation in rare earth-treated A413.1 alloy: A metallographic study
  12. Short Communications
  13. Microstructure and magnetic properties of iron–cobalt-based alloys processed by metal injection moulding
  14. Solid-state synthesis and magnetic properties of rhombohedral phase Mg2SiNi3
  15. DGM News
  16. DGM News
https://doi.org/10.3139/146.111589
Schlagwörter für diesen Artikel
Fe-50 %Co; Metal injection moulding; Magnetic properties; Microstructure

Artikel in diesem Heft

  1. Contents
  2. Contents
  3. Original Contributions
  4. Phase-field simulation of the solidified microstructure in a new commercial 6××× aluminum alloy ingot supported by experimental measurements
  5. Hydrogen sorption and corrosion properties of La2Ni9CoSn0.2 alloy
  6. Isothermal sections of the Co–Ni–Ti system at 950 and 1 000 °C
  7. Experimental and theoretical study of temperature-dependent variable stiffness of magnetorheological elastomers
  8. Photocatalytic properties of nano-structured carbon nitride: a comparison with bulk graphitic carbon nitride
  9. Effects of solution treatment on mechanical properties and corrosion resistance of 4A duplex stainless steel
  10. Three-body abrasive wear behaviour of metastable spheroidal carbide cast irons with different chromium contents
  11. Intermetallic precipitation in rare earth-treated A413.1 alloy: A metallographic study
  12. Short Communications
  13. Microstructure and magnetic properties of iron–cobalt-based alloys processed by metal injection moulding
  14. Solid-state synthesis and magnetic properties of rhombohedral phase Mg2SiNi3
  15. DGM News
  16. DGM News
Jetzt anmelden und 20% sparen
Institutioneller Zugang
Wie funktioniert Authentifizierung?
Haben Sie eine Idee, wie wir unsere Website verbessern können?
Bitte schreiben Sie uns.
© 2025 De Gruyter Brill
Heruntergeladen am 15.11.2025 von https://www.degruyterbrill.com/document/doi/10.3139/146.111589/pdf
Button zum nach oben scrollen