Three-dimensional viscoelastic numerical analysis of the effects of gas flow on L-profiled polymers in gas-assisted coextrusion
-
Xiaozhen Deng
Abstract
In this study, polymer gas-assisted coextrusion experiments were performed. The influence of a traditional coextrusion flow zone on the gas groove and the relationship between the gas pressure and the melt flow rate were studied. To determine the effects of the gas flow on gas-assisted coextrusion, a three-dimensional simulation was developed in which the gas layer was considered as an independent flow zone. The influence of the gas pressure, gas layer thickness and melt flow rate on the melts’ profile and the deflection deformation degree (DDD) was studied, and the relationship between the gas pressure, gas layer thickness and melt flow rate was obtained. The numerical results indicated that a traditional coextrusion flow zone in front of a gas-assisted coextrusion flow zone could allow products to avoid a gas groove. The quality of the products could be improved by decreasing the gas pressure and gas layer thickness or increasing the melt flow rate. Additionally, the minimum gas pressure decreased as the gas layer thickness increased and increased as the melt flow rate increased. The numerical results were in good agreement with the experimental results, despite a slight quantitative error. Therefore, reasonably controlling the gas flow condition is key in practical applications of gas-assisted coextrusion, and the effects of the gas layer should be considered in gas-assisted coextrusion simulations.
Acknowledgments
This work was supported by the Science and Technology Project Founded by the Education Department of Jiangxi Province (no. GJJ161103), Open Funding of Jiangxi Province Key Laboratory of Precision Drive and Control, China (no. PLPDC-KFKT-201613) and the National Natural Science Foundation of China (no. 51163011).
References
[1] Alfey JT, Schrenk WJ. Science 1980, 208, 813–818.10.1126/science.208.4446.813Suche in Google Scholar
[2] Han CD. Multiphase Flow in Polymer Processing. Academic Press: New York, 1981.10.1007/978-1-4684-3746-1_19Suche in Google Scholar
[3] Mitsoulis E. Adv. Polym. Tech. 1988, 8, 225–242.10.1002/adv.1988.060080302Suche in Google Scholar
[4] Lamnawar K, Zhang H, Maazouz A. Encyclopedia of Polymer Science and Engineering, Wiley Library: New York, 2013.Suche in Google Scholar
[5] Keawkanoksilp C, Apimonsiri W, Patcharaphun S, Sombatsompop N. J. Appl. Polym. Sci. 2012, 125, 2187–2195.10.1002/app.36427Suche in Google Scholar
[6] Borzacchiello D, Leriche E, Blottiere B, Guillet J. J. Rheol. 2014, 58, 493–512.10.1122/1.4865817Suche in Google Scholar
[7] Yang C, Li Z. J. Appl. Polym. Sci. 2016, 133, 43522.10.1002/app.44340Suche in Google Scholar
[8] Han CD, Chin HB. Polym. Eng. Sci. 1979, 19, 1156-1162.10.1002/pen.760191605Suche in Google Scholar
[9] Rungruangsuparata S, Patcharaphunb S, Sombatsompopa N. Polym. Test. 2017, 57, 184–191.10.1016/j.polymertesting.2016.11.025Suche in Google Scholar
[10] Dooley J, Hyun SH, Hughes K. Polym. Eng. Sci. 1998, 38, 1060–1071.10.1002/pen.10274Suche in Google Scholar
[11] Wilson GM, Khomami B. J. Non-Newton. Fluid. 1992, 45, 355–384.10.1016/0377-0257(92)80068-9Suche in Google Scholar
[12] Lamnawar K, Bousmina M, Maazouz A. Macromolecules 2012, 45, 441–454.10.1021/ma201151kSuche in Google Scholar
[13] Xu L, Zhang H, Shi T. Polymer 2016, 99, 185–192.10.1016/j.polymer.2016.06.011Suche in Google Scholar
[14] Karagiannis A, Hrymak AN, Vlachopoulos J. Rheol. Acta. 1990, 29, 71–87.10.1007/BF01331802Suche in Google Scholar
[15] Bondon A, Lamnawar K, Maazouz A. Polym. Eng. Sci. 2015, 55, 2542–2552.10.1002/pen.24146Suche in Google Scholar
[16] Zhang HG, Lamnawar K, Maazouz A. Polym. Eng. Sci. 2015, 55, 771–791.10.1002/pen.23945Suche in Google Scholar
[17] Zeng GS, Qu JP. Mater. Sci. Technol. (China) 2008, 16, 235–238.Suche in Google Scholar
[18] Yin YG, Zhu YJ, Wang XF, Xie T. Plast. Sci. Technol. (China) 1997, 3, 44–46.Suche in Google Scholar
[19] Brzoskowski R, White JL, Szydlowski W, Weissert FC, Nakajima N, Min K. Rubber Chem. Technol. 1987, 60, 945–956.10.5254/1.3536166Suche in Google Scholar
[20] Liang RF, Mackley MR. J. Rheol. 2001, 45, 211–226.10.1122/1.1332786Suche in Google Scholar
[21] Arda DR, Mackley MR. Rheol. Acta. 2005, 44, 352–359.10.1007/s00397-004-0416-1Suche in Google Scholar
[22] Huang XY, Liu HS, Zhou GF, Lou ZM, Li SY. China Plastics (China) 2005, 19, 17–19.Suche in Google Scholar
[23] Deng XZ, Liu HS, Huang YB, Huang XY, He JT. Polym. Mater. Sci. Eng. (China) 2013, 29, 169–172.Suche in Google Scholar
[24] Ren Z, Huang XY, Liu HS, Deng XZ, He JT. J. Appl Polym. Sci. 2015, 132, 42682.10.1002/app.42682Suche in Google Scholar
[25] Hu CZ. Master’s thesis. Nanchang, China: Nanchang University, 2006.Suche in Google Scholar
[26] Sun Y. Master’s thesis. Chengdu, China: Sichuan University, 2006.Suche in Google Scholar
[27] Zhang M, Huang CZ, Jia YX. Polym. Mater. Sci. Eng. (China) 2012, 28, 176–179.Suche in Google Scholar
[28] Li P. Master’s thesis. Haerbin, China: Harbin University of Science and Technology, 2010.Suche in Google Scholar
[29] Zhou GF, Zhou WY, Hu CZ. J. Plast. Eng. (China) 2008, 15, 198–203.10.1016/S1872-5791(08)60054-8Suche in Google Scholar
[30] Liu H, Deng XZ, Huang YB, Huang XY, Li MS. J. Polym. Eng. 2013, 33, 625–632.10.1515/polyeng-2013-0108Suche in Google Scholar
[31] Huang YB, Liu HS, Huang XY, Xiong AH. Polym. Mater. Sci. Eng. (China) 2012, 28, 187–190.10.1016/j.jes.2014.06.048Suche in Google Scholar
[32] Zhou WY, Zhou GF. Acta Mater. Compos. Sin. (China) 2009, 26, 90–98.Suche in Google Scholar
[33] Liu HS, Deng XZ, Huang YB, Huang XY, Lia JM. Polym. Mater. Sci. Eng. (China) 2014, 30, 119–123.Suche in Google Scholar
[34] Deng XZ, Liu HS, Huang YB, Huang XY, He JT. J. Cent. South Univ. Sci. Technol. (China) 2016, 47, 2227–2234.Suche in Google Scholar
[35] Phan-Thien N, Tanner RI. J. Non-Newt. Fluid Mech. 1977, 2, 353–365.10.1016/0377-0257(77)80021-9Suche in Google Scholar
[36] Ansys. Ansys Polyflow 14.5 User’s Guide [M], Ansys. Southpointe, 2012.Suche in Google Scholar
[37] Takase M, Kihara S, Funatsu K. Rheol. Acta. 1998, 37, 624–634.10.1007/s003970050149Suche in Google Scholar
[38] Sunwoo KB, Park SJ, Lee SJ, Ahn KH, Lee SJ. J. Non-Newt. Fluid Mech. 2001, 99, 125–144.10.1016/S0377-0257(01)00115-XSuche in Google Scholar
[39] Sunwoo KB, Park SJ, Lee SJ, Ahn KH, Lee SJ. Rheol. Acta. 2002, 41, 144–153.10.1007/s003970200013Suche in Google Scholar
[40] Li L, Yang JP, Zhang Z. Appl. Chem. Ind. (China), 2008, 37, 33–36.Suche in Google Scholar
[41] Huang YB. PhD dissertation. Nanchang, China: Nanchang University, 2011.Suche in Google Scholar
©2018 Walter de Gruyter GmbH, Berlin/Boston
Artikel in diesem Heft
- Frontmatter
- Material properties
- Structural, optical, and aging studies of biocompatible PVC-PVP blend films
- Structure-property relationships in polypropylene/poly(ethylene-co-octene)/multiwalled carbon nanotube nanocomposites prepared via a novel eccentric rotor extruder
- Swelling behavior of poly (N-hydroxymethylacrylamide-co-acrylic acid) hydrogels and release of potassium nitrate as fertilizer
- Preparation and assembly
- Preparation of poly(L-lactide)/poly(ethylene glycol)/organo-modified montmorillonite nanocomposites via melt intercalation under continuous elongation flow
- Engineering and processing
- Glass fiber–reinforced polypropylene composites fabricated by direct fiber feeding injection molding
- Dip coated stretchable and bendable PEDOTPSS films on low modulus micro-bumpy PDMS substrate
- Influence of a locally variable mold temperature on injection molded thin-wall components
- Process control strategies for injection molding processes with changing raw material viscosity
- Three-dimensional numerical simulation of total warpage deformation for short-glass-fiber-reinforced polypropylene composite injection-molded parts using coupled FEM
- Three-dimensional viscoelastic numerical analysis of the effects of gas flow on L-profiled polymers in gas-assisted coextrusion
Artikel in diesem Heft
- Frontmatter
- Material properties
- Structural, optical, and aging studies of biocompatible PVC-PVP blend films
- Structure-property relationships in polypropylene/poly(ethylene-co-octene)/multiwalled carbon nanotube nanocomposites prepared via a novel eccentric rotor extruder
- Swelling behavior of poly (N-hydroxymethylacrylamide-co-acrylic acid) hydrogels and release of potassium nitrate as fertilizer
- Preparation and assembly
- Preparation of poly(L-lactide)/poly(ethylene glycol)/organo-modified montmorillonite nanocomposites via melt intercalation under continuous elongation flow
- Engineering and processing
- Glass fiber–reinforced polypropylene composites fabricated by direct fiber feeding injection molding
- Dip coated stretchable and bendable PEDOTPSS films on low modulus micro-bumpy PDMS substrate
- Influence of a locally variable mold temperature on injection molded thin-wall components
- Process control strategies for injection molding processes with changing raw material viscosity
- Three-dimensional numerical simulation of total warpage deformation for short-glass-fiber-reinforced polypropylene composite injection-molded parts using coupled FEM
- Three-dimensional viscoelastic numerical analysis of the effects of gas flow on L-profiled polymers in gas-assisted coextrusion