A brief guide to conducting failure analysis on ceramic components
-
W. Harrer
Abstract
Failure investigations are mainly conducted for the purpose of clarifying the root causes for component failure. Possible aims of these investigations are to analyze the unexpected failure of a component during operation, to improve the material and to assess the quality of a product. Usually, ceramics can be used in similar ways as other structural materials. There are particularities, however, which need to be considered in failure analysis of ceramic components.
This paper will therefore give a brief overview of the types of damage which may occur in ceramic materials, with the focus being on failures occurring at room temperature and medium temperatures (e. g., brittle fracture, contact stresses or stresses caused by rapid temperature changes).
Kurzfassung
Schadensanalysen dienen in erster Linie dazu, die Ursachen für das Versagen von Bauteilen aufzuklären. Mögliche Ziele dieser Untersuchungen sind ein unerwartetes Versagen der Teile im Betrieb zu analysieren, das Material zu verbessern oder die Qualität eines Produktes zu untersuchen. Für gewöhnlich können Keramiken ähnlich wie andere Strukturwerkstoffe eingesetzt werden, allerdings gibt es Besonderheiten auf die bei einer Schadensanalyse keramischer Bauteile achtgegeben werden muss.
Diese Arbeit gibt daher auch einen kurzen Überblick über Schadensformen, die bei keramischen Werkstoffen auftreten können. Fokus wird dabei auf Versagensursachen gelegt, die bei Raumtemperatur und mittleren Temperaturen auftreten (z. B. Sprödbruch, Kontaktbeanspruchungen oder Beanspruchungen durch schnelle Temperaturwechsel).
References / Literatur
[1] Morrell, R.: Fractography of Brittle Materials, Measurement Good Practice Guide No. 14, HMSO, National Physical Laboratory, UK, 1999.Suche in Google Scholar
[2] Danzer, R.; Lube, T.; Supancic, P.; Damani R.: Advanced Engineering Materials 10 (2008) 4, 275-298. https://doi.org/10.1002/adem.20070034710.1002/adem.200700347Suche in Google Scholar
[3] Quinn, D. G.: Fractography of Ceramics and Glasses, U. S. Government Printing Office, Washington, USA, 2007, NIST Special publication, pp. 960–917.Suche in Google Scholar
[4] Rice, R. W.: ASTM STP 827 (1984), pp. 5–103.Suche in Google Scholar
[5] Rice, R. W.: Advances in Ceramics 22 (1988), pp. 3–56. https://doi.org/10.1007/BF00581096Suche in Google Scholar
[6] Quinn, D. G.: Journal of Mat. Science 25 (1990), pp. 4361–4376.10.1007/BF00581096Suche in Google Scholar
[7] EN 843-6: 2009-Advanced technical ceramics-Mechanical properties of monolithic ceramics at room temperature, part 6: Guidance for fractographic investigation.Suche in Google Scholar
© 2023 Walter de Gruyter GmbH, Berlin/Boston, Germany
Artikel in diesem Heft
- Contents
- Editorial
- Dear readers
- Metallographic preparation of a composite of meteorite iron, steel, pure iron, and nickel manufactured by the Damascus technique
- The WG Fractography Online Database – stage of development and planning
- Failure Analysis
- A brief guide to conducting failure analysis on ceramic components
- Intergranular Corrosion in X39CrMo17-1 – A Review
- Picture of the Month
- Picture of the Month
- People
- Nachruf auf Dr. Jörg Trempler
- News
- Eine neue Ära des metallografischen Ätzens – Von der wissenschaftlichen Idee zum Serienprodukt „ThEtching“
- Meeting Diary
- Meeting Diary
Artikel in diesem Heft
- Contents
- Editorial
- Dear readers
- Metallographic preparation of a composite of meteorite iron, steel, pure iron, and nickel manufactured by the Damascus technique
- The WG Fractography Online Database – stage of development and planning
- Failure Analysis
- A brief guide to conducting failure analysis on ceramic components
- Intergranular Corrosion in X39CrMo17-1 – A Review
- Picture of the Month
- Picture of the Month
- People
- Nachruf auf Dr. Jörg Trempler
- News
- Eine neue Ära des metallografischen Ätzens – Von der wissenschaftlichen Idee zum Serienprodukt „ThEtching“
- Meeting Diary
- Meeting Diary