Volume 78, Issue 5

The mechanical properties of wood are affected by member size and loading rate. Axial compression tests with different seismic strain rates and sizes of specimens were carried out to investigate the static and dynamic dimensional effects of Yunnan pine timber. And obtained load-displacement curves, compressive strength, modulus of elasticity, peak strain and Poisson’s ratio. Weibull’s weakest chain theory, Bazant’s law of dimensional effects and Carpinteri’s law of multiple fractal dimensional effects were used to analyze the dimensional effects on the compressive strength of wood, and to establish a wood strength model that takes strain rate effects and dimensional effects into account. The results showed that the compressive strength, elastic modulus, and Poisson’s ratio of Yunnan pine wood exhibit both size and strain rate effects. Under the coupling effect of strain rate effect and size effect, the size effect of Yunnan pine wood strength decreases with increasing strain rate, while the strain rate effect increases with increasing size. A size effect model for compressive strength of wood considering strain rate effect based on three theories and experimental data can well describe the dynamic size effect of Yunnan pine wood strength.

Humins are heterogeneous and polydisperse furanic macromolecules derived from sugar biorefinery. Improving wood properties by humination has become of interest recently. This study examined the photodegradation stability of European pine sapwood microveneers modified with humins at different concentrations of citric acid (CA) and succinic acid (SA) as reaction catalysts, e.g., 1.5 %, 3 %, and 4.5 % wt.%. The photostability of huminated wood was assessed after 48 h, 96 h, and 144 h of exposure to the accelerated weathering test by means of mass loss and finite-span tensile strength. The results were compared with unmodified and also unweathered samples. The FT-IR spectroscopy showed apparent changes in the chemical structure of wood by humination modifications. The weight percentage gains of the samples increased with increasing the concentration of the catalyst. While no differences were observed between the samples after two weeks of the water leaching. The strength losses of weathered microveneers were, however, mostly reduced by humin-based formulas containing catalysts, where the microveneers modified with 1.5 % and 3 % CA showed respectively 32 % and 41 % lower strength loss values than the unmodified samples after 144 h of weathering. Overall, the results showed a high potential for humins to protect wood against photodegradation.

This study investigated the inhibition effect of nanoscale silver–copper particle (20 nm) against Coriolus versicolor and Gloeophyllum trabeum . Poplar wood samples ( Populus L.) were vacuum-impregnated using aqueous nano-AgCu solutions at concentrations of 0.01 %, 0.02 %, 0.03 %, 0.05 %, 0.075 %, and 0.1 %. Alkaline copper quaternary (ACQ, 0.1 %), boric acid (0.2 %) and untreated control group (CK) were employed for comparisons. Decay resistance and leachability were studied. The anti-fungi effects were compared between nano-AgCu, nano-Ag, Ag + (silver nitrate), Cu 2+ (copper nitrate), and a composite of Ag + –Cu 2+ . Nano-AgCu particle exhibited effective resistance to fungi after 12 weeks of exposure. The threshold retention of the nano-AgCu against C. versicolor and G. trabeum on poplar wood was 0.19 kg m −3 and 0.62 kg m −3 , respectively. The silver–copper nanoparticles demonstrated excellent leach resistance, and the inhibition effect was retained after leaching. The nano-AgCu particle provided better antifungal effects than single ions or metal nanoparticles. This study illustrates the potential of using nano-AgCu particle as an efficient wood preservative compared to commercial water-soluble preservatives.

The bark of Pinus radiata offers an underutilized source of high-value renewable chemicals such as extractable polyphenols and lipophilic compounds (waxes and suberin). Here, the depolymerization and extraction of suberin from P. radiata bark and its repolymerization to form novel polyesters are reported. Three different strategies were evaluated for repolymerization of the suberin monomers, with starting materials and products characterized using chemical and thermal analysis techniques. The inclusion of comonomer (1,12-dodecanediol) to provide stoichiometric balance improved the conversion, product yield, solubility and increased molecular weight. Enzymatic polymerization conditions gave the highest yield, while the highest molecular weight was achieved using titanium butoxide, demonstrating that polymerization conditions could be varied to target desired product properties. Products were hydrophobic, as shown by contact angles, ϴ  ≥ 90° after 30 s. This work highlights opportunities for utilizing suberin to add value to a  P. radiata bark biorefinery concept. Potential future applications include its use as a starting material for novel bio-based polymers that can serve as water-repellent surfaces and coatings, replacing established products derived from fossil resources.