Investigations on Additive Manufacturing of WCCo Hard Metals by Laser Beam Melting
-
T. Schubert
Abstract
Tungsten carbide-cobalt hard metal produced by additive manufacturing offers opportunities to meet the increasingly complex requirements of high-performance machining. Besides a high level of design freedom and the easy integration of functional properties, the additive manufacturing of hard metals also offers potential for cost savings and conservation of resources. A window of favorable process parameters for laser beam melting was established using commercially available carbide powder with 17 % Co content, which serves to build carbide samples by laser-based additive manufacturing. Compared to conventionally manufactured carbides, deviations can still be noticed with regard to microstructural and mechanical properties. However, bending strengths of > 1 000 MPa and fracture toughness in the range of 10–12 Mpa √m are promising for the future additive manufacturing of WCCo hard metals.
Kurzfassung
Additiv gefertigtes Wolframkarbid-Kobalt-Hartmetall bietet Chancen, komplexer werdenden Anforderungen der Hochleistungszerspanung zu begegnen. Neben hohen Gestaltungsfreiräumen und der einfachen Integration von Funktionseigenschaften birgt die additive Fertigung von Hartmetallen auch Potenzial zur Kosten- und Ressourceneinsparung. Mit kommerziell erhältlichem Hartmetallpulver mit 17 % Co-Anteil wurde für Laserstrahlschmelzen ein Fenster günstiger Prozessparameter ermittelt, mit dem sich Hartmetall-Probenkörper mittels laserbasierter additiver Fertigung aufbauen lassen. Die Charakterisierung der Gefügeausbildung und der mechanischen Eigenschaften zeigen noch Abweichungen im Vergleich zu konventionell hergestelltem Hartmetall. Biegefestigkeiten von > 1 000 MPa und Bruchzähigkeiten im Bereich von 10–12 Mpa √m sind jedoch vielversprechend für eine zukünftige additive Fertigung von WCCo-Hartmetallen.
References / Literatur
[1] DIN e. V.: Additive Fertigung – Grundlagen – Terminologie, DIN EN ISO/ASTM 52900: 2017Suche in Google Scholar
[2] Gibson, I. et al. Additive manufacturing technologies: 3D printing, rapid prototyping and direct digital manufacturing, Springer, New York, 2015, p. 113–121. 10.1007/978-1-4939-2113-3Suche in Google Scholar
[3] Bondar, A. et al.: Carbon-Cobalt-Tungsten, Ref. Met. Sys., Springer, 2010, 249–28910.1007/978-3-642-02700-0_19Suche in Google Scholar
[4] Kolaska, H.: Pulvermetallurgie der Hartmetalle, Fachverband Pulvermetallurgie, 1992, 6/4–6/9Suche in Google Scholar
[5] Baum, A.: Untersuchung prozessbedingter Strukturabweichung laserauftragsgeschweißter Hartmetalle vom regulären Gefüge der Sinterhartmetalle, TUDpress Verl., 2014Suche in Google Scholar
[6] DIN e. V.: Hartmetalle-Bestimmung der Biegebruchfestigkeit, DIN EN ISO 3327: 2009Suche in Google Scholar
[7] DIN e. V.: Hochleistungskeramik-Prüfverfahren (SEVNB-Verfahren), DIN CEN/TS 14425-5: 2009Suche in Google Scholar
[8] Gläser, T.: Untersuchung zum Lasersintern von Wolframkarbid-Kobalt, Apprimus-Verl.; 2010Suche in Google Scholar
© 2017, Carl Hanser Verlag, München
Artikel in diesem Heft
- Contents/Inhalt
- Contents
- Editorial
- Editorial
- Technical Contributions/Fachbeiträge
- Investigations on Additive Manufacturing of WCCo Hard Metals by Laser Beam Melting
- Unlocking the Secrets of Austenite – Metallographic Detective Work in the Laboratory
- Microstructure Characteristics of Electrical Steel for Electrical Power Converters
- Materialographic Microstructural Analysis during the Process Development for the Gas Phase Synthesis of Silicon Carbide
- Meeting Diary/Veranstaltungskalender
- Meeting Diary
Artikel in diesem Heft
- Contents/Inhalt
- Contents
- Editorial
- Editorial
- Technical Contributions/Fachbeiträge
- Investigations on Additive Manufacturing of WCCo Hard Metals by Laser Beam Melting
- Unlocking the Secrets of Austenite – Metallographic Detective Work in the Laboratory
- Microstructure Characteristics of Electrical Steel for Electrical Power Converters
- Materialographic Microstructural Analysis during the Process Development for the Gas Phase Synthesis of Silicon Carbide
- Meeting Diary/Veranstaltungskalender
- Meeting Diary