Using the Control Chart Approach to Evaluate Hardness Tester Performance
-
G. F. Vander Voort
Abstract
The control chart data analysis approach is an ideal method to evaluate the quality of test data using a specific tester, such as a microindentation hardness tester, over a period of usage time. The method described in ASTM E2554 was used for this work. This analysis is done by plotting a Mean s and a standard deviation control chart of the weekly/periodic verification data obtained with certified hardness test blocks at a specific test force and a specific hardness level. The method is illustrated using a Knoop hardness test block certified at a test force of 500 gf and with a long diagonal length of 116.18 μm (527.1 HK). From this data, one can easily calculate the uncertainty of the measurements.
Kurzfassung
Die Datenanalyse anhand von Regelkarten ist ein ideales Verfahren zur Beurteilung der Qualität von Prüfdaten bei Verwendung eines speziellen Prüfgeräts über einen bestimmten Gebrauchszeitraum hinweg, beispielsweise eines Geräts zur Mikroindentierung. Für diese Arbeit wurde mit dem in ASTM E2554 beschriebenen Verfahren gearbeitet. Durchgeführt wird die Untersuchung durch grafische Darstellung einer Mittelwert-Regelkarte und einer Standardabweichungs-Regelkarte mit den wöchentlichen/periodischen Prüfdaten, die mittels zertifizierter Härteprüfblöcke bei einer bestimmten Prüfkraft und einem bestimmten Härtegrad erzielt werden. Das Verfahren wird veranschaulicht am Einsatz eines Knoop-Härteprüfblocks, der bei einer Prüfkraft von 500 gf und mit einer Länge der langen Diagonalen von 116,18 μm (527,1 HK) zertifiziert wurde. Anhand dieser Daten lässt sich der Grad der Messunsicherheit einfach berechnen.
References / Literatur
[1] N.Ullman, “Easy Estimation of Measurement Uncertainty,” ASTM Standardization News, November–December 2014, pp. 20–22.Suche in Google Scholar
© 2016, Carl Hanser Verlag, München
Artikel in diesem Heft
- Contents/Inhalt
- Contents
- Editorial
- Editorial
- Technical Contributions/Fachbeiträge
- Materialographic Preparation of Lithium-Carbon Intercalation Compounds
- Using the Control Chart Approach to Evaluate Hardness Tester Performance
- 10.3139/147.110347
- 10.3139/147.110346
- Conference Proceedings of the 50th Metallography Conference, September 9th to 23rd in Berlin
- Scheme of the Failure Analysis Taking the Example of Profile Wire Breaks in the Support Cable of a Cable Car System
- Meeting Diary/Veranstaltungskalender
- Meeting Diary
Artikel in diesem Heft
- Contents/Inhalt
- Contents
- Editorial
- Editorial
- Technical Contributions/Fachbeiträge
- Materialographic Preparation of Lithium-Carbon Intercalation Compounds
- Using the Control Chart Approach to Evaluate Hardness Tester Performance
- 10.3139/147.110347
- 10.3139/147.110346
- Conference Proceedings of the 50th Metallography Conference, September 9th to 23rd in Berlin
- Scheme of the Failure Analysis Taking the Example of Profile Wire Breaks in the Support Cable of a Cable Car System
- Meeting Diary/Veranstaltungskalender
- Meeting Diary