Influences of the Edge Area Preparation Suitable for EBSD of Ferrous Materials of Different Degrees of Hardness

Dedicated to Prof. Günter Petzow on the occasion of his 90th birthday
  • K. Rochlus , S. Slawik und F. Mücklich
Veröffentlicht/Copyright: 8. Juli 2016
Veröffentlichen auch Sie bei De Gruyter Brill
Manuskript einreichen Informationen für Autor*innen
Practical Metallography
Aus der Zeitschrift Practical Metallography Band 53 Heft 7

Abstract

Electron Backscatter Diffraction (EBSD) is a sensitive method to analyze samples with regard to their surface deformation condition. Hence, a possibly planar cross section without edge rounding as well as a best possible sample preparation are essential for the examination of edge areas up to the edge. Both objectives are quite contrary to each other, so that a comprehensive examination is important. Using Differential Interference Contrast (DIC) and Confocal Laser Scanning Microscopy (CLSM) and taking the example of soft pure iron, it was examined how different grinding media as well as mounting resins affect the cross section. The preparation quality was quantified by means of the EBSD Image Quality (IQ). The findings obtained were applied to the preparation of harder, technologically more relevant ferrous materials. It could be evidenced that the preparation using epoxy resin in combination with hardness regulator is a feasible method which meets both requirements.

Kurzfassung

Elektronenrückstreubeugung (EBSD) ist ein sensitives Verfahren für den Oberflächenverformungszustand von Proben. Daher ist zur Untersuchung von Randbereichen bis zum Rand hin ein möglichst ebener Querschnitt ohne Kantenabrundung sowie eine bestmögliche Probenpräparation entscheidend. Da sich beide Ziele konträr gegenüberstehen, ist eine grundlegende Untersuchung von Bedeutung. Am Beispiel von weichem Reineisen wurde mittels Differentialinterferenzkontrast (DIC) und konfokaler Laserscanningmikroskopie (CLSM) untersucht inwiefern sich verschiedene Schleifmedien sowie Einbettmittel auf den Querschnitt auswirken. Die Präparationsqualität wurde unter Verwendung der EBSD Image-Quality (IQ) quantifiziert. Die gewonnenen Erkenntnisse wurden zur Präparation von härteren, technologisch relevanteren Eisenwerkstoffen herangezogen. Es konnte nachgewiesen werden, dass mit Epoxidharz in Kombination mit Härteangleicher eine Präparationsmethodik realisierbar ist, die beiden gestellten Ansprüchen genügt.

Translation: E. Engert

References / Literatur

[1] Schwartz, A. J.; Kumar, M.; Adams, B. L.: Electron Backscatter Diffraction in Materials Science, 2. Auflage, Springer Science+Business Media, New York, USA, 2009, 1310.1007/978-0-387-88136-2Suche in Google Scholar

[2] Oettel, H.; Schuhmann, H.: Metallografie, 15. Auflage, WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim, Deutschland, 2011, 146ffSuche in Google Scholar

[3] Bjerregaard, L.; Geels, K.; Ottesen, B.; Rückert,M.: Metalog Guide, 3. Auflage, StruersA/S (Ed.), Roedovre, Dänemark, 1992, 17ffSuche in Google Scholar

[4] Vander Voort, G. F.: BUEHLER SumMet – Die Summe unserer Erfahrung, 3. Auflage, Buehler GmbH (Ed.), 2007, 37 ffSuche in Google Scholar

[5] Katrakova, D.; Damgaard, M. J.; Mücklich,F.: Praktische Metallographie. 38 (2001) 10, 547–565Suche in Google Scholar

[6] Geels, K.: Metallographic and Materialographic Specimen Preparation, Light Microscopy, Image Analysis and Hardness Testing, ASTM International, West Conshohocken, USA, 2007, S. 5710.1520/MNL46-EBSuche in Google Scholar

[7] SchüllerH. J.; Schwaab, P.: Praktische Metallographie. 12 (1970) 12, 679–690Suche in Google Scholar

[8] Vander VoortG. F.: Metallography – Principles and Practice, 4. Auflage, ASM International, Materials Park, USA, 2007, S. 86ffSuche in Google Scholar

Received: 2016-03-31
Accepted: 2016-04-18
Published Online: 2016-07-08
Published in Print: 2016-07-15

© 2016, Carl Hanser Verlag, München

Artikel in diesem Heft

  1. Contents/Inhalt
  2. Contents
  3. Editorial
  4. Editorial
  5. Technical Contributions/Fachbeiträge
  6. Influences of the Edge Area Preparation Suitable for EBSD of Ferrous Materials of Different Degrees of Hardness
  7. The Microstructural Development of Laser-Powder-Bed-Fusion Manufactured Tungsten Carbide – Cobalt Hard Metals
  8. Microstructural Design of Bi2Te3- In2Te3 Thermoelectric Composites
  9. Prediction of Size and Position of Fracture Relevant Defects of Samples Fatigued in the VHCF Area on the Basis of Metallographic Examinations
  10. Phase Characterization of a Biocompatible Co-Cr-W Alloy Via Correlative Microscopy
  11. Moments in Life of Günter Petzow
  12. Meeting Diary/Veranstaltungskalender
  13. Meeting Diary
https://doi.org/10.3139/147.110405

Artikel in diesem Heft

  1. Contents/Inhalt
  2. Contents
  3. Editorial
  4. Editorial
  5. Technical Contributions/Fachbeiträge
  6. Influences of the Edge Area Preparation Suitable for EBSD of Ferrous Materials of Different Degrees of Hardness
  7. The Microstructural Development of Laser-Powder-Bed-Fusion Manufactured Tungsten Carbide – Cobalt Hard Metals
  8. Microstructural Design of Bi2Te3- In2Te3 Thermoelectric Composites
  9. Prediction of Size and Position of Fracture Relevant Defects of Samples Fatigued in the VHCF Area on the Basis of Metallographic Examinations
  10. Phase Characterization of a Biocompatible Co-Cr-W Alloy Via Correlative Microscopy
  11. Moments in Life of Günter Petzow
  12. Meeting Diary/Veranstaltungskalender
  13. Meeting Diary
Jetzt anmelden und 20% sparen
Institutioneller Zugang
Wie funktioniert Authentifizierung?
Haben Sie eine Idee, wie wir unsere Website verbessern können?
Bitte schreiben Sie uns.
© 2025 De Gruyter Brill
Heruntergeladen am 3.10.2025 von https://www.degruyterbrill.com/document/doi/10.3139/147.110405/html
Button zum nach oben scrollen