Typical Zirconium Alloys Microstructures in Nuclear Components

  • A. V. Flores , A. G. Gomez , G. A. Juarez , N. Loureiro , R. I. Samper , J. R. Santisteban , M. A. Vicente Alvarez , A. Tolley , A. Condó , R. D. Bianchi , A. D. Banchik and P. Vizcaíno
Published/Copyright: September 4, 2014
Become an author with De Gruyter Brill
Submit Manuscript Author Information
Practical Metallography
From the journal Practical Metallography Volume 51 Issue 9

Abstract

The different microstructures typically found in nuclear components made of zirconium alloys are discussed in this paper. These include material in a variety of thermo-mechanical conditions, e. g., cold rolled, stress relieved, recrystallized, welded, biphasic, together with minority second phases belonging to the original material or incorporated due to in-service conditions. The anisotropic crystalline structure of zirconium is exploited in microscopical observations by means of polarizer filters that enhance the contrast between different grains, and greatly aid the identification in most microstructures. Most microstructural variations across a wide range of length-scales, such as those produced by welding processes, can be effectively resolved by traditional optical microscopy (OM). However, some finer microstructures like those found in CANDU1 (CANada Deuterium Uranium) reactor pressure tube material, or some minority second phase particles like the Zr(Fe, Cr)2 precipitates in Zircaloy-4 cannot be completely resolved by this technique. Thus, scanning electron microscopy (SEM), and transmission electron microscopy (TEM) are required in such cases. For SEM observations we show the valuable issue of the scale in specific microstructural studies, which allows quantifying microstructural parameters using image analysis. For TEM observations, we have greatly benefited from the electron diffraction diagrams, which have allowed us to investigate the crystalline structure of irradiated second phase particles, which would remain unnoticed to both, OM or SEM observations.

Kurzfassung

Diese Arbeit beschäftigt sich mit den unterschiedlichen, in Komponenten kerntechnischer Anlagen aus Zirconiumlegierungen typischerweise auftretenden Mikrostrukturen. Dabei handelt es sich um Werkstoffe mit verschiedenen, durch thermomechanische Behandlung herbeigeführten Zuständen, z. B. kaltgewalzt, spannungsarm geglüht, rekristallisiert, geschweißt, zweiphasig nebst sekundären Minoritätsphasen, die zum Originalwerkstoff gehören oder aufgrund der Betriebsbedingungen enthalten sind. Die anisotrope Kristallstruktur von Zirconium wurde in mikroskopischen Betrachtungen mittels Polarisationsfiltern ausgewertet, die den Kontrast zwischen unterschiedlichen Körnern verstärken und bei der Identifizierung der meisten Mikrostrukturen eine große Hilfe sind. Die meisten mikrostrukturellen Varianten, wie beispielsweise solche, die durch Schweißvorgänge entstehen, können in einer großen Bandbreite von Längenskalen anhand der traditionellen optischen Mikroskopie (OM) effizient aufgelöst werden. Einige feinere Mikrostrukturen, wie solche, wie sie im Druckröhrenwerkstoff des CANDU-Reaktors1 (CANada Deuterium Uranium) auftreten, oder einige sekundäre Minoritätsphasenpartikel wie die Zr(Fe, Cr)2-Ausscheidungen in Zircaloy-4 können anhand dieser Technik nicht vollständig aufgelöst werden. Daher ist in solchen Fällen der Einsatz von Rasterelektronenmikroskopie (REM) und Transmissionselektronenmikroskopie (TEM) erforderlich. Wir beschäftigen uns auf der Basis von REM-Betrachtungen mit dem wichtigen Thema der Skalierung bei bestimmten Mikrostrukturuntersuchungen, durch die Mikrostrukturparameter mittels Bildanalyse quantitativ erfasst werden können. Bei den TEM-Betrachtungen waren uns die Elektronenbeugungsdiagramme sehr nützlich. Sie haben es uns ermöglicht, die Kristallstruktur der bestrahlten Sekundärphasenpartikel zu untersuchen, die sowohl im OM als auch bei einer Betrachtung im REM unbemerkt bleiben würden.

Übersetzung: E. Engert

References / Literatur

[1] Strasser, A.; Adamson, R.; Garzarolli, F.: ZIRAT SPECIAL TOPIC REPORT, Volume I. A.N.T. Int. September 2008.Search in Google Scholar

[2] Strasser, A.; Ruddling, P.; Cox, B.; Garzarolli, F.: ZIRAT 13 SPECIAL TOPIC REPORT, Volume II. A.N.T. Int. August 2008.Search in Google Scholar

[3] Adamson, R.; Garzarolli, F.; Patterson, C.: ZIRAT 14 SPECIAL TOPIC REPORT. A.N.T. Int. September 2009.Search in Google Scholar

[4] Flores, A. V.; Lovey, F.; Chiou, W. A.; Bianchi, R. D.; Motillo, L.; Vizcaino, P.; Lai, L. C.; Banchik, A. D.: 17th Int. Microscopy Congress (IMC17). September 19 to 24, 2010, Rio de Janeiro, Brazil.Search in Google Scholar

[5] Cheadle, A.; Aldridge, S. A.: Journal of Nuclear Materials47 (1973) 255–258. 10.1016/0022-3115(73)90109-8Search in Google Scholar

[6] Marshall, R. P.: J. Nucl. Mater, 1967; 24: 49–59. 10.1016/0022-3115(67)90079-7Search in Google Scholar

[7] Juárez, G. A.: Degree Thesis. J. A. Sábato Institute. San Martin University, Buenos Aires, Argentina. August 2012.Search in Google Scholar

[8] Santisteban, J. R.; Vicente-Alvarez, M. A.; Vizcaino, P.; Banchik, A. D.; AlmerJ.D.: Acta Materialia, Volume 58, Issue 20, December, 2010, pp. 6609–6618. 10.1016/j.actamat.2010.08.022Search in Google Scholar

[9] Motta, A. T.; Lemaignan, C.: J. Nucl. Mater.195 (1992) 277. 10.1016/0022-3115(92)90519-QSearch in Google Scholar

[10] Etoh, Y.; Shimada, S.: J. Nucl. Mater.200 (1993) 59. 10.1016/0022-3115(93)90009-NSearch in Google Scholar

[11] Yang, W. J. S.: J. Nucl. Mater.158 (1988) 71. 10.1016/0022-3115(88)90156-0Search in Google Scholar

[12] Vizcaíno, P.; Banchik, A. D.; AbriataJ. P.: J. of Nucl. Mater. Vol./Issue 304/2–3, (2002), pp. 96–106.Search in Google Scholar

[13] Vizcaíno, P.; Flores, A. V.; Bozzano, P. B.; Banchik, A. D.; Versaci, R. A.; Ríos, R. O.: J. of ASTM Int. Zirconium in the Nuclear Industry, 16th International Symposium. STP 1529, December 2011, pp.: 754–783.10.1520/STP49282TSearch in Google Scholar

[14] Coleman, C.; Grigoriev, V.; Inozemtsev, V.; Markelov, V.; Roth, M.; Makarevicius, V.; Kim, Y. S. Liaqat; Ali, K.; Chackravartti, J. K.; Mizrahi, R.; Lalgudi, R.: J. of ASTM Int. Zirconium in the Nuclear Industry, 16th International Symposium. STP 1529, December 2011, pp. 544–574.10.1520/STP49372SSearch in Google Scholar

Received: 2014-05-12
Accepted: 2014-07-04
Published Online: 2014-09-04
Published in Print: 2014-09-08

© 2014, Carl Hanser Verlag, München

Articles in the same Issue

  1. Contents/Inhalt
  2. Contents
  3. Editorial
  4. Editorial
  5. Technical Contributions/Fachbeiträge
  6. Assessing the Power of Electron Back Scattering Diffraction Characterization of Deformed F-138 Steel from the View Point of Crystal Diffraction
  7. Typical Zirconium Alloys Microstructures in Nuclear Components
  8. Review on Ceramic Interphases by Transmission and Scanning Electron Microscopy
  9. Microscopic Investigation of Pitting Corrosion in Plasma Nitrided Austenitic Stainless Steel
  10. Meeting Diary/Veranstaltungskalender
  11. Meeting Diary
https://doi.org/10.3139/147.110304

Articles in the same Issue

  1. Contents/Inhalt
  2. Contents
  3. Editorial
  4. Editorial
  5. Technical Contributions/Fachbeiträge
  6. Assessing the Power of Electron Back Scattering Diffraction Characterization of Deformed F-138 Steel from the View Point of Crystal Diffraction
  7. Typical Zirconium Alloys Microstructures in Nuclear Components
  8. Review on Ceramic Interphases by Transmission and Scanning Electron Microscopy
  9. Microscopic Investigation of Pitting Corrosion in Plasma Nitrided Austenitic Stainless Steel
  10. Meeting Diary/Veranstaltungskalender
  11. Meeting Diary
Sign up now to receive a 20% welcome discount
Institutional Access
How does access work?
Have an idea on how to improve our website?
Please write us.
© 2025 De Gruyter Brill
Downloaded on 3.11.2025 from https://www.degruyterbrill.com/document/doi/10.3139/147.110304/html?lang=en
Scroll to top button