Assessing the Power of Electron Back Scattering Diffraction Characterization of Deformed F-138 Steel from the View Point of Crystal Diffraction

  • R. E. Bolmaro , M. C. Avalos , N. S. De Vincentis , A. M. Kliauga and H.-G. Brokmeier
Published/Copyright: September 4, 2014
Become an author with De Gruyter Brill

Abstract

Microstructural characterization by combined EBSD and X-ray diffraction analysis is shown for an FCC material deformed by rolling and further heat treatment on air. The wide variety of x-rays sources combined with EBSD allows some correlations between microstructural parameters to be withdrawn by carefully analyzing x-ray peak broadening. The combination of both techniques provides a deeper understanding of anisotropic accumulation of dislocation arrays on a deformed F 138 stainless steel. The anisotropy results in a smaller peak breadth for crystal orientations with [110] planes contained on the rolling plane, further explained as resulting from a lower storage of dislocations. After heat treatment the effect is reverted and the formerly less misoriented orientations become more uniformly oriented revealing a faster dislocation migration and annihilation and/or trapping.

Kurzfassung

Behandelt wird die mikrostrukturelle Charakterisierung mittels kombinierter EBSD- und Röntgenbeugungsanalyse für einen durch Walzen und Wärmebehandlung an Luft verformten kfz-Werkstoff. Die Kombination eines breiten Spektrums an Röntgenquellen und EBSD ermöglicht auf der Grundlage einer sorgfältigen Analyse der Röntgenpeakverbreiterung die Ableitung einiger zwischen mikrostrukturellen Parametern bestehenden Korrelationen. Die Kombination beider Techniken sorgt für ein tieferes Verständnis der anisotropen Ansammlung von Versetzungsanordnungen in rostfreiem Stahl F 138. Aus der Anisotropie ergibt sich eine geringere Peakbreite für in der Walzebene enthaltene Kristallorientierungen mit [110]-Ebenen, die auch als Folge einer geringeren Einlagerung an Versetzungen erklärt werden kann. Nach der Wärmebehandlung kommt es zu einer Umkehrung des Effekts und die zuvor wenig fehlorientierten Ausrichtungen richten sich einheitlicher aus und weisen eine schnellere Versetzungswanderung und -annihilation und/oder Trapping (etwa: „Einfangen“) auf.


Übersetzung: E. Engert


References / Literatur

[1] P.Scherrer: Nachr. Ges. Wiss. Göttingen26 (1918) 98100.Search in Google Scholar

[2] Adams, B.L.; Wright, S.I.; Kunze, K.: Met. & Mat. Trans. A.24, 4 (1993) 819831. 10.1007/BF02656503Search in Google Scholar

[3] Baudin, T.; Dahms, M.; Quesne, C.; Penelle, R.: J. de Physique IV, Colloque 2, suppl. J. de Physique111, 6 (1996) 141146.Search in Google Scholar

[4] Wright, S.I.; Nowell, M. M.; Bingert, J. F.: Met. & Mat. Trans. A38A (2007) 1845–1855. 10.1007/s11661-007-9226-2Search in Google Scholar

[5] Engler, O.: J. Appl. Cryst.42 (2009) 11471157. 10.1107/S0021889809041685Search in Google Scholar

[6] Wilkinson, A.J.: Mater. Sci. Tech.13 (1997) 1, 7984. 10.1179/mst.1997.13.1.79Search in Google Scholar

[7] Wilkinson, A.J.; Meaden, G.; Dingley, D.J.: Ultramicrosopy106, 45 (2006) 307313.10.1016/j.ultramic.2005.10.001Search in Google Scholar

[8] Wilkinson, A.J.; Meaden, G.; Dingley, D.J.: Mater. Sci. Tech. 22, 11 (2006) 12711278. 10.1179/174328406X130966Search in Google Scholar

[9] WilliamsonG.; HallW.: Acta Metall.1 (1953) 2231. 10.1016/0001-6160(53)90006-6Search in Google Scholar

[10] Ungár, T.; GubiczaJ.; Ribárik, G.; BorbélyA.: J. Appl. Cryst.34 (2001) 298310. 10.1107/S0021889801003715Search in Google Scholar

[11] UngárT., DragomirI., RévészÁ., BorbélyA.: J. Appl. Cryst.32 (1999) 9921002. 10.1107/S0021889899009334Search in Google Scholar

[12] Ashby, M. F.: Phil. Mag.21 (1970) 339343. 10.1080/14786437008238426Search in Google Scholar

[13] Nye, J.F.: Acta Metall.1 (1953) 153162. 10.1016/0001-6160(53)90054-6Search in Google Scholar

[14] Sun, S.; Adams, B.L.; King, W.E.: Phil. Mag. A, 80 (2000) 1, 925.10.1080/01418610008212038Search in Google Scholar

[15] He, W.; Ma, W.; Pantleon, W.: Mat. Sci. and Eng. A, 494 (2008) 2127. 10.1016/j.msea.2007.10.092Search in Google Scholar

[16] Voort, G.F. Vander: Pract. Metallogr.48 (2011) 9, 454473.Search in Google Scholar

[17] Wright, S. I.; Nowell, M.M.; Field, D.P.: Microsc. Microanal.17 (2011) 316329. 10.1017/S1431927611000055Search in Google Scholar PubMed

Received: 2014-05-12
Accepted: 2014-07-25
Published Online: 2014-09-04
Published in Print: 2014-09-08

© 2014, Carl Hanser Verlag, München

Downloaded on 3.11.2025 from https://www.degruyterbrill.com/document/doi/10.3139/147.110305/html
Scroll to top button