Chloride-Induced Stress Corrosion Cracking in 316Ti Fuel Oil Pipes of a Gas Turbine Power Plant

  • A. Neidel und B. Fischer
Veröffentlicht/Copyright: 1. Januar 2014
Veröffentlichen auch Sie bei De Gruyter Brill
Manuskript einreichen Informationen für Autor*innen
Practical Metallography
Aus der Zeitschrift Practical Metallography Band 51 Heft 1

Abstract

Two bent pipe sections of the fuel oil system of a heavy-duty gas turbine engine had to be disassembled due to leakage. One of the two specimens received by the laboratory of the engine manufacturer featured a sub-standard weld repair performed by customer personnel. A metallurgical failure investigation was ordered to determine the root cause of the leakage and to verify the results of a laboratory investigation already performed by a third party at the customer's request. The repair-welded bent pipe section failed due to halide-induced pitting corrosion that propagated through-wall in a transgranular stress corrosion cracking (SCC) mode.

Kurzfassung

Zwei gebogene Rohrabschnitte des Heizölsystems einer Industrie-Gasturbine mussten aufgrund einer Leckage demontiert werden. Eine der beiden Proben, die im Labor des Maschinenherstellers eingegangen sind, wies eine durch Mitarbeiter des Kunden durchgeführte minderwertige Reparaturschweißung auf. Eine metallurgische Fehleruntersuchung wurde angeordnet, um die Ursache der Leckage zu bestimmen und die Ergebnisse einer auf Anfrage des Kunden bereits durch Dritte durchgeführte Laboruntersuchung zu überprüfen. Der gebogene Rohrabschnitt mit der Reparaturschweißung versagte aufgrund von halogenidinduzierter Lochkorrosion, die sich durch die Rohrwand als transkristalline Spannungsrisskorrosion (SpRK) ausbreitete.

Übersetzung: E. Engert

References / Literatur

[1] Seume, J.; Lechner, C. (Ed.): Stationäre Gasturbinen, Springer-Verlag, Berlin, Heidelberg, 200310.1007/978-3-662-10016-5Suche in Google Scholar

[2] Neidel, A.; Ullrich, T.; Fischer, B.: Internal report GT BLN QM / 2011 / 0710g_revSuche in Google Scholar

[3] van Buer, R.: Internal memo, November 14, 2011Suche in Google Scholar

[4] van Buer, R.: Internal memo, November 21, 2011Suche in Google Scholar

[5] DGTLV-411615001, Index A: October 2007, internal purchasing specification of engine manufacturer.Suche in Google Scholar

[6] Generic Welding Procedure Specification WPS OE1–2007–447, Index 0: September 27, 2007, internal welding specification of engine manufacturer.Suche in Google Scholar

[7] TÜV Nord Systems GmbH & Co. KG, report 1424/668640800/2011Suche in Google Scholar

[8] http://en.wikipedia.org/wiki/Sodium_hypochlorite, accessed March 8, 2013, 09: 25.Suche in Google Scholar

[9] Lange, G. (Hrsg.): Systematische Beurteilung technischer Schadensfälle. 3. Auflage, DGM, 1992Suche in Google Scholar

[10] Grosch, J.: Schadenskunde im Maschinenbau, 4. Auflage, Expert Verlag, 2004Suche in Google Scholar

[11] ASM Handbook, Volume 11: Failure Analysis and Prevention. 6. Auflage, ASM International, 1998Suche in Google Scholar

[12] VDI-Richtlinie 3822, Part 3: March 2007: Failure analysis - Failures caused by corrosion in electrolytes. Beuth-Verlag GmbH, Berlin, Düsseldorf2007Suche in Google Scholar

[13] Neidel, A. (Ed.): Handbuch Metallschäden, 1. Auflage, Hanser-Verlag, München201010.3139/9783446429666.001Suche in Google Scholar

Published Online: 2014-01-01
Published in Print: 2014-01-17

© 2014, Carl Hanser Verlag, München

Artikel in diesem Heft

  1. Contents/Inhalt
  2. Contents
  3. Editorial
  4. Editorial
  5. Technical Contributions/Fachbeiträge
  6. New Quality Evaluation Approaches for Lithium Ion Batteries Using the Interference Layer Metallography in Combination with Quantitative Structural Analysis
  7. Characterization and Kinetics of VC Coatings on AISI D3 Steel Performed by Thermo-Reactive Diffusion Technique
  8. Chloride-Induced Stress Corrosion Cracking in 316Ti Fuel Oil Pipes of a Gas Turbine Power Plant
  9. Conference proceedings, 47th Metallography Conference
  10. Meeting Diary/Veranstaltungskalender
  11. Meeting Diary
https://doi.org/10.3139/147.110243

Artikel in diesem Heft

  1. Contents/Inhalt
  2. Contents
  3. Editorial
  4. Editorial
  5. Technical Contributions/Fachbeiträge
  6. New Quality Evaluation Approaches for Lithium Ion Batteries Using the Interference Layer Metallography in Combination with Quantitative Structural Analysis
  7. Characterization and Kinetics of VC Coatings on AISI D3 Steel Performed by Thermo-Reactive Diffusion Technique
  8. Chloride-Induced Stress Corrosion Cracking in 316Ti Fuel Oil Pipes of a Gas Turbine Power Plant
  9. Conference proceedings, 47th Metallography Conference
  10. Meeting Diary/Veranstaltungskalender
  11. Meeting Diary
Jetzt anmelden und 20% sparen
Institutioneller Zugang
Wie funktioniert Authentifizierung?
Haben Sie eine Idee, wie wir unsere Website verbessern können?
Bitte schreiben Sie uns.
© 2025 De Gruyter Brill
Heruntergeladen am 19.10.2025 von https://www.degruyterbrill.com/document/doi/10.3139/147.110243/html?lang=de
Button zum nach oben scrollen