Practical Metallography
Aus der Zeitschrift Practical Metallography Band 49 Heft 7

Abstract

Preparation artifacts such as scratches, surface deformation and smearing are often difficult to remove by conventional grinding and polishing.

Vibratory polishing is a mechanical process. It provides a very gentle polishing treatment. This final preparation step provides for a removal of ground specimen surfaces without causing deformations. The sample surface was examined on the basis of different mechanical and chemical/mechanical preparation steps with regard to its suitability for subsequent examinations using a scanning electron microscope (for example EBSD measurements).

Kurzfassung

Präparationsartefakte wie Kratzer, Oberflächenverformung und Verschmierungen sind durch das konventionelle Schleifen und Polieren oft nur schwer zu beseitigen.

Das Vibrationspolieren ist ein mechanisches und sehr schonendes Polierverfahren. Mit diesem finalen Präparationsschritt lassen sich Schliffoberflächen verformungsfrei abtragen. Die Eignung der Probenoberfläche für weiterführende rasterelektronenmikroskopische Untersuchungen wie z.B. EBSD-Messungen wurde in Abhängigkeit verschiedener mechanisch bzw. chemisch-mechanischer Präparationsschritte untersucht.

Translation: E. Engert

Philipp Watermeyer Born in 1985; 2001/05 vocational training as materials tester at the IWM, RWTH Aachen; 2005 technical employee in the SEM team in the Central Facility for Electron Microscopy at RWTH Aachen; appointed head of the Working Group Metallography Aachen in 2005; since 2008 technical employee at the German Aerospace Center Institute of Materials Research of Cologne in the Department for Microanalysis and Metallography. http://www.dlr.de/wf/

References / Literatur

[1] Krill, F. M.: Metal progress, 70 (1956) 81–82Suche in Google Scholar

[2] Petzow, G.; Gessner, L.; Hölscher, D.: Zeitschrift für Metallkunde, 53 (1962) 535–540Suche in Google Scholar

[3] Chen, D.; Kuo, J.-C; Wu, W.-T.: Ultramicros-copy, 111 (2011) 1488–149410.1016/j.ultramic.2011.06.007Suche in Google Scholar PubMed

[4] Schumann, H.; Oettel, H.: Metallografie, 14. Auflage, Wiley-VCH, Weinheim, Deutschland, 2005, S. 210Suche in Google Scholar

[5] Süess, M.J.; Müller, E.; Wepf, R.: Ultramicros-copy, 111 (2011) 1224–123210.1016/j.ultramic.2011.03.004Suche in Google Scholar PubMed

[6] Buehler VibroMet 2 Vibrationspoliergerät, http://www.buehlermet.de/fileadmin/userupload/pdf/Prospekte/VibroMet2_DE_72.pdf (06.10.2011)Suche in Google Scholar

Received: 2012-2-10
Accepted: 2012-5-16
Published Online: 2013-05-23
Published in Print: 2012-07-01

© 2012, Carl Hanser Verlag, München

Artikel in diesem Heft

  1. Contents/Inhalt
  2. Contents
  3. Editorial
  4. Editorial
  5. Technical Contributions/Fachbeiträge
  6. Microstructures of Erbium Modified Aluminum-Copper Alloys
  7. Vibratory Polishing of a Nickel-Based Superalloy (MAR 247) Using VibroMet 2
  8. The Kinetics of Individual Grains in Polycrystalline Materials
  9. Fracture Investigation on a „Rotating Air Seal“ of an Aircraft Engine
  10. Meeting Diary/Veranstaltungskalender
  11. Meeting Diary
https://doi.org/10.3139/147.110178

Artikel in diesem Heft

  1. Contents/Inhalt
  2. Contents
  3. Editorial
  4. Editorial
  5. Technical Contributions/Fachbeiträge
  6. Microstructures of Erbium Modified Aluminum-Copper Alloys
  7. Vibratory Polishing of a Nickel-Based Superalloy (MAR 247) Using VibroMet 2
  8. The Kinetics of Individual Grains in Polycrystalline Materials
  9. Fracture Investigation on a „Rotating Air Seal“ of an Aircraft Engine
  10. Meeting Diary/Veranstaltungskalender
  11. Meeting Diary
Jetzt anmelden und 20% sparen
Institutioneller Zugang
Wie funktioniert Authentifizierung?
Haben Sie eine Idee, wie wir unsere Website verbessern können?
Bitte schreiben Sie uns.
© 2025 De Gruyter Brill
Heruntergeladen am 3.11.2025 von https://www.degruyterbrill.com/document/doi/10.3139/147.110178/pdf
Button zum nach oben scrollen