Particle Distribution and Tool Wear in Friction Stir Processed Al-SiCp Coatings

  • Prasad Rao Kalvala , Anand Patil , RaghuRaj Rangaraju , K.S. Raja und M. Misra
Veröffentlicht/Copyright: 13. Mai 2013
Veröffentlichen auch Sie bei De Gruyter Brill
Manuskript einreichen Informationen für Autor*innen
Practical Metallography
Aus der Zeitschrift Practical Metallography Band 47 Heft 4

Abstract

Al-Mg alloy was friction stir processed (FSP) incorporating two different sized SiC particles. Reduction of particle size after FSP was very significant with coarser SiC particles than finer. The density of SiC particles in FSP nugget was found to be uniform from top to bottom with coarser SiC particles, whereas it was more at the bottom than the top with finer. Tool wear after FSP was found to be relatively more with coarser particles than finer.

Kurzfassung

Eine Al-Mg-Legierung wurde mit dem Rührreibverfahren behandelt (friction stir process, FSP). Dabei wurden zwei SiC-Partikel verschiedener Größe eingebracht. Nach dem FSP war eine Verringerung der Partikelgröße bei groben Partikeln eher als bei feinen Partikeln charakteristisch. Eine gleichförmige Dichte von SiC-Partikeln in FSP-Nuggets vom oberen hin zum unteren Teil bei gröberen SiC-Partikeln konnte festgestellt werden, wobei dies für feinere Partikel mehr im unteren als im oberen Teil der Fall war. Es konnte festgestellt werden, dass nach der Behandlung mit FSP verhältnismäßig mehr Werkzeugverschleiß bei gröberen als bei feineren Partikeln auftritt.

∗ Corresponding Author: Prasad Rao Kalvala, , Phone: 408-824-4667, Fax: 775-784-4949

Anand Patil Bachelor Degree in Mechanical Engineering from College of Engineering, Pune, India. Currently working as as a Research Assistant at Chemical and Materials Engineering Department, University of Nevada, Reno, USA. Thesis work relates to friction Stir Processing of various alloys for wear resistance and biomedical applications

Prasad Rao Kalvala Professor at the department of Metallurgical and materials Engineering, Indian Institute of technolgy madras, Chennai, India. Currently Visiting Professor, Chemical and materials Engineering department, university of Nevada Reno, USA. Research interests include joining of materials and surface engineering

References/Literatur

[1] Mishra, R. S.; Ma, Z. Y.; Charit, I.: Materials Science and Engineering A, 341 (2003) 307–31010.1016/S0921-5093(02)00199-5Suche in Google Scholar

[2] Shafiei-Zarghani, A.; Kashani-Bozorg, S.F.; Zarei-Hanzaki, A.: Materials Science and Engineering: A, 500 (2009) 84–9110.1016/j.msea.2008.09.064Suche in Google Scholar

[3] Uzun, H.: Materials&Design, 28 (2007) 1440–1446Suche in Google Scholar

[4] Mishra, R.S.; Ma, Z.Y.: Materials Science and Engineering: 50 (2005) 1–7810.1016/j.mser.2005.07.001Suche in Google Scholar

[5] Sutton, M.A.; Yang, B.; ReynoldsA.P.; Taylor, R.: Mater Sci EngA323 (2002) 160–16610.1016/S0921-5093(01)01358-2Suche in Google Scholar

[6] Mishra, R.S.; Mahoney, M.W.: Mater. Sci. Forum357–359 (2001) 507–51410.4028/www.scientific.net/MSF.357-359.507Suche in Google Scholar

[7] McClure, J.C.; Tang, W.; Murr, L.E.; Guo, X.; FengZ.; Gould, J.E.: In Proc.Conf. Trends in Welding Research: J.M. Vitak, S.A. David, J.A. Johnson, H.B. Smartt and T. Deb Roy, Editors, Am Welding Soc/ASM Int, Materials Park, OH (1999), 590–595Suche in Google Scholar

[8] Prado, R.A.; Murr, L.E.; SotoK.F.; McClure, J.C.: Mater. Sci. Eng. A, 349 (2003), 156–16410.1016/S0921-5093(02)00750-5Suche in Google Scholar

[9] Prado, R.A.; Murr, L.E.; Shindo, D.J., Soto, K.F.: Scripta Mater., 45 (2001) 75–8010.1016/S1359-6462(01)00994-0Suche in Google Scholar

[10] Feng, A.H.; Xiao, B.L.; Ma, Z.Y.: Composites Science and Technology, 68 (2008) 2141–214810.1016/j.compscitech.2008.03.010Suche in Google Scholar

[11] Shindo, D.J.; Rivera, A.R.; Murr, L.E.: J. Mater. Sci.37 (2002) 4999–500510.1023/A:1021023329430Suche in Google Scholar

[12] Guerra, M.; McClure, J.C.; Murr, L.E.; Nunes, A.C.: Processing Ed: K.V. Jata, M.W. Mahoney, R.S. Mishra, S.L. Semiatin and D.P. Field, TMS (The Minerals, Metals and Materials Society), Warrendale, PA (2001), 25–34.Suche in Google Scholar

Received: 2009-1-20
Accepted: 2009-11-27
Published Online: 2013-05-13
Published in Print: 2010-04-01

© 2010, Carl Hanser Verlag, München

Artikel in diesem Heft

  1. Contents/Inhalt
  2. Contents/Inhalt
  3. Editorial
  4. Schnelle praktische Hilfe — jetzt noch innovativer, benutzerfreundlicher und vielseitiger
  5. Technical Contributions/Fachbeiträge
  6. An Investigation on Weldability of AISI 304 and AISI 1040 Steels on Friction Welding
  7. Application of the Disector to Determine the Distribution of True Interlamellar Spacing in Lamellar Microstructures
  8. Particle Distribution and Tool Wear in Friction Stir Processed Al-SiCp Coatings
https://doi.org/10.3139/147.110041

Artikel in diesem Heft

  1. Contents/Inhalt
  2. Contents/Inhalt
  3. Editorial
  4. Schnelle praktische Hilfe — jetzt noch innovativer, benutzerfreundlicher und vielseitiger
  5. Technical Contributions/Fachbeiträge
  6. An Investigation on Weldability of AISI 304 and AISI 1040 Steels on Friction Welding
  7. Application of the Disector to Determine the Distribution of True Interlamellar Spacing in Lamellar Microstructures
  8. Particle Distribution and Tool Wear in Friction Stir Processed Al-SiCp Coatings
Jetzt anmelden und 20% sparen
Institutioneller Zugang
Wie funktioniert Authentifizierung?
Haben Sie eine Idee, wie wir unsere Website verbessern können?
Bitte schreiben Sie uns.
© 2025 De Gruyter Brill
Heruntergeladen am 3.11.2025 von https://www.degruyterbrill.com/document/doi/10.3139/147.110041/pdf
Button zum nach oben scrollen