Mechanical Behavior and Deformation Modes of Commercially Pure Titanium under Impact Tensile Load
-
Abstract
The impact tensile test was carried out on hot-rolled commercially pure titanium at temperature from 293 K to 77 K. The microstructures after fracture were examined by transmission electron microscope to determine the deformation modes. Strength and ductility increase with decreasing temperature from 293 K to 77 K. The investigation on the microstructure shows that slip cooperates with twinning in the deformation, and twinning becomes more active at lower temperature. At high strain rate titanium exhibits obvious strain hardening and twinning plays an important role in strain hardening. {1012} twin is identified in the microstructure at room temperature and three types of twins were identified at 77 K, which are {1011}, {1012}, {1121} twins.
Kurzfassung
Die Schlagzugprüfung wurde an warmgewalzten kommerziell reinem Titan bei Temperaturen von 293 K bis 77 K durchgeführt. Die Gefüge nach dem Bruch wurden im Transmissionselektronenmikroskop zur Bestimmung der Verformungsmodi untersucht. Festigkeit und Duktilität erhöhten sich mit der Temperaturabnahme von 293 K auf 77 K. Die Gefügeuntersuchung zeigt, dass das Gleiten mit Zwillingsbildung bei der Verformung zusammenwirkt und dass Zwillingsbildung bei niedrigeren Temperaturen häufiger auftritt. Bei hohen Dehnraten zeigt Titan offensichtlich Kaltverfestigung und Zwillingsbildung spielt eine wichtige Rolle darin. Ein {1012}-Zwilling wird im Gefüge bei Raumtemperatur identifiziert und drei Zwillingsarten wurden bei 77 K identifiziert, und zwar {1011}, {1012}, {1121}-Zwillinge.
References/Literatur
[1] TanXiaoli, GuHaicheng, ZhangShufen and C.Laird, Mater.Sci.Eng. A189 (1994), 77.Search in Google Scholar
[2] Z.F.Zhang, H.C.Gu, and X.L.Tan, Mater. Sci.Eng. A252 (1998), 85.10.1016/S0921-5093(98)00650-9Search in Google Scholar
[3] Q. Y.Sun, X.P.Song, H.C.Gu. International Journal of fatigue. 23 (2001), 191.10.1016/S0142-1123(00)00089-XSearch in Google Scholar
[4] Q.Y.Sun, H.C.Gu. Mater. Sci.Eng. A316 (2001), 8310.1088/0965-0393/11/1/307Search in Google Scholar
[5] M.A.Meyers, O.Vöhringer, V.A.Lubarda. Acta Mater.49 (2001), 402510.1016/S1359-6454(01)00300-7Search in Google Scholar
[6] LiuYongning, ZhuJinhua and ZhouHuijiu, Metall. Trans.A.23A (1992), 335.Search in Google Scholar
[7] D.R.Chichili, K.T.Ramesh and K.J.Hemker, Acta Mater.46 (1998), 1025.10.1016/S1359-6454(97)00287-5Search in Google Scholar
[8] S.Nemat-Nasser, W.G.Guo and J.Y.Cheng, Acta Mater.47 (1999), 3705.10.1016/S1359-6454(99)00203-7Search in Google Scholar
[9] Q.Y.Sun, X.L.Tan, H.C.Gu. Pratical metallography39 (2002) 5, 245Search in Google Scholar
[10] Ayman A.Salem, Surya R.Kalidindi, Roger D.Doherty, Acta materials.51 (2003), 4225.10.1016/S1359-6454(03)00239-8Search in Google Scholar
[11] S.Mahajan, D.F.Williams, Int. Metall. Rev.18 (1973), 43.10.1179/imtlr.1973.18.2.43Search in Google Scholar
[12] R.P.Arthey and W.T.Roberts, Metals Technology, (1976) 7, 317.Search in Google Scholar
© 2006, Carl Hanser Verlag, München
Articles in the same Issue
- Contents/Inhalt
- Inhalt / Contents
- Editorial
- Editorial
- Technical Contributions/Fachbeiträge
- Laudatio zur Ernennung des Ehrenvorsitzenden des FA Materialographie der DGM Prof. Dr. rer. nat. Dr. h. c. mult. Günter Petzow im Rahmen der Eröffnung der 12. Internationalen Metallographietagung am 27. September 2006 im Audimax der Montanuniversität Leoben
- SEM Micrographs from NiTi-based Shape Memory Alloys after Mechanical Polishing and Electropolishing
- Metallographische Präparation von dotiertem Tantal für licht- und rasterelektronenmikroskopische Mikrostrukturuntersuchungen
- Mechanical Behavior and Deformation Modes of Commercially Pure Titanium under Impact Tensile Load
Articles in the same Issue
- Contents/Inhalt
- Inhalt / Contents
- Editorial
- Editorial
- Technical Contributions/Fachbeiträge
- Laudatio zur Ernennung des Ehrenvorsitzenden des FA Materialographie der DGM Prof. Dr. rer. nat. Dr. h. c. mult. Günter Petzow im Rahmen der Eröffnung der 12. Internationalen Metallographietagung am 27. September 2006 im Audimax der Montanuniversität Leoben
- SEM Micrographs from NiTi-based Shape Memory Alloys after Mechanical Polishing and Electropolishing
- Metallographische Präparation von dotiertem Tantal für licht- und rasterelektronenmikroskopische Mikrostrukturuntersuchungen
- Mechanical Behavior and Deformation Modes of Commercially Pure Titanium under Impact Tensile Load