Microstructural Investigation of Hard Phases in As-Cast Ni-Ti Memory Alloy
-
Sadegh Badakhshan Raz
Abstract
Ti4Ni2O, Ti4Ni2N, TiC and Ti2Ni are brittle compounds usually formed during production and processing of the Ti-Ni SMA alloys. These compounds adversely affect on workability and shape memory properties of the alloy. This paper presents most recent findings related to the morphologies of various inclusions and Ti-Ni phases formed during and after vacuum induction melting and casting of Ti-45wt.% Ni material. Cast samples were mechanically and/or electrolytically polished and etched. Extensive optical and scanning electron microscopic studies were carried out to characterize the composition and microstructure of the as cast Ti-Ni alloys. Results indicated that mechanical polishing followed by etching was not proficient to reveal sufficient data on physical specifications and morphological changes of the born brittle oxide and nitride and carbide phases. An innovative set of electropolishing/etching conditions was, therefore, prescribed to yield detailed information on morphologies of the brittle phases. Experimental conditions were devised for characterization of the Ti2Ni precipitates, as well.
Kurzfassung
Ti4Ni2O, Ti4Ni2N, TiC und Ti2Ni sind spröde Bestandteile, die üblicherweise während Produktion und Bearbeitung von Ti-Ni-Formgedächtnislegierungen gebildet werden. Diese Bestandteile beeinflussen nachhaltig Bearbeitbarkeit und Eigenschaften des Formgedächtnisses der Legierung. Die vorliegende Arbeit stellt die neuesten Ergebnisse hinsichtlich der Morphologien der verschiedenen Einschlüsse und der Ti-Ni-Phasen vor, die während und nach dem Vakuuminduktionsschmelzen und Gießen des Ti-45 Gew.-%-Ni Materials gebildet werden. Gussproben wurden mechanisch und/oder elektrolytisch poliert und geätzt. Umfangreiche optische und rasterelektronenmikroskopische Untersuchungen wurden zur Charakterisierung von Zusammensetzung und Gefüge der Ti-Ni-Gusslegierungen durchgeführt. Die Ergebnisse ließen den Schluss zu, dass mechanisches Polieren mit nachfolgendem Ätzen nicht geeignet war, ausreichend Daten der physikalischen Spezifikationen und der morphologischen Veränderungen der entstandenen spröden Oxid-, Nitrid- und Karbidphasen zu erhalten. Eine innovative Zusammenstellung der Bedingungen des Elektropolierens/Ätzens wurde daher beschrieben, um detaillierte Informationen zur Morphologie der spröden Phasen zu erhalten. Ebenso wurden experimentelle Bedingungen zur Charakterisierung der Ti2Ni-Ausscheidungen entwickelt.
Literatur/References
[1] Metals Handbook, Properties and Selection: Non ferrous alloys and special purpose materials, Tenth edition, Volume 2, ASM International, USA, 1994Suche in Google Scholar
[2] Lebedof, M.P.: Titanium Alloys, Mir publication, 1985Suche in Google Scholar
[3] Muller, M.H.: Trans. AIME, Vol. 227, 1963, P 64710.2307/2009461Suche in Google Scholar
[4] Jafee, R.I.: Alloy of Titanium with Carbon, Oxygen, Nitrogen, Trans. AIME, Vol. 188, 1950, P 126110.1007/BF03399142Suche in Google Scholar
[5] Kufman, L.: Shape Memory Effect in Alloy, Plenium Press, 1975Suche in Google Scholar
[6] Duerig, T.W.; Pelton, R.A.: Ni-Ti Shape Memory Alloy, Material Properties Handbook: Titanium Handbook, ASM International, USA, 1994Suche in Google Scholar
[7] Rozner, A.G.; Heintzelman, E.F. et al.: Effect of Addition of Oxygen, Nitrogen and Hydrogen on Microstructure and Hardness of Cast TiNi Intermetallic Compound, Transaction of the ASM, Vol. 58. 1965, P 415Suche in Google Scholar
[8] Their, M. et al.: Microstructure of as Cast NiTi Alloy, Mat. Characterization, Vol. 27, P 13310.1016/1044-5803(91)90056-ASuche in Google Scholar
[9] Finlay, W.L.: Optical Metalography of Titanium, Ind. Eng. Che., Vol. 42, 1950, P 21810.1021/ie50482a011Suche in Google Scholar
[10] Middleton, L.A. et al., Metalographic Method for Nitinol, Metallography, No. 17, 1985, P 5110.1016/0026-0800(85)90033-3Suche in Google Scholar
[11] Raz, S.B.: Parameters Influencing Production of Ni-Ti Memory Alloys via Melting and Casting Method, MSc Thesis, Sharif University of Technology, Tehran, Iran, 1380 [in Persian]Suche in Google Scholar
[12] Kufman, L.: Shape Memory Effect in Alloy, Plenum Press, (1975), USASuche in Google Scholar
[13] Stover, E.R.; Wulf, J.: The Nickel – Titanium – Carbon System, Trans. AIME, Vol. 215, 1959, P 127Suche in Google Scholar
© 2005, Carl Hanser Verlag, München
Artikel in diesem Heft
- Contents/Inhalt
- Inhalt / Contents
- Technical Contributions/Fachbeiträge
- Metallographie – Tagung (Bildbericht)
- Dünne Bänder aus CuAlNi-Formgedächtnislegierungen hergestellt durch Melt-Spinning
- Surface Upheavals, Pseudo Martensite, and Martensite Ghosts
- Microstructural Investigation of Hard Phases in As-Cast Ni-Ti Memory Alloy
- The Investigation of the Electrolytic Etching Parameters for a Gold Alloy
Artikel in diesem Heft
- Contents/Inhalt
- Inhalt / Contents
- Technical Contributions/Fachbeiträge
- Metallographie – Tagung (Bildbericht)
- Dünne Bänder aus CuAlNi-Formgedächtnislegierungen hergestellt durch Melt-Spinning
- Surface Upheavals, Pseudo Martensite, and Martensite Ghosts
- Microstructural Investigation of Hard Phases in As-Cast Ni-Ti Memory Alloy
- The Investigation of the Electrolytic Etching Parameters for a Gold Alloy