Microstructure of a Thin Cast Al-Fe-Mn-Si Strip
-
Yücel Birol
Abstract
The recent trend in Twin Roll Casting has been to reduce the casting gauge to less than 3 mm in order to reduce the processing costs, to take advantage of increasing rates of solidification and to increase productivity. Conventional casters typically cast strips 6 to 10 mm thick and operate at essentially constant production rates in this range. The new generation casters, on the other hand, are able to cast strips down to 1mm and offer a notable increase in the casting speed and thus in the caster productivity. It has been reported that the thin strips show some marked differences with respect to conventional strips owing to the temperature gradients and deformation involved in the thin-gauge casting process and may require different down stream processing cycles. The characterization of the thin strip structure is thus essential. This paper describes the microstructure of a thin-cast (3 mm) Al-Fe-Mn-Si (AA8006) strip in comparison with another strip of the same alloy cast at conventional gauge (6 mm).
Kurzfassung
Der neueste Trend zum Doppelwalzenguss (TRC – Twin Roll Casting) mit einer Reduzierung des Gussmaßes auf weniger als 3 mm dient zur Herabsetzung der Prozesskosten, zur Nutzung der zunehmenden Erstarrungsraten und zur Steigerung der Produktivität. In konventionellen Gussanlagen werden üblicherweise Bänder mit einer Dicke von 6 bis 10 mm gegossen und mit einer notwendig konstanten Produktionsrate in diesem Bereich betrieben. Andererseits ist eine neue Generation von Gussanlagen in der Lage, Bänder bis nur 1 mm Dicke zu gießen, bietet so eine bemerkenswerte Verbesserung der Gießgeschwindigkeit und somit der Gießanlagenproduktivität. Es wird berichtet, dass dünne Bänder in Bezug auf konventionelle Bänder einige deutliche Unterschiede aufgrund von Temperaturgradienten und Verformung im Dünngussprozess aufweisen und andere nachfolgende Prozesszyklen erfordern könnten. Die Charakterisierung des Gefüges von dünnen Bändern ist daher unbedingt notwendig. Die vorliegende Arbeit beschreibt das Gefüge eines Al-Fe-Mn-Si-Bandes (AA8006) im Dünngussverfahren im Vergleich mit einem Band derselben Legierung im konventionellen Gussmaß (6 mm).
Literatur/References
[1] Vangala, P.; Smith, D.; Duvvuri, R.; Romanowski, C., in Melt-Spinning and Strip Casting: Research and Implementation, E.F.Matthys (Ed.), The Minerals, Metals & Materials Society, Pennsylvania, 1992.Suche in Google Scholar
[2] Strid, J.: in Proc. 3rd Int. Conf. on Aluminium Alloys, L.Arnberg, O.Lohne, E.Nes, N.Ryum (Eds.), Trondheim, 1992.Suche in Google Scholar
[3] Taraglio, B.; Romanowski, C.: in Light Metals, J.Evans (Ed.) The Minerals, Metals & Materials Society, Pennsylvania, 1995.Suche in Google Scholar
[4] Essadiqi, E.; Caron, S.; Hamel, F.G.; Masdunave, J.; in Light Metals, C.M.Bickert (Ed.) The Minerals, Metals & Materials Society, Pennsylvania, 1990.Suche in Google Scholar
[5] Espedal, A.B.;, Roder, R.: in Light Metals, U.Mannweiler (Ed.), The Minerals, Metals & Materials Society, Pennsylvania, 1994.Suche in Google Scholar
[6] Saitoh, T.; Hojo, H.; Taguchi, H.; Kang, C.G.: Metallurgical Transactions B, 20B (1989) 3, 381–390.10.1007/BF02696990Suche in Google Scholar
[7] Beals, R.; Taraglio, B.; Carey, B.; Romanowski, C.: in tals & Materials Society, Pennsylvania, 1997.Suche in Google Scholar
[8] Daaland, O.; Espedal, A.B.; Nedreberg, M.L.; Alvestad, I.: in Light Metals, R.Huglen (Ed.), The Minerals, Metals & Materials Society, Pennsylvania, 1997.Suche in Google Scholar
[9] Birol, Y.; Kara, G.; Akkurt, S.; Romanowski, C.: in Proc. Int. Conf. Continous Casting, K.Ehrke and W.Schneider (Eds.) DGM-Wiley-VCH, 2000.Suche in Google Scholar
[10] Ertan, S.; Dündar, M.; Birol, Y.; Sariolu, K.; Özden, E.; Akkurt, S.; Yiιldiιzbayrak, G.; Hamer, S.; Romanowski, C.: in Light Metals, R.Huglen (Ed.), The Minerals, Metals & Materials Society, Pennsylvania, 2000.Suche in Google Scholar
[11] Cook, R.; Grocock, P.G.; Thomas, P.M.; Edmonds, D.V.; Hunt, J.D.: Journal of Materials Processing Technology, 55 (1995) 2, 76–84.10.1016/0924-0136(95)01788-7Suche in Google Scholar
[12] Monaghan, D.J.; Hendersson, M.B.; Hunt, J.D.; Edmonds, D.V.: Materials Science and Engineering, A173 (1993) 1–2, 251–254.10.1016/0921-5093(93)90224-3Suche in Google Scholar
[13] Birol, Y.; Zeybekolu, H.G.; Okumu, E.; Kara, G.; Akkurt, S.; Romanowski, C.: in Light Metals, J.L.Anjier (Ed.), The Minerals, Metals & Materials Society, Pennsylvania, 2001.Suche in Google Scholar
[14] Berg, B.S.; Hansen, V.; Zagierski, P.T.; Nedreberg, M.L.; Olsen, A.; Gjonnes, J.: Journal of Materials Processing Technology, 53 (1995) 1–2, 65–74.10.1016/0924-0136(95)01962-ESuche in Google Scholar
[15] Hollingsworth, E.H.; Frank, G.R.; Wilett, R.E.: Trans. AIME, 224 (1962) 188.Suche in Google Scholar
© 2005, Carl Hanser Verlag, München
Artikel in diesem Heft
- Contents/Inhalt
- Inhalt/Contents
- Technical Contributions/Fachbeiträge
- Microstructure of a Thin Cast Al-Fe-Mn-Si Strip
- Beitrag zur Metallographie von Kupfer und Kupferlegierungen
- Schadensanalyse der gebrochenen Rotorwelle einer Windenergieanlage mit überraschendem Resultat
Artikel in diesem Heft
- Contents/Inhalt
- Inhalt/Contents
- Technical Contributions/Fachbeiträge
- Microstructure of a Thin Cast Al-Fe-Mn-Si Strip
- Beitrag zur Metallographie von Kupfer und Kupferlegierungen
- Schadensanalyse der gebrochenen Rotorwelle einer Windenergieanlage mit überraschendem Resultat