Orientation relations between four phases of AgI
Starting with wurtzite-type single crystals, AgI was investigated at room temperature and pressures up to 0.5 GPa by means of a polarizing light microscope and with the precession technique. Distinct orientation relations were observed between four different AgI phases that occur suc cessively under increasing pressure. At 0.35 GPa a reverse-obverse (111) twin of zincblende-type AgI is formed with twin plane parallel to the (001) plane of the wurtzite-type structure. The antilitharge type of AgI occurs at 0.39 GPa. Its tetragonal [001] direction runs parallel to one of the (100) directions of the zincblende type. At almost the same pres sure the transformation to the NaCl-type form takes place. This AgI modification shows also twinning on (111) and the basis vectors are oriented parallel to those of the zincblende type. The transition between the zincblende- and the anti litharge-type phase shows a hysteresis: The back transfor mation occurs at 0.35 GPa. NaCl-type AgI transforms di rectly to the zincblende-type form at approximately 0.2 GPa when pressure is released.
The observed orientation relations between zincblende-, antilitharge- and NaCl-type AgI support transition mecha nisms that have been proposed earlier [Keen & Hull, J. Phys.: Condens. Matter 5 (1993) 23–32].
© Oldenbourg Wissenschaftsverlag
Artikel in diesem Heft
- Charge flipping combined with histogram matching to solve complex crystal structures from powder diffraction data
- Homometric model sets and window covariograms
- Doped γ-Bi2O3: synthesis of microcrystalline samples and crystal chemical analysis of structural data
- Symmetry reduction and cation ordering in alum solid solutions
- XRD and DSC study of the formation and the melting of a new zeolite like borosilicate CsBSi5O12 and (Cs,Rb)BSi5O12 solid solutions
- Orientation relations between four phases of AgI
- Crystal structure of potassium and ammonium tetraperoxovanadates (V)
- Two N-[(3′-4-aryl)prop-2′-ynyl]-N,N′-1,2-phenylenedi-p-tosylamides: synthesis, spectroscopic and X-ray structural studies
Artikel in diesem Heft
- Charge flipping combined with histogram matching to solve complex crystal structures from powder diffraction data
- Homometric model sets and window covariograms
- Doped γ-Bi2O3: synthesis of microcrystalline samples and crystal chemical analysis of structural data
- Symmetry reduction and cation ordering in alum solid solutions
- XRD and DSC study of the formation and the melting of a new zeolite like borosilicate CsBSi5O12 and (Cs,Rb)BSi5O12 solid solutions
- Orientation relations between four phases of AgI
- Crystal structure of potassium and ammonium tetraperoxovanadates (V)
- Two N-[(3′-4-aryl)prop-2′-ynyl]-N,N′-1,2-phenylenedi-p-tosylamides: synthesis, spectroscopic and X-ray structural studies