Experimental and Numerical Investigation of the Surface Layer Conditions after Carbonitriding of Powder Metallurgical Steels. Part 2: Surface Layer States in Components of Graded Porosity
-
J. M. Damon
,
S. Pulvermacher
Abstract
Case hardening processes such as carbonitriding can be used to improve the performance of powder metallurgical (PM) structural components. The partially open porosity of these components leads to a significant increase in diffusion, which in turn leads to a change in the element gradient in the surface layer (and consequently the surface layer state) compared to melting metallurgic materials. Within the scope of a two-part work, the surface layer states in common densities are investigated after the case hardening process. The present part 2 comprises the characterisation of the resulting surface layer states depending on the carbon and nitrogen profile and the tempering heat treatment. Through the deep rolling and the subsequent carbonitriding treatment, hardness of up to 850 HV0.1, retained austenite contents of up to 25 vol-% and residual stresses of up to –300 MPa are determined across densities. The extensions to the numerical models described in this paper enable the FE model to predict the surface layer states in a wide range of process combinations and densities with an error tolerance of ±20 %.
Kurzfassung
Zur Verbesserung der Leistungsfähigkeit von pulvermetallurgischen (PM) Strukturbauteilen können Einsatzhärteverfahren wie das Carbonitrieren eingesetzt werden. Die zum Teil offene Porosität dieser Bauteile führt zu einer signifikanten Steigerung der Diffusion, die wiederum zu einer Veränderung des Elementgradienten in der Randschicht im Vergleich zu schmelzmetallurgischen Werkstoffen führt. Im Rahmen einer zweiteiligen Arbeit werden die Randschichtzustände in für PM-Stahl gängigen Dichten nach dem Prozess des Einsatzhärtens untersucht. Der vorliegende Teil 2 umfasst die Charakterisierung der resultierenden Randschichtzustände (Mikrohärte, Restaustenit, Eigenspannungen) in Abhängigkeit des Kohlen- und Stickstoffprofils und der Anlasswärmebehandlung. Durch die Festwalzbehandlung und die anschließende Carbonitrierbehandlung konnten dichteübergreifend Härten von bis zu 850 HV0,1, Restaustenitanteile von bis zu 25 Vol-% und Eigenspannungen von bis zu −300 MPa festgestellt werden. Durch die in dieser Arbeit beschriebenen Erweiterungen der numerischen Modelle kann das FE-Modell die Randschichtzustände in einer Vielzahl an Prozesskombinationen und Dichten mit einer Fehlertoleranz von ±20 % prognostizieren.
9 Acknowledgement
The IGF project (19887 N) of the research association Arbeitsgemeinschaft Wärmebehandlung und Werkstofftechnik e.V. (AWT) was supported by the German Federation of Industrial Research Associations „Otto von Guericke“ e.V. (AiF) within the framework of the programme for the promotion of joint industrial research and development (IGF) by the Federal Ministry for Economic Affairs and Energy (BMWi) on the basis of a resolution of the German Bundestag. The authors gratefully acknowledge the financial support of the project. Additional thanks go to Höganäs AB for providing the powder metallurgical samples and to Dr. Holger Surm from Leibniz-IWT Bremen for carrying out the case hardening heat treatments and for the intensive scientific exchange.
9 Danksagung
Das IGF-Vorhaben (19887 N) der Forschungsvereinigung Arbeitsgemeinschaft Wärmebehandlung und Werkstofftechnik e.V. (AWT) wurde über die Arbeitsgemeinschaft industrieller Forschungsvereinigungen ”Otto von Guericke” e.V. (AiF) im Rahmen des Programms zur Förderung der industriellen Gemeinschaftsforschung und -entwicklung (IGF) vom Bundesministerium für Wirtschaft und Energie (BMWi) aufgrund eines Beschlusses des Deutschen Bundestages gefördert. Die Autoren bedanken sich für die finanzielle Unterstützung des Vorhabens. Zusätzlicher Dank gilt Höganäs AB für die Bereitstellung der pulvermetallurgischen Proben sowie Dr. Holger Surm vom Leibniz-IWT Bremen für die Durchführung der Einsatzhärte-Wärmebehandlungen und den intensiven wissenschaftlichen Austausch.
References
1 Grosch, J.; Küper, A.; Trautmann, F.: Einsatzhärten: Grundlagen – Verfahren – Anwendung – Eigenschaften einsatzgehärteter Gefüge und Bauteile. 5. Berarb. Aufl., Expert, Tübingen, 2019. – ISBN: 978-3-81693-468-4Suche in Google Scholar
2 Dossett, J. L.: Carbonitriding of Steels. Steel Heat Treating Fundamentals and Processes, ASM International, Materials Park, Ohio, 2013, pp. 599–561. – ISBN: 978-1-62708-011-810.31399/asm.hb.v04a.a0005762Suche in Google Scholar
3 Kell, G.; Liedtke, D.; Roempler, D.; Vogel, W.; Weisssohn, K. H.; Wyss, U.: Stand der Erkenntnisse über die mathematische Voraussage des Härteprofils einsatzgehärteter Bauteile. HTM Härterei-Techn. Mitt. 56 (2001) 3, pp. 166–178Suche in Google Scholar
4 Katemi, R. J.: Influence of Carbonitriding Process on Phase Transformation During Case Hardening, Retained Austenite and Residual Stresses. Dissertation, Universität Bremen, 2019Suche in Google Scholar
5 Lombardo, S.; Steinbacher, M.: Carbozahn: Carbonitrieren von verzahnten Getriebebauteilen: Abschlussbericht, Forschungsvorhaben Nr. 513 I, FVA-Heft 970, Frankfurt, 2011Suche in Google Scholar
6 Saddei, P.: Gefügeaufbau und mechanische Eigenschaften nach Einsatzhärten außerhalb des üblichen Parameterfeldes. Dissertation, Universität Bremen, Shaker Verlag, Düren, 2019. – ISBN: 978-3-84406-501-5Suche in Google Scholar
7 Dlapka, M.; Strobl, S.; Danninger, H.; Gierl, C.: Austenitkorngröße in sintergehärteten pulvermetallurgischen Stählen. Practical Metall. 47 (2010) 12, pp. 686–699, DOI:10.3139/147.11009910.3139/147.110099Suche in Google Scholar
8 Huppmann, W. J.; Dalal, K.; Wellner, P.; Elssner, G.: Metallographic Characterization of PM Materials. Powder Metallurgy 26 (1983) 1, pp. 23–30, DOI:10.1179/ pom.1983.26.1.2310.1179/pom.1983.26.1.23Suche in Google Scholar
9 Kremel, S.; Danninger, H.; Altena, H.; Yu, Y.: Low-pressure carburizing of sintered alloy steels with varying porosity. Powder Metallurgy Progress 4 (2004) 3, pp. 119–131Suche in Google Scholar
10 Damon, J.; Dietrich, S.; Schulze, V.: Implications of carbon, nitrogen and porosity on the gamma-alpha’ martensite phase transformation and resulting hardness in PM-steel Astaloy 85Mo. J. Mat. Res. Techn. 9 (2020) 4, pp. 8245–8257, DOI:10.1016/j. jmrt.2020.05.03510.1016/j.jmrt.2020.05.035Suche in Google Scholar
11 Nußkern, P.: Prozesssimulation der Herstellung einsatzgehärteter pulvermetallurgischer Bauteile. Dissertation, Universität Karlsruhe, 2013Suche in Google Scholar
12 Warke, V. S.: Predicting the Response of Powder Metallurgy Steel Components to Heat Treatment. Dissertation, Worcester Polytechnic Institute, 2008Suche in Google Scholar
13 Eck, S.; Ecker, W.; Wlanis, T.; Gänser, H.-P.; Ebner, R.: Through Process Modelling of Surface Densified PM Gears. BHM Berg- und Hüttenmännische Monatshefte 159 (2014) 9, pp. 371–374, DOI:10.1007/s00501-014-0283-810.1007/s00501-014-0283-8Suche in Google Scholar
14 Damon, J. M.; Surm, H.; Saddei, P.; Dietrich, S.; Schulze, V.: Experimental and Numerical Investigation of the Surface Layer Conditions after Carbonitriding of Powder Metallurgical Steels. Part 1: Diffusion in Components of Graded Porosity. HTM J. Heat Treatm. Mat. 76 (2021) 1, pp. 36–57, DOI:10.1515/htm-2020-000310.1515/htm-2020-0003Suche in Google Scholar
15 Damon, J. M.; Jung, E.; Zürn, M.; Dietrich, S.; Schulze, V.: High-cycle fatigue and surface layer stability of case-hardened PM-steels with graded porosity. Powder Metallurgy (2021), pp. 1–11, DOI:10.1080/00325899.2021.190102710.1080/00325899.2021.1901027Suche in Google Scholar
16 Liscic, B.: Quenching theory and technology. 2. Aufl., CRC Press, Zürich, 2010. – ISBN: 978-0-84939-279-510.1201/9781420009163Suche in Google Scholar
17 Diemar, A.: Simulation des Einsatzhärtens und Abschätzung der Dauerfestigkeit einsatzgehärteter Bauteile. Dissertation, Bauhaus-Universität Weimar, 2007Suche in Google Scholar
18 Trapp, N.: Methoden und Strategien zur Simulation der Wärmebehandlung komplexer Bauteile aus 20 MnCr 5. Dissertation, Universität Karlsruhe, Shaker Verlag, Düren, 2011. – ISBN: 978-3-84400-107-5Suche in Google Scholar
19 Hoferer, M.: Einfluß des Kohlenstoffprofils, des Grundwerkstoffs und des Abschreckmediums auf die Spannungs- und Eigenspannungsausbildung beim Einsatzhärten verschiedener Eisenbasiswerkstoffe. Dissertation, Universität Karlsruhe, 199710.1515/htm-1996-510205Suche in Google Scholar
20 Franz, C.: Experimentelle Untersuchungen und Simulationen der Eigenspannungsausbildung und des Verzugsverhaltens bei der Durch- und Einsatzhärtung von Stählen. Dissertation, Universität Karlsruhe, Shaker Verlag, Düren, 2005. – ISBN: 978-383224-099-8Suche in Google Scholar
21 Ehlers, M.; Güttler, J.; Schwarzer, J.: Computer Aided Simulation of Heat Treatment (C. A.S. H.). HTM J. Heat Treatm. Mat. 61 (2006) 1, pp. 5–9, DOI:10.3139/ 105.10035810.3139/105.100358Suche in Google Scholar
22 Prenosil, B.: Eigenschaften von durch Diffusion des Kohlenstoffs und Stickstoffs im Austenit entstehenden carbonitrierten Schichten. 2. Die Martensitumwandlung des Fe-CN-Austenits. HTM Härterei-Techn. Mitt. 21 (1966) 2, pp. 124–137Suche in Google Scholar
23 Prenosil, B.: Mechanische Eigenschaften Karbonitrierter Stähle: II: Die Dauerfestigkeit Karbonitrierter Stähle, Die Beziehung zwischen dem Restaustenitgehalt in Karbonitrierten Schichten und der Dauerfestigkeit. HTM Härterei-Techn. Mitt. 21 (1966) 4, pp. 271–285Suche in Google Scholar
24 Danninger, H.; Dlapka, M.: Heat Treatment of Sintered Steels – what is different? HTM J. Heat Teatm. Mat. 73 (2018) 3, pp. 117–130, DOI:10.3139/105.11035310.3139/105.110353Suche in Google Scholar
25 Eigenmann, B.; Macherauch, E.: Röntgenographische Untersuchung von Spannungszuständen in Werkstoffen. Mat. wiss. und Werkstofftechnik 26 (1995) 3, pp. 148– 160, DOI:10.1002/mawe.1995026031010.1002/mawe.19950260310Suche in Google Scholar
26 Klages, G.: Landolt–Börnstein, Zahlenwerte und Funktionen aus Naturwissenschaft und Technik. Gruppe ÜI: Kristall–und Festkörperphysik. Bd. 1: Elastische, piezoelektrische, piezooptische und elektrooptische Konstanten von Kristallen. Hearmon. Springer–Verlag, Berlin, 1966.Suche in Google Scholar
27 Faninger, G.; Hartmann, U.: Physikalische Grundlagen der quantitativen röntgenographischen Phasenanalyse (RPA). HTM Härterei-Techn. Mitt. 27 (1972), pp. 233–244Suche in Google Scholar
28 Mühl, F.; Damon, J.; Dietrich, S.; Schulze, V.: Simulation of induction hardening: Simulative sensitivity analysis with respect to material parameters and the surface layer state. Computational Mat. Sc. 184 (2020), p. 109916, DOI:10.1016/ j.commatsci.2020.10991610.1016/j.commatsci.2020.109916Suche in Google Scholar
29 Koistinen, D. P.; Marburger, R. E.: A general equation prescribing the extent of the austenite-martensite transformation in pure iron-carbon alloys and plain carbon steels. Acta Metallurgica 7 (1959) 1, pp. 59–60, DOI:10.1016/0001-6160(59)90170-110.1016/0001-6160(59)90170-1Suche in Google Scholar
30 Gierl, C.; Danninger, H.; Silva, M.; Schmidt, J.; Specht, E.: European Powder Metallurgy Association: Thermophysical Properties of Sintered Steels – Effect of Porosity and Composition. World powder metallurgy congress & exhibition. Proc. of the Powder Metallurgy World Congress & Exhibition.10.-14.10.2010, Florence, Italy, European Powder Matallurgy Association, Shrewsbury, 2010, pp. 41–50. – ISBN: 9781899072101Suche in Google Scholar
31 Hasan, H. S.; Peet, M. J.; Jalil, J. M.; Bhadeshia, H. K. D. H.: Heat transfer coefficients during quenching of steels. Heat and Mass Transfer 47 (2011) 3, pp. 315–321, DOI:10.1007/s00231-010-0721-410.1007/s00231-010-0721-4Suche in Google Scholar
© 2021 Walter de Gruyter GmbH, Berlin/Boston, Germany
Artikel in diesem Heft
- Contents
- Experimental Determination of Heat Transfer using a Polymer Solution Shower during Induction Hardening*
- Optimized Nitriding for Subsequent Induction Heat Treatment
- Experimental and Numerical Investigation of the Surface Layer Conditions after Carbonitriding of Powder Metallurgical Steels. Part 2: Surface Layer States in Components of Graded Porosity
- Tribological Stress Behaviour of Cast Iron without and with Surface Treatment under Concentrated Contact Load*
- Impressum/Imprint
- From and for Practice / Praxis-Informationen
- AWT-Info / HTM 04-2021
- HTM Praxis
Artikel in diesem Heft
- Contents
- Experimental Determination of Heat Transfer using a Polymer Solution Shower during Induction Hardening*
- Optimized Nitriding for Subsequent Induction Heat Treatment
- Experimental and Numerical Investigation of the Surface Layer Conditions after Carbonitriding of Powder Metallurgical Steels. Part 2: Surface Layer States in Components of Graded Porosity
- Tribological Stress Behaviour of Cast Iron without and with Surface Treatment under Concentrated Contact Load*
- Impressum/Imprint
- From and for Practice / Praxis-Informationen
- AWT-Info / HTM 04-2021
- HTM Praxis