Oxidation Behavior of Nanocrystalline Cu-Si Alloys Prepared by Mechanical Alloying
-
Y. Su,
Published/Copyright:
March 10, 2011
Published Online: 2011-03-10
Published in Print: 2009-06
©2011 by Walter de Gruyter GmbH & Co.
Articles in the same Issue
- TABLE OF CONTENTS
- Evaluation of Ti Aluminide Intermetallics Processed Through Reaction Synthesis
- Influence of Metal Oxide on the Fixation of Chlorine in Thermal Decomposition of Poly (vinylidene chloride co vinyl chloride)
- Synergetic Effect of Ultrasound Irradiation in the COD Removal and Degradation of L-Ascorbic Acid in Aqueous Solution by Aerobic Treatment
- Comparison of Hot Corrosion Behaviour of Fe-Cr and Fe-Al Alloys beneath Chloride Salt Melt
- Oxidation Behavior of Nanocrystalline Cu-Si Alloys Prepared by Mechanical Alloying
- Response Surface Methodology Applied to Optimize the Experimental Conditions for Preparing Synthetic Rutile by Microwave Irradiation
- Wear Mechanism of Chromium Pre-Alloyed Sintered Steel
- Reinvestigation of the Permeation Behaviour of a Ba0.5Sr0.5Co0.8Fe0.2O3-δ Perovskite-type Membrane
- Production of Polymer Matrix Composite Particleboard from Pistachio Shells and Improvement of its Fire Resistance by Fly Ash
Creative Commons
BY-NC-ND 3.0
Articles in the same Issue
- TABLE OF CONTENTS
- Evaluation of Ti Aluminide Intermetallics Processed Through Reaction Synthesis
- Influence of Metal Oxide on the Fixation of Chlorine in Thermal Decomposition of Poly (vinylidene chloride co vinyl chloride)
- Synergetic Effect of Ultrasound Irradiation in the COD Removal and Degradation of L-Ascorbic Acid in Aqueous Solution by Aerobic Treatment
- Comparison of Hot Corrosion Behaviour of Fe-Cr and Fe-Al Alloys beneath Chloride Salt Melt
- Oxidation Behavior of Nanocrystalline Cu-Si Alloys Prepared by Mechanical Alloying
- Response Surface Methodology Applied to Optimize the Experimental Conditions for Preparing Synthetic Rutile by Microwave Irradiation
- Wear Mechanism of Chromium Pre-Alloyed Sintered Steel
- Reinvestigation of the Permeation Behaviour of a Ba0.5Sr0.5Co0.8Fe0.2O3-δ Perovskite-type Membrane
- Production of Polymer Matrix Composite Particleboard from Pistachio Shells and Improvement of its Fire Resistance by Fly Ash