Parameters of wood welding: A study with infrared thermography
-
Christelle Ganne-Chédeville
Abstract
Welding of wood is a well-known joining procedure that offers several advantages over traditional mechanical fasteners or gluing. During welding, extensive solid-state transformation phases occur in the so-called melting zone and the heat-affected zone. The nature and the extension of such transformations are correlated to the energy input and thus to the heat generated during the process at the wood joint interface. In the present work the influence of the welding parameters and wood grain orientation on the temperature profile and distribution and final strength of welded connections was investigated. For this purpose, the characteristics of the joints were evaluated with both destructive and non-destructive techniques. Non-destructive evaluation was performed with infrared thermography, which allowed measurement of the maximal and average peak temperature, temperature profile and distribution, and rate of temperature increase. Thus, this technique can also be used to detect welding defects and to provide information on material modification during welding.
References
Banerjee, P., Govardhan, S., Wikle, H.C., Liu, J.Y., Chin, B.A. (1993) Infrared sensing for on-line weld process monitoring and control. J. Manuf. Sci. Eng.115:907–918.Suche in Google Scholar
Davé, V.R., Cola, M.J., Hussen, N.A. (2001) Heat generation in inertia welding of dissimilar tubes. Weld. J. Res. Suppl.10:246–252.Suche in Google Scholar
European standard (2003) EN 205, Adhesives – Wood adhesives for non-structural applications. Determination of the tensile-shear strength of lap joints.Suche in Google Scholar
Fengel, D., Wegener, G. (2003) Wood – Chemistry, Ultrastructure, Reactions. Verlag Kessel, Remagen, 2003.Suche in Google Scholar
Ganne-Chédeville, C., Pizzi, A., Thomas, A., Leban, J.-M., Bocquet, J.-F., Despres, A., Mansouri, H. (2005) Parameter interactions, two-block welding and the wood nail concept in wood dowels welding. J. Adhes. Sci. Technol.19:1157–1174.10.1163/156856105774429037Suche in Google Scholar
Gerber, C., Gfeller, B. (2000) Joint connection with welded thermoplastic dowels and Wood Welding Technologies. In: Proceedings of the World Conference on Timber Engineering, British Columbia, Canada.Suche in Google Scholar
Gfeller, B., Properzi, M. (2003) Woobration, CTI scientific report. BFH-HSB, Bienne, Switzerland.Suche in Google Scholar
Gfeller, B., Pizzi, A., Zanetti, M., Properzi, M., Pichelin, F., Lehmann, M., Delmotte, L. (2004) Solid wood joints by in situ welding of structural wood constituents. Holzforschung58:45–52.10.1515/HF.2004.007Suche in Google Scholar
Gliniorz, K.U., Mohr, S., Natterer, J., Navi, P. (2001) Wood welding. In: Proceedings of the 1st International Conference of the European Society for Wood Mechanics, Lausanne, Switzerland.Suche in Google Scholar
Kulticova, E.V. (1999) Structure and proprieties relationship of densified wood. M.Sc. Thesis, Polytechnic Institute and State University, Blacksburg, VA, USA.Suche in Google Scholar
Leban, J.-M., Pizzi, A., Wieland, S., Zanetti, M., Properzi, M., Pichelin, F. (2004) X-Ray microdensitometry analysis of vibration-welded wood. J. Adhes. Sci. Technol.18:673–685.10.1163/156856104839310Suche in Google Scholar
Lin, C.B., Mu, C.K., Wu, W.W., Hung, C.H. (1999) The effect of joint design and volume fraction on friction welding proprieties of A360/SiC (p) composites. Weld. J. Res. Suppl3:100–108.Suche in Google Scholar
Meola, C., Squillace, A., Minutolo, F.M.C., Morace, R.E. (2004) Analysis of stainless steel welded joints: a comparison between destructive and non-destructive techniques. J. Mater. Process. Technol.155:1893–1899.10.1016/j.jmatprotec.2004.04.303Suche in Google Scholar
Pichelin, F., Pizzi, A., Frühwald, A. (2000) Improving oriented strand board proprieties by using high moisture tolerant adhesives. In: Proceedings of the International Conference on Wood and Wood Fiber Composites, Otto-Graf-Institute, Stuttgart, Germany, pp. 429–438.Suche in Google Scholar
Properzi, M., Leban, J.-M., Pizzi, A., Wieland, S., Pichelin, F., Lehamann, M. (2005) Influence of the grain direction in vibrational wood welding. Holzforschung59:23–27.10.1515/HF.2005.004Suche in Google Scholar
Stamm, B., Natterer, J., Navi, P. (2005) Joining of wood by friction welding. Holz Roh Werkst.63:313–320.10.1007/s00107-005-0007-6Suche in Google Scholar
Sundqvist, B. (2004) Colour change and acid formation in wood during heating. PhD. Thesis, Lulea University of Technology, Sweden.Suche in Google Scholar
Sutthoff, B., Franz, U., Hentschel, H., Schaaf, A. (1996) Verfahren zum reibschweissartigen Fügen und Verbinden von Holz. German Patent DE 19620273 C2.Suche in Google Scholar
Venkatraman, B., Baldev, R., Menaka, M. (2005) Online infrared detection of inclusions and lack of penetration during welding. Mater. Eval.9:933–937.Suche in Google Scholar
Wang, Y., Chin, B.A. (1986) Online sensing of weld penetration using infrared thermography. Opt. Tech. Insp.34:314–320.Suche in Google Scholar
Wieland, S., Shi, B., Pizzi, A., Properzi, M., Stampanoni, M., Abela, R., Lu, X., Pichelin, F. (2005) Vibration welding of wood: X-ray tomography, additives, radical concentration. For. Prod. J.55:84–87.Suche in Google Scholar
Wikle, H.C., Kottilingam, R.H., Zee, R.H., Chin, B.A. (2001) Infrared sensing technique for penetration depth control of the submerged arc welding process. J. Mater. Process. Technol.113:228–233.10.1016/S0924-0136(01)00587-8Suche in Google Scholar
©2006 by Walter de Gruyter Berlin New York
Artikel in diesem Heft
- Upgrading of paper-grade pulps to dissolving pulps by nitren extraction: Optimisation of extraction parameters and application to different pulps
- De-esterification and sulfonation in spruce CTMP: Effects on pulp and paper properties
- The nature of chromophores in high-extractives mechanical pulps: Western red cedar (Thuja plicata Donn) chemithermomechanical pulp (CTMP)
- On the relationship between fibre length, cellulose chain length and pulp viscosity of a softwood sulfite pulp
- The formation of aromatic end group structures in O-alkyl substituted celluloses under alkaline pulping conditions
- Kraft pulp from budworm-infested Jack pine
- Elucidation of the structure of cellulolytic enzyme lignin
- Effect of acetyl groups on enzymatic hydrolysis of cellulosic substrates
- NIR PLSR results obtained by calibration with noisy, low-precision reference values: Are the results acceptable?
- The hydration of paper studied with solid-state magnetisation-exchange 1H NMR spectroscopy
- Impact of drying temperature and pressing time factor on VOC emissions from OSB made of Scots pine
- Factors influencing timber gluability with one-part polyurethanes – studied with nine Australian timber species
- Mechanical characterisation of wood-adhesive interphase cell walls by nanoindentation
- Parameters of wood welding: A study with infrared thermography
- Polycarboxylic acids as non-formaldehyde anti-swelling agents for wood
- Influence of variation in modulus of elasticity on creep of wood during changing process of moisture
- Permeability changes in heartwood of Picea abies and Abies alba induced by incubation with Physisporinus vitreus
- Combined effect of boron compounds and heat treatments on wood properties: Boron release and decay and termite resistance
- Antioxidant activity of extracts from the bark of Chamaecyparis lawsoniana (A. Murray) Parl.
- Obituary Carlton W. Dence (1926–2006)
- Characteristics of NAEM salt-catalyzed alcohol organosolv pulping as a biorefinery
Artikel in diesem Heft
- Upgrading of paper-grade pulps to dissolving pulps by nitren extraction: Optimisation of extraction parameters and application to different pulps
- De-esterification and sulfonation in spruce CTMP: Effects on pulp and paper properties
- The nature of chromophores in high-extractives mechanical pulps: Western red cedar (Thuja plicata Donn) chemithermomechanical pulp (CTMP)
- On the relationship between fibre length, cellulose chain length and pulp viscosity of a softwood sulfite pulp
- The formation of aromatic end group structures in O-alkyl substituted celluloses under alkaline pulping conditions
- Kraft pulp from budworm-infested Jack pine
- Elucidation of the structure of cellulolytic enzyme lignin
- Effect of acetyl groups on enzymatic hydrolysis of cellulosic substrates
- NIR PLSR results obtained by calibration with noisy, low-precision reference values: Are the results acceptable?
- The hydration of paper studied with solid-state magnetisation-exchange 1H NMR spectroscopy
- Impact of drying temperature and pressing time factor on VOC emissions from OSB made of Scots pine
- Factors influencing timber gluability with one-part polyurethanes – studied with nine Australian timber species
- Mechanical characterisation of wood-adhesive interphase cell walls by nanoindentation
- Parameters of wood welding: A study with infrared thermography
- Polycarboxylic acids as non-formaldehyde anti-swelling agents for wood
- Influence of variation in modulus of elasticity on creep of wood during changing process of moisture
- Permeability changes in heartwood of Picea abies and Abies alba induced by incubation with Physisporinus vitreus
- Combined effect of boron compounds and heat treatments on wood properties: Boron release and decay and termite resistance
- Antioxidant activity of extracts from the bark of Chamaecyparis lawsoniana (A. Murray) Parl.
- Obituary Carlton W. Dence (1926–2006)
- Characteristics of NAEM salt-catalyzed alcohol organosolv pulping as a biorefinery