LCF Fracture in Helical Tension Springs of Medium Voltage Switches

  • , , , and
Published/Copyright: October 31, 2020
Become an author with De Gruyter Brill
Submit Manuscript Author Information
Practical Metallography
From the journal Practical Metallography Volume 57 Issue 11

Abstract

Helical tension springs used in switch mechanisms of medium voltage switches failed prematurely in test rigs. The switch mechanism assemblies did not reach the required number of cycles to failure. The springs failed by low cycle fatigue fracture. They were phosphate coated for corrosion protection but not shot peened. The material used for the springs is a usual patented spring steel. Chemical composition, mechanical properties, and microstructure of the failed springs and a reference spring alike were all unremarkable. The subject springs were assembled and rig tested at three different locations but failed only at two of them, not in the third. It was concluded that misalignment from assembly was the root cause of failure.

Kurzfassung

Bei Spiralzugfedern, die in Schalterantrieben von Mittelspannungsschaltern eingesetzt werden, kam es bei Tests am Prüfstand zum frühzeitigen Versagen. Die Schalterantriebe als Baugruppe erreichten vor ihrem Versagen nicht die geforderte Anzahl von Zyklen. Grund für das Versagen der Federn waren niederzyklische Schwingbrüche. Die Federn waren zum Schutz vor Korrosion phosphatiert, jedoch nicht kugelgestrahlt worden. Das Federmaterial ist ein gängiger patentierter Federstahl. Die chemische Zusammensetzung, die mechanischen Eigenschaften sowie die Mikrostruktur der gebrochenen Federn sowie einer intakten Vergleichsfeder waren gleichermaßen unauffällig. Die betreffenden Federn wurden an drei verschiedenen Standorten montiert und am gleichen Ort in Prüfständen getestet. Zum Bauteilversagen kam es jedoch nur in zwei dieser Standorte, nicht am dritten. Es wird davon ausgegangen, dass der Hauptgrund für das Bauteilversagen in einem montagebedingten Fluchtungsfehler liegt.

Übersetzung: V. Müller

References / Literatur

[1] Gädicke, T.; Cagliyan, E.; Riesenbeck, S.: Internal Report BLN MT/2016/0633, Berlin, December 21, 2016Search in Google Scholar

[2] VDI-Richtlinie 3822 Blatt 2, Schadensanalyse – Schäden durch mechanische BeanspruchungenSearch in Google Scholar

[3] DIN 17223 (withdrawn) Search in Google Scholar
Received: 2020-02-27
Accepted: 2020-05-25
Published Online: 2020-10-31
Published in Print: 2020-11-16

© 2020, Carl Hanser Verlag, München

Articles in the same Issue

  1. Contents/Inhalt
  2. Contents
  3. Editorial
  4. Editorial
  5. Technical Contributions/Fachbeiträge
  6. Image Segmentation Variants for Semi-Automated Quantitative Microstructural Analysis with ImageJ
  7. Laser Scanning Microscopy for the Evaluation of the Solid Particle Erosion Resistance of Different Hardpaint Wear Protection Layers
  8. Modified Determination of Flake Length Distribution in Lamellar Grey Iron (GJL)
  9. LCF Fracture in Helical Tension Springs of Medium Voltage Switches
  10. Meeting Diary/Veranstaltungskalender
  11. Meeting Diary
https://doi.org/10.3139/147.110648

Articles in the same Issue

  1. Contents/Inhalt
  2. Contents
  3. Editorial
  4. Editorial
  5. Technical Contributions/Fachbeiträge
  6. Image Segmentation Variants for Semi-Automated Quantitative Microstructural Analysis with ImageJ
  7. Laser Scanning Microscopy for the Evaluation of the Solid Particle Erosion Resistance of Different Hardpaint Wear Protection Layers
  8. Modified Determination of Flake Length Distribution in Lamellar Grey Iron (GJL)
  9. LCF Fracture in Helical Tension Springs of Medium Voltage Switches
  10. Meeting Diary/Veranstaltungskalender
  11. Meeting Diary
Downloaded on 21.4.2026 from https://www.degruyterbrill.com/document/doi/10.3139/147.110648/html
Scroll to top button