Microstructural Characterization of Martensitic All-Weld Metal Samples
-
P. Haslberger
Abstract
The development of welding consumables is permanently challenged with matching the increasing strength and toughness of thermomechanically treated or quenched and tempered steels. A martensitic microstructure offers promising prospects to guarantee such requirements in the all-weld metal as well. A thorough characterization of the microstructure is indispensable to understand its effects on the mechanical properties. This paper shall summarize how light optical microscopy and electron backscatter diffraction can be used to deepen the understanding of fully martensitic weld metal. It was found that electron backscatter diffraction offers a variety of information that light optical microscopy cannot deliver, particularly regarding the prior austenite grain structure. Grain sizes of the primary dendrites, the prior austenite grains and the martensitic structure can be measured with a combination of these techniques.
Kurzfassung
Bei der Entwicklung von Schweißzusätzen werden für thermomechanisch behandelte oder vergütete Stähle mit stetig steigender Festigkeit und Zähigkeit entsprechend geeignete mechanische Gütewerte gefordert. Ein martensitisches Gefüge bietet für die Erfüllung solcher Anforderungen auch im reinen Schweißgut vielversprechende Perspektiven. Eine eingehende Gefügecharakterisierung ist unverzichtbar für das Verständnis der Auswirkungen des Gefüges auf die mechanischen Eigenschaften. Diese Arbeit erklärt zusammenfassend, wie Lichtmikroskopie und Elektronenrückstreubeugung genutzt werden können, um ein tieferes Verständnis vollständig martensitischen Schweißgutes zu gewinnen. Es konnte festgestellt werden, dass Elektronenrückstreubeugung eine Vielzahl an Informationen liefert, die die Lichtmikroskopie nicht liefern kann, insbesondere im Bezug auf die ehemalige Austenitkornstruktur. Korngrößen primärer Dendriten, der ehemaligen austenitischen Körner und des martensitischen Gefüges können durch eine Kombination dieser Techniken vermessen werden.
References / Literatur
[1] Johnson, M. O.; Evans, G. M.; Edwards, G.: ISIJ Int.35 (1995) 10, 1222–123110.2355/isijinternational.35.1222Suche in Google Scholar
[2] Bose-Filho, W. W.; Carvalho, A. L. M.; Strangwood, M.: Mater. Charact.58 (2007) 1, 29–3910.1016/j.matchar.2006.03.004Suche in Google Scholar
[3] Keehan, E.; Zachrisson, J.; Karlsson, L.: Sci. Technol. Weld. Join.15 (2010) 3, 233–23810.1179/136217110X12665048207692Suche in Google Scholar
[4] Bajic, N.; Sijacki-Zeravcic, V.; Bobic, B.; Cikara, D.; Arsic, M.: Weld. J.90 (2011) 4, 55s–62sSuche in Google Scholar
[5] Jiang, Q. L.; Li, Y. J.; Wang, J.; Zhang, L.: Mater. Sci. Technol.27 (2011) 10, 1565–156910.1179/026708310X12815992418535Suche in Google Scholar
[6] Sumi, H.; Oi, K.; Yasuda, K.: Weld. World59 (2015) 2, 173–17810.1007/s40194-014-0191-2Suche in Google Scholar
[7] Zhang, T.; Li, Z.; Ma, S.; Kou, S.; Jing, H.: Sci. Technol. Weld. Join.21 (2016) 3, 186–19310.1179/1362171815Y.0000000079Suche in Google Scholar
[8] Evans, G. M.: Weld. J.77 (1998) 6, 239–248Suche in Google Scholar
[9] Wansheng, D.; Yun, P.; Hongjun, X.; Changhong, H.; Zhiling, T.: Mater. Sci. Forum638–642 (2010), 3441–344610.4028/www.scientific.net/MSF.638-642.3441Suche in Google Scholar
[10] Bhadeshia, H. K. D. H.; Honeycombe, R. W. K.: Steels: Microstructure and Properties, 3. Auflage, Butterworth-Heinemann, Oxford, Großbritannien, 200610.1016/B978-075068084-4/50016-9Suche in Google Scholar
[11] Nishiyama, Z.: Martensitic Transformation, Academic Press Inc., London, Großbritannien, 1978Suche in Google Scholar
[12] Krauss, G.; Marder, A. R.: Metall. Trans.2 (1971), 2343–235710.1007/BF02814873Suche in Google Scholar
[13] Krauss, G.: Mater. Sci. Eng. A273–275 (1999) 7, 40–57Suche in Google Scholar
[14] Cohen, M.: Trans. TMS–AIME224 (1962), 638–657Suche in Google Scholar
[15] Kluken, A. O.; Grong, Ø; Hjelen, J.: Metall. Trans. A22 (1991) 3, 657–66310.1007/BF02670288Suche in Google Scholar
[16] Dingley, D. J.; Randle, V.: J. Mater. Sci.27 (1992), 4545–456610.1007/BF01165988Suche in Google Scholar
[17] Hall, M. G.; Aaronson, H. I.: Metall. Mater. Trans. A25 (1994), 1923–193110.1007/BF02649040Suche in Google Scholar
[18] Bouyne, E.; Flower, H. M.; Lindley, T. C.; Pineau, A.: Scr. Mater.39 (1998) 3, 295–30010.1016/S1359-6462(98)00170-5Suche in Google Scholar
[19] Gourgues, A.-F.; Flower, H. M.; Lindley, T. C.: Mater. Sci. Technol.16 (2000) 1, 26–4010.1179/026708300773002591Suche in Google Scholar
[20] Morito, S.; Tanaka, H.; Konishi, R.; Furuhara, T.; Maki, T.: Acta Mater.51 (2003), 1789–179910.1016/S1359-6454(02)00577-3Suche in Google Scholar
[21] Furuhara, T.; Kawata, H.; Morito, S.; Maki, T.: Mater. Sci. Eng. A431 (2006) 1–2, 228–236 10.1016/j.msea.2006.06.032Suche in Google Scholar
[22] Morito, S.; Adachi, Y.; Ohba, T.: Mater. Trans.50 (2009) 8, 1919–192310.2320/matertrans.MRA2008409Suche in Google Scholar
[23] Du, C.; Hoefnagels, J. P. M.; Vaes, R.; Geers, M. G. D.: Scr. Mater.116 (2016), 117–12110.1016/j.scriptamat.2016.01.043Suche in Google Scholar
[24] Vanovsek, W.; Bernhard, C.; Fiedler, M.; Posch, G.: Weld. World57 (2013) 1, 73–8310.1007/s40194-012-0021-3Suche in Google Scholar
[25] Vanovsek, W.; Bernhard, C.; Fiedler, M.; Schnitzer, R.: Weld. World57 (2015) 5, 665–674Suche in Google Scholar
[26] LePera, F. S.: JOM32 (1980) 3, 38–3910.1007/BF03354553Suche in Google Scholar
[27] Schwartz, A. J.; Kumar, M.; Adams, B. L.; FieldD. P.: Electron Backscatter Diffraction in Materials Science, 2. Auflage, Springer US, Boston, USA, 200910.1007/978-0-387-88136-2Suche in Google Scholar
[28] Humphreys, F. J.: J. Mater. Sci.36 (2001) 16, 3833–385410.1023/A:1017973432592Suche in Google Scholar
[29] Petzow, G.: Metallographic Etching, 2. Auflage, ASM International, Materials Park (Ohio), USA, 1999Suche in Google Scholar
[30] Schacht, E.; Richter, J.: Prakt. Met.35 (1998) 7, 384–395Suche in Google Scholar
[31] Haslberger, P.; Ernst, W.; Schnitzer, R.: BHM161 (2016) 7, 321–324Suche in Google Scholar
[32] Abbasi, M.; Nelson, T. W.; Sorensen, C. D.; Wei, L.: Mater. Charact.66 (2012), 1–810.1016/j.matchar.2012.01.010Suche in Google Scholar
[33] Cayron, C.; Artaud, B.; Briottet, L.: Mater. Charact.57 (2006) 4–5, 386–401 10.1016/j.matchar.2006.03.008Suche in Google Scholar
[34] Cayron, C.: J. Appl. Crystallogr.40 (2007) 6, 1183–118810.1107/S0021889807048777Suche in Google Scholar PubMed PubMed Central
[35] Greninger, A. B.; Troiano, A. R.: Trans. AIME185 (1949), 590–59810.1007/BF03398900Suche in Google Scholar
[36] Weyand, S.; Britz, D.; Rupp, D.; Mücklich, F.: Mater. Perform. Charact.4 (2015) 3, 322–340Suche in Google Scholar
[37] Haslberger, P.; Ernst, W.; Schnitzer, R.: Sci. Technol. Weld. Join.22 (2017) 4, 336–34210.1080/13621718.2016.1240980Suche in Google Scholar
© 2017, Carl Hanser Verlag, München
Artikel in diesem Heft
- Contents/Inhalt
- Contents
- Editorial
- Editorial
- Technical Contributions/Fachbeiträge
- 30 Years of Component Metallography in the DGM Materialography Technical Committee
- Microstructural Characterization of Martensitic All-Weld Metal Samples
- Effects of Sintering Temperature and Time on the Properties of Al-Cu PM Alloy
- Failure Analysis
- Intergranular Corrosion in Unserviced Austenitic Stainless Steel Pipes Made of Alloy 904L
- Meeting Diary/Veranstaltungskalender
- Meeting Diary
Artikel in diesem Heft
- Contents/Inhalt
- Contents
- Editorial
- Editorial
- Technical Contributions/Fachbeiträge
- 30 Years of Component Metallography in the DGM Materialography Technical Committee
- Microstructural Characterization of Martensitic All-Weld Metal Samples
- Effects of Sintering Temperature and Time on the Properties of Al-Cu PM Alloy
- Failure Analysis
- Intergranular Corrosion in Unserviced Austenitic Stainless Steel Pipes Made of Alloy 904L
- Meeting Diary/Veranstaltungskalender
- Meeting Diary