Metallographic Examination of Fire Damages in Electronic Equipment
-
K. Reiter
Abstract
Defects in electronic components and defects caused by electronic components are a frequent cause of fire damage. 35 % of examined cases of fire damage are found to be caused by electrical equipment or by the handling of electricity. Fire damage caused by electronic elements and in electronic assemblies may have a multitude of causes. Minor damages occurring during the manufacture of electronic components and assemblies can lead to operational disruptions in electronic devices and to life-threatening situations. In order to reconstruct a fire damage, a complex failure analysis and comprehensive knowledge of the principle of operation of the devices is required. Metallographic target preparation serves to detect and describe faults. Some damage patterns taken from practice are presented and analyzed here.
Kurzfassung
Defekte in und durch elektronische Bauteile sind häufig Ursache für Brandschäden. Die Ursache in 35 % untersuchter Brandschäden ist in elektrischen Anlagen oder im Umgang mit Strom zu finden. Für Brandschäden durch Elektronik und in elektronischen Baugruppen gibt es eine Vielzahl von Ursachen. Kleine Schäden in der Fertigung von elektronischen Bauteilen und Baugruppen können zu Störungen im Betrieb elektronischer Geräte und zu lebensgefährlichen Situationen führen. Um Brandschäden zu rekonstruieren, ist eine aufwändige Fehleranalyse und umfassende Kenntnis der Funktionsweise der Geräte erforderlich. Metallographische Zielpräparation wird zur Fehlerfindung und Beschreibung eingesetzt. Einige Schadensbilder aus der Praxis werden vorgestellt und analysiert.
References / Literatur
[1] http://www.brand-feuer.de/index.php/Elektrostatische_EntladungSuche in Google Scholar
[2] IPC A610 Kapitel 3Suche in Google Scholar
[3] Automobil-Elektronik Februar 2010 Christoph Thienel, BoschSuche in Google Scholar
[4] „Stress kann tödlich sein. Unerklärlichen Steuergeräteausfällen auf der Spur“ www.krafthand.de Thomas MareisSuche in Google Scholar
© 2017, Carl Hanser Verlag, München
Artikel in diesem Heft
- Contents/Inhalt
- Contents
- Editorial
- Editorial
- Technical Contributions/Fachbeiträge
- Metallographic Examination of Fire Damages in Electronic Equipment
- The Microstructure and Properties of Sr-Modified Al-3Si-0.45Mg-0.45Cu-0.2Sc-0.2Zr Cast Alloy
- Damage on Roller Bearing Races and Gear Teeth – Classification and Methods of Analysis
- Meeting Diary/Veranstaltungskalender
- Meeting Diary
Artikel in diesem Heft
- Contents/Inhalt
- Contents
- Editorial
- Editorial
- Technical Contributions/Fachbeiträge
- Metallographic Examination of Fire Damages in Electronic Equipment
- The Microstructure and Properties of Sr-Modified Al-3Si-0.45Mg-0.45Cu-0.2Sc-0.2Zr Cast Alloy
- Damage on Roller Bearing Races and Gear Teeth – Classification and Methods of Analysis
- Meeting Diary/Veranstaltungskalender
- Meeting Diary