Analysis of Crack Propagation, Determination of Dynamic Strength and Metallographic Examination / Hardness Test using the Example of a 25 CrMo 4 Monobloc Tubular Shaft
-
A. Lietz
Abstract
After performing an alternating load test for several monobloc tubular shafts (so called MTS) a fractographical evaluation with subsequent metallographic examination as well as a review of the heat treatment according to drawing requirements were carried out on a test component which had reached the lowest number of cycles.
An example is used to present a typical examination procedure in a quality laboratory which helps to ensure high product quality in a automotive supplier company and is supposed to highlight the close connection to and support for elaborate bench tests through the instrument of metallography. Besides the fractographical determination of the damage origin, an evaluation of heat treatment and microstructural development of the components is prerequisite for assessing the examination results.
Kurzfassung
Nach der Durchführung eines Wechsellast-Tests an mehreren Monoblock-Rohrwellen (sog. MTS) wurde an einem Test-Teil, das die niedrigste Anzahl von Zyklen erreicht hatte, eine fraktographische Bewertung mit anschließender metallographischer Untersuchung sowie eine Überprüfung der Wärmebehandlung nach Zeichnungsvorgaben vorgenommen.
Anhand dieses Beispiels soll ein typischer Untersuchungsablauf in einem Qualitätslabor präsentiert werden, der zur Gewährleistung einer hohen Produktqualität in einem Automobilzulieferunternehmen beiträgt und die enge Verbindung und Unterstützung von aufwendigen Prüfstandversuchen mit dem Instrument der Metallographie verdeutlichen soll. Voraussetzung für eine Bewertung der Untersuchungsergebnisse der Prüfstandtests ist neben der fraktographischen Bestimmung des Schadensursprungs eine Beurteilung von Wärmebehandlung und Gefügeausbildung der Komponenten.
© 2016, Carl Hanser Verlag, München
Articles in the same Issue
- Contents/Inhalt
- Contents
- Editorial
- Editorial
- Technical Contributions/Fachbeiträge
- Analysis of Crack Propagation, Determination of Dynamic Strength and Metallographic Examination / Hardness Test using the Example of a 25 CrMo 4 Monobloc Tubular Shaft
- Development of HT-Brazing Systems for Non-Similar Material Composites
- Cause of Damage – Hot Cracking
- Failure of Hot-Dip Galvanized Steel Parts
- Meeting Diary/Veranstaltungskalender
- Meeting Diary
Articles in the same Issue
- Contents/Inhalt
- Contents
- Editorial
- Editorial
- Technical Contributions/Fachbeiträge
- Analysis of Crack Propagation, Determination of Dynamic Strength and Metallographic Examination / Hardness Test using the Example of a 25 CrMo 4 Monobloc Tubular Shaft
- Development of HT-Brazing Systems for Non-Similar Material Composites
- Cause of Damage – Hot Cracking
- Failure of Hot-Dip Galvanized Steel Parts
- Meeting Diary/Veranstaltungskalender
- Meeting Diary