Impact of Phase Distribution on the Fracture Toughness of High Temperature Resistant Mo-Si-B Alloys

  • J. Becker und M. Krüger
Veröffentlicht/Copyright: 3. Juni 2015
Veröffentlichen auch Sie bei De Gruyter Brill
Manuskript einreichen Informationen für Autor*innen
Practical Metallography
Aus der Zeitschrift Practical Metallography Band 52 Heft 6

Abstract

Due to their high melting point and good creep resistance, Mo-Si-B alloys have the potential to be used as structural materials at extremely high temperatures in the future. Apart from the relatively ductile Mo solid solution, three-phase molybdenum-based alloys including the intermetallic phases Mo3Si und Mo5SiB2, which enable low fracture toughness, especially at room temperature. A promising approach for fracture toughness improvement consists in the production of a microstructure in which the intermetallic phases are embedded in the ductile Mo solid solution matrix. This paper looks at different powder- and ingot-metallurgical production processes and the resulting microstructures. Particular attention will be paid to the impact of structural component size and phase distribution on the fracture toughness at room temperature.

Kurzfassung

Mo-Si-B-Legierungen besitzen bedingt durch ihren hohen Schmelzpunkt sowie die gute Kriechbeständigkeit das Potential, zukünftig als Konstruktionswerkstoffe bei extrem hohen Temperaturen eingesetzt zu werden. Dreiphasige Molybdänbasislegierungen weisen neben dem relativ duktilen Mo-Mischkristall die intermetallischen Phasen Mo3Si und Mo5SiB2 auf, die vor allem bei Raumtemperatur für eine geringe Bruchzähigkeit sorgen. Ein vielversprechender Ansatz zur Verbesserung der Bruchzähigkeit besteht in der Herstellung einer Mikrostruktur, in der die intermetallischen Phasen in der duktilen Mo-Mischkristallmatrix eingebettet sind. In diesem Artikel werden verschiedene pulver- und schmelzmetallurgische Herstellungsprozesse und die daraus resultierenden Mikrostrukturen betrachtet. Dabei wird besonders auf den Einfluss der Größe der Gefügebestandteile und der Phasenverteilung auf die Bruchzähigkeit bei Raumtemperatur eingegangen.

Translation: M. Lackas

References / Literatur

[1] Dimiduk, D.M.;Perepezko, J. H.: MRS Bull. 28 (2003), 639–645. 10.1557/mrs2003.191Suche in Google Scholar

[2] Jackson, J.;Olson, D.;Mishra, B.;Lasseigne-Jackson, A.: Int.J. HydrogenEnergy, 32 (2007), 16, 37891–3796. 10.1016/j.ijhydene.2006.08.053Suche in Google Scholar

[3] Berczik, D. M.: U.S. Patents No. 5595616 and 5693156, 1997.Suche in Google Scholar

[4] Krüger, M.;Franz, S.;Saage, H.;Heilmaier, M.;Schneibel, J.H.;Jéhanno, P.;Böning, M.;Kestler, H.: Intermetallics, 16 (2008), 7, 933–941. 10.1016/j.intermet.2008.04.015Suche in Google Scholar

[5] Nieh, T;Wang, J.;Liu, C.: Intermetallics, 9 (2001), 73–79. 10.1016/S0966-9795(00)00098-4Suche in Google Scholar

[6] Parthasarathy, T. A.;Mendiratta, M. G.;Dimiduk, D. M.: Acta Mater., 50 (2002), 1857–1868. 10.1016/S1359-6454(02)00039-3Suche in Google Scholar

[7] Kumar, K.S.;Alur, A.P.: Intermetallics15 (2007), 5–6, 687–693. 10.1016/j.intermet.2006.10.008Suche in Google Scholar

[8] Mousa, M.;Wanderka, N.;Timpel, M.;Singh, S.;Krüger, M.;Heilmaier, M.;Banhart, J.: Ultramicroscopy, 111 (2011), 6, 706–10.10.1016/j.ultramic.2010.12.002Suche in Google Scholar PubMed

[9] Krüger, M.;Schliephake, D.;Jain, P.;Kumar, K. S.;Schumacher, G.;Heilmaier, M.: JOM65 (2012), 2, 301–306.10.1007/s11837-012-0475-1Suche in Google Scholar

[10] Palmqvist, S.: Arch. für das Eisenhüttenwesen9 (1962), 629–634.10.1002/srin.196203379Suche in Google Scholar

[11] Quinn, G.D.;Bradt, R.C.: J. Am. Ceram. Soc.90 (2007), 3, 673–680. 10.1111/j.1551-2916.2006.01482.xSuche in Google Scholar

[12] Li, Z.;Ghosh, A.;Kobayashi, A.S.;Bradt, R.C.: J. Am. Ceram. Soc.72 (1989), 6, 904–911.Suche in Google Scholar

[13] Sturm, D.;Heilmaier, M.;Schneibel, J. H.;Jéhanno, P.;Skrotzki, B.;Saage, H.: Mater. Sci. Eng. A463 (2007), 1 2, 107–114. 10.1016/j.msea.2006.07.153Suche in Google Scholar

[14] Ito, K.;Ihara, K.;Tanaka, K.;Fujikura, M.;Yamaguchi, M.: Intermetallics9 (2001), 7, 591–602. 10.1016/S0966-9795(01)00049-8Suche in Google Scholar

[15] Ihara, K.;Ito, K.;Tanaka, K.;Yamaguchi, M.: Mater. Sci. Eng. A329–331 (2002), 222–227.10.1016/S0921-5093(01)01575-1Suche in Google Scholar

[16] Quinn, G.D.;Bradt, R.C.: J. Am. Ceram. Soc.90 (2007), 3, 673–680. 10.1111/j.1551-2916.2006.01482.xSuche in Google Scholar

[17] Wright, R. N.;Schneibel, J. H.;Kramer, M. J.: Intermetallics9 (2001), 25–31. 10.1016/S0966-9795(01)00071-1Suche in Google Scholar

[18] Kruzic, J. J.;Schneibel, J. H.;Ritchie, R. O.: Scripta Mater. 50 (2004), 4, 459–464. 10.1016/j.scriptamat.2003.11.002Suche in Google Scholar

[19] Schneibel, J. H.;Kramer, M. J.;Easton, D. S.: Scripta Mater. 46 (2002), 217–221. 10.1016/S1359-6462(01)01227-1Suche in Google Scholar

[20] Krüger, M.;Jain, P.;Kumar, K. S.;Heilmaier, M.: Intermetallics48 (2014), 10–18. 10.1016/j.intermet.2013.10.025Suche in Google Scholar

[21] Saage, H.;Krüger, M.;Sturm, D.;Heilmaier, M.;Schneibel, J.H.;George, E.;Heatherly, L.;Somsen, C.;Eggeler, G.;Yang, Y.: Acta Mater. 57 (2009), 13, 3895–3901. 10.1016/j.actamat.2009.04.040Suche in Google Scholar

[22] Choe, H.;Schneibel, J. H.;Ritchie, R. O.: Metall. and Mater. Transactions A34 (2003), 225–239. 10.1007/s11661-003-0325-4Suche in Google Scholar

[23] Ito, K.;Kumagai, M.;Hayashi, T.;Yamaguchi, M.: Scripta Mater. 49 (2003), 4, 285–290. 10.1016/S1359-6462(03)00289-6Suche in Google Scholar

[24] Jéhanno, P.;Heilmaier, M.;Kestler, H.: Intermetallics12 (2004), 7–9, 1005–1009. 10.1016/j.intermet.2004.03.006Suche in Google Scholar

[25] Li, B.;Zhang, G.;Feng, J.;Shuai, R.;Gang, L.;Jun, S.: J. Alloys Compd.609 (2014), 80–85. 10.1016/j.jallcom.2014.04.141Suche in Google Scholar

Received: 2014-10-02
Accepted: 2015-03-16
Published Online: 2015-06-03
Published in Print: 2015-06-15

© 2015, Carl Hanser Verlag, München

Artikel in diesem Heft

  1. Contents/Inhalt
  2. Contents
  3. Editorial
  4. Editorial
  5. Technical Contributions/Fachbeiträge
  6. Impact of Phase Distribution on the Fracture Toughness of High Temperature Resistant Mo-Si-B Alloys
  7. The Applicability of Nanoindentation for the Examination of Microstructured Areas in CP Titanium Samples
  8. Influence of the Sample Preparation Technique on the μ Phase Fraction Analysis in a Fe-25Co-15Mo Alloy by Means of XRD
  9. Uncharacteristic Circumferential TMF Cracking in a Heavy-duty Stationary Gas Turbine Engine Burner Outlet
  10. Meeting Diary/Veranstaltungskalender
  11. Meeting Diary
https://doi.org/10.3139/147.110322

Artikel in diesem Heft

  1. Contents/Inhalt
  2. Contents
  3. Editorial
  4. Editorial
  5. Technical Contributions/Fachbeiträge
  6. Impact of Phase Distribution on the Fracture Toughness of High Temperature Resistant Mo-Si-B Alloys
  7. The Applicability of Nanoindentation for the Examination of Microstructured Areas in CP Titanium Samples
  8. Influence of the Sample Preparation Technique on the μ Phase Fraction Analysis in a Fe-25Co-15Mo Alloy by Means of XRD
  9. Uncharacteristic Circumferential TMF Cracking in a Heavy-duty Stationary Gas Turbine Engine Burner Outlet
  10. Meeting Diary/Veranstaltungskalender
  11. Meeting Diary
Jetzt anmelden und 20% sparen
Institutioneller Zugang
Wie funktioniert Authentifizierung?
Haben Sie eine Idee, wie wir unsere Website verbessern können?
Bitte schreiben Sie uns.
© 2025 De Gruyter Brill
Heruntergeladen am 9.12.2025 von https://www.degruyterbrill.com/document/doi/10.3139/147.110322/html
Button zum nach oben scrollen