Synthesis of REE and Y phosphates by Pb-free flux methods and their utilization as standards for electron microprobe analysis and in design of monazite chemical U-Th-Pb dating protocol
-
D.J. Cherniak
,
J. Pyle
Abstract
(REE,Y) phosphates were synthesized in a 1 atm furnace by ß ux-growth methods involving Pb-free ß uxes. Microcrystalline (REE,Y) phosphate was precipitated from a solution of (REE,Y) chlorides or nitrates plus ammonium dihydrogen phosphate, and mixed with a M2CO3 (M = Li or Na)-MoO3 flux (75:25:2 molar ratio M2CO3:MoO3:REEPO4). Crystal growth was achieved over the temperature range 1350.870 °C, with extended (15 h) high-T soaking, and cooling rates of 3 °C/h. Crystals grown by this method are clear, generally inclusion-free, up to several mm in length, and are easily extracted from the water-soluble flux. Crystal size and habit are influenced by the alkali component of the flux. Successful LREE phosphate synthesis is favored by both Li-and Na-bearing fluxes, whereas better results for Y and MREE-HREE phosphates were achieved with Na-bearing fluxes. Li-bearing fluxes produced LREE phosphates with an overall platy habit, in contrast to more prismatic-to-equant LREEMREE phosphates produced with Na-bearing fluxes.
Structural refinements of single-crystal X-ray diffraction data show that LREEPO4 (La-Gd) crystallize with the monoclinic monazite structure, and HREEPO4 (Tb-Lu) plus YPO4 crystallize with the tetragonal xenotime structure. Element distribution maps of synthetic REEPO4 reveal homogeneous distribution of REE and P at grain-size scale and below, and both wavelength-dispersive (WD) spectral scans and quantitative electron microprobe analyses show no other elements (e.g., flux inclusions) present at significant levels.
The synthetic phosphates grown with this method are suitable for use as electron microprobe standards and as compositionally simplified monazite analogs for use in the design of U-Th-Pb chemical dating protocols. WD scans of synthetic unary and ternary (La-Ce-Nd) phosphates reveal that Ar X-ray detectors produce non-filterable LREE escape peaks with pulse-height analyzers optimized for Pb analysis. Such LREE escape peaks complicate collection of both U and Pb peak and background counts. Due to the larger energy difference between LREE peaks and Xe (relative to Ar), LREE escape peaks produced in Xe detectors are filterable with pulse height analyzers, resulting in LREE-free spectra over the wavelength range sampled for Pb peak and background collection.
© 2015 by Walter de Gruyter Berlin/Boston
Articles in the same Issue
- The origin of the color of pearls in iridescence from nano-composite structures of the nacre
- “Invisible„ gold revealed: Direct imaging of gold nanoparticles in a Carlin-type deposit
- Behavior of cation vacancy in kenotetrahedral Cr-spinels from Albanian eastern belt ophiolites
- Displacement and strain fields around a [100] dislocation in olivine measured to sub-angstrom accuracy
- Kiglapait mineralogy IV: The augite series
- Metasomatic formation of kosmochlor-bearing diopside in peridotite xenoliths from North Island, New Zealand
- Determination of standard thermodynamic properties of sulfides in the Ag-Au-S system by means of a solid-state galvanic cell
- Hydroxyl ordering in igneous apatite
- Accommodation of the carbonate ion in apatite: An FTIR and X-ray structure study of crystals synthesized at 2–4 GPa
- Mg/Si ratios of aqueous fluids coexisting with forsterite and enstatite based on the phase relations in the Mg2SiO4-SiO2-H2O system
- The activity of silica, water, and the equilibration of intermediate and silicic magmas
- The CO2–H2O system: IV. Empirical, isothermal equations for representing vapor-liquid equilibria at 110–350 °C, P ≤ 150 MPa
- Repercussions of size heterogeneity on the measurement of specific surface areas of colloidal minerals: Combination of macroscopic and microscopic analyses
- The crystal-structure of synthetic NaNa2Mg5Si8O21(OH)3, a triclinic C1̄ amphibole with a triple-cell and excess hydrogen
- High-pressure phase transitions in Ca0.2Sr0.8Al2Si2O8feldspar
- Phase transition of Ca-perovskite and stability of Al-bearing Mg-perovskite in the lower mantle
- Mineralogy and petrology of a mullite-bearing pseudotachylyte: Constraints on the temperature of coseismic frictional fusion
- New developments in two-feldspar thermometry
- Ordered distribution of Au and Ag in the crystal structure of muthmannite, AuAgTe2, a rare telluride from Sacarîmb, western Romania
- Polytypism of cookeite in low-grade metapelites of the Cameros Basin, Spain: Lack of correlation of well-ordered polytypes with pressure
- Evolution of mineral compositions during eclogitization of subducting basaltic crust
- Mass balance during retrogression of eclogite-facies minerals in the Rongcheng eclogite, eastern Sulu ultrahigh-pressure terrane, China
- Synthesis of REE and Y phosphates by Pb-free flux methods and their utilization as standards for electron microprobe analysis and in design of monazite chemical U-Th-Pb dating protocol
- The chemistry and crystal structure of okanoganite-(Y) and comparison with vicanite-(Ce)
- An automated system for phase identification and quantitative composition determination using the electron microprobe: Theory and applications
- Piston-cylinder calibration at 400 to 500 MPa: A comparison of using water solubility in albite melt and NaCl melting
- Letter. Comparative planetary mineralogy: V/(Cr + Al) systematics in chromite as an indicator of relative oxygen fugacity
- Letter. Porous titanosilicate nanorods in the structure of yuksporite, (Sr,Ba)2K4(Ca,Na)14(⃞,Mn,Fe) {(Ti,Nb)4(O,OH)4[Si6O17]2[Si2O7]3}(H2O,OH)n, resolved using synchrotron radiation
Articles in the same Issue
- The origin of the color of pearls in iridescence from nano-composite structures of the nacre
- “Invisible„ gold revealed: Direct imaging of gold nanoparticles in a Carlin-type deposit
- Behavior of cation vacancy in kenotetrahedral Cr-spinels from Albanian eastern belt ophiolites
- Displacement and strain fields around a [100] dislocation in olivine measured to sub-angstrom accuracy
- Kiglapait mineralogy IV: The augite series
- Metasomatic formation of kosmochlor-bearing diopside in peridotite xenoliths from North Island, New Zealand
- Determination of standard thermodynamic properties of sulfides in the Ag-Au-S system by means of a solid-state galvanic cell
- Hydroxyl ordering in igneous apatite
- Accommodation of the carbonate ion in apatite: An FTIR and X-ray structure study of crystals synthesized at 2–4 GPa
- Mg/Si ratios of aqueous fluids coexisting with forsterite and enstatite based on the phase relations in the Mg2SiO4-SiO2-H2O system
- The activity of silica, water, and the equilibration of intermediate and silicic magmas
- The CO2–H2O system: IV. Empirical, isothermal equations for representing vapor-liquid equilibria at 110–350 °C, P ≤ 150 MPa
- Repercussions of size heterogeneity on the measurement of specific surface areas of colloidal minerals: Combination of macroscopic and microscopic analyses
- The crystal-structure of synthetic NaNa2Mg5Si8O21(OH)3, a triclinic C1̄ amphibole with a triple-cell and excess hydrogen
- High-pressure phase transitions in Ca0.2Sr0.8Al2Si2O8feldspar
- Phase transition of Ca-perovskite and stability of Al-bearing Mg-perovskite in the lower mantle
- Mineralogy and petrology of a mullite-bearing pseudotachylyte: Constraints on the temperature of coseismic frictional fusion
- New developments in two-feldspar thermometry
- Ordered distribution of Au and Ag in the crystal structure of muthmannite, AuAgTe2, a rare telluride from Sacarîmb, western Romania
- Polytypism of cookeite in low-grade metapelites of the Cameros Basin, Spain: Lack of correlation of well-ordered polytypes with pressure
- Evolution of mineral compositions during eclogitization of subducting basaltic crust
- Mass balance during retrogression of eclogite-facies minerals in the Rongcheng eclogite, eastern Sulu ultrahigh-pressure terrane, China
- Synthesis of REE and Y phosphates by Pb-free flux methods and their utilization as standards for electron microprobe analysis and in design of monazite chemical U-Th-Pb dating protocol
- The chemistry and crystal structure of okanoganite-(Y) and comparison with vicanite-(Ce)
- An automated system for phase identification and quantitative composition determination using the electron microprobe: Theory and applications
- Piston-cylinder calibration at 400 to 500 MPa: A comparison of using water solubility in albite melt and NaCl melting
- Letter. Comparative planetary mineralogy: V/(Cr + Al) systematics in chromite as an indicator of relative oxygen fugacity
- Letter. Porous titanosilicate nanorods in the structure of yuksporite, (Sr,Ba)2K4(Ca,Na)14(⃞,Mn,Fe) {(Ti,Nb)4(O,OH)4[Si6O17]2[Si2O7]3}(H2O,OH)n, resolved using synchrotron radiation