Vapor-phase diethyl oxalate pretreatment of wood chips: Part 1. Energy savings and improved pulps
-
William Kenealy
Published/Copyright:
April 26, 2007
Abstract
Diethyl oxalate (DEO) was injected into a digester containing wood chips (pine, spruce, or aspen) preheated to 130–140°C and held for 30 min at the same temperature. When mechanical pulps were produced from these pretreated chips, savings in electrical refiner energy could be achieved. For southern yellow pine (Pinus taeda), the electrical refiner energy required to produce pulps with Canadian standard freeness (CSF) of 100 ml was 38– 55% less than for an untreated control. Energy savings were also observed for aspen (Populus spp.) and spruce (Picea spp.). DEO-treated pine handsheets showed a 26% improvement in tear index compared with a control at 100 ml CSF. Under the pretreatment conditions de-scribed, DEO rapidly vaporizes, reacts with water already present in the chip, and forms an oxalic acid (OA) solution. Reported handsheet properties and energy savings for pine chips treated with a solution of OA are similar to DEO-treated handsheets. It can be concluded that the effect of DEO treatment is due to reactions catalyzed by OA.
Keywords: energy savings; ester; mechanical; oxalate; oxalic; refining; thermomechanical; vapor phase
Received: 2006-4-27
Accepted: 2007-1-19
Published Online: 2007-04-26
Published in Print: 2007-5-1
©2007 by Walter de Gruyter Berlin New York
You are currently not able to access this content.
You are currently not able to access this content.
Articles in the same Issue
- To all readers, authors and subscribers
- Vapor-phase diethyl oxalate pretreatment of wood chips: Part 1. Energy savings and improved pulps
- Vapor-phase diethyl oxalate pretreatment of wood chips: Part 2. Release of hemicellulosic carbohydrates
- Size exclusion chromatographic and UV-VIS absorption analyses of unbleached and bleached softwood kraft pulps using LiCl/1,3-dimethyl-2-imidazolidinone as a solvent
- A new method for the titration of free phenolic groups in pulps
- Adsorption of water-soluble organic dyes on ferrofluid-modified sawdust
- Mechanical properties and creep behavior of lyocell fibers by nanoindentation and nano-tensile testing
- Deformation behavior of wet lignocellulosic fibers
- Changes in physical, mechanical and chemical properties of wood during sterilisation by gamma radiation
- Penetration of poly(ethylene glycol) into wood cell walls of red pine
- Transverse mechanical behaviour and moisture absorption of waterlogged archaeological wood from the Vasa ship
- Determination of residual stress in bonded wood components
- Decohesion of glue bonds in wood connections
- Delamination assessment after drilling medium-density fibreboard (MDF) by digital image analysis
- Effects of thinning and fertilisation on tracheid dimensions and lignin content of Norway spruce
- Detection of β-1-4-galactan in compression wood of Sitka spruce [Picea sitchensis (Bong.) Carrière] by immunofluorescence
- Laboratory and outdoor water repellency and dimensional stability of southern pine sapwood treated with a waterborne water repellent made from resin acids
- Evidence of fungicidal and termicidal properties of Prunus africana heartwood extractives
- The effectiveness of silica treatments against wood-boring invertebrates
- Sap-staining fungi from logs and boards of two commercially important pines in Korea
- Improved quantitative determination of benzalkonium chloride in treated wood by liquid chromatography
- Obituary Anders Björkman (1920–2006)
Keywords for this article
energy savings;
ester;
mechanical;
oxalate;
oxalic;
refining;
thermomechanical;
vapor phase
Articles in the same Issue
- To all readers, authors and subscribers
- Vapor-phase diethyl oxalate pretreatment of wood chips: Part 1. Energy savings and improved pulps
- Vapor-phase diethyl oxalate pretreatment of wood chips: Part 2. Release of hemicellulosic carbohydrates
- Size exclusion chromatographic and UV-VIS absorption analyses of unbleached and bleached softwood kraft pulps using LiCl/1,3-dimethyl-2-imidazolidinone as a solvent
- A new method for the titration of free phenolic groups in pulps
- Adsorption of water-soluble organic dyes on ferrofluid-modified sawdust
- Mechanical properties and creep behavior of lyocell fibers by nanoindentation and nano-tensile testing
- Deformation behavior of wet lignocellulosic fibers
- Changes in physical, mechanical and chemical properties of wood during sterilisation by gamma radiation
- Penetration of poly(ethylene glycol) into wood cell walls of red pine
- Transverse mechanical behaviour and moisture absorption of waterlogged archaeological wood from the Vasa ship
- Determination of residual stress in bonded wood components
- Decohesion of glue bonds in wood connections
- Delamination assessment after drilling medium-density fibreboard (MDF) by digital image analysis
- Effects of thinning and fertilisation on tracheid dimensions and lignin content of Norway spruce
- Detection of β-1-4-galactan in compression wood of Sitka spruce [Picea sitchensis (Bong.) Carrière] by immunofluorescence
- Laboratory and outdoor water repellency and dimensional stability of southern pine sapwood treated with a waterborne water repellent made from resin acids
- Evidence of fungicidal and termicidal properties of Prunus africana heartwood extractives
- The effectiveness of silica treatments against wood-boring invertebrates
- Sap-staining fungi from logs and boards of two commercially important pines in Korea
- Improved quantitative determination of benzalkonium chloride in treated wood by liquid chromatography
- Obituary Anders Björkman (1920–2006)