High Temperature Corrosion of Steel X15CrNiSi25-21 (1.4841) in a Mixed Gas Atmosphere – Sample Preparation and Damage Mechanism
-
A. Schmid
Abstract
Steel 1.4841 was tested as a possible reactor material for a cracking process of anthropogenic resources under simulated laboratory conditions at 680 °C. The gas atmosphere present in this process contains HCl as well as H2S.
In order to evaluate the corrosion behavior, metallographic sections were prepared from the corroded samples. The preparation for the SEM/EDS examination had to be performed under exclusion of water, as otherwise the readily water-soluble metal chlorides would not have been detected.
A layered, porous structure of the corrosion products (oxides and sulfides of Cr) could be observed. The lowermost layer contains chromium and iron chlorides. Nickel could not be found in any of the corrosion products.
In order to estimate the long-term resistance, aging tests were performed at 680 °C in an inert atmosphere for up to 1600 h before the actual corrosion tests. The formation of Cr23C6 and also of Ϭ phase could be evidenced by TEM. Compared to the non-aged samples, the chromium depletion caused by aging resulted in slightly increased corrosion rates.
Kurzfassung
Der Stahl 1.4841 wurde als möglicher Reaktorwerkstoff, für einen Crackprozess von anthropogenen Ressourcen unter simulierten Laborbedingungen, bei 680 °C getestet. Die auftretende Gasatmosphäre enthält sowohl HCl als auch H2S.
Zur Evaluierung des Korrosionsverhaltens wurden metallographische Schliffe der korrodierten Proben angefertigt. Um diese mittels REM/EDX untersuchen zu können, musste die Präparation unter Ausschluss von Wasser stattfinden, da die leicht wasserlöslichen Metallchloride andernfalls nicht erfasst worden wären.
Es wurde ein schichtförmiger, poröser Aufbau der Korrosionsprodukte (Oxide und Sulfide von Cr) nachgewiesen. Die unterste Schicht enthält Chloride von Chrom und Eisen. Nickel wurde in keinem der Korrosionsprodukte gefunden.
Zur Abschätzung der Langzeitbeständigkeit wurden vor den eigentlichen Korrosionsversuchen Auslagerungstests bis zu 1600 h, bei 680 °C, in inerter Atmosphäre, durchgeführt. Es wurde die Bildung von Cr23C6 und auch der Ϭ-Phase mittels TEM nachgewiesen. Die dadurch verursachte Chromverarmung führte im Vergleich zu nicht ausgelagerten Proben, zu leicht erhöhten Korrosionsraten.
References / Literatur
[1] Plastics Europe – the facts 2016: An analysis of the European plastics production, demand and waste date, 2017Suche in Google Scholar
[2] Plastics Europe – the facts 2017: An analysis of the European plastics production, demand and waste date, 2018Suche in Google Scholar
[3] Haanappel, V. A. C.; Fransen, T.; GellingsP. J.: High Temperature Materials and Processes,10 (1992) 67–89. 10.1515/HTMP.1992.10.2.67Suche in Google Scholar
[4] Asteman, H.; Spiegel, M.: Corrosion Science,49 (2007) 3626–3637. 10.1016/j.corsci.2007.03.028Suche in Google Scholar
[5] Schmid, A.; Mori, G.; Haubner, R.; Weil, M.; Hönig, S.: Materials and Corrosion,69 (2018) 1328–1337. 10.1002/maco.201709992Suche in Google Scholar
[6] Schmid, A.; Mori, G.; Hönig, S.; Weil, M.; Strobl, S.; Haubner, R.: Corrosion Science,139 (2018) 76–82. 10.1016/j.corsci.2018.04.042Suche in Google Scholar
[7] White, W. E; Le MayI.: Metallography,3 (1970) 51–60. 10.1016/0026 – 0800(70)90004 – 2Suche in Google Scholar
[8] Pohl, M.; Storz, O.: Z. Metallkd.95 (2004) 631–638. 10.3139/146.017999Suche in Google Scholar
[9] Gajewski, M.; Kasińska, J.: Archives of Foundry Engineering12 (2012) 47–52. 10.2478/v10266–012–0105-ySuche in Google Scholar
[10] Schmid, A.; Mori, G.; Bucher, E.; Haubner, R.: Oxidation of Metals91 (2019) 1–10. 10.1007/s11085–018–9876-zSuche in Google Scholar
© 2019, Carl Hanser Verlag, München
Artikel in diesem Heft
- Contents/Inhalt
- Contents
- Editorial
- Editorial
- Technical Contributions/Fachbeiträge
- Combination of Nanoindentation and Microscopy for the Examination of Aluminum Alloys in Coarse- and Ultrafine-Grained Condition
- Metallographic Contrasting of Weld Joints on Duplex Stainless Steel
- Examination of Oxide Scales Formed During Hot Rolling of Steels
- High Temperature Corrosion of Steel X15CrNiSi25-21 (1.4841) in a Mixed Gas Atmosphere – Sample Preparation and Damage Mechanism
- Meeting Diary/Veranstaltungskalender
- Meeting Diary
Artikel in diesem Heft
- Contents/Inhalt
- Contents
- Editorial
- Editorial
- Technical Contributions/Fachbeiträge
- Combination of Nanoindentation and Microscopy for the Examination of Aluminum Alloys in Coarse- and Ultrafine-Grained Condition
- Metallographic Contrasting of Weld Joints on Duplex Stainless Steel
- Examination of Oxide Scales Formed During Hot Rolling of Steels
- High Temperature Corrosion of Steel X15CrNiSi25-21 (1.4841) in a Mixed Gas Atmosphere – Sample Preparation and Damage Mechanism
- Meeting Diary/Veranstaltungskalender
- Meeting Diary